CN103358797B - The manufacture craft that pottery plate is drawn - Google Patents
The manufacture craft that pottery plate is drawn Download PDFInfo
- Publication number
- CN103358797B CN103358797B CN201310245385.3A CN201310245385A CN103358797B CN 103358797 B CN103358797 B CN 103358797B CN 201310245385 A CN201310245385 A CN 201310245385A CN 103358797 B CN103358797 B CN 103358797B
- Authority
- CN
- China
- Prior art keywords
- pottery plate
- drawn
- pottery
- oxide
- kiln
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses the manufacture craft that a kind of plate of making pottery is drawn, comprise the following steps successively: S1. gets the clay of 30 weight portions, the aluminium oxide of 40 weight portions, the kaolin of 25 weight portions, the iron powder of 1-3 weight portion, the manganese of 2-5 weight portion, calcium or zinc powder, by above-mentioned raw materials through pulverizing, crossing 200 mesh sieves, obtain mud powder; S2. in above-mentioned mud powder, add appropriate water, the amount of the water added and the weight ratio of mud powder are 1: 9, after be pressed into pottery plate through press, the pottery plate that obtains is placed normal temperature laboratory ventilation and is dried in the shade; S3. the pottery plate obtained by step S2 loads klining 14-16 in kiln individual hour, cooling kiln discharge; S4. get metal oxide, first add frankincense, porphyrize becomes paste, does the pottery plate of diluent after cooling kiln discharge is drawn a picture afterwards with camphorated oil; S5. the pottery plate obtained by step S4 is drawn and is reinstalled klining 7-9 hour in kiln, cooling kiln discharge; Stable in properties of the present invention, can not produce with air and again be oxidized, continue to have look for a long time, is applicable to exterior decoration, draws a picture can embody the pen and ink effect of Chinese painting at Tao Banshang.
Description
Technical field
The present invention relates to the manufacture craft that a kind of plate of making pottery is drawn.
Background technology
The like product (pottery plate is drawn) of existing market all cannot keep the original ink and wash effect of Chinese painting and long-time preservation meeting variable color, and character is unstable.
Summary of the invention
In order to the shortcoming that prior art exists, the invention provides a kind of stable in properties, to continue to have look for a long time, the manufacture craft that the pottery plate that can embody the pen and ink effect of Chinese painting is drawn.
The manufacture craft that plate of making pottery is drawn, is characterized in that, comprise the following steps successively:
S1. get the clay of 30 weight portions, the aluminium oxide of 40 weight portions, the kaolin of 25 weight portions, the iron powder of 1-3 weight portion, the manganese of 2-5 weight portion, calcium or zinc powder, by above-mentioned raw materials through pulverizing, crossing 200 mesh sieves, obtain mud powder;
S2. in above-mentioned mud powder, add appropriate water, the amount of the water added and the weight ratio of mud powder are 1:9, after be pressed into pottery plate through press, the pottery plate that obtains is placed normal temperature laboratory ventilation and is dried in the shade;
S3. the pottery plate obtained by step S2 loads klining 14-16 in kiln individual hour, and kiln temperature controls at 1500-1700 degree Celsius, cooling kiln discharge;
S4. get metal oxide, first add frankincense, porphyrize becomes paste, does the pottery plate of diluent after cooling kiln discharge is drawn a picture afterwards with camphorated oil;
S5. the pottery plate obtained by step S4 is drawn and is reinstalled klining 7-9 hour in kiln, and kiln temperature controls at 700-900 degree Celsius, cooling kiln discharge;
Further, in step S4, metal oxide is iron oxide, cobalt oxide, chromium oxide, titanium oxide or praseodymium oxide.
Compared with prior art, beneficial effect of the present invention is: 1. because pottery plate is drawn synthesized by burning, stable in properties, can not produce with air and again be oxidized, then through high-temperature fusion, not be afraid of and expose to the sun and rain, continue to have look for a long time, is applicable to exterior decoration.2. this pottery plate composition have clay components have certain adsorptivity with rice paper similar, so draw a picture at Tao Banshang to embody withered, wet, dense, the light pen and ink effect of Chinese painting.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is described in further detail.Following examples for illustration of the present invention, but are not used for limiting the scope of the invention.Experimental technique described in following embodiment, if no special instructions, is conventional method; Described raw material, if no special instructions, all can obtain from commercial channels.
Embodiment 1
The manufacture craft that plate of making pottery is drawn, is characterized in that, comprise the following steps successively:
S1. get 30kg clay, 40kg aluminium oxide, 25kg kaolin, 1kg iron powder, 2kg manganese powder, by above-mentioned raw materials through pulverizing, crossing 200 mesh sieves, obtain mud powder;
S2. get 90kg mud powder, add 10kg water in proportion, be pressed into pottery plate through press in this mud powder, the pottery plate obtained is placed normal temperature laboratory ventilation and is dried in the shade;
S3. klining 14 hours in pottery plate loading kiln step S2 obtained, kiln temperature controls at 1500 degrees Celsius, cooling kiln discharge;
S4. get metal oxide, first add frankincense, porphyrize becomes paste, does the pottery plate of diluent after cooling kiln discharge is drawn a picture afterwards with camphorated oil;
S5. the pottery plate that obtained by step S4 is drawn and to be reinstalled in kiln klining 7 hours, and kiln temperature controls at 700 degrees Celsius, cooling kiln discharge;
Further, in step S4, metal oxide is iron oxide, cobalt oxide, chromium oxide, titanium oxide or praseodymium oxide.
