MX2015005838A - Plancha de acero galvanizado en caliente super-resistente y de elevada aptitud de conformacion y su metodo de fabricacion. - Google Patents

Plancha de acero galvanizado en caliente super-resistente y de elevada aptitud de conformacion y su metodo de fabricacion.

Info

Publication number
MX2015005838A
MX2015005838A MX2015005838A MX2015005838A MX2015005838A MX 2015005838 A MX2015005838 A MX 2015005838A MX 2015005838 A MX2015005838 A MX 2015005838A MX 2015005838 A MX2015005838 A MX 2015005838A MX 2015005838 A MX2015005838 A MX 2015005838A
Authority
MX
Mexico
Prior art keywords
super
steel plate
strength
hot galvanizing
conformation
Prior art date
Application number
MX2015005838A
Other languages
English (en)
Other versions
MX380341B (es
Inventor
Li Wang
Yong Zhong
Weijun Feng
Liyang Zhang
Original Assignee
Baoshan Iron & Steel
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Baoshan Iron & Steel filed Critical Baoshan Iron & Steel
Publication of MX2015005838A publication Critical patent/MX2015005838A/es
Publication of MX380341B publication Critical patent/MX380341B/es

Abstract

Una placa de acero galvanizado por inmersión en caliente, de resistencia super-elevada y elevada aptitud de conformación, cuya composición química comprende, basándose en porcentaje en peso, C: 0,15~0,25 % en peso, Si: 1,00~2,00 % en peso, Mn: 1,50~3,00 % en peso, P = 0,015 % en peso, S = 0,012 % en peso, Al: 0,03~0,06 % en peso, N = 0,008 % en peso, siendo el equilibrio de hierro e impurezas inevitables. La estructura a temperatura ambiente de la placa de acero comprende un 10-30 % de ferrita, un 60-80 % de martensita y un 5-15 % de austenita residual. La placa de acero tiene un límite aparente de fluencia de 600-900 MPa, una resistencia frente a la tracción de 980-1200 MPa, y un estiramiento de un 15-22 %. A través de un diseño de composición apropiado, se fabrica una placa de acero galvanizado por inmersión en caliente, laminado en frío, de resistencia super-elevada por medio de recocido continuo, en que no se añaden elementos de aleación costosos; en lugar de ello, se puede lograr un aumento marcado de la resistencia junto con buena plasticidad por medio del aumento apropiado de los contenidos de Si, Mn en combinación con los procesos apropiados de recocido y control de la atmósfera del horno. Además, la placa de acero posee una buena calidad de galvanización que cumple el requisito de una placa de acero galvanizado por inmersión en caliente, laminado en frío y de resistencia super-elevada para automóviles.
MX2015005838A 2012-11-15 2013-02-21 Plancha de acero galvanizado en caliente super-resistente y de elevada aptitud de conformacion y su metodo de fabricacion. MX380341B (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN201210461860.6A CN103805840B (zh) 2012-11-15 2012-11-15 一种高成形性热镀锌超高强度钢板及其制造方法
PCT/CN2013/071716 WO2014075405A1 (zh) 2012-11-15 2013-02-21 一种高成形性热镀锌超高强度钢板及其制造方法

Publications (2)

Publication Number Publication Date
MX2015005838A true MX2015005838A (es) 2016-01-12
MX380341B MX380341B (es) 2025-03-12

Family

ID=50703217

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2015005838A MX380341B (es) 2012-11-15 2013-02-21 Plancha de acero galvanizado en caliente super-resistente y de elevada aptitud de conformacion y su metodo de fabricacion.

Country Status (9)

Country Link
US (1) US10100385B2 (es)
EP (1) EP2921569B1 (es)
JP (1) JP6208246B2 (es)
KR (1) KR102100727B1 (es)
CN (1) CN103805840B (es)
CA (1) CA2889927C (es)
ES (1) ES2701407T3 (es)
MX (1) MX380341B (es)
WO (1) WO2014075405A1 (es)

