WO2014065536A1 - 가변적 투명도를 갖는 수중유 형태의 오르가노겔 화장료 조성물 - Google Patents

가변적 투명도를 갖는 수중유 형태의 오르가노겔 화장료 조성물 Download PDF

Info

Publication number
WO2014065536A1
WO2014065536A1 PCT/KR2013/009263 KR2013009263W WO2014065536A1 WO 2014065536 A1 WO2014065536 A1 WO 2014065536A1 KR 2013009263 W KR2013009263 W KR 2013009263W WO 2014065536 A1 WO2014065536 A1 WO 2014065536A1
Authority
WO
WIPO (PCT)
Prior art keywords
oil
cosmetic composition
water
weight
organogel
Prior art date
Application number
PCT/KR2013/009263
Other languages
English (en)
French (fr)
Inventor
유현오
김종철
곽재훈
최은경
박동균
Original Assignee
주식회사 제닉
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 제닉 filed Critical 주식회사 제닉
Priority to JP2015538021A priority Critical patent/JP6038334B2/ja
Priority to US14/434,845 priority patent/US20150305990A1/en
Priority to CN201380055355.4A priority patent/CN104736139B/zh
Priority to EP13848453.0A priority patent/EP2913046A4/en
Publication of WO2014065536A1 publication Critical patent/WO2014065536A1/ko

Abstract

본 발명은 가변적 투명도를 갖는 수중유 형태의 오르가노겔 화장료 조성물에 관한 것으로서, 구체적으로 본 발명에 따른 유상부 및 수상부를 포함하는 수중유(oil in water, O/W) 형태의 오르가노겔(organogel) 화장료 조성물로서, 총 중량 대비 0.05 내지 50 중량%의 유상부 및 50 내지 99.95 중량%의 수상부를 포함하며 유상부와 수상부의 굴절률 차가 0.03 내지 0.16인 것을 특징으로 하는 화장료 조성물은, i) 온도 및 시간에 따른 제형 안정성이 우수할 뿐 아니라 ii) 수상부 및 유상부 내 함유 성분의 함량 조절을 통해 피부에 적용되었을 때 불투명한 유백색에서 투명하게 변색되어 적용 최적 시간을 용이하게 식별할 수 있으므로, 마스크 팩 등의 일정 적용시간을 필요로 하는 화장료 제품 개발 등에 유용하게 활용될 수 있다.

Description

가변적 투명도를 갖는 수중유 형태의 오르가노겔 화장료 조성물
본 발명은 가변적 투명도를 갖는 수중유 형태의 오르가노겔 화장료 조성물에 관한 것으로, 보다 구체적으로는 유상부 및 수상부를 포함하는 수중유(oil in water, O/W) 형태의 오르가노겔(organogel) 화장료 조성물로서, 유상부와 수상부의 굴절률 차의 변화를 통해 사용자의 피부 컨디션, 온도 및 습도 등에 따른 조성물의 최상의 적용시간을 육안으로 확인할 수 있도록 하는 팩 화장료 조성물에 관한 것이다.
팩은 스킨, 로션 및 크림과 같은 일반적인 기초 화장료 제품 유형의 하나로서, 피부에 단시간 적용하여 흡수시키는 다른 제품 유형들과 달리 장시간의 적용을 통해 수분 및 영양분의 공급을 극대화시킬 수 있는 기능성 화장료 유형이다. 이러한 팩의 종류로는 부직포에 에센스 액을 충진하거나 고형의 겔 타입으로 제조하여 피부에 부착 후 떼어낼 수 있는 마스크 타입, 또는 피부에 고르게 도포한 후 일정 시간이 지난 후에 물 등으로 씻어내거나 고형화된 화장료를 떼어낼 수 있는 크림 타입 등이 시판되고 있으며, 소비자의 기호에 따라 다양하게 선택하여 사용할 수 있다.
이러한 팩 화장료 조성물의 경우 통상적으로 피부에 일정시간 적용하여 수분 및 성분 흡수를 극대화한 후 제거하는 방법으로 사용하게 되는데, 사용자의 피부 컨디션, 피부의 온도 및 습도 등에 따라 최적의 적용시간이 달라질 수 있으므로 이를 육안으로 확인할 수 있도록 하는 화장료 조성물에 대한 연구가 당 분야에 지속적으로 이루어지고 있다.
이에 대한 지금까지의 연구들을 살펴보면, 일본특허공개 제1982-48905호 등에는 알칼리성 환경에서 변색되는 작용기를 갖는 페놀계 pH 지시약을 배합하는 방법이 개시되어 있으나 이러한 페놀계 지시약은 피부 트러블을 일으키는 문제가 있어 실제 화장료 조성물에 적용하기가 어려우며, 일본특허공개 제1995-82129호 및 미국특허등록 제6007799호 등에는 굴절률 차이가 적은 유상부와 수상부로 이루어진 수중유 에멀전(oil in water emulsion, O/W emulsion) 형태의 팩 화장료 조성물이 개시되어 있으나 이 경우에는 굴절률 차이를 이용할 수 없어, 투명에서 유백색으로 변화되는 시간을 조절하기가 어렵다.
