CN103694474B - 网状聚酰亚胺泡沫塑料制备方法 - Google Patents
网状聚酰亚胺泡沫塑料制备方法 Download PDFInfo
- Publication number
- CN103694474B CN103694474B CN201310689362.1A CN201310689362A CN103694474B CN 103694474 B CN103694474 B CN 103694474B CN 201310689362 A CN201310689362 A CN 201310689362A CN 103694474 B CN103694474 B CN 103694474B
- Authority
- CN
- China
- Prior art keywords
- polyimide foam
- foam
- netted
- netted polyimide
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种网状聚酰亚胺泡沫塑料制备方法，包括获得前体溶液、得到泡沫中间体，最后采用燃烧法得到网状聚酰亚胺泡沫塑料步骤。本发明提供的网状聚酰亚胺泡沫塑料的制备方法，先制取带有较粗泡室结构的半闭孔型的聚酰亚胺泡沫塑料，然后采取燃烧法除去泡沫泡室的壁膜，只留下其经络骨架而得到网状聚酰亚胺泡沫塑料，能够完全替代现有网状聚氨酯泡沫塑料，大幅提高液化气罐、油箱及各类易燃易爆气体和液体贮存容器的安全性。
Description
技术领域
本发明涉及一种网状聚酰亚胺泡沫塑料的制备方法，具体的说是网状聚酰亚胺泡沫塑料的工艺配方技术及其后期除去聚酰亚胺泡沫塑料泡室的膜而只留下其立体网状经络骨架的工艺方法。
背景技术
网状泡沫塑料填充到燃油系统及贮油设施内可起到抑制和延缓爆炸的作用，可应用到液化气罐、油箱及各类易燃易爆气体和液体贮存容器中，可避免意外雷电、静电、撞击、弹击等导致设备发生爆炸的风险，大大提高其安全性。当前最通行的做法是使用网状聚氨酯泡沫，由于聚氨酯泡沫在塑料在耐温、耐候、耐老化等方面存在一些缺陷。而聚酰亚胺材料刚好就没有以上缺点，因此，以聚酰亚胺代替聚氨酯制成的网状泡沫塑料具有更加广阔的应用前景。
发明内容
本发明的目的在于提供了一种网状聚酰亚胺泡沫塑料的制备方法，为实现上述目的本发明的具体方案如下：
一种网状聚酰亚胺泡沫塑料制备方法，包括以下步骤：
芳香二酐或芳香四酸配以交联剂、催化剂、有机硅表面活性剂、助剂、交联剂，在极性溶剂中搅拌混合获得前体溶液；
前体溶液中加入异氰酸酯、发泡剂控制搅拌得到泡沫中间体；
泡沫中间体用燃烧法处理成为网状聚酰亚胺泡沫塑料。
优选的，所述极性溶剂为N,N-二甲基甲酰胺。
优选的，所述交联剂为低分子醇。
优选的，所述催化剂由乙酸钾、三乙醇胺、三乙烯二胺组成。
优选的，所述助剂为超高分子量聚醚。
优选的，所述发泡剂包括甲醇、水或其混合物。
优选的，所述燃烧法包括以下步骤：
泡沫中间体置于能承受一定压强的密封容器中；
注入适量的氧气及相应量的甲烷；
火花塞点火让氧气和甲烷气在瞬间完全燃烧。
本发明提供的网状聚酰亚胺泡沫塑料的制备方法，先制取带有较粗泡室结构的半闭孔型的聚酰亚胺泡沫塑料，然后采取燃烧法除去泡沫泡室的壁膜，只留下其经络骨架而得到网状聚酰亚胺泡沫塑料，能够完全替代现有网状聚氨酯泡沫塑料，大幅提高液化气罐、油箱及各类易燃易爆气体和液体贮存容器的安全性。
具体实施方式
下面将以具体实施例来详细说明本发明，在此本发明的示意性实施例以及说明用来解释本发明，但并不作为对本发明的限定。
实施例
一种网状聚酰亚胺泡沫塑料制备方法，包括以下步骤：
1、芳香二酐或芳香四酸配以交联剂、催化剂、有机硅表面活性剂、助剂，在极性溶剂中搅拌混合获得前体溶液；
优选的，所述极性溶剂为N,N-二甲基甲酰胺。
优选的，所述交联剂为低分子醇。
优选的，所述催化剂由乙酸钾、三乙醇胺、三乙烯二胺组成。
优选的，所述助剂为超高分子量聚醚。
2、前体溶液中加入异氰酸酯、发泡剂控制搅拌得到泡沫中间体，基本化学反应如下：
优选的，所述发泡剂包括甲醇、水或其混合物。
工艺技术配方方案
| 原料 | 配方用量（重量份） |
| 芳香二酐 | 38 |
| 极性溶剂 | 62 |
| 低分子醇（分子量600左右） | 2.9 |
| 超高分子量聚醚 | 3.6 |
| 乙酸钾 | 0.01 |
| 三乙醇胺 | 0.30 |
| 三乙烯二胺 | 0.30 |
| 有机硅表面活性剂 | 5.15 |
| 无水甲醇 | 0.5 |
| 水 | 9 |
| 异氰酸酯 | 22+69（前体+发泡） |
3、泡沫中间体用燃烧法处理成为网状聚酰亚胺泡沫塑料
网化成型采用能承压20MPa以上的钢制密封容器，将聚酰亚胺泡沫置于其中，并确保其气密性、稳定性及环境安全性；
然后先注入适量的氧气，然后低速注入相应量的甲烷气体；
用火花塞点火让氧气和甲烷气在瞬间完全燃烧。
以上对本发明实施例所提供的技术方案进行了详细介绍，本文中应用了具体个例对本发明实施例的原理以及实施方式进行了阐述，以上实施例的说明只适用于帮助理解本发明实施例的原理；同时，对于本领域的一般技术人员，依据本发明实施例，在具体实施方式以及应用范围上均会有改变之处，综上所述，本说明书内容不应理解为对本发明的限制。
Claims (4)
1.一种网状聚酰亚胺泡沫塑料制备方法，其特征在于包括以下步骤：
芳香二酐或芳香四酸配以交联剂、催化剂、有机硅表面活性剂、助剂，在极性溶剂中搅拌混合获得前体溶液；
前体溶液中加入异氰酸酯、发泡剂控制搅拌得到泡沫中间体；
泡沫中间体用燃烧法处理成为网状聚酰亚胺泡沫塑料；
所述极性溶剂为N,N-二甲基甲酰胺；
所述交联剂为低分子醇；所述催化剂由乙酸钾、三乙醇胺、三乙烯二胺组成。
2.如权利要求1 所述的网状聚酰亚胺泡沫塑料制备方法，其特征在于：所述助剂为超高分子量聚醚。
3.如权利要求1 所述的网状聚酰亚胺泡沫塑料制备方法，其特征在于：所述发泡剂包括甲醇、水或其混合物。
4.如权利要求1 所述的网状聚酰亚胺泡沫塑料制备方法，其特征在于：所述燃烧法包括以下步骤：
泡沫中间体置于能承受一定压强的密封容器中；
先后注入适量的氧气及相应量的甲烷；
火花塞点火让氧气和甲烷气在瞬间完全燃烧。