CN113430073B - 一种富勒烯手工皂的制备方法 - Google Patents
一种富勒烯手工皂的制备方法 Download PDFInfo
- Publication number
- CN113430073B CN113430073B CN202110627769.6A CN202110627769A CN113430073B CN 113430073 B CN113430073 B CN 113430073B CN 202110627769 A CN202110627769 A CN 202110627769A CN 113430073 B CN113430073 B CN 113430073B
- Authority
- CN
- China
- Prior art keywords
- fullerene
- parts
- oil
- base oil
- soap
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供一种富勒烯手工皂的制备方法，所述制备方法包括加热预混基础油、加入透明质酸钠和富勒烯、制备碱溶液、加碱皂化、加盐、熟化。本发明制备的富勒烯手工皂得得到的手工皂塑性好，硬度为6.1‑6.4PI/mm；成型率97.5‑98.9%，成型率高；甘油量为26.1‑27.3%，具有良好的养护效果；常温放置12个月，无酸败，开裂现象，稳定性好；不单独添加任何脂肪酸作为皂化剂，不添加植物精油、食用色素、蜂蜜等添加剂，可以保存手工皂的纯天然程度，减少传统制备手工皂对使用者的潜在刺激；通过密封烘干促进熟化，使最终的制作时间由传统的3‑5月，缩短至3天，很大程度的节省了时间成本。
Description
技术领域
本发明涉及手工皂领域，具体涉及富勒烯手工皂的加工方法及得到的富勒烯手工皂。
背景技术
目前手工皂分为热制皂、冷制皂和再生皂。热制皂是利用热制法做成的皂，在油脂与氢氧化钠进行皂化反应至稠状阶段时，再以断续加热的方式，使其快速皂化，脱模后放置一周使水分蒸发，即可使用。市面上手工皂多为热制皂，为工业提炼脂肪酸后剩余的皂基，再添加各种添加剂制作而成。热制皂色彩多绚丽，但是使用功效多仅限于洗手，洁面会有紧绷和干燥感。冷制皂是相对于工业皂所采用的热溶法而言的，油脂、强碱溶液溶液混合后，发生皂化反应，除了混合前需将固体的油脂加热溶化成液体外，在成皂的过程中是不需要高温加热的，反应完成后，皂液入模使其自然干燥，待三至五月后脱模使用。制作工时长，时间成本高。且制作的手工皂会有裂纹、酸败、软糯等现象，成型率有待提高。再生皂即是对冷制皂和热制皂的再次加工、优化，目前市面上宣传各种功效，添加了精油和提取物的精油皂均属于再生皂。
专利201410278294.4涉及一种皂基型肥皂和一种快速让油脂连续皂化的方法。具体通过是按比例添加油脂和脂肪酸，实现油脂的连续皂化。用脂肪酸作为皂化促进剂。同时采用酸板式换热器和碱板式换热器提高原料的反应温度。最终使皂化反应的时间达到8~12min。此专利手工皂的类型为皂基型皂，也是热制皂，不适用于冷制皂的制作。
专利201910530068 .3涉及的一种皂化时间缩短的手工皂及其制备方法。具体是通过氨基酸盐代替传统强碱用于油脂的皂化过程。通过配制、混合、熟化、晾晒，最终使皂化缩短至3-6周。此专利使用氨基酸盐代替了传统的强碱，氨基酸盐虽在市面上可以买到，但还是不如强碱的使用量大、使用方便。且在熟化工序后，仍然需要晾晒。制作周期3-6周，时间成本仍高。
针对冷制皂的加速皂化方法不多。对冷制皂的纯天然成分保存有待提升，且产品容易出现裂纹、酸败、软糯等现象，成型率有待提高。冷制皂是相对于工业皂所采用的热溶法而言的，油脂、氢氧化钠溶液混合后，发生皂化反应，除了混合前需将固体的油脂加热溶化成液体外，在成皂的过程中是不需要高温加热的，反应完成后，皂液入模使其自然干燥，待三至五月后脱模使用。制作工时长，时间成本高。