따라서, 사용자의 피부 컨디션, 피부의 온도 및 습도 정도 등에 따라 최상의 적용시간을 육안으로 확인할 수 있도록 하는 팩 화장료 조성물에 대한 연구가 당 분야에 요구되고 있다.
[선행기술문헌]
특허문헌 1 일본특허공개 제1982-48905호
특허문헌 2 일본특허공개 제1995-82129호
특허문헌 3 미국특허등록 제6007799호
이에 본 발명자들은 사용자의 피부 컨디션, 온도 및 습도 등에 따라 화장료의 최상의 적용시간을 육안으로 확인할 수 있도록 하는 팩 화장료 조성물을 개발하기 위해 예의 연구한 결과, 유상부 및 수상부를 포함하는 수중유(oil in water, O/W) 형태의 오르가노겔(organogel) 화장료 조성물로서, 유상부와 수상부의 굴절률 차가 0.03 내지 0.16인 것을 특징으로 하는 화장료 조성물이 i) 제형 안정성이 우수하면서도 ii) 피부에 적용 시 수분 증발에 의해 불투명한 유백색에서 투명하게 변화됨으로써 개인차에 따른 최적의 제품 적용시간을 육안으로 확인할 수 있도록 함을 발견하여 본 발명을 완성하였다.
따라서, 본 발명의 목적은 사용자의 피부 컨디션, 온도 및 습도 등에 따라 달라지는 화장료의 최상의 적용 시간을 육안으로 용이하게 확인할 수 있도록 하는 수중유 형태의 오르가노겔 화장료 조성물을 제공하는 것이다.
상기 목적에 따라, 본 발명은 유상부 및 수상부를 포함하는 수중유(oil in water, O/W) 형태의 오르가노겔(organogel) 화장료 조성물로서, 총 중량 대비 0.05 내지 50.00 중량%의 유상부 및 50 내지 99.95 중량%의 수상부를 포함하며 유상부와 수상부의 굴절률 차가 0.03 내지 0.16인 것을 특징으로 하는 가변적 투명도를 갖는 오르가노겔 화장료 조성물을 제공한다.
본 발명의 일 실시예에 따르면, 상기 오르가노겔 화장료 조성물은 총 중량 대비 5 내지 20 중량%의 유상부 및 80 내지 95 중량%의 수상부를 포함할 수 있다.
본 발명의 일 실시예에 따르면, 상기 유상부 또는 수상부의 굴절률은 각각 1.350 내지 1.550 범위일 수 있다.
본 발명의 일 실시예에 따르면, 상기 수상부는 보습제, 겔화 고분자 및 정제수를 포함할 수 있다.
본 발명의 일 실시예에 따르면, 상기 보습제는 다가알코올류, 글리세린류, 당류 또는 이들의 혼합물로서, 조성물 총 중량 대비 1 내지 70 중량%로 포함될 수 있다.
본 발명의 일 실시예에 따르면, 상기 겔화 고분자로는 천연 당류, 친수성 겔화제 또는 이들의 혼합물로서, 조성물 총 중량 대비 0.1 내지 10 중량%로 포함될 수 있다.
본 발명의 일 실시예에 따르면, 상기 유상부는 통상적인 오일 및 계면활성제를 포함할 수 있다.
본 발명의 일 실시예에 따르면, 상기 오일은 에스테르계 오일, 탄화수소계 오일, 왁스류, 천연오일, 실리콘 오일 또는 이들의 혼합물로서, 조성물 총 중량 대비 0.05 내지 50.00 중량%로 포함될 수 있다.
본 발명의 일 실시예에 따르면, 상기 계면활성제는 다가 알코올과 지방산의 에스테르계 비이온계면활성제, 지방족 폴리옥시에틸렌 중합계의 비이온계면활성제, 솔비탄 에스테르의 폴리옥시에틸렌 에테르계의 비이온계면활성제, 천연유의 폴리옥시에틸렌 에테르계 비이온계면활성제, 폴리옥시에틸렌 에테르계 비이온계면활성제, 알칼리성 음이온계면활성제, 중성 음이온계면활성제 또는 이들의 혼합물로서, 조성물 총 중량 대비 10 중량% 이하로 포함될 수 있다.