Families Citing this family (49)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10400320B2 (en) 2015-05-15 2019-09-03 Nucor Corporation Lead free steel and method of manufacturing
EP3378958B1 (en) * 2015-09-22 2021-08-04 Hyundai Steel Company Plated steel plate and manufacturing method thereof
KR101758485B1 (ko) * 2015-12-15 2017-07-17 주식회사 포스코 표면품질 및 점 용접성이 우수한 고강도 용융아연도금강판 및 그 제조방법
CN105648317B (zh) * 2016-01-28 2019-01-01 河北钢铁股份有限公司邯郸分公司 一种高强度高塑性中锰q&p钢冷轧退火板及其制备工艺
US11453926B2 (en) 2016-03-31 2022-09-27 Jfe Steel Corporation Steel sheet, plated steel sheet, method for producing hot-rolled steel sheet, method for producing cold-rolled full hard steel sheet, method for producing steel sheet, and method for producing plated steel sheet
CN105908089B (zh) * 2016-06-28 2019-11-22 宝山钢铁股份有限公司 一种热浸镀低密度钢及其制造方法
CN106086745A (zh) * 2016-08-23 2016-11-09 蚌埠精科机床制造有限公司 一种机床部件热电浸镀的方法
CN106244923B (zh) * 2016-08-30 2018-07-06 宝山钢铁股份有限公司 一种磷化性能和成形性能优良的冷轧高强度钢板及其制造方法
CN106350731B (zh) * 2016-08-30 2018-08-10 宝山钢铁股份有限公司 一种具有优良磷化性能和成形性的冷轧高强度钢板及其制造方法
CN108018484B (zh) * 2016-10-31 2020-01-31 宝山钢铁股份有限公司 抗拉强度1500MPa以上成形性优良的冷轧高强钢及其制造方法
CN108070791B (zh) * 2016-11-18 2021-12-21 北方工业大学 一种矿山加固用高强度锚杆
JP6414246B2 (ja) 2017-02-15 2018-10-31 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP6962452B2 (ja) 2018-03-28 2021-11-05 Ｊｆｅスチール株式会社 高強度合金化溶融亜鉛めっき鋼板およびその製造方法
EP3754043B1 (en) * 2018-03-30 2022-01-19 JFE Steel Corporation High-strength galvanized steel sheet, high-strength member, and method for manufacturing the same
US11788163B2 (en) * 2018-03-30 2023-10-17 Jfe Steel Corporation High-strength steel sheet and method for manufacturing same
CN110760771B (zh) * 2018-07-27 2022-07-22 宝山钢铁股份有限公司 一种具有优良Fe-Al合金层特征的热镀锌高强钢及其制造方法
CN110760773B (zh) * 2018-07-27 2022-10-21 宝山钢铁股份有限公司 一种具有高表面质量和优良耐蚀性的热镀锌高强度钢板及其制造方法
CN109365606A (zh) * 2018-11-30 2019-02-22 宝山钢铁股份有限公司 一种耐腐蚀性优良的锌系镀层钢板或钢带的成形方法
WO2020128574A1 (en) * 2018-12-18 2020-06-25 Arcelormittal Cold rolled and heat-treated steel sheet and method of manufacturing the same
CN111748745B (zh) * 2019-03-29 2022-03-18 宝山钢铁股份有限公司 780MPa级具有较高成形性的冷轧热镀锌双相钢及其制造方法
CN109881106B (zh) * 2019-04-01 2021-10-26 山东钢铁集团日照有限公司 一种生产不同屈服强度级别的780MPa级热镀锌双相钢及其生产方法
CN110747391A (zh) * 2019-08-30 2020-02-04 武汉钢铁有限公司 一种具有优良延伸率的冷轧超高强钢及其制备方法
