CN103951466A - Double-layer reaction glaze and producing method thereof - Google Patents
Double-layer reaction glaze and producing method thereof Download PDFInfo
- Publication number
- CN103951466A CN103951466A CN201410135752.9A CN201410135752A CN103951466A CN 103951466 A CN103951466 A CN 103951466A CN 201410135752 A CN201410135752 A CN 201410135752A CN 103951466 A CN103951466 A CN 103951466A
- Authority
- CN
- China
- Prior art keywords
- parts
- coat enamel
- ground
- glaze
- cover
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a double-layer reaction glaze and a producing method thereof. The double-layer reaction glaze comprises a ground-coat glaze and a cover-coat glaze. The ground-coat glaze comprises the following components in parts by weight: 30 parts-50 parts of a feldspar powder, 15 parts-20 parts of a quartz powder, 5 parts-12 parts of calcite, 3 parts-5 parts of low-temperature frits, 5 parts-15 parts of kaolin, 2 parts-8 parts of zinc oxide, and 5 parts-20 parts of manganese carbonate or iron oxide. The cover-coat glaze comprises the following components in parts by weight: 20 parts-45 parts of low-temperature frits, 10 parts-20 parts of a quartz powder, 8 parts-15 parts of calcite, 5 parts-10 parts of zinc oxide, 4 parts-8 parts of dolomite, 4 parts-12 parts of kaolin, and 8 parts-30 parts of a pigment. The double-layer reaction glaze can present a quite good pattern-flowing effect, so that decoration is rich and colorful, and is the most changeful.
Description
Technical field
The present invention relates to a kind of double-deck reaction glaze and preparation method thereof.
Background technology
At present, in ceramic industry, the moulding of porcelain base is that the allotment of the basic glaze of quality products makes porcelain more dazzling brilliant, the porcelain base of same moulding, often because of glaze difference, and make human consumer's vision produce different impacts, under modern civilization tide promotes, the expectation of the aesthstic level of people to ceramic and pursuit are increasingly strong, and the ceramic of different decorative patterns makes ceramic effect field more colourful.But existing technique can not be controlled the decorative pattern that will present well, even cause it on cover-coat enamel, can not present decorative pattern.
Summary of the invention
Technical problem to be solved by this invention is the defect that overcomes prior art, and a kind of double-deck reaction glaze is provided, and it can present good decorative pattern flow effect, makes to decorate rich and varied, changeful.
In order to solve the problems of the technologies described above, technical scheme of the present invention is: a kind of double-deck reaction glaze, and it has ground-coat enamel and cover-coat enamel, and the component of described ground-coat enamel and each component weight part are as follows:
30 parts～50 parts of Feldspar Powders; 15 parts～20 parts of silica powders;
5 parts～12 parts, calcite; 3 parts～5 parts of low temperature frits;
5 parts～15 parts of kaolin; 2 parts～8 parts, zinc oxide;
5 parts～20 parts of manganous carbonate or ferric oxide;
The component of described cover-coat enamel and each component weight part are as follows:
20 parts～45 parts of low temperature frits; 10 parts～20 parts of silica powders;
8 parts～15 parts, calcite; 5 parts～10 parts, zinc oxide; 4 parts～8 parts of rhombspars;
4 parts～12 parts of kaolin; 8 parts～30 parts, colorant.
The present invention also provides a kind of making method of double-deck reaction glaze, and its step is as follows:
(1) get the raw materials ready according to following component and each component weight part:
A, ground-coat enamel:
30 parts～50 parts of Feldspar Powders;
15 parts～20 parts of silica powders; 5 parts～12 parts, calcite;
3 parts～5 parts of low temperature frits; 5 parts～15 parts of kaolin;
2 parts～8 parts, zinc oxide; 5 parts～20 parts of manganous carbonate or ferric oxide;
B, cover-coat enamel:
20 parts～45 parts of low temperature frits; 10 parts～20 parts of silica powders;
8 parts～15 parts, calcite; 5 parts～10 parts, zinc oxide; 4 parts～8 parts of rhombspars;
4 parts～12 parts of kaolin; 8 parts～30 parts, colorant;
(2) ground-coat enamel is pressed ground-coat enamel Liao ︰ Qiu ︰ water=1 ︰ 1.5 ︰ 0.5, wet ball grinding 12～16 hours, and the glaze after ball milling is crossed after 200 mesh sieves, then the ground-coat enamel of furnishing 30～50 degree Beaume slurry, gets the bright and clean base substrate of appearance and immerses this ground-coat enamel slurry, dry rear stand-by;
(3) cover-coat enamel is pressed cover-coat enamel Liao ︰ Qiu ︰ water=1 ︰ 1.5 ︰ 0.5, wet ball grinding 12～18 hours, the glaze after ball milling is crossed after 200 mesh sieves, then the cover-coat enamel of furnishing 30～50 degree Beaume slurry, the base substrate of upper base glaze slip is sprayed to this cover-coat enamel slurry, under the oxidizing atmosphere of 1170～1200 DEG C, fire finished product.