본 발명에 따른 유상부 및 수상부를 포함하는 수중유(oil in water, O/W) 형태의 오르가노겔(organogel) 화장료 조성물로서, 총 중량 대비 0.05 내지 50 중량%의 유상부 및 50 내지 99.95 중량%의 수상부를 포함하며, 유상부와 수상부의 굴절률 차가 0.03 내지 0.16인 것을 특징으로 하는 가변적 투명도를 갖는 오르가노겔 화장료 조성물은, i) 온도 및 시간에 따른 제형 안정성이 우수할 뿐 아니라 ii) 수상부 및 유상부 내 함유 성분의 함량 조절을 통해 피부에 적용되었을 때 불투명한 유백색에서 투명하게 변화되어 적용 최적 시간을 육안으로 용이하게 식별할 수 있으므로, 마스크 팩 등의 일정 적용시간을 필요로 하는 화장료 제품 개발에 유용하게 활용될 수 있다.
이하, 본 발명을 상세히 설명한다.
본 발명의 가변적 투명도를 갖는 오르가노겔 화장료 조성물은 유상부 및 수상부를 포함하는 수중유(oil in water, O/W) 형태의 오르가노겔(organogel) 화장료 조성물로서, 총 중량 대비 0.05 내지 50.00 중량%의 유상부 및 50 내지 99.95 중량%의 수상부를 포함하며 유상부와 수상부의 굴절률 차가 0.03 내지 0.16인 것을 특징으로 한다. 따라서, 피부에 적용하는 경우 피부 온도에서 수분이 증발함에 따라 수상부와 유상부간의 굴절률차가 줄어들어 투명하게 변화됨으로써 개인차에 따른 최상의 제품 적용시간을 육안으로 쉽게 확인할 수 있는 장점이 있다.
본 발명의 화장료 조성물은 유상부가 수상부에 용해된 수중유 형태의 오르가노겔 화장료 조성물로서 보습감과 유분감이 우수하다. 본 발명의 화장료 조성물에서 상기 유상부는 조성물 총 중량 대비 0.05 내지 50.00 중량%, 바람직하게는 5 내지 20 중량%로 포함될 수 있으며, 이때 0.05 중량% 미만인 경우에는 함량이 미비하여 불투명한 유백색을 구현하는 것이 어렵고, 50.00 중량% 초과인 경우에는 수중유 형태의 제형 안정성이 떨어질 수 있다. 또한, 상기 수상부는 조성물 총 중량 대비 50 내지 99.95 중량%, 바람직하게는 80 내지 95 중량%로 포함될 수 있으며, 이때 50 중량% 미만인 경우에는 수중유 형태의 에멀젼 형성이 어렵고, 99.5 중량% 초과인 경우에는 불투명한 유백색 구현이 어렵다.
또한, 본 발명의 수중유 형태의 오르가노겔 화장료 조성물은 상기 수상부와 유상부 간의 굴절률 차가 0.03 내지 0.16으로 불투명한 유백색을 나타내며, 피부에 적용하는 경우 피부 온도에 의해 수분이 증발함으로써 수상부와 유상부 간의 굴절률 차가 줄어들어 투명하게 변화되는 것을 특징으로 한다. 본 발명의 일 실시예에 따르면, 상기 유상부 또는 수상부의 굴절률은 각각 1.350 내지 1.550 범위일 수 있고, 상기 굴절률 차는 0.03 내지 0.16, 바람직하게는 0.08일 수 있으며, 이때 굴절률의 차가 0.03 미만인 경우에는 불투명한 유백색 구현이 어렵고, 0.16을 초과하는 경우에는 굴절률 차가 너무 커져 피부 온도에서의 수분 증발 정도로 효과적인 투명 변색을 기대하기 어려울 수 있다.
본 발명의 화장료 조성물은 이러한 수상부와 유상부 간의 굴절률 차를 이용한 가변적 투명도를 가짐으로써 개인차에 따른 최상의 적용시간을 육안으로 쉽게 확인할 수 있는 장점이 있다.
본 발명의 화장료 조성물에서 수상부와 유상부 간의 굴절률 차는 화장료 조성물의 필수 성분, 적용 대상, 목적하는 적정 시간 등에 따라 상기 범위 내에서 적절히 조절할 수 있다. 이때, 유상부와 수상부의 굴절률의 차를 조절하기 위해, 수상부에 포함되는 보습제나 유상부에 첨가되는 오일 등의 함량을 조절할 수 있으며, 보다 구체적으로는 굴절률 차를 낮추기 위해서는 수상부에 포함되는 다가알코올류, 글리세린류 또는 당류 등의 함량을 높이거나 유상부에 포함되는 오일 등의 함량을 낮추거나 굴절률이 낮은 오일을 사용하는 방법을 채택할 수 있으며, 반대로 굴절률 차를 높이기 위해서는 수상부의 다가알코올류, 글리세린류 또는 당류 등의 함량을 낮추거나 유상부 오일의 함량 또는 굴절률을 높이는 방법을 채택할 수 있다.