CN112760554A (zh) * 2019-10-21 2021-05-07 宝山钢铁股份有限公司 一种延展性优异的高强度钢及其制造方法
JP7440800B2 (ja) * 2020-06-08 2024-02-29 日本製鉄株式会社 鋼板及びその製造方法
CN111850263B (zh) * 2020-06-22 2022-07-26 鞍钢蒂森克虏伯汽车钢有限公司 一种连续热镀锌烘烤硬化钢板提升耐时效性能的生产方法
CN111850262B (zh) * 2020-06-22 2022-07-26 鞍钢蒂森克虏伯汽车钢有限公司 一种超低碳烘烤硬化连续热镀锌钢板的生产方法
CN114438400B (zh) * 2020-10-30 2022-12-16 宝山钢铁股份有限公司 一种具有高延伸率的980MPa级热镀锌钢板及其制造方法
CN112795849B (zh) * 2020-11-20 2022-07-12 唐山钢铁集团有限责任公司 一种1300Mpa级高韧性热镀锌钢板及其生产方法
CN114807737B (zh) * 2021-01-21 2023-06-13 宝山钢铁股份有限公司 一种热镀锌钢及其制造方法
CN114807736A (zh) * 2021-01-21 2022-07-29 宝山钢铁股份有限公司 一种抗lme钢及抗lme钢板的制造方法
KR20230145441A (ko) * 2021-03-08 2023-10-17 가부시키가이샤 고베 세이코쇼 용융 아연 도금 강판의 제조 방법 및 합금화 용융 아연 도금 강판의 제조 방법
US20240167130A1 (en) * 2021-04-02 2024-05-23 Baoshan Iron & Steel Co., Ltd. Low-carbon low-alloy q&p steel or hot-dip galvanized q&p steel with tensile strength greater than or equal to 1180 mpa, and manufacturing method therefor
CN115181891B (zh) * 2021-04-02 2023-07-11 宝山钢铁股份有限公司 980MPa级别低碳低合金热镀锌双相钢及快速热处理热镀锌制造方法
CN115181887B (zh) * 2021-04-02 2023-08-11 宝山钢铁股份有限公司 一种1180MPa级别低碳低合金Q＆P钢及其快速热处理制造方法
CN113416889B (zh) * 2021-05-21 2022-07-22 鞍钢股份有限公司 焊接性能良好超高强热镀锌dh1470钢及制备方法
CN113403551B (zh) * 2021-05-21 2022-08-16 鞍钢股份有限公司 高屈强比抗氢脆冷轧dh980钢板及其制备方法
CN113403529B (zh) * 2021-05-21 2022-07-19 鞍钢股份有限公司 冷冲压用1470MPa级合金化镀锌钢板及其制备方法
CN115505834A (zh) * 2021-06-07 2022-12-23 宝山钢铁股份有限公司 一种热镀锌钢板及其制造方法
CN113528950B (zh) * 2021-06-22 2022-10-21 首钢集团有限公司 一种具有良好焊接性能的热镀锌高强钢的制备方法
CN113355604B (zh) * 2021-06-25 2022-05-24 攀钢集团攀枝花钢铁研究院有限公司 低成本700MPa级热镀锌复相钢板及其制备方法
CN114045437A (zh) * 2021-11-16 2022-02-15 攀钢集团攀枝花钢铁研究院有限公司 800MPa级热镀锌用增强塑性双相钢及其制备方法
CN114045440B (zh) * 2021-11-19 2023-03-03 鞍钢股份有限公司 汽车用具有抗氧化性的高强高塑热成形钢及热成形工艺
CN114574674A (zh) * 2022-02-24 2022-06-03 山东钢铁集团日照有限公司 一种可同时生产连退、镀锌dp780双相钢的制备方法
CN116732445A (zh) * 2022-03-01 2023-09-12 宝山钢铁股份有限公司 一种用于镀锌钢板的冷轧基板、镀锌钢板及其制造方法
CN115386782B (zh) * 2022-08-17 2023-07-25 武汉钢铁有限公司 一种低成本高强镀锌板及其夹芯板的制造工艺
CN118685699A (zh) * 2023-03-23 2024-09-24 宝山钢铁股份有限公司 一种磷化性能优异的冷轧高强钢板及其制造方法
CN116716546A (zh) * 2023-05-30 2023-09-08 鞍钢股份有限公司 汽车用多用途高强钢及其制备方法
CN117144251A (zh) * 2023-09-07 2023-12-01 武汉钢铁有限公司 一种高硅低成本热镀锌高强钢及其生产方法
CN117802419B (zh) * 2023-12-25 2025-06-03 鞍钢股份有限公司 一种1.0GPa级抗氢脆型冷轧CH钢及其制备方法