综上所述，当前技术制备手工皂仍有以下缺点：
（1）产品容易出现裂纹、酸败、软糯等现象，成型率低；
（2）冷制皂需自然干燥，制作工时长，时间成本高。
发明内容
本发明所要解决的技术问题是克服上述现有技术存在的缺陷，提供一种纯天然的手工皂的制备方法，实现以下发明目的：
（1）减少冷制皂的酸败现象，增加冷制皂塑性；
（2）缩短冷制皂的皂化、熟化时间。
为解决上述技术问题，本发明采取以下技术方案：
一种富勒烯手工皂的制备方法，所述制备方法包括加热预混基础油、加入透明质酸钠和富勒烯、加碱皂化、加盐、熟化。
以下是对上述技术方案的进一步改进：
所述制备方法，具体包括以下步骤：
（1）加热预混基础油：
按重量份数混合：椰子油10-15份、棕榈油10-15份、橄榄油15-20份、甜杏仁油5-10份、乳木果油15-20份、米糠油5-10份、月见草油5-10份、葵花油10-15份放入反应器中，在水浴锅中预热到40±0.5℃，得到预混基础油。
（2）加入透明质酸钠和富勒烯：
向预混基础油中加入占预混基础油重量2-4%的透明质酸钠、3-5%的富勒烯，以40-60rpm进行搅拌15-25min，得到含富勒烯的预混基础油。
（3）制备碱溶液：
将氢氧化钠溶于蒸馏水中，冷却控制温度至40℃，得到质量浓度为30-35wt%的氢氧化钠溶液，总量占预混基础油重量的3-5%。
（4）加碱皂化
将所得碱溶液分两次缓慢加入到含富勒烯的预混基础油中；第一次加入碱溶液的2/3，3-7min缓慢加入完，以30-50rpm搅拌10-20min；第二次加入碱溶液剩余的1/3，2-5min缓慢加入完，继续以30-50rpm搅拌1.5-2.5h，得到皂化液，上述加碱皂化的温度控制在30-40℃。
（5）加盐：
将质量占比为0.05-0.1%的氯化钠、0.04-0.08%的硅酸钠缓慢加入到皂化液中，以30-50rpm搅拌5-15min。
（6）熟化：
将加盐后的皂化液倒入模具，封盖，用保鲜膜密封完全，35-45℃温度下连续加热60-84h。
（7）脱模：
得到手工皂。
（8）分切：
将手工皂进行分切，包装后即可得到成品手工皂。
本发明方法具有以下有益效果：
（1）本发明制备的富勒烯手工皂得得到的手工皂塑性好，硬度为6.1-6.4PI/mm；
（2）本发明制备的富勒烯手工皂的成型率97.5-98.9%，成型率高 ；
（3）本发明制备的富勒烯手工皂的甘油量为26.1-27.3%，具有良好的养护效果；
（4）本发明制备的富勒烯手工皂得常温放置12个月，无酸败，开裂现象，稳定性好;
（5）本发明配方中不单独添加任何脂肪酸作为皂化剂，不添加植物精油、食用色素、蜂蜜等添加剂，可以保存手工皂的纯天然程度，减少传统制备手工皂对使用者的潜在刺激;
（6）本发明制备的富勒烯手工皂通过密封烘干促进熟化，使最终的制作时间由传统的3-5月，缩短至3天，很大程度的节省了时间成本;
（7）本发明制备的富勒烯手工皂，皂溶解后的pH为7.8-8.3。
具体实施方式
实施例1一种富勒烯手工皂的制备方法
包括以下步骤
（1）加热预混基础油
按重量份数混合：椰子油10份、棕榈油10份、橄榄油20份、甜杏仁油10份、乳木果油20份、米糠油5份、月见草油5份、葵花油10份放入反应器中，在水浴锅中预热到40℃，搅拌均匀得到预混基础油；
（2）加入透明质酸钠和富勒烯
向预混基础油中加入占预混基础油重量3%的透明质酸钠、4%的富勒烯，以50rpm进行搅拌20min，得到含富勒烯的预混基础油；
（3）制备碱溶液