본 발명의 오르가노겔 화장료 조성물에서, 상기 수상부는 통상적인 보습제, 겔화 고분자 및 정제수 등을 포함할 수 있다.
이때, 상기 보습제로는 피부에 수분을 공급하기 위한 통상적인 화장료 보습제 성분이라면 어느 것이든 사용할 수 있으며, 예를 들면 부틸렌글리콜, 프로필렌글리콜, 펜틸렌글리콜, 헥실렌글리콜, 폴리에틸렌글리콜 등의 다가알코올류; 글리세린, 디글리세린, 폴리글리세린 등의 글리세린류; 및 솔비톨 멀티톨, 자당, 전분당, 라쿠치톨 등의 당류 등을 포함하는 군으로부터 하나 이상 선택하여 사용할 수 있으나, 이에 제한되는 것은 아니다. 상기 보습제의 함량은 조성물 총 중량 대비 1 내지 70 중량%, 바람직하게는 5 내지 45 중량%일 수 있으며, 이때 1 중량% 미만인 경우에는 수상부와 유상부 간의 굴절률 차가 너무 커져 투명도 변화가 일어나기 어려우며, 70 중량% 초과인 경우에는 수상부와 유상부의 굴절률의 차가 너무 낮아져 유백색 구현이 어려워질 수 있다.
또한, 상기 겔화 고분자로는 화장료 조성물의 오르가노겔 형태 구현을 위해 사용되는 통상적인 겔화 고분자라면 어느 것이든 사용할 수 있으며, 예를 들면 갈락토만난, 글루코만난, 구아껌, 로카스트 빈 껌, 플루로닉, 아가, 알긴, 카라기난, 잔탄, 겔란, 젤라틴, 메틸셀룰로오스, 셀룰로오스, 카르복시메틸셀룰로오스, 히드록시에틸셀룰로오스 등의 천연 당류; 및 폴리아크릴레이트 또는 그의 염, 폴리메타크릴산, 카르복시비닐폴리머, 폴리비닐알코올, 폴리아크릴아미드, 폴리에틸렌옥시드, 폴리에틸렌이민, 폴리비닐피롤리돈 등의 친수성 겔화제를 포함하는 군으로부터 하나 이상 선택하여 사용할 수 있으나, 이에 제한되는 것은 아니다. 상기 겔화고분자는 조성물 총 중량 대비 0.1 내지 10 중량%, 바람직하게는 0.5 내지 5 중량%로 포함될 수 있으며, 이때 0.1 중량% 미만의 경우에는 겔의 경화로 인해 유연성이 떨어져 피부에 적용 시 밀착성이 떨어질 수 있고, 10 중량% 초과의 경우에는 겔의 연화가 심해져 형태 유지가 어렵고 탄력성이 떨어질 수 있다.
또한, 본 발명의 화장료 조성물에서, 상기 유상부는 통상적인 오일 및 계면활성제 등을 포함할 수 있다.
이때, 상기 오일로는 화장료 조성물에 통상적으로 사용될 수 있는 오일이라면 어느 것이든 사용할 수 있으며, 예를 들면 이소프로필미리스테이트, 에틸라우레이트, 에틸미리스테이트, 이소프로필팔미테이트, 부틸라우레이트, 헥실라우레이트, 카프릴릭/카프릭트리글리세라이드, 부틸렌글라이콜디카프릴레이트/디카프레이트, 이소프로필미리스테이트, 트리에틸헥사노인, 세틸에틸헥사노에이트, 옥틸도데칸올, 폴리올에스테르 등의 에스테르계 오일; 시클로도데칸, 이소옥탄, 리퀴드파라핀, 바세린, 하이드로제네이티드폴리데센, 시클로옥탄, 시클로펜탄 및 스쿠알렌 등의 탄화수소계 오일; 마이크로리스탈린왁스, 비즈왁즈, 라놀린왁스, 오조케라이트왁스, 칸데릴라왁스, 카르나우바왁스, 합성왁스 등의 왁스류; 호호바오일, 아보카도오일, 아몬드오일, 올리브오일, 참기름, 밀배아유, 사플라워오일, 동백기름, 피마자유, 포도씨오일, 녹차씨오일, 마카다미아넛츠오일, 야자유, 로즈힙오일, 경화유, 아르간오일, 산자나무오일, 아르간트리커넬오일 및 라벤더오일 등의 천연오일; 및 사이클로메치콘, 페닐트리메치콘, 사이클로펜타실록산, 디메치콘 등의 실리콘 오일을 포함하는 군으로부터 하나 이상 선택하여 사용할 수 있으나, 이에 제한되는 것은 아니다. 본 발명의 바람직한 일실시예에 따르면, 올리브오일, 디메치콘, 카프릴릭/카프릭트리글리세라이드, 세틸에틸헥사노에이트, 리퀴드파라핀 또는 이들의 혼합물 등을 사용할 수 있다. 상기 오일은 본 발명의 조성물 총 중량 대비 0.05 내지 50.00 중량%, 바람직하게는 5 내지 20 중량%로 포함될 수 있으며, 이때 0.05 중량% 미만인 경우에는 오르가노겔의 유백색 구현이 어렵고, 50.00 중량% 초과의 경우에는 수중유 타입의 에멀젼 형성이 어려워 제형 안정성이 떨어질 수 있다.