Adopt after technique scheme, need only in cover-coat enamel, add colorant, on the basis of ground-coat enamel, execute cover-coat enamel, cover-coat enamel and ground-coat enamel generation oxidizing reaction, level of response is different, make ceramic present good decorative pattern flow effect, make the more lively nature of decorative pattern of ceramic, careful, make to decorate rich and varied, changeful.
Embodiment
For content of the present invention is more easily expressly understood, below according to specific embodiment, the present invention is further detailed explanation.
Embodiment mono-
A kind of double-deck reaction glaze, it has ground-coat enamel and cover-coat enamel, and the component of described ground-coat enamel and each component weight part are as follows:
30 parts of Feldspar Powders; 15 parts of silica powders;
5 parts, calcite; 3 parts of low temperature frits;
5 parts of kaolin; 2 parts, zinc oxide;
5 parts of ferric oxide;
The component of described cover-coat enamel and each component weight part are as follows:
20 parts of low temperature frits; 10 parts of silica powders;
15 parts, calcite; 5 parts, zinc oxide; 4 parts of rhombspars;
4 parts of kaolin; 8 parts, colorant.
A making method for double-deck reaction glaze, its step is as follows:
(1) according to above component and each component weight part standby ground-coat enamel material and glaze material respectively:
(2) ground-coat enamel is pressed ground-coat enamel Liao ︰ Qiu ︰ water=1 ︰ 1.5 ︰ 0.5, and wet ball grinding is about 13 hours, and the glaze after ball milling is crossed after 200 mesh sieves, then the ground-coat enamel slurry of furnishing 35 degree Beaume left and right, gets the bright and clean base substrate of appearance and immerses this ground-coat enamel slurry, dry rear stand-by;
(3) cover-coat enamel is pressed cover-coat enamel Liao ︰ Qiu ︰ water=1 ︰ 1.5 ︰ 0.5, wet ball grinding 13 hours, the glaze after ball milling is crossed after 200 mesh sieves, then the cover-coat enamel slurry of furnishing 35 degree Beaume left and right, the base substrate of upper base glaze slip is sprayed to this cover-coat enamel slurry, under the oxidizing atmosphere of 1170～1200 DEG C, fire finished product.
The glaze of the bilayer reaction glaze that the method is fired can present good decorative pattern flow effect, makes to decorate rich and varied, changeful.
Embodiment bis-
A kind of double-deck reaction glaze, it has ground-coat enamel and cover-coat enamel, and the component of described ground-coat enamel and each component weight part are as follows:
50 parts of Feldspar Powders; 20 parts of silica powders;
12 parts, calcite; 5 parts of low temperature frits;
15 parts of kaolin; 8 parts, zinc oxide;
20 parts of manganous carbonates;
The component of described cover-coat enamel and each component weight part are as follows:
45 parts of low temperature frits; 20 parts of silica powders;
8 parts, calcite; 10 parts, zinc oxide; 8 parts of rhombspars;
12 parts of kaolin; 30 parts, colorant.
A making method for double-deck reaction glaze, its step is as follows:
(1) according to above component and each component weight part standby ground-coat enamel material and glaze material respectively:
(2) ground-coat enamel is pressed ground-coat enamel Liao ︰ Qiu ︰ water=1 ︰ 1.5 ︰ 0.5, and wet ball grinding is about 15 hours, and the glaze after ball milling is crossed after 200 mesh sieves, then the ground-coat enamel slurry of furnishing 45 degree Beaume left and right, gets the bright and clean base substrate of appearance and immerses this ground-coat enamel slurry, dry rear stand-by;
(3) cover-coat enamel is pressed cover-coat enamel Liao ︰ Qiu ︰ water=1 ︰ 1.5 ︰ 0.5, about wet ball grinding 17 hours, the glaze after ball milling is crossed after 200 mesh sieves, then the cover-coat enamel slurry of furnishing 45 degree Beaume left and right, the base substrate of upper base glaze slip is sprayed to this cover-coat enamel slurry, under the oxidizing atmosphere of 1170～1200 DEG C, fire finished product.
The glaze of the bilayer reaction glaze that the method is fired can present good decorative pattern flow effect, makes to decorate rich and varied, changeful.
