CN110194838B - 1-芘基官能化聚砜材料及其制备方法 - Google Patents
1-芘基官能化聚砜材料及其制备方法 Download PDFInfo
- Publication number
- CN110194838B CN110194838B CN201910449625.9A CN201910449625A CN110194838B CN 110194838 B CN110194838 B CN 110194838B CN 201910449625 A CN201910449625 A CN 201910449625A CN 110194838 B CN110194838 B CN 110194838B
- Authority
- CN
- China
- Prior art keywords
- polysulfone
- pyrenyl
- functionalized
- solution
- brominated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种具有对溶氧响应的荧光特性的1‑芘基官能化聚砜材料及其制备方法。该1‑芘基官能化聚砜材料的结构式为：
n=84~106。本方法通过铃木反应（Suzuki coupling reaction）将具有荧光活性的1‑芘基官能团偶联于双酚A型聚砜骨架，制得1‑芘基官能化聚砜。本发明制备的1‑芘基官能化聚砜不但具有良好的荧光活性，还具有优越的成膜性能和耐水性能。本发明制备的1‑芘基官能化聚砜的荧光特性对氧气和溶氧具有良好的响应，可用于制备荧光溶氧传感膜，具有良好的应用前景。
Description
技术领域
本发明涉及一种具有对溶氧响应的荧光特性的新型高分子荧光材料及其制备方法，具体涉及一种1-芘基官能化聚砜材料(1-pyrenyl functionalized polysulfone)及其制备方法。
背景技术
荧光溶氧传感器具有操作简单、灵敏度高、响应速度高、测量过程在不消耗氧气等优点，是溶氧检测的主要方案。目前，荧光溶氧传感器通常以分散在有机聚合物或有机改性硅酸盐无机聚合物等主体材料中的荧光染料分子作为探针分子。
荧光染料分子与主体材料的兼容性及其抗溶出性是影响荧光溶氧传感器性能与使用寿命的重要因素。高分子荧光材料具有良好的荧光特性、优越的成膜性能、耐水性能，甚至无需考虑荧光染料与主体材料的相互作用及其主体材料的选择，在荧光传感乃至光电领域都有很好的应用前景。本发明以此为应用背景，制备一种具有对溶氧响应的荧光特性的1-芘基官能化聚砜材料。
发明内容
本发明的目的之一在于提供了一种具有对溶氧响应的荧光特性的1-芘基官能化聚砜材料。
本发明的目的之二在于提供了一种该具有对溶氧响应的荧光特性的1-芘基官能化聚砜材料的制备方法。
为达到上述目的，本发明采用如下技术方案：
一种1-芘基官能化聚砜材料，其特征在于该1-芘基官能化聚砜材料的结构式为：
n＝84～106。
一种制备上述的1-芘基官能化聚砜材料的方法，其特征在于该方法的具体步骤为：
a.将双酚A型聚砜溶于氯仿中，得到透明溶液；在惰性气氛保护下加入催化量的无水三氯化铁后，再缓慢滴加液溴，在80～100℃反应24～36h小时，得到棕红色溶液；所述的聚砜与液溴的质量比为1:1～2；