또한, 상기 계면활성제로는 화장료 조성물의 수중유 형태 구현 및 유지를 위해 통상적으로 사용되는 계면활성제라면 어느 것이든 사용할 수 있으며, 예를 들면 솔비탄 스테아레이트, 솔비탄 라우레이트, 솔비탄 팔미테이트, 글리세릴 스테아레이트, 폴리글리세릴 스테아레이트 등의 다가 알코올과 지방산의 에스테르계의 비이온계면활성제; 폴리옥시에틸렌 스테아릴에테르, 폴리옥시에틸렌 올리에이트 등의 지방족 폴리옥시에틸렌 중합계의 비이온계면활성제; 폴리옥시에틸렌 솔비탄 스테아레이트, 폴리옥시에틸렌 솔비탄 라우레이트, 폴리옥시에틸렌 솔비탄 올리에이트, 폴리옥시에틸렌 솔비톨 헥사올레이트 등의 솔비탄 에스테르의 폴리옥시에틸렌 에테르계의 비이온계면활성제; 폴리옥시에틸렌 하이드로제네이티드 캐스터오일 등의 천연유의 폴리옥시에틸렌 에테르계 비이온계면활성제; 폴록사머 168, 폴록사머 407등의 폴리옥시 프로필렌의 폴리옥시에틸렌 에테르계 비이온계면활성제; 소듐스테아레이트, 포타슘스테아레이트, 소듐 라우레이트 등의 알칼리성 음이온계면활성제; 및 소듐라우릴설페이트, 소듐라우레스설페이트, 암모늄라우레스설페이트, 포타슘세틸포스페이트 등의 중성 음이온계면활성제로 이루어진 군으로부터 하나 이상을 선택하여 사용할 수 있으나, 이에 제한되는 것은 아니다. 상기 계면활성제는 조성물 총 중량 대비 10 중량% 이하로, 바람직하게는 5 중량% 이하로 포함될 수 있으며, 이때 10.00 중량% 초과의 경우에는 피부자극을 유발할 수 있을 뿐 아니라 겔화 고분자의 겔화 형성을 저해할 수 있어 적절치 않다.
본 발명에 따른 수중유 형태의 오르가노겔 화장료 조성물은 상기 성분들 외에도 조성물의 효과를 떨어트리지 않는 범위 내에서 통상적인 pH조절제, 보존제, 향료, 색소, 살균제, 산화안정화제 또는 펄제 등을 추가로 포함할 수 있다.
본 발명의 수중유 형태의 오르가노겔 화장료 조성물은 통상적인 수중유 형태의 오르가노겔 화장료 조성물의 제조방법에 따라 제조할 수 있으며, 구체적으로 해당 성분들을 실온 또는 가열 혼합하는 방법을 통해 각각 수상부 혼합물 및 유상부 혼합물을 수득한 후 이들의 굴절률을 측정하고, 수득한 수상부 혼합물과 유상부 혼합물을 가열 혼합 후 냉각시키는 공정을 통해 제조할 수 있다.
본 발명의 바람직한 일 실시예에 따르면, 유상부의 각 성분들을 혼합 후 80℃로 가열하여 용해하여 유상부 혼합물을 수득하고, 수상부의 각 성분들을 실온에서 혼합 용해시켜 수상부 혼합물을 수득할 수 있었으며, 각 혼합물의 굴절률을 측정한 후 이들 수상부 및 유상부 혼합물들을 호모믹서를 이용하여 70~90℃ 및 3,000~3,500 rpm 조건에서 15~20분간 교반 혼합시키고 감압 탈포 후 35℃로 냉각하는 공정을 통해 본 발명의 오르가노겔 화장료 조성물을 제조할 수 있었다.
본 발명의 일실시예에 따르면, 본 발명에 따른 오르가노겔 화장료 조성물은 i) 온도 및 시간에 따른 제형 안정성이 우수할 뿐 아니라 ii) 수상부 및 유상부 내 함유 성분들의 함량을 조절하여 적합한 적용시간에 투명도를 나타낼 수 있도록 조절할 수 있음을 알 수 있었으며, 따라서 본 발명의 화장료 조성물을 피부에 적용하는 경우 적용 화장료가 불투명한 유백색에서 투명하게 변화되어 개인차에 따른 최적의 적용 시간을 육안으로 용이하게 식별할 수 있으므로 필수 성분 흡수의 극대화를 실현할 수 있다.