Embodiment 2
The manufacture craft that plate of making pottery is drawn, is characterized in that, comprise the following steps successively:
S1. get 30kg clay, 40kg aluminium oxide, 25kg kaolin, 2kg iron powder, 3kg calcium powder, by above-mentioned raw materials through pulverizing, crossing 200 mesh sieves, obtain mud powder;
S2. get 90kg mud powder, add 10kg water in proportion, be pressed into pottery plate through press in this mud powder, the pottery plate obtained is placed normal temperature laboratory ventilation and is dried in the shade;
S3. klining 15 hours in pottery plate loading kiln step S2 obtained, kiln temperature controls at 1600 degrees Celsius, cooling kiln discharge;
S4. get metal oxide, first add frankincense, porphyrize becomes paste, does the pottery plate of diluent after cooling kiln discharge is drawn a picture afterwards with camphorated oil;
S5. the pottery plate that obtained by step S4 is drawn and to be reinstalled in kiln klining 8 hours, and kiln temperature controls at 800 degrees Celsius, cooling kiln discharge;
Further, in step S4, metal oxide is iron oxide, cobalt oxide, chromium oxide, titanium oxide or praseodymium oxide.
Embodiment 3
The manufacture craft that plate of making pottery is drawn, is characterized in that, comprise the following steps successively:
S1. get 30kg clay, 40kg aluminium oxide, 25kg kaolin, 3kg iron powder, 5kg zinc powder, by above-mentioned raw materials through pulverizing, crossing 200 mesh sieves, obtain mud powder;
S2. get 90kg mud powder, add 10kg water in proportion, be pressed into pottery plate through press in this mud powder, the pottery plate obtained is placed normal temperature laboratory ventilation and is dried in the shade;
S3. klining 16 hours in pottery plate loading kiln step S2 obtained, kiln temperature controls at 1700 degrees Celsius, cooling kiln discharge;
S4. get metal oxide, first add frankincense, porphyrize becomes paste, does the pottery plate of diluent after cooling kiln discharge is drawn a picture afterwards with camphorated oil;
S5. the pottery plate that obtained by step S4 is drawn and to be reinstalled in kiln klining 9 hours, and kiln temperature controls at 900 degrees Celsius, cooling kiln discharge;
Further, in step S4, metal oxide is iron oxide, cobalt oxide, chromium oxide, titanium oxide or praseodymium oxide.
Compared with prior art, beneficial effect of the present invention is: 1. because pottery plate is drawn synthesized by burning, stable in properties, can not produce with air and again be oxidized, then through high-temperature fusion, not be afraid of and expose to the sun and rain, continue to have look for a long time, is applicable to exterior decoration.2. this pottery plate composition have clay components have certain adsorptivity with rice paper similar, so draw a picture at Tao Banshang to embody withered, wet, dense, the light pen and ink effect pen and ink effect of Chinese painting.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvement and modification, these improve and modification also should be considered as protection scope of the present invention.
Claims (2)
1. the manufacture craft that plate of making pottery is drawn, is characterized in that, comprise the following steps successively:
S1. get the clay of 30 weight portions, the aluminium oxide of 40 weight portions, the kaolin of 25 weight portions, the iron powder of 1-3 weight portion, the manganese of 2-5 weight portion, calcium or zinc powder, by above-mentioned raw materials through pulverizing, crossing 200 mesh sieves, obtain mud powder;
S2. in above-mentioned mud powder, add appropriate water, the amount of the water added and the weight ratio of mud powder are 1: 9, after be pressed into pottery plate through press, the pottery plate that obtains is placed normal temperature laboratory ventilation and is dried in the shade;
S3. the pottery plate obtained by step S2 loads klining 14-16 in kiln individual hour, and kiln temperature controls at 1500-1700 degree Celsius, cooling kiln discharge;
S4. get metal oxide, first add frankincense, porphyrize becomes paste, does the pottery plate of diluent after cooling kiln discharge is drawn a picture afterwards with camphorated oil;
S5. the pottery plate obtained by step S4 is drawn and is reinstalled klining 7-9 hour in kiln, and kiln temperature controls at 700-900 degree Celsius, cooling kiln discharge.
2. the manufacture craft of pottery plate picture according to claim 1, it is characterized in that, in step S4, metal oxide is iron oxide, cobalt oxide, chromium oxide, titanium oxide or praseodymium oxide.