Family Cites Families (29)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2652539B2 (ja) 1987-09-21 1997-09-10 株式会社神戸製鋼所 張出し成形性及び疲労特性にすぐれる複合組織高強度冷延鋼板の製造方法
JPH0735536B2 (ja) * 1988-01-14 1995-04-19 株式会社神戸製鋼所 高延性高強度複合組織鋼板の製造法
JP3257009B2 (ja) 1991-12-27 2002-02-18 日本鋼管株式会社 高加工性高強度複合組織鋼板の製造方法
JP2776203B2 (ja) * 1993-06-17 1998-07-16 住友金属工業株式会社 常温非時効性に優れた冷延鋼板の製造方法
TW504519B (en) 1999-11-08 2002-10-01 Kawasaki Steel Co Hot dip galvanized steel plate excellent in balance of strength and ductility and in adhesiveness between steel and plating layer, and method for producing the same
DE10347312B3 (de) 2003-10-08 2005-04-14 Air Liquide Deutschland Gmbh Verfahren zur Wärmebehandlung von Eisenwerkstoffen
JP3889768B2 (ja) * 2005-03-31 2007-03-07 株式会社神戸製鋼所 塗膜密着性と延性に優れた高強度冷延鋼板および自動車用鋼部品
EP1978113B1 (en) * 2005-12-06 2018-08-01 Kabushiki Kaisha Kobe Seiko Sho High-strength galvannealed sheet steels excellent in powdering resistance and process for production of the same
JP4503001B2 (ja) 2006-11-21 2010-07-14 株式会社神戸製鋼所 耐パウダリング性と加工性に優れた高強度合金化溶融亜鉛めっき鋼板
JP5092507B2 (ja) 2007-04-06 2012-12-05 住友金属工業株式会社 高張力合金化溶融亜鉛めっき鋼板とその製造方法
EP2009127A1 (en) * 2007-06-29 2008-12-31 ArcelorMittal France Process for manufacturing a galvanized or a galvannealed steel sheet by DFF regulation
EP2009129A1 (en) * 2007-06-29 2008-12-31 ArcelorMittal France Process for manufacturing a galvannealed steel sheet by DFF regulation
JP5402007B2 (ja) 2008-02-08 2014-01-29 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
US8808656B2 (en) 2008-07-25 2014-08-19 National Institute For Materials Science Garnet-type single crystal, optics using same and related apparatus thereof
JP5402357B2 (ja) 2008-07-30 2014-01-29 Ｊｆｅスチール株式会社 化成処理性に優れた高Ｓｉ冷延鋼板の製造方法
JP5239644B2 (ja) 2008-08-29 2013-07-17 Ｊｆｅスチール株式会社 熱疲労特性、高温疲労特性、耐酸化性および靭性に優れるフェライト系ステンレス鋼
JP5438302B2 (ja) * 2008-10-30 2014-03-12 株式会社神戸製鋼所 加工性に優れた高降伏比高強度の溶融亜鉛めっき鋼板または合金化溶融亜鉛めっき鋼板とその製造方法
JP5305149B2 (ja) * 2009-01-05 2013-10-02 新日鐵住金株式会社 成形性に優れた溶融亜鉛めっき高強度鋼板およびその製造方法
JP5185874B2 (ja) 2009-03-30 2013-04-17 株式会社神戸製鋼所 高強度鋼板の製造方法
CN102341518B (zh) * 2009-04-03 2013-04-10 株式会社神户制钢所 冷轧钢板及其制造方法
JP5493986B2 (ja) * 2009-04-27 2014-05-14 Ｊｆｅスチール株式会社 加工性に優れた高強度鋼板および高強度溶融亜鉛めっき鋼板並びにそれらの製造方法
JP5703608B2 (ja) * 2009-07-30 2015-04-22 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5327106B2 (ja) 2010-03-09 2013-10-30 Ｊｆｅスチール株式会社 プレス部材およびその製造方法
JP5668337B2 (ja) 2010-06-30 2015-02-12 Ｊｆｅスチール株式会社 延性及び耐遅れ破壊特性に優れる超高強度冷延鋼板およびその製造方法
WO2012020511A1 (ja) 2010-08-12 2012-02-16 Ｊｆｅスチール株式会社 加工性および耐衝撃性に優れた高強度冷延鋼板およびその製造方法
TWI475114B (zh) * 2010-08-18 2015-03-01 Jfe Steel Corp High strength cold rolled steel sheet excellent in workability and impact resistance and a method of manufacturing the same
JP5462742B2 (ja) 2010-08-20 2014-04-02 株式会社神戸製鋼所 機械的特性の安定性に優れた高強度鋼板の製造方法
JP5825119B2 (ja) * 2011-04-25 2015-12-02 Ｊｆｅスチール株式会社 加工性と材質安定性に優れた高強度鋼板およびその製造方法
CN102758143A (zh) * 2011-04-25 2012-10-31 宝山钢铁股份有限公司 一种抗拉强度大于1180MPa的热镀锌钢板及其制造方法