이하, 실시예를 통하여 본 발명을 더욱 상세히 설명하고자 한다. 이들 실시예는 오로지 본 발명을 예시하기 위한 것으로서, 본 발명의 범위가 이들 실시예에 의해 제한되는 것으로 해석되지 않는 것은 당 업계에서 통상의 지식을 가진 자에게 있어서 자명할 것이다.
실시예 1 내지 5
하기 표 1의 조성에 따라, 유상부의 각 성분들을 혼합 후 80℃로 가열하여 용해하였으며, 수상부의 각 성분들을 실온에서 혼합 용해시켰다. 이렇게 혼합된 수상부 및 유상부의 각 굴절률을 Abbe refractometers(A. KRUSS Optronic, Japan)를 이용하여 측정하였으며, 측정 후 각 실시예에 해당하는 수상부 및 유상부를 70~90℃ 및 3,000~3,500 rpm 조건에서 호모믹서를 이용하여 15~20분간 교반 혼합하였다. 교반된 수중유 유화물을 감압 탈포 후 35℃로 냉각하여 실시예 1 내지 5의 오르가노겔 화장료 조성물을 수득하였다.
표 1
구분 조성(중량%) 실시예 1 실시예 2 실시예 3 실시예 4 실시예 5
유상 세틸에틸헥사노에이트 8.80 8.80 9.60 0.4 44.40
디메치콘 0.80 0.80 - - 4.00
폴리소르베이트 60 0.30 0.30 0.30 - 1.50
프로필파라벤 0.10 0.10 0.10 0.1 0.10
합계 10 10 10 0.5 50
수상 카라기난 1.00 1.00 1.00 1.00 1.00
로커스트빈껌 1.50 1.50 1.50 1.50 1.50
글리세린 28.30 50.30 8.30 31.80 15.30
부틸렌글리콜 6.00 8.00 2.00 7.00 3.00
메틸파라벤 0.20 0.20 0.20 0.20 0.20
정제수 53.00 29.00 77.00 58.00 29.00
합계 90 90 90 99.5 50
상기 실시예 1 내지 5의 화장료 조성물들의 유상부 및 수상부의 굴절률, 이들의 굴절률 차 및 중량비를 하기 표 2에 나타내었다.
표 2
실시예 1 실시예 2 실시예 3 실시예 4 실시예 5
수상부 굴절률 1.395 1.445 1.350 1.395 1.395
유상부 굴절률 1.475 1.475 1.500 1.475 1.475
O/W 굴절률 차 0.080 0.030 0.160 0.08 0.08
비교예 1 내지 4
상기 실시예 1 내지 5에서와 동일한 방법으로, 하기 표 3의 조성에 따라 비교예 1 내지 4의 화장료 조성물을 수득하였다.
표 3
구분 조성(중량%) 비교예1 비교예2 비교예3 비교예4
유상 세틸에틸헥사노에이트 8.80 - 0.2 53.10
페닐트리메티콘 - 9.60 - -
디메치콘 0.80 - - 5.00
폴리소르베이트 60 0.30 0.30 - 1.80
프로필파라벤 0.10 0.10 0.1 0.10
합계 10 10 0.3 60
수상 카라기난 1.00 1.00 1.00 1.00
로커스트빈껌 1.50 1.50 1.50 1.50
글리세린 55.30 2.30 31.90 12.80
부틸렌글리콜 8.00 1.00 7.00 2.5
메틸파라벤 0.20 0.20 0.20 0.20
정제수 24.00 84.00 58.10 22.00
합계 90 90 99.7 40
상기 비교예 1 내지 4의 화장료 조성물들의 유상부 및 수상부의 굴절률, 이들의 굴절률 차 및 중량비를 하기 표 4에 나타내었다.
표 4
비교예 1 비교예 2 비교예 3 비교예 4
수상부 굴절률 1.465 1.535 1.395 1.395
유상부 굴절률 1.475 1.335 1.475 1.475
O/W 굴절률 차 0.010 0.2 0.08 0.08
시험예
상기 실시예 1 내지 5 및 비교예 1 내지 4에서 제조된 오르가노겔 화장료 조성물들의 안정성 및 백색에서 투명으로 변화되는 시간을 다음과 같이 평가하였다.
1) 안정성 평가
각 화장료 조성물을 실온, 35℃, 50℃ 또는 사이클링(cycling) 환경(-4℃~45℃/일) 조건에서 1주일, 2주일, 1개월, 2개월 또는 3개월 단위로 보관한 후, 각 조건에서의 제형의 안정성을 육안으로 관찰하여 하기 평가기준에 따라 평가하였으며, 그 결과를 표 5 및 표 6에 나타내었다.