b.将步骤a所得上述棕红色溶液倾入甲醇中，生成絮状沉淀；分离该絮状沉淀物，用甲醇洗涤至近无色，烘干，得溴化聚砜粗品；将该粗品溶于1,2-二氯乙烷，滤去不溶杂质，得浅黄色滤液；将该浅黄色滤液倾入5倍体积的甲醇中，生成沉淀，将该沉淀物在60℃下干燥，得到精制溴化聚砜，其结构式为：
c.将步骤b所得溴化聚砜和1-芘硼酸溶于四氢呋喃，再加入碳酸铯和高纯水，完全溶解后得到黄色溶液；在惰性气氛保护下，将双(三苯基磷)二氯化钯(II)加入到黄色溶液中，在80～100℃下反应24～36小时，得到深棕色溶液；用氯仿稀释该深棕色溶液，过滤去除不溶杂质，得到浅棕色滤液；将该浅棕色滤液浓缩，加入甲醇，得到絮状沉淀物，将该絮状物洗涤至近无色后烘干，得到淡黄色1-芘基官能化聚砜粉末；所述的溴化聚砜、1-芘硼酸、碳酸铯的质量比为30:25～37:16，四氢呋喃与高纯水的体积比为10：1；所述的双(三苯基磷)二氯化钯(II)与溴化聚砜的质量比为7～10:30。
上述的氯仿与所述深棕色溶液的体积比为5～8:1，甲醇与浓缩后的浅棕色滤液体积比为2～5:1。
本发明成功制备了一种具有对溶氧响应的荧光特性的新型高分子材料——1-芘基官能化聚砜，其创新之处在于利用铃木反应将荧光基团接枝在聚砜骨架上，得到对溶氧具有良好响应的高分子荧光材料。本发明的制备工艺简单，原材料容易得到。重要的是，本发明制备的1-芘基官能化聚砜是新的物质，材料本身及其合成方法未见国内外专利或文献报道。
本发明制备的具有对溶氧响应的荧光特性的高分子荧光材料，其芘基荧光基团与聚砜骨架形成一个更大的共轭体系，对氧气有良好的响应。
附图说明
图1为溴化聚砜、1-芘基官能化聚砜的核磁共振氢谱图；
图2为1-芘基官能化聚砜的氯仿溶液的荧光激发和发射光谱；
图3为1-芘基官能化聚砜对氮气和氧气的荧光响应。
具体实施方法
下面结合实施实例对本发明进行详细说明。
实例一：第一步为溴化聚砜的制备，第二步为1-芘基官能化聚砜的制备。
1.溴化聚砜的制备
在100mL的二颈瓶中，先加入2.6674g聚砜，再加入30mL氯仿作为溶剂，待聚砜完全溶解，充换氮气3次。在氮气流下，加入0.3165g无水三氯化铁后，再缓慢加入液溴(0.85mL)。继续在氮气保护下25℃反应24小时，得棕红色溶液。待反应完全后，将棕红色溶液慢慢倾入甲醇中，生成絮状沉淀。分离沉淀物，并用甲醇洗涤至近无色后，于60℃下烘干。然后，将烘干后的沉淀物重新溶于1,2-二氯乙烷中，滤去不溶物。将滤液倾入甲醇中析出沉淀物，洗涤沉淀物三次。最后，将沉淀物转移到表面皿中，在60℃下干燥24小时，得到白色溴化聚砜粉末。其结构式为：
2.1-芘基官能化聚砜的制备
在25mL的二颈瓶中，依次加入0.3g溴化聚砜，0.2460g 1-芘基硼酸，4mL四氢呋喃。待原料完全溶解后，先后加入0.1629g碳酸铯和0.4mL高纯水。充换氮气4次后，继续在氮气流下保护下加入0.0702g双(三苯基磷)二氯化钯(II)，并在80℃下反应24小时。反应完成后，加入16mL氯仿稀释，滤去不溶物。将滤液转入旋转浓缩器蒸发浓缩后，再用无水甲醇析出沉淀，洗涤三次。最后，在65℃下烘干24小时，得到淡黄色1-芘基官能化聚砜粉末，其结构式为，
实例二：第1步为溴化聚砜的制备，第2步为PSF-g-Py的制备。
1.溴化聚砜的制备
