JP2011528382A - 可塑剤としてシクロヘキサン−1,2−ジカルボン酸エステルを有するポリビニルアセタールからなる可塑剤含有のシート - Google Patents
可塑剤としてシクロヘキサン−1,2−ジカルボン酸エステルを有するポリビニルアセタールからなる可塑剤含有のシート Download PDFInfo
- Publication number
- JP2011528382A JP2011528382A JP2011507934A JP2011507934A JP2011528382A JP 2011528382 A JP2011528382 A JP 2011528382A JP 2011507934 A JP2011507934 A JP 2011507934A JP 2011507934 A JP2011507934 A JP 2011507934A JP 2011528382 A JP2011528382 A JP 2011528382A
- Authority
- JP
- Japan
- Prior art keywords
- plasticizer
- sheet
- polyvinyl acetal
- containing sheet
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
合わせ安全ガラスは、一般に2枚のガラス板とそのガラス板と結合する中間シートとからなる。シート材料として、主に可塑剤含有の部分アセタール化されたポリビニルアルコール(ポリビニルアセタール)、特にポリビニルブチラール(PVB)が使用される。合わせ安全ガラス(VSG)は、例えば自動車分野においてフロントガラス又はサイドガラスとして、並びに建築分野において安全ガラスとして使用される。
低コストで調達でき、シート中で3G8と比べて低い湿分吸収を生じさせ、かつ十分に高いアセタール化度の部分アセタール化されたポリビニルアルコールと組み合わせて相容性であり、かつ良好な冷間柔軟性を有するシートを生じさせる可塑剤の使用下で、PVBシートを調製するという必要性が生じる。
1,2−シクロヘキサンジカルボン酸のジエステルで軟化させた、低い軟化温度(Tg)を有するポリビニルブチラールを含有するシートは、軟化剤として3G8を有するシートと比較して低い湿分吸収を有することが見出された。この組成のシートは、良好な可塑剤相容性及び良好な冷間柔軟性を有する。
従って、本発明の主題は、74℃より低い軟化温度を有するポリビニルアセタールを60〜90%及びエステル基中で4〜17個のC原子を有する少なくとも1種のシクロヘキサンジカルボン酸エステルを10〜40質量%(シートの全配合物に対して)含有する可塑剤含有のシートである。
・ 多価の脂肪族又は芳香族の酸のエステル、例えばジアルキルアジパート、例えばジヘキシルアジパート、ジオクチルアジパート、ヘキシルシクロヘキシルアジパート、ヘプチルアジパートとノニルアジパートとの混合物、ヘプチルノニルアジパート並びにアジピン酸と環式脂肪族又はエーテル結合を有するエステルアルコールとのエステル、ジアルキルセバカート、例えばジブチルセバカート並びにセバシン酸と環式脂肪族又はエーテル結合を含有するエステルアルコールとのエステル、フタル酸のエステル、例えばブチルベンジルフタラート又はビス−2−ブトキシエチルフタラート。
・ 多価の脂肪族又は芳香族のアルコールのエステル又はエーテル又は1種又は数種の非分枝又は分枝した脂肪族又は芳香族置換基を有するオリゴエーテルグリコール、例えばジ−、トリ−又はテトラグリコールと線状又は分枝した脂肪族又は環式脂肪族のカルボン酸とのエステル;後者のグループについての例として、ジエチレングリコール−ビス−(2−エチルヘキサノアート)、トリエチレングリコール−ビス−(2−エチルヘキサノアート)、トリエチレングリコール−ビス−(2−エチルブタノアート)、テトラエチレングリコール−ビス−n−ヘプタノアート、トリエチレングリコール−ビス−n−ヘプタノアート、トリエチレングリコール−ビス−n−ヘキサノアート、テトラエチレングリコール−ジメチルエーテル及び/又はジプロピレングリコールベンゾアート。
表1
本発明によるシートは、特に合わせ安全ガラスの製造のために1枚以上のガラス板と、当業者に公知の方法で貼り合わせることにより使用することができる。この合わせ安全ガラスは、自動車分野において例えばフロントガラスとして、建築分野において透明な部材として又は家具において使用することができる。本発明によるシートのわずかな湿分吸収及び可塑剤放出に基づき、これはガラス/シート/プラスチック積層体の製造のために、例えばPET層を有するガラス板の持続的な接着のため良好に適している。例えばポリカーボネート又はPMMAからなる2つのプラスチック板の接着も、本発明によるシートを用いて実施可能である。
a)透明な前面カバーと、
b)1つ又は複数の光敏感性の半導体層と、
c)少なくとも1つの可塑剤含有の、ポリビニルアセタールをベースとするシートと
d)背面のカバーとからなる積層体を有し、その際、この可塑剤含有のシートは74℃未満の軟化温度Tgを有するポリビニルアセタール60〜90%と、可塑剤としてエステル基中に4〜17個のC原子を有する少なくとも1つのシクロヘキサンジカルボン酸エステル10〜40質量%とを含有する光起電力モジュールである。
