CN1297519C - 一种具远红外线照射作用的纳米釉料及其应用方法 - Google Patents
一种具远红外线照射作用的纳米釉料及其应用方法 Download PDFInfo
- Publication number
- CN1297519C CN1297519C CNB2003101016846A CN200310101684A CN1297519C CN 1297519 C CN1297519 C CN 1297519C CN B2003101016846 A CNB2003101016846 A CN B2003101016846A CN 200310101684 A CN200310101684 A CN 200310101684A CN 1297519 C CN1297519 C CN 1297519C
- Authority
- CN
- China
- Prior art keywords
- glaze
- far
- oxide
- nano
- ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明一种具远红外线照射作用的纳米釉料，是由35～65%的熔剂、1～35%的助熔剂、0～25%的耐火剂、0.1～5%的黏剂、0.5～30%的远红外线粉材以及0.5～10%的纳米材料所混合而成，再加水研磨成浓度为330g/200cc～370g/200cc，细度为200～325目的釉料，并于实际施作时是披覆于陶瓷生胚或素胚的表面，以1120℃～1350℃的温度烧结成具有远红外线照射作用以及具有纳米特性的陶瓷制品，得以经由纳米材料的特性常效保持该陶瓷制品表面的光洁、美观，并产生具有防止细菌、病毒附着滋生的抗菌作用，以及经由该陶瓷制品的远红外线照射功能，常效活化所盛装或所通过物质的分子特性，而得以提升该物质的功能。
Description
技术领域
本发明涉及一种可披覆于陶瓷生胚或素胚的表面，并连同陶瓷胚料烧结成具有远红外线照射作用以及具纳米特性的陶瓷制品的釉料。
背景技术
按，一般应用于饮食容器、建材、卫生设备等的陶瓷制品，主要是将黏土、长石、石英等陶瓷粉末颗粒经混合、球磨、成形等步骤，做成陶瓷胚体，陶瓷生胚的表面会忠实的反映出模具表面的粗糙程度及所使用陶瓷粉末颗粒的外貌及大小；也即，起始原料的颗粒越大，表面的粗糙度也将越大。
一般陶瓷产品的表面皆会被施加上一层釉药A，如图1所示，釉药A的原料与生胚或素胚B原料的主要成分大同小异；在烧成后釉药的玻璃相较多，而借此玻璃相流动使胚体的表面较为平滑且光亮，釉药中又常加入色料，使釉面除能覆盖颜色较黄的胚体外，更能产生不同颜色，达美观的目的。
但因釉药的原料也是同陶瓷原料粉末一样。须经混合、球磨等步骤准备，所以釉层表面粗糙程度易受其原料颗粒大小的影响，当然也会同时受到胚体表面的粗糙度影响，再加上在烧成时，胚体及釉面皆会收缩，造成表面常有凹凸不平及针孔等缺陷的存在。这些凹凸不平的表面及针孔将会成为产生污物及细菌的积存位置，这些污物及细菌会不断累积及繁殖，使得陶瓷产品的表面肮脏，而须常常以刷洗及盐酸酸洗等方式才能除去污物及细菌，造成许多不便。
以致于，坊间即有在陶瓷制品表面喷涂光触媒在紫外线的照射下产生足以破坏病毒结构的氢氧自由基，但是如此的作法其杀菌功能不但将随着光触媒的脱离而消失，且其必须在紫外光的照射下方具有杀菌功能，且杀菌作用相对应抗菌作用更为消极，而无法真正达到如预期防止病毒扩散的目的。
又，在市面上也常见于陶瓷器皿中加入远红外线粉材，以使陶瓷器皿具有远红外线放射的效果，其是将远红外线粉体采大量地直接混合于陶瓷中，经拉胚烧结成食器，即可使该陶瓷器皿达到有效放射远红外线波，并借由该界面材黏附效果，而可对陶瓷器皿表面做毛孔填补功能有效隔离水体，但该远红外线粉体的原料是由铁、锰、铜或铬等金属所构成，故其颜色仅能维持在土黑色等仅数种颜色，无法达到多彩色泽的使用。