[평가기준]
◎: 분리현상 발생 없음 △: 일부 분리현상 발생
×: 분리현상 발생 심함
표 5
실시예 온도 1주일 2주일 1개월 2개월 3개월
실시예 1 실온 ◎ ◎ ◎ ◎ ◎
35℃ ◎ ◎ ◎ ◎ ◎
50℃ ◎ ◎ ◎ ◎ ◎
사이클링 ◎ ◎ ◎ ◎ ◎
실시예 2 실온 ◎ ◎ ◎ ◎ ◎
35℃ ◎ ◎ ◎ ◎ ◎
50℃ ◎ ◎ ◎ ◎ ◎
사이클링 ◎ ◎ ◎ ◎ ◎
실시예 3 실온 ◎ ◎ ◎ ◎ ◎
35℃ ◎ ◎ ◎ ◎ ◎
50℃ ◎ ◎ ◎ ◎ ◎
사이클링 ◎ ◎ ◎ ◎ ◎
실시예 4 실온 ◎ ◎ ◎ ◎ ◎
35℃ ◎ ◎ ◎ ◎ ◎
50℃ ◎ ◎ ◎ ◎ ◎
사이클링 ◎ ◎ ◎ ◎ ◎
실시예 5 실온 ◎ ◎ ◎ ◎ ◎
35℃ ◎ ◎ ◎ ◎ ◎
50℃ ◎ ◎ ◎ ◎ ◎
사이클링 ◎ ◎ ◎ ◎ ◎
표 6
비교예 1 실온 ◎ ◎ ◎ ◎ ◎
35℃ ◎ ◎ ◎ ◎ ◎
50℃ ◎ ◎ ◎ ◎ ◎
사이클링 ◎ ◎ ◎ ◎ ◎
비교예 2 실온 ◎ ◎ ◎ ◎ ◎
35℃ ◎ ◎ ◎ ◎ ◎
50℃ ◎ ◎ ◎ ◎ ◎
사이클링 ◎ ◎ ◎ ◎ ◎
비교예 3 실온 ◎ ◎ ◎ ◎ ◎
35℃ ◎ ◎ ◎ ◎ ◎
50℃ ◎ ◎ ◎ ◎ ◎
사이클링 ◎ ◎ ◎ ◎ ◎
비교예 4 실온 △ × × × ×
35℃ △ × × × ×
50℃ × × × × ×
사이클링 △ × × × ×
그 결과, 상기 표 5 및 6에서 볼 수 있는 바와 같이, 실시예 1 내지 5의 오르가노겔 화장료 조성물 및 비교예 1 내지 3의 조성물은 모두 실온, 35℃ 50℃ 또는 사이클링 환경(-4℃~45℃/일) 조건에서 유상부와 수상부의 상 분리 현상이 발견되지 않았으며 안정성을 유지하는 것으로 확인하였다. 반면, 비교예 4의 화장료 조성물의 경우에는 수상부와 유상부의 상분리 현상이 확인되었으며, 다양한 온도 변화를 갖는 사이클링 조건에서도 제형 안정성이 현저히 떨어지는 것을 확인하였다.
2) 투명도 변화 평가
건강한 성인 남녀 50명을 대상으로 실시예 1 내지 5 및 비교예 1 내지 4의 오르가노겔 화장료 조성물을 각각 피부에 도포하여 1, 5, 10, 15, 20, 30, 40, 50 또는 60 분 후에 유백색에서 투명으로 변화된 정도를 육안으로 관찰하여 투명도 변화 평가기준(평가값: 1 - 불투명, 2 - 약간 불투명, 3 - 보통, 4 - 우수, 5 - 매우 우수)에 따라 평가하게 하였으며, 각 평가 결과들의 평균값을 산출하여 하기 표 7에 나타내었다.
표 7
　 평균값
1분 5분 10분 15분 20분 30분 40분 50분 1시간
실시예 1 1.00 1.3 1.9 2.98 3.43 4.44 5.00 5.00 5.00
실시예 2 2.98 3.45 4.75 5.00 5.00 5.00 5.00 5.00 5.00
실시예 3 1.00 1 1.60 2.12 3.12 3.58 3.98 4.12 4.85
실시예 4 1.00 1.27 2.13 3.22 3.52 4.54 5.00 5.00 5.00
실시예 5 1.00 1.32 2.34 3.32 3.64 4.62 5.00 5.00 5.00
비교예 1 5.00 5.00 5.00 5.00 5.00 5.00 5.00 5.00 5.00
비교예 2 1.00 1.00 1.00 1.23 1.45 1.99 2.21 2.48 2.85
비교예 3 4.80 5.00 5.00 5.00 5.00 5.00 5.00 5.00 5.00
비교예 4 1.00 1.12 2.08 3.14 3.39 4.48 5.00 5.00 5.00
그 결과, 상기 표 7에서 볼 수 있는 바와 같이, 본 발명에 따른 실시예 1 내지 5의 오르가노겔 화장료 조성물들은 배합 한도에 따라 변화 시간에 차이는 있었으나 시간이 지남에 따라 유백색 불투명에서 투명으로 변화하는 것을 확인한 반면, 비교예 1 내지 4의 경우 처음부터 투명하거나(비교예 1 및 3), 불투명이어도 투명으로의 변화가 거의 일어나지 않거나(비교예 2), 일어나더라도 안정성이 떨어지는 것을 확인하였다(비교예 4).