アルカリタイターの測定のために、可塑剤含有のポリビニルアセタールフィルムの3〜4gを、エタノール/THF(80:20)の混合物100ml中に一晩中磁気撹拌機で溶かした。これに希塩酸(c=0.01mol/リットル)10mlを添加し、引き続き、2−プロパノール(c=0.01mol/リットル)中のテトラブチルアンモニウムヒドロキシド(TBAH)の溶液でTitroprozessor を用いてブランクに対して電位差滴定した。このアルカリタイターは、次のように算出される:
アルカリタイター=試料100g当たりのHCl ml=(グラムで示す試料の質量によるTBAHブランク−TBAH試料×100の消費量)。
この実施例の本発明のシートは、通常では合わせ安全ガラス又は光起電力モジュールのためにPVBシートに課せられる要求を満たし、この要求は詳細には次のものである:高い透明性又は曇りの不在、わずかな固有色及びこの場合に特に低い黄色値、十分な機械的強度、低い固有臭、通常の粘着防止剤の添加の際の粘着性低下の可能性、ガラスに対する良好でかつ均一な接着作用及び高い体積抵抗。
Claims (15)
- 74℃未満の軟化温度Tgを有するポリビニルアセタール60〜90%と、可塑剤としてエステル基中で4〜17個のC原子を有する少なくとも1種のシクロヘキサンジカルボン酸エステル10〜40質量%とを有する、可塑剤含有のシート。
- 前記シートは、さらに少なくとも1種の他の可塑剤1〜40質量%を有することを特徴とする、請求項1記載の可塑剤含有のシート。
- 前記シートは、さらにジ−(2−ブトキシエチル)−アジパート(DBEA)、ジ−(2−ブトキシエチル)−セバカート(DBES)、ジ−(2−ブトキシエチル)−アゼラート、ジ−(2−ブトキシエチル)−グルタラート、ジ−(2−ブトキシエトキシエチル)−アジパート(DBEEA)、ジ−(2−ブトキシエトキシエチル)−セバカート(DBEES)、ジ−(2−ブトキシエトキシエチル)−アゼラート、ジ−(2−ブトキシエトキシエチル)−グルタラート、ジ−(2−ヘキソキシエチル)−アジパート、ジ−(2−ヘキソキシエチル)−セバカート、ジ−(2−ヘキソキシエチル)−アゼラート、ジ−(2−ヘキソキシエチル)−グルタラート、ジ−(2−ヘキソキシエトキシエチル)−アジパート、ジ−(2−ヘキソキシエトキシエチル)−セバカート、ジ−(2−ヘキソキシエトキシエチル)−アゼラート、ジ−(2−ヘキソキシエトキシエチル)−グルタラート、ジ−(2−ブトキシエチル)−フタラート及びジ−(2−ブトキシエトキシエチル)−フタラートの群から選択される、高い極性を有する少なくとも1種の可塑剤1〜40質量%を有することを特徴とする、請求項1又は2記載の可塑剤含有のシート。
- 前記シートは、さらに可塑剤として、式100×(O原子の数)/(C原子の数+H原子の数)により計算して9.4以下の極性を有する少なくとも1種の化合物1〜40質量%を有することを特徴とする、請求項1から3までのいずれか1項記載の可塑剤含有のシート。
- 前記ポリビニルアセタールのアセタール化度が81質量%以上であることを特徴とする、請求項1から4までのいずれか1項記載の可塑剤含有のシート。
- 前記ポリビニルアセタールのアセタート含有量が5質量%未満であることを特徴とする、請求項1から5までのいずれか1項記載の可塑剤含有のシート。
- 前記シートは、20〜30質量%のシクロヘキサンジカルボン酸エステルの含有量を有することを特徴とする、請求項1から6までのいずれか1項記載の可塑剤含有のシート。
- 前記シートは、4質量%未満の可塑剤放出を有することを特徴とする、請求項1から7までのいずれか1項記載の可塑剤含有のシート。
- ポリビニルアセタールとして、ポリビニルブチラールが使用されることを特徴とする、請求項1から8までのいずれか1項記載の可塑剤含有のシート。
- 合わせガラス、フロントガラス又は光起電力モジュールを製造するための、請求項1から9までのいずれか1項記載の可塑剤含有のシートの使用。
- a)透明な前面カバーと、b)1つ又は複数の光敏感性の半導体層と、c)少なくとも1つの可塑剤含有の、ポリビニルアセタールをベースとするシートと、d)背面のカバーとからなる積層体を有する光起電力モジュールにおいて、前記可塑剤含有のシートは74℃未満の軟化温度Tgを有するポリビニルアセタール60〜90%と、可塑剤としてエステル基中に4〜17個のC原子を有する少なくとも1つのシクロヘキサンジカルボン酸エステル10〜40質量%とを有することを特徴とする、光起電力モジュール。
- 前記可塑剤含有の、ポリビニルアセタールをベースとするシートc)が、塩基性化合物として1〜15個の炭素原子を有するカルボン酸の金属塩を含有することを特徴とする、請求項11記載の光起電力モジュール。
- 前記可塑剤含有の、ポリビニルアセタールをベースとするシートが、SiO2 0.001〜5質量%を含有することを特徴とする、請求項11又は12記載の光起電力モジュール。
- 透明な前面カバーa)又は背面のカバーd)上に1つ又は複数の光敏感性の半導体層b)が設けられ、可塑剤含有の、ポリビニルアセタールをベースとする少なくとも1つのシートc)により相互に接着されていることを特徴とする、請求項11から13までのいずれか1項記載の光起電力モジュール。
- 前記光敏感性の半導体層b)が、2つのシートc)の間に埋め込まれ、カバーa)及びb)と接着されていることを特徴とする、請求項1から13までのいずれか1項記載の光起電力モジュール。