将氢氧化钠溶于蒸馏水中，冷却控制温度至40℃，得到质量浓度为33.3wt%的氢氧化钠溶液，总量占预混基础油重量的4%；
（4）加碱皂化
将所得氢氧化钠溶液分两次缓慢加入到含富勒烯的预混基础油中；第一次加入2/3氢氧化钠溶液，5min缓慢加入完,以40rpm搅拌15min；第二次加入1/3氢氧化钠溶液，3min缓慢加入完，继续以40rpm搅拌2h，得到皂化液，上述加碱皂化的温度控制在35℃；
（5）加盐
将占皂化液质量比为0.1%的氯化钠、0.05%的硅酸钠缓慢加入到皂化液中，以40rpm搅拌10min；
（6）熟化
将加盐后的皂化液倒入模具，封盖，用保鲜膜密封完全，加入到40℃的烘箱中，连续加热72h；
（7）脱模
得到手工皂；
（8）分切
将手工皂进行分切，包装后即可得到成品手工皂；皂溶解后的pH为8.0。
本实施例的有益效果为：
（1）本发明实施例1制备的富勒烯手工皂的塑性好，硬度为6.4PI/mm；
（2）本发明实施例1制备的富勒烯手工皂的成型率98.9%，成型率高 ；
（3）本发明实施例1制备的富勒烯手工皂的甘油量为27.3%，具有良好的养护效果；
（4）本发明制备实施例1的富勒烯手工皂常温放置12个月，无酸败，开裂现象，稳定性好。
实施例2一种富勒烯手工皂的制备方法
包括以下步骤
（1）加热预混基础油
按重量份数混合：椰子油15份、棕榈油10份、橄榄油20份、甜杏仁油10份、乳木果油20份、米糠油10份、月见草油5份、葵花油15份放入反应器中，在水浴锅中预热到40℃，得到预混基础油；
（2）加入透明质酸钠和富勒烯
向预混基础油中加入占预混基础油重量2%的透明质酸钠、3%的富勒烯，以40rpm进行搅拌15min，得到含富勒烯的预混基础油；
（3）制备碱溶液
将氢氧化钠溶于蒸馏水中，冷却控制温度至40℃，得到质量浓度为33.3wt%的氢氧化钠溶液，总量占预混基础油重量的3%；
（4）加碱皂化
将所得碱溶液分两次缓慢加入到含富勒烯的预混基础油中；第一次加入碱溶液的2/3,3min缓慢加入完,以30rpm搅拌10min；第二次加入碱溶液剩余的1/3，2min缓慢加入完，继续以30rpm搅拌1.5h，得到皂化液，上述加碱皂化的温度控制在30℃；
（5）加盐
将质量占比为0.05%的氯化钠、0.04%的硅酸钠缓慢加入到皂化液中，以30rpm搅拌5min；
（6）熟化
将步骤加盐后的皂化液倒入模具，封盖，用保鲜膜密封完全。加入到35℃的烘箱中，连续加热60h；
（7）脱模
得到手工皂；
（8）分切
将手工皂进行分切，包装后即可得到成品手工皂，皂溶解后的pH为7.8。
本实施例的有益效果为：
（1）本发明实施例2制备的富勒烯手工皂得到的手工皂塑性好，硬度为6.1PI/mm；
（2）本发明实施例2制备的富勒烯手工皂的成型率97.5%，成型率高 ；
（3）本发明实施例2制备的富勒烯手工皂的甘油量为26.1%，具有良好的养护效果；
（4）本发明实施例2制备的富勒烯手工皂常温放置12个月，无酸败，开裂现象，稳定性好。
实施例3一种富勒烯手工皂的制备方法
包括以下步骤
（1）加热预混基础油
按重量份数混合：椰子油10份、棕榈油15份、橄榄油15份、甜杏仁油10份、乳木果油15份、米糠油5份、月见草油5份、葵花油10份放入反应器中，在水浴锅中预热到40℃，得到预混基础油；
（2）加入透明质酸钠和富勒烯
向预混基础油中加入占预混基础油重量4%的透明质酸钠、5%的富勒烯，以60rpm进行搅拌25min，得到含富勒烯的预混基础油；
（3）制备碱溶液
将氢氧化钠溶于蒸馏水中，冷却控制温度至40℃，得到质量浓度为33.3wt%的氢氧化钠溶液，总量占预混基础油重量的5%；
（4）加碱皂化
