CN103358797A - Manufacturing technology for ceramic plate paintings - Google Patents
Manufacturing technology for ceramic plate paintings Download PDFInfo
- Publication number
- CN103358797A CN103358797A CN2013102453853A CN201310245385A CN103358797A CN 103358797 A CN103358797 A CN 103358797A CN 2013102453853 A CN2013102453853 A CN 2013102453853A CN 201310245385 A CN201310245385 A CN 201310245385A CN 103358797 A CN103358797 A CN 103358797A
- Authority
- CN
- China
- Prior art keywords
- ceramic plate
- kiln
- oxide
- pottery plate
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a manufacturing technology for ceramic plate paintings. The manufacturing technology sequentially comprises the following steps of: S1. smashing 30 weight parts of clay, 40 weight parts of aluminum oxide, 25 weight parts of kaoline, 1-3 weight parts of iron powder, 2-5 weight parts of manganese, calcium or zinc powder, and filtering the raw materials through a sieve being 200 meshes to obtain mud powder, S2. adding a proper amount of water into the mud powder according to the weight ratio of 1:9, then pressing the mixture by a press to obtain a ceramic plate, and drying the obtained ceramic plate at an indoor normal-temperature ventilating position, S3. putting the ceramic plate obtained in the step S2 into a kiln for sintering for 14-16 hours, cooling the ceramic plate, and discharging the ceramic plate out of the kiln, S4. adding olibanum into a metal oxide, grinding the mixture into paste, and then drawing pictures on the cooled ceramic plate out of the kiln by taking camphorated oil as a diluent, and S5. putting the ceramic plate painting obtained in the step S4 into the kiln for sintering for 7-9 hours, cooling and discharging the ceramic plate painting. The ceramic plate painting is stable in property and cannot be reoxidized in air; the ceramic plate painting can be stored for a long time, and the color can be kept; the ceramic plate painting is suitable for outdoor decoration; an ink effect of Chinese paintings can be reflected by drawing on the ceramic plate.
Description
Technical field
The present invention relates to the manufacture craft that a kind of plate of making pottery is drawn.
Background technology
The like product of existing market (pottery plate picture) all can't keep the original ink and wash effect of Chinese painting and long-time preservation meeting variable color, and character is unstable.
Summary of the invention
For the shortcoming that prior art exists, the invention provides a kind of stable in properties, the long-time look that continues to have, can embody the manufacture craft that the pottery plate of the pen and ink effect of Chinese painting is drawn.
The manufacture craft that a kind of plate of making pottery is drawn is characterized in that, may further comprise the steps successively:
S1. get the clay of 30 weight portions, the aluminium oxide of 40 weight portions, the kaolin of 25 weight portions, the iron powder of 1-3 weight portion, manganese, calcium or the zinc powder of 2-5 weight portion, above-mentioned raw materials through pulverizing, crossing 200 mesh sieves, is got the mud powder;
S2. add an amount of water in above-mentioned mud powder, the weight ratio of the amount of the water of adding and mud powder is 1: 9, is pressed into the pottery plate through press afterwards, and the pottery plate that obtains is placed the normal temperature laboratory ventilation and dried in the shade;
S3. the pottery plate that step S2 is obtained was packed in the kiln klining 14-16 hour, and kiln temperature is controlled at 1500-1700 degree centigrade, the cooling kiln discharge;
S4. get metal oxide, add first frankincense, porphyrize becomes paste, makes the pottery plate of diluent behind the cooling kiln discharge with camphorated oil afterwards and draws a picture;
S5. the pottery plate that step S4 obtained is drawn and is reinstalled in the kiln klining 7-9 hour, and kiln temperature is controlled at 700-900 degree centigrade, the cooling kiln discharge;
Further, among the step S4, metal oxide is iron oxide, cobalt oxide, chromium oxide, titanium oxide or praseodymium oxide.
Compared with prior art, beneficial effect of the present invention is: 1. because the pottery plate is drawn by burning to be synthesized, stable in properties can not produce again oxidation with air, again through high-temperature fusion, is not afraid of a day Sai and drenches with rain, and the look that continues to have for a long time is fit to exterior decoration.2. to have the clay composition to have certain adsorptivity similar with rice paper for this pottery plate composition, can embody withered, wet, dense, the light pen and ink effect of Chinese painting so draw a picture at Tao Banshang.
The specific embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is described in further detail.Following examples are used for explanation the present invention, but are not used for limiting the scope of the invention.Experimental technique described in the following embodiment if no special instructions, is conventional method; Described raw material if no special instructions, all can obtain from commercial channels.
Embodiment 1
The manufacture craft that a kind of plate of making pottery is drawn is characterized in that, may further comprise the steps successively:
S1. get 30kg clay, 40kg aluminium oxide, 25kg kaolin, 1kg iron powder, 2kg manganese powder, above-mentioned raw materials through pulverizing, crossing 200 mesh sieves, is got the mud powder;
S2. get 90kg mud powder, add in proportion 10kg water in this mud powder, be pressed into the pottery plate through press, the pottery plate that obtains is placed the normal temperature laboratory ventilation and is dried in the shade;
S3. the pottery plate that step S2 the is obtained klining 14 hours of packing in the kiln, kiln temperature is controlled at 1500 degrees centigrade, the cooling kiln discharge;
S4. get metal oxide, add first frankincense, porphyrize becomes paste, makes the pottery plate of diluent behind the cooling kiln discharge with camphorated oil afterwards and draws a picture;
S5. the pottery plate that step S4 obtained is drawn and was reinstalled in the kiln klining 7 hours, and kiln temperature is controlled at 700 degrees centigrade, the cooling kiln discharge;
Further, among the step S4, metal oxide is iron oxide, cobalt oxide, chromium oxide, titanium oxide or praseodymium oxide.