Also Published As

Publication number Publication date
CA2889927A1 (en) 2014-05-22
US20160108492A1 (en) 2016-04-21
JP2016504490A (ja) 2016-02-12
MX380341B (es) 2025-03-12
WO2014075405A1 (zh) 2014-05-22
EP2921569A4 (en) 2016-07-27
CN103805840A (zh) 2014-05-21
US10100385B2 (en) 2018-10-16
CN103805840B (zh) 2016-12-21
CA2889927C (en) 2021-10-26
EP2921569B1 (en) 2018-10-31
EP2921569A1 (en) 2015-09-23
JP6208246B2 (ja) 2017-10-04
KR20150084062A (ko) 2015-07-21
KR102100727B1 (ko) 2020-04-14
ES2701407T3 (es) 2019-02-22

Similar Documents

Publication Publication Date Title
MX2015005838A (es) Plancha de acero galvanizado en caliente super-resistente y de elevada aptitud de conformacion y su metodo de fabricacion.
UA117865C2 (uk) Високоміцна багатофазна сталь, спосіб її одержання та застосування
UA117134C2 (uk) Холоднокатаний сталевий лист, спосіб його виробництва і автотранспортний засіб
MX388381B (es) Acero de elevada resistencia y procedimiento de fabricacion.
MX2018007649A (es) Metodo para producir una lamina de acero recubierta de alta resistencia que tenga ductilidad y conformabilidad mejorada, y lamina de acero recubierta obtenida.
UA122878C2 (uk) Спосіб виробництва високоміцної листової сталі, яка характеризується покращеними пластичністю і штампованістю, і одержана листова сталь
MX395449B (es) Lámina de acero galvanizada de alta resistencia y método para producir la misma.
WO2016001898A3 (en) Method for producing a high strength steel sheet having improved strength, ductility and formability
IN2014DN11262A (es)
MX2017015841A (es) Acero de alta resistencia y metodo de fabricacion.
MX2016001013A (es) Hoja de acero que tiene propiedades mecanicas de resistencia y ductibilidad muy altas, metodo de fabricacion y uso de tales hojas.
MX387576B (es) Acero martensítico con resistencia a fractura retardada y método de fabricación.
MX2016014963A (es) Tira de acero que tiene alta resistencia y alta plasticidad, la tira de acero tiene un recubrimiento a base de zinc en caliente.
UA119459C2 (uk) Спосіб виготовлення високоміцного сталевого листа і одержаний лист
WO2016001895A3 (en) Method for producing a high strength coated steel sheet having improved strength, ductility and formability
UA114877C2 (uk) Двічі відпалений сталевий лист з високою механічною міцністю і пластичністю, спосіб виготовлення і використання такого листа
UA115745C2 (uk) Спосіб виготовлення високоміцного сталевого листа з покриттям або без покриття і одержаний лист
MX389187B (es) Metodo para producir una hoja de acero de alta resistencia que tiene resistencia y capacidad de formacion mejoradas y hoja obtenida.
RU2016151388A (ru) Способ получения высокопрочного стального листа с покрытием, имеющего улучшенную прочность и пластичность, и полученный лист
MX2013005011A (es) Hoja de acero laminado de frio de alta resistencia que tiene capacidad de embuticion profunda y capacidad de temple en horno excelentes y metodo para su fabricacion.
UA118706C2 (uk) Спосіб виробництва сталевого листа з покриттям, що має підвищену міцність, пластичність і деформованість
RU2016151793A (ru) Способ изготовления высокопрочной листовой стали, имеющей улучшенную формуемость, и полученный лист
MX2015013579A (es) Lamina de acero recocida despues de galvanizada de alta resistencia y metodo para la fabricacion de la misma.
CA3061264C (en) Method for producing a high strength steel sheet having high ductility, formability and weldability, and obtained steel sheet
WO2016001892A3 (en) Method for manufacturing a high strength steel sheet having improved formability and ductility and sheet obtained