이로써, 본 발명에 따른 오르가노겔 화장료 조성물은 수상부 및 유상부 내 함유 성분의 함량 조절을 통해 적합한 적용시간에 투명도를 나타낼 수 있도록 조절할 수 있음을 알 수 있었으며, 온도 및 시간에 따른 제형 안정성이 우수한 것을 알 수 있다.
이제까지 본 발명에 대하여 그 바람직한 실시예들을 중심으로 살펴보았다. 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자는 본 발명이 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 변형된 형태로 구현될 수 있음을 이해할 수 있을 것이다. 그러므로 개시된 실시예들은 한정적인 관점이 아니라 설명적인 관점에서 고려되어야 한다. 본 발명의 범위는 전술한 설명이 아니라 특허청구범위에 나타나 있으며, 그와 동등한 범위 내에 있는 모든 차이점은 본 발명에 포함된 것으로 해석되어야 할 것이다.

Claims (9)

  1. 유상부 및 수상부를 포함하는 수중유(oil in water, O/W) 형태의 오르가노겔(organogel) 화장료 조성물로서, 총 중량 대비 0.05 내지 50.00 중량%의 유상부 및 50 내지 99.95 중량%의 수상부를 포함하며 유상부와 수상부의 굴절률 차가 0.03 내지 0.16인 것을 특징으로 하는 가변적 투명도를 갖는 오르가노겔 화장료 조성물.
  2. 제 1 항에 있어서, 상기 오르가노겔 화장료 조성물은 총 중량 대비 5 내지 20 중량%의 유상부 및 80 내지 95 중량%의 수상부를 포함하는 것을 특징으로 하는 오르가노겔 화장료 조성물.
  3. 제 1 항에 있어서,
    상기 유상부 및 수상부의 굴절률은 각각 1.350 내지 1.550 범위인 것을 특징으로 하는 오르가노겔 화장료 조성물.
  4. 제 1 항에 있어서,
    상기 수상부는 보습제, 겔화 고분자 및 정제수를 포함하는 것을 특징으로 하는 오르가노겔 화장료 조성물.
  5. 제 4 항에 있어서,
    상기 보습제는 다가알코올류, 글리세린류, 당류 또는 이들의 혼합물로서, 조성물 총 중량 대비 1 내지 70 중량%로 포함되는 것을 특징으로 하는 오르가노겔 화장료 조성물.
  6. 제 4 항에 있어서,
    상기 겔화 고분자로는 천연 당류, 친수성 겔화제 또는 이들의 혼합물로서, 조성물 총 중량 대비 0.1 내지 10 중량%로 포함되는 것을 특징으로 하는 오르가노겔 화장료 조성물.
  7. 제 1 항에 있어서,
    상기 유상부는 오일 및 계면활성제를 포함하는 것을 특징으로 하는 오르가노겔 화장료 조성물.
  8. 제 7 항에 있어서,
    상기 오일은 에스테르계 오일, 탄화수소계 오일, 왁스류, 천연오일, 실리콘 오일 또는 이들의 혼합물로서, 조성물 총 중량 대비 0.05 내지 50.00 중량%로 포함되는 것을 특징으로 하는 오르가노겔 화장료 조성물.
  9. 제 7 항에 있어서,
    상기 계면활성제는 다가 알코올과 지방산의 에스테르계의 비이온계면활성제, 지방족 폴리옥시에틸렌 중합계의 비이온계면활성제, 솔비탄 에스테르의 폴리옥시에틸렌 에테르계의 비이온계면활성제, 천연유의 폴리옥시에틸렌 에테르계 비이온계면활성제, 폴리옥시에틸렌 에테르계 비이온계면활성제, 알칼리성 음이온계면활성제, 중성 음이온계면활성제 또는 이들의 혼합물로서, 조성물 총 중량 대비 10 중량% 이하로 포함되는 것을 특징으로 하는 오르가노겔 화장료 조성물.
PCT/KR2013/009263 2012-10-23 2013-10-16 가변적 투명도를 갖는 수중유 형태의 오르가노겔 화장료 조성물 WO2014065536A1 (ko)