Embodiment 2
The manufacture craft that a kind of plate of making pottery is drawn is characterized in that, may further comprise the steps successively:
S1. get 30kg clay, 40kg aluminium oxide, 25kg kaolin, 2kg iron powder, 3kg calcium powder, above-mentioned raw materials through pulverizing, crossing 200 mesh sieves, is got the mud powder;
S2. get 90kg mud powder, add in proportion 10kg water in this mud powder, be pressed into the pottery plate through press, the pottery plate that obtains is placed the normal temperature laboratory ventilation and is dried in the shade;
S3. the pottery plate that step S2 the is obtained klining 15 hours of packing in the kiln, kiln temperature is controlled at 1600 degrees centigrade, the cooling kiln discharge;
S4. get metal oxide, add first frankincense, porphyrize becomes paste, makes the pottery plate of diluent behind the cooling kiln discharge with camphorated oil afterwards and draws a picture;
S5. the pottery plate that step S4 obtained is drawn and was reinstalled in the kiln klining 8 hours, and kiln temperature is controlled at 800 degrees centigrade, the cooling kiln discharge;
Further, among the step S4, metal oxide is iron oxide, cobalt oxide, chromium oxide, titanium oxide or praseodymium oxide.
Embodiment 3
The manufacture craft that a kind of plate of making pottery is drawn is characterized in that, may further comprise the steps successively:
S1. get 30kg clay, 40kg aluminium oxide, 25kg kaolin, 3kg iron powder, 5kg zinc powder, above-mentioned raw materials through pulverizing, crossing 200 mesh sieves, is got the mud powder;
S2. get 90kg mud powder, add in proportion 10kg water in this mud powder, be pressed into the pottery plate through press, the pottery plate that obtains is placed the normal temperature laboratory ventilation and is dried in the shade;
S3. the pottery plate that step S2 the is obtained klining 16 hours of packing in the kiln, kiln temperature is controlled at 1700 degrees centigrade, the cooling kiln discharge;
S4. get metal oxide, add first frankincense, porphyrize becomes paste, makes the pottery plate of diluent behind the cooling kiln discharge with camphorated oil afterwards and draws a picture;
S5. the pottery plate that step S4 obtained is drawn and was reinstalled in the kiln klining 9 hours, and kiln temperature is controlled at 900 degrees centigrade, the cooling kiln discharge;
Further, among the step S4, metal oxide is iron oxide, cobalt oxide, chromium oxide, titanium oxide or praseodymium oxide.
Compared with prior art, beneficial effect of the present invention is: 1. because the pottery plate is drawn by burning to be synthesized, stable in properties can not produce again oxidation with air, again through high-temperature fusion, is not afraid of a day Sai and drenches with rain, and the look that continues to have for a long time is fit to exterior decoration.2. to have the clay composition to have certain adsorptivity similar with rice paper for this pottery plate composition, can embody withered, wet, dense, the light pen and ink effect pen and ink effect of Chinese painting so draw a picture at Tao Banshang.
The above only is preferred embodiment of the present invention; should be pointed out that for those skilled in the art, under the prerequisite that does not break away from the technology of the present invention principle; can also make some improvement and modification, these improve and modification also should be considered as protection scope of the present invention.
Claims (2)
1. the manufacture craft that the plate of making pottery is drawn is characterized in that, may further comprise the steps successively:
S1. get the clay of 30 weight portions, the aluminium oxide of 40 weight portions, the kaolin of 25 weight portions, the iron powder of 1-3 weight portion, manganese, calcium or the zinc powder of 2-5 weight portion, above-mentioned raw materials through pulverizing, crossing 200 mesh sieves, is got the mud powder;
S2. add an amount of water in above-mentioned mud powder, the weight ratio of the amount of the water of adding and mud powder is 1: 9, is pressed into the pottery plate through press afterwards, and the pottery plate that obtains is placed the normal temperature laboratory ventilation and dried in the shade;
S3. the pottery plate that step S2 is obtained was packed in the kiln klining 14-16 hour, and kiln temperature is controlled at 1500-1700 degree centigrade, the cooling kiln discharge;
S4. get metal oxide, add first frankincense, porphyrize becomes paste, makes the pottery plate of diluent behind the cooling kiln discharge with camphorated oil afterwards and draws a picture;
S5. the pottery plate that step S4 obtained is drawn and is reinstalled in the kiln klining 7-9 hour, and kiln temperature is controlled at 700-900 degree centigrade, the cooling kiln discharge.
2. the manufacture craft of pottery plate picture according to claim 1 is characterized in that among the step S4, metal oxide is iron oxide, cobalt oxide, chromium oxide, titanium oxide or praseodymium oxide.