发明内容
本发明的主要目的在于提供一种可披覆于陶瓷生胚或素胚的表面，并连同陶瓷胚料烧结成具有远红外线照射作用以及具纳米特性的陶瓷制品的釉料，使该陶瓷制品表面常常有效保持光洁、美观，并产生具有防止细菌、病毒附着滋生的抗菌作用，以及常效活化所盛装或所通过物质的分子特性，以提升该物质的功能。
为了实现上述目的，本发明采用的技术方案为：
一种具远红外线照射作用的纳米釉料，其中：
该纳米釉料包括：
35～65％的熔剂、1～35％的助熔剂、0～25％的耐火剂、0.1～5％的黏剂、0.5～30％的远红外线粉材以及0.5～10％的纳米材料，所有百分数为重量百分数；其中，
该熔剂为长石、硼、硼酸、硼砂、硅酸硼和石英粉中的一种或数种；
该助熔剂为碳酸钙、碳酸钡、碳酸锂、碳酸镁、氧化锌和滑石粉中的一种或数种；
该耐火剂为高岭土和蛙目土中的一种或两种；
该黏剂由二氧化硅、氧化镁、三氧化二铝、三氧化二铁、氧化钙、氧化钠、氧化钾、氧化锂及无机树脂所构成；
该远红外线粉材为锆元素所构成的粉材；
该纳米材料为银、硅、铝、钠、钾、镁、钙、钛、铁、锂元素的组合物，或者为银、硅、铝、钠、钾、镁、钙、钛、铁、锂元素组合物的氧化物。
该硼由硼酸、硼砂、硅酸硼或硼的化合物中取得。
一种应用前述纳米釉料的方法，其中：
将该混合后的纳米釉料加水研磨成浓度为330g/200cc～370g/200cc，细度为200～325目的釉料，并于实际施作时是披覆于陶瓷生胚或素胚的表面，以1120℃～1350℃的温度烧结成具有远红外线照射作用以及具有纳米特性的陶瓷制品，得以经由纳米材料的特性常效保持该陶瓷制品表面的光洁、美观，并产生具有防止细菌、病毒附着滋生的抗菌作用，以及经由该陶瓷制品的远红外线照射功能，常效活化所盛装或所通过物质的分子特性，而得以提升该物质的功能。
附图说明
图1为一般陶瓷釉药喷施在胚体上的示意图；
图2为本发明的纳米釉料在胚体上的示意图；
【图号说明】
A 釉药
B 生胚或素胚
1 纳米釉料
具体实施方式
为能使贵审查员清楚本发明的结构组成，以及整体运作方式，现配合附图说明如下：
本发明一种具远红外线照射作用的纳米釉料，其整体釉料的组成物包括有：
A.熔剂，可以由长石、硼、硼酸、硼砂、硅酸硼或石英粉所构成，其比例约占釉料含量的35～65％。
B.助熔剂，可以由碳酸钙、碳酸钡、碳酸锂.碳酸镁、氧化锌或滑石粉所构成，其比例约占釉料含量的1～35％。
C.耐火剂，可以由高岭土或蛙目土所构成，其比例约占釉料含量的0～25％。
D.黏剂，可以由38.42％的二氧化硅、17.13％的氧化镁、0.69％的三氧化二铝、0.11％的三氧化二铁、3.25％的氧化钙、4.96％的氧化钠、0.07％的氧化钾、0.72％的氧化锂及24.84％的无机树脂所构成，其比例约占釉料含量的0.1～5％。
E.远红外线粉材，为锆元素的远红外线粉材，其比例约占釉料含量的0.5～30％。
F.纳米材料，可以为银、硅、铝、钠、钾、镁、钙、钛、铁、锂等元素的组合物，或其氧化物，其比例约占釉料含量的0.5～10％。
据以，即将前述熔剂、助熔剂、耐火剂、黏剂、远红外线材料以及纳米材料依适当的比例混合后，再加入相当于0.6～1.5倍釉料量的水加以充份研磨，将所有材料料研磨成浓度为330/200cc～370/200cc，细度为200～325目的釉料。