在100mL的二颈瓶中，依次加入2.6674g聚砜和30mL氯仿。待聚砜完全溶解，充换氮气3次。继续在氮气流下，先加入0.3165g无水三氯化铁，再缓慢加入液溴(1.70mL)。在氮气的持续保护下，在25℃反应24小时。反应完成后，得棕红色溶液。将棕红色溶液倾入甲醇中，生成絮状沉淀。分离沉淀物，并用甲醇洗涤至近无色后，于60℃下烘干。然后，将烘干后的沉淀物重新溶解于1,2-二氯乙烷中，过滤除去不溶杂质。将滤液倾入甲醇中析出沉淀，洗涤沉淀物3次。将沉淀物转移到表面皿中，在60℃下干燥24小时，得到白色溴化聚砜粉末。其结构式为，
2.1-芘基官能化聚砜的制备
同实例一实例三：第1步为溴化聚砜的制备，第2步为1-芘基官能化聚砜的制备。
1.溴化聚砜的制备
同实例二
2.1-芘基官能化聚砜的制备
在25mL二颈瓶中，依次加入0.2274g溴化聚砜，0.3690g 1-芘基硼酸，4mL四氢呋喃。待原料完全溶解后，先后加入0.1629g碳酸铯和0.4mL的高纯水。充换氮气4次，并在氮气流下加入0.0702g双(三苯基磷)二氯化钯(II)。在持续的氮气保护下80℃反应24小时，终止反应。向反应产物中加入16mL氯仿，稀释溶液，过滤除去不溶杂质。将滤液旋转蒸发浓缩后，用无水甲醇析出沉淀，洗涤沉淀物三次。最后，将沉淀物在65℃下烘干，得到淡黄色1-芘基官能化聚砜粉末。
荧光光谱表征
这里，采用荧光光谱的方法表征1-芘基官能化聚砜对溶氧响应的荧光特性。
将制备的1-芘基官能化聚砜溶解于氯仿，配制成浓度为2.22mmol·dm-3的溶液。采用RF5301型荧光分光光度计测试溶液的荧光强度，结果如附图2。
为研究1-芘基官能化聚砜对氧气的响应，在两份2.22mmol·dm-3的1-芘基官能化聚砜溶液，分别鼓入氮气和氧气，得到无氧、饱和氧的1-芘基官能化聚砜溶液。采用RF5301型荧光分光光度计分别测量在氮气和氧气条件下的1-芘基官能化聚砜溶液的荧光强度，结果如附图3。
Claims (3)
1.一种1-芘基官能化聚砜材料，其特征在于该1-芘基官能化聚砜材料的结构式为：
n＝84～106。
2.一种制备根据权利要求1所述的1-芘基官能化聚砜材料的方法，其特征在于该方法的具体步骤为：
a.将双酚A型聚砜溶于氯仿中，得到透明溶液；在惰性气氛保护下加入催化量的无水三氯化铁后，再缓慢滴加液溴，在80～100℃反应24～36h小时，得到棕红色溶液；所述的聚砜与液溴的质量比为1:1～2；
b.将步骤a所得上述棕红色溶液倾入甲醇中，生成絮状沉淀；分离该絮状沉淀，用甲醇洗涤至近无色，烘干，得溴化聚砜粗品；将该粗品溶于1,2-二氯乙烷，滤去不溶杂质，得浅黄色滤液；将该浅黄色滤液倾入5倍体积的甲醇中，生成沉淀，将该沉淀在60℃下干燥，得到精制溴化聚砜，其结构式为：
c.将步骤b所得溴化聚砜和1-芘硼酸溶于四氢呋喃，再加入碳酸铯和高纯水，完全溶解后得到黄色溶液；在惰性气氛保护下，将双(三苯基磷)二氯化钯加入到黄色溶液中，在80～100℃下反应24～36小时，得到深棕色溶液；用氯仿稀释该深棕色溶液，过滤去除不溶杂质，得到浅棕色滤液；将该浅棕色滤液浓缩，加入甲醇，得到絮状沉淀物，将该絮状沉淀 物洗涤至近无色后烘干，得到淡黄色1-芘基官能化聚砜粉末；所述的溴化聚砜、1-芘硼酸、碳酸铯的质量比为30:25～37:16，四氢呋喃与高纯水的体积比为10：1；所述的双(三苯基磷)二氯化钯与溴化聚砜的质量比为7～10:30。
3.根据权利要求2所述的方法，其特征在于所述的氯仿与所述深棕色溶液的体积比为5～8:1，甲醇与浓缩后的浅棕色滤液体积比为2～5:1。