将所得碱溶液分两次缓慢加入到含富勒烯的预混基础油中；第一次加入碱溶液的2/3, 7min缓慢加入完,以50rpm搅拌20min；第二次加入碱溶液剩余的1/3， 5min缓慢加入完，继续以50rpm搅拌2.5h，得到皂化液，上述加碱皂化的温度控制在40℃；
（5）加盐
将质量占比为0.1%的氯化钠、0.08%的硅酸钠缓慢加入到皂化液中，以50rpm搅拌15min；
（6）熟化
将加盐后的皂化液倒入模具，封盖，用保鲜膜密封完全。加入到45℃的烘箱中，连续加热84h；
（7）脱模
得到手工皂；
（8）分切
将手工皂进行分切，包装后即可得到成品手工皂，皂溶解后的pH为8.3。
本实施例的有益效果为：
（1）本发明实施例3制备的富勒烯手工皂得到的手工皂塑性好，硬度为6.3PI/mm；
（2）本发明实施例3制备的富勒烯手工的皂成型率98.2%，成型率高 ；
（3）本发明实施例3制备的富勒烯手工的皂甘油量为26.7%，具有良好的养护效果；
（4）本发明实施例3制备的富勒烯手工皂常温放置12个月，无酸败，开裂现象，稳定性好。
对比例1
在实施例1的基础上，省略步骤（2）的加入透明质酸和富勒烯、步骤（5）加入氯化钠和硅酸钠的步骤，并采用了不同的熟化和晾晒步骤，具体步骤如下：
（1）加热预混基础油
按重量份数混合：椰子油10份、棕榈油10份、橄榄油20份、甜杏仁油10份、乳木果油20份、米糠油5份、月见草油5份、葵花油10份放入反应器中，在水浴锅中预热到40℃，搅拌均匀得到预混基础油；
（2）制备碱溶液
将氢氧化钠溶于蒸馏水中，冷却控制温度至40℃，得到质量浓度为33.3wt%的氢氧化钠溶液，总量占预混基础油重量的4%；
（3）加碱皂化
将所得氢氧化钠溶液分两次缓慢加入到预混基础油中。第一次加入2/3氢氧化钠溶液，5min缓慢加入完,以40rpm搅拌15min；第二次加入1/3氢氧化钠溶液，3min缓慢加入完，继续以40rpm搅拌2h，得到皂化液，上述加碱皂化的温度控制在35℃；
（4）熟化
将得到的皂化液转入模具中，35℃下进行熟化反应48h，得到初级皂；
（5）脱模分切
将熟化后的初级皂脱模，切皂；
（6）通风晾制
将上述熟化后的初级皂脱模，切皂，随后放置在阴凉通风处8周，即可完全皂化。
本对比例达到的效果：
（1）得到的手工皂硬度为4.1PI/mm；
（2）成型率78.6% ；
（3）制作周期长。
Claims (1)
1.一种富勒烯手工皂的制备方法，其特征在于，所述制备方法包括以下步骤：
（1）加热预混基础油：按重量份数将椰子油10-15份、棕榈油10-15份、橄榄油15-20份、甜杏仁油5-10份、乳木果油15-20份、米糠油5-10份、月见草油5-10份、葵花油10-15份混合，放入反应器中，在水浴锅中预热到40±0.5℃，得到预混基础油；
（2）加入透明质酸钠和富勒烯：向预混基础油中加入占预混基础油重量2-4%的透明质酸钠、3-5%的富勒烯，以40-60rpm进行搅拌15-25min，得到含富勒烯的预混基础油；
（3）制备碱溶液：将氢氧化钠溶于蒸馏水中，冷却控制温度至40℃，得到质量浓度为30-35wt%的氢氧化钠溶液，总量占预混基础油重量的3-5%；
（4）加碱皂化：将所得碱溶液分两次缓慢加入到含富勒烯的预混基础油中；第一次加入碱溶液的2/3，3-7min缓慢加入完，以30-50rpm搅拌10-20min；第二次加入碱溶液剩余的1/3，2-5min缓慢加入完，继续以30-50rpm搅拌1.5-2.5h，得到皂化液，上述加碱皂化的温度控制在30-40℃；
（5）加盐：将质量占比为0.05-0.1%的氯化钠、0.04-0.08%的硅酸钠缓慢加入到皂化液中，以30-50rpm搅拌5-15min；
（6）熟化：将加盐后的皂化液倒入模具，封盖，用保鲜膜密封完全，35-45℃温度下连续加热60-84h；
（7）脱模；
（8）分切，包装后即可得到成品手工皂。