据以，所完成的釉料1在实际施作时，即可以披覆于陶瓷生胚或素胚B的表面，如图2所示，并连同陶瓷胚料以1120℃～1350℃的温度烧结成具有远红外线照射作用以及具有纳米特性的如饮水容器、滤材、建材、卫浴用具，甚至于油品活化器等陶瓷制品，令该陶瓷制品在实际使用时得以经由纳米材料的特性而完全不会让灰尘、油渍等污染物附着，而可常保该陶瓷制品表面的光洁、美观，并产生具有防止细菌、病毒附着滋生的抗菌作用，而得以应用在如马桶、小便斗的便器，以避免混于使排泄物中的病菌滋生，其抗菌作用较现有杀菌积极，而可有效防止传染病的扩散。
以及可经由该陶瓷制品的远红外线照射功能，活化所盛装或所通过物质的分子特性，而得以提升该物质的功能，并且使用锆元素为远1～3秒即作用，而经专家证实远红外线具有以下的特性：
1.放射形态为一辐射波，无须通过空气传导。
2.渗透力可直接深达人体皮下组织，直接从肌肤内部强化身体。
3.共鸣、吸收的形态因远红外线的波长可控制与人体所需所散发的远红外线的波长相近(4-50um)，物体受照射后，内部分子会产生共振共鸣作用，利于人体吸收，促进身体机能活化。
而其对人体直接助益有：
1.促进新陈代谢：改善血液循环不良、稳定血压、调和神经系统、排出长期有害的蓄积物、远离疾病。
2.预防癌细胞滋长：“温热疗法”为远红外线在医学上对人体的一大贡献，有效抑制及杀灭癌细胞。
3.预防及延缓老化：细胞活化后，内部代谢正常，外部皮肤毛孔不易残留化妆品或空气中的尘垢。
4.提升细胞再生力：活化细胞再生力，使头脑清醒，提升免疫力，进而对生殖能力也有相当的帮助。
又，本发明的釉料已有实际的试做成品，其中，应用在饮水容器时，在倒入茶或酒于试验陶瓷釉杯及普通陶瓷杯中，在一至三秒钟的时间作用下，即可明显感到不同的水质变化。
而当应用在香烟滤嘴的滤料使用时，在香烟点燃并立即吸烟的情况下，可马上感觉到烟味的不同，且发现该滤材因远红外线作用不会吸附焦油，故焦油无法吸附在滤材上，而使焦油残留于香烟的滤嘴中，当然人体也不会吸入过多的焦油量。
又，使用试验陶瓷釉茶杯分别以铅笔及沙拉油来测试，将铅笔于试验陶瓷釉茶杯的表面来回刮划，却丝毫不见铅笔芯的痕迹，或将沙拉油适量倒入试验陶瓷釉茶杯中，则完全不会附着于试验陶瓷釉茶杯釉面上。
而如此的抗菌、抗污的优越特性，本申请人也委托台湾检验科技股份有限公司(SGS)做测试：
测试一：在样品内外表面各滴入数滴污染剂(葡萄汁，湿茶包，咖啡，口红)，将样品静置温度23℃，相对湿度50％环境中16小时，使用一般抹布在沾有污染剂的表面上，施于正常手的力量来回擦拭二十次，记录擦拭后表面污染剂残留情形，其测试结果：表面无残留。
具体测试情况如下：
样品名称：奈米化远红外线陶瓷
产品叙述：抗菌、抗污
供应厂商：顺航工业有限公司
收样日期：2003年8月20日
测试日期：2003年8月22日
测试项目及方法：
抗污试验 参照ANSIZ124.6
1、在样品内外表面各滴数滴污染剂
2、将样品静置温度23℃，相对湿度50％环境中16小时
3、使用一般抹布在沾有污染剂的表面上，施于正常手的力量来回擦拭20次
4、记录擦拭后表面污染剂残留情形
测试结果：
| 污染剂 | 测试结果 |
| 葡萄汁湿茶包咖啡口红 | 表面无残留物表面无残留物表面无残留物表面无残留物 |
测试二：针对金黄色葡萄球菌及大肠杆菌的抗菌测试，其结果皆在小于10的测试极限，使证明本产品的抗菌效果极佳。
具体测试情况如下：
样品名称：奈米化远红外线陶瓷
产品叙述：抗菌、抗污
供应厂商：顺航工业有限公司
收样日期：2003年8月20日
检验日期：2003年8月26日
2003年9月02、09、19、23日
测试项目及方法：
抗菌测试：参照U.S.Pharmacopeia 24 NF 19 Microbiological
Tests(51)Antimicrobial Effectiveness Testing.
