[go: up one dir, main page]

JP3698143B2 - フィルタ用多孔質Ｓｉ３Ｎ４とその製造方法 - Google Patents

フィルタ用多孔質Ｓｉ３Ｎ４とその製造方法 Download PDF

Info

Publication number
JP3698143B2
JP3698143B2 JP2003012370A JP2003012370A JP3698143B2 JP 3698143 B2 JP3698143 B2 JP 3698143B2 JP 2003012370 A JP2003012370 A JP 2003012370A JP 2003012370 A JP2003012370 A JP 2003012370A JP 3698143 B2 JP3698143 B2 JP 3698143B2
Authority
JP
Japan
Prior art keywords
powder
porous
mass
parts
binder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP2003012370A
Other languages
English (en)
Other versions
JP2004223359A (ja
Inventor
武 佐藤
辰珠 朴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sumitomo Electric Industries Ltd
Original Assignee
Sumitomo Electric Industries Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sumitomo Electric Industries Ltd filed Critical Sumitomo Electric Industries Ltd
Priority to JP2003012370A priority Critical patent/JP3698143B2/ja
Priority to US10/750,870 priority patent/US7153484B2/en
Priority to CNB2004100014782A priority patent/CN1247488C/zh
Priority to KR1020040003643A priority patent/KR20040067951A/ko
Priority to EP04250236A priority patent/EP1443030B1/en
Priority to TW093101308A priority patent/TWI316052B/zh
Publication of JP2004223359A publication Critical patent/JP2004223359A/ja
Application granted granted Critical
Publication of JP3698143B2 publication Critical patent/JP3698143B2/ja
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Description

【０００１】
【発明の属する技術分野】
本発明は、半導体を研磨した水など液体中の異物を分離あるいは除去するためのフィルタ用多孔質Si3N4の製造方法に関するものである。
【０００２】
【従来の技術】
Si3N4焼結体の原料として、Si3N4粉末を原料とするものと金属珪素粉末を原料とするものがある。特許文献1は、原料のα-Si3N4粉末に希土類元素の化合物を加えて焼結し、アスペクト比が3以上の柱状β-Si3N4粒子が絡み合ったSi3N4多孔体が開示されている。この多孔体は、気孔率が30％以上、平均細孔径が0.05〜12μmの範囲にあり、気孔率が高くかつ強度の高いセラミックス多孔体である。そして、このような特性は、Si3N4の結晶粒が6角柱状の形態を持つことによって達成される(例えば、特許文献1）。
【０００３】
また特許文献2には、金属珪素粒子と珪素酸化物粒子を出発原料とし、ガスなどの流体との接触面積を大きくしたおおむね柱状体の外形を有する窒化珪素多孔体に関する発明が開示されている。この多孔体は、以下の工程を経て製造される。即ち、まず平均粒子径1〜150μmの金属珪素粒子100質量部と、珪素酸化物粒子をSiO2に換算して0.2〜45質量部含む混合物に、成形助剤と水を加えて混練する。次に、混練物を金型押出しにより互いに平行な貫通孔を2つ以上有するように成形し、得られた脱バインダ体を温度1200℃〜1400℃の窒素雰囲気中で第一