Embodiment tri-
A kind of double-deck reaction glaze, it has ground-coat enamel and cover-coat enamel, and the component of described ground-coat enamel and each component weight part are as follows:
40 parts of Feldspar Powders; 18 parts of silica powders;
8 parts, calcite; 4 parts of low temperature frits;
10 parts of kaolin; 5 parts, zinc oxide;
13 parts of manganous carbonates;
The component of described cover-coat enamel and each component weight part are as follows:
33 parts of low temperature frits; 15 parts of silica powders;
11 parts, calcite; 8 parts, zinc oxide; 6 parts of rhombspars;
8 parts of kaolin; 19 parts, colorant.
A making method for double-deck reaction glaze, its step is as follows:
(1) according to above component and each component weight part standby ground-coat enamel material and glaze material respectively:
(2) ground-coat enamel is pressed ground-coat enamel Liao ︰ Qiu ︰ water=1 ︰ 1.5 ︰ 0.5, and wet ball grinding is about 15 hours, and the glaze after ball milling is crossed after 200 mesh sieves, then the ground-coat enamel slurry of furnishing 40 degree Beaume left and right, gets the bright and clean base substrate of appearance and immerses this ground-coat enamel slurry, dry rear stand-by;
(3) cover-coat enamel is pressed cover-coat enamel Liao ︰ Qiu ︰ water=1 ︰ 1.5 ︰ 0.5, about wet ball grinding 14 hours, the glaze after ball milling is crossed after 200 mesh sieves, then the cover-coat enamel slurry of furnishing 40 degree Beaume left and right, the base substrate of upper base glaze slip is sprayed to this cover-coat enamel slurry, under the oxidizing atmosphere of 1170～1200 DEG C, fire finished product.
The glaze of the bilayer reaction glaze that the method is fired can present good decorative pattern flow effect, makes to decorate rich and varied, changeful.
Above-described specific embodiment; technical problem, technical scheme and beneficial effect that the present invention is solved further describe; institute is understood that; the foregoing is only specific embodiments of the invention; be not limited to the present invention; within the spirit and principles in the present invention all, any amendment of making, be equal to replacement, improvement etc., within all should being included in protection scope of the present invention.
Claims (1)
1. a double-deck reaction glaze, is characterized in that: it has ground-coat enamel and cover-coat enamel,
The component of described ground-coat enamel and each component weight part are as follows:
30 parts～50 parts of Feldspar Powders; 15 parts～20 parts of silica powders;
5 parts～12 parts, calcite; 3 parts～5 parts of low temperature frits;
5 parts～15 parts of kaolin; 2 parts～8 parts, zinc oxide;
5 parts～20 parts of manganous carbonate or ferric oxide;
The component of described cover-coat enamel and each component weight part are as follows:
20 parts～45 parts of low temperature frits; 10 parts～20 parts of silica powders;
8 parts～15 parts, calcite; 5 parts～10 parts, zinc oxide; 4 parts～8 parts of rhombspars;
4 parts～12 parts of kaolin; 8 parts～30 parts, colorant.
A making method for double-deck reaction glaze as claimed in claim 1, is characterized in that the step of the method is as follows:
(1) get the raw materials ready according to following component and each component weight part:
A, ground-coat enamel:
30 parts～50 parts of Feldspar Powders;
15 parts～20 parts of silica powders; 5 parts～12 parts, calcite;
3 parts～5 parts of low temperature frits; 5 parts～15 parts of kaolin;
2 parts～8 parts, zinc oxide; 5 parts～20 parts of manganous carbonate or ferric oxide;
B, cover-coat enamel:
20 parts～45 parts of low temperature frits; 10 parts～20 parts of silica powders;
8 parts～15 parts, calcite; 5 parts～10 parts, zinc oxide; 4 parts～8 parts of rhombspars;
4 parts～12 parts of kaolin; 8 parts～30 parts, colorant;
(2) ground-coat enamel is pressed ground-coat enamel Liao ︰ Qiu ︰ water=1 ︰ 1.5 ︰ 0.5, wet ball grinding 12～16 hours, and the glaze after ball milling is crossed after 200 mesh sieves, then the ground-coat enamel of furnishing 30～50 degree Beaume slurry, gets the bright and clean base substrate of appearance and immerses this ground-coat enamel slurry, dry rear stand-by;
(3) cover-coat enamel is pressed cover-coat enamel Liao ︰ Qiu ︰ water=1 ︰ 1.5 ︰ 0.5, wet ball grinding 12～18 hours, the glaze after ball milling is crossed after 200 mesh sieves, then the cover-coat enamel of furnishing 30～50 degree Beaume slurry, the base substrate of upper base glaze slip is sprayed to this cover-coat enamel slurry, under the oxidizing atmosphere of 1170～1200 DEG C, fire finished product.