测试结果：
| 菌株名称 | 原接菌量 | 作用时间 | |||
| 9/02 | 9/09 | 9/19 | 9/23 | ||
| 黄金色葡萄球菌(CFU/直径4.5*4.5cm)大肠杆菌 (CFU/直径4.5*4.5cm) | 1.4*1051.9*105 | ＜10＜10 | ＜10＜10 | ＜10＜10 | ＜10＜10 |
尤其，本发明的釉料是与陶瓷生胚或素胚表面同时进行烧结成为完整的陶瓷制品，故其远红外线照射功能以及纳米特性是长效存在，不会因为长时间使用而衰退。
如上所述，本发明“一种具远红外线照射作用的纳米釉料”，于实际施行时是可披覆于陶瓷生胚或素胚的表面，并连同陶瓷胚料烧结成具有远红外线照射作用的及具纳米特性的陶瓷制品的釉料，使该陶瓷制品表面常效保持光洁、美观，并产生具有防止细菌、病毒附着滋生的抗菌作用，以及长效活化所盛装或所通过物质的分子特性，以提升该物质的功能，于是依法提呈发明专利申请；但是，以上的实施说明及图式所示，是本发明较佳实施例之一，并非以此局限本发明，因此，举凡与本发明的构造、装置、特征等近似或相雷同的，均应属本发明的创设目的及申请专利范围之内。
Claims (3)
1.一种具远红外线照射作用的纳米釉料，其特征在于：
该纳米釉料包括：
35～65％的熔剂、1～35％的助熔剂、0～25％的耐火剂、0.1～5％的黏剂、0.5～30％的远红外线粉材以及0.5～10％的纳米材料，所有百分数为重量百分数；
其中，该熔剂为长石、硼、硼酸、硼砂、硅酸硼和石英粉中的一种或数种；
该助熔剂为碳酸钙、碳酸钡、碳酸锂、碳酸镁、氧化锌和滑石粉中的一种或数种；
该耐火剂为高岭土和蛙目土中的一种或两种；
该黏剂由二氧化硅、氧化镁、三氧化二铝、三氧化二铁、氧化钙、氧化钠、氧化钾、氧化锂及无机树脂所构成；
该远红外线粉材为锆元素所构成的粉材；
该纳米材料为银、硅、铝、钠、钾、镁、钙、钛、铁、锂元素的组合物，或者为银、硅、铝、钠、钾、镁、钙、钛、铁、锂元素组合物的氧化物。
2.如权利要求1所述的一种具远红外线照射作用的纳米釉料，其中，该硼由硼酸、硼砂、硅酸硼或硼的化合物中取得。
3.一种应用如权利要求1至2所述的任一种纳米釉料的方法，其特征在于：
将该混合后的纳米釉料加水研磨成浓度为330g/200cc～370g/200cc，细度为200～325目的釉料，并于实际施作时是披覆于陶瓷生胚或素胚的表面，以1120℃～1350℃的温度烧结成具有远红外线照射作用以及具有纳米特性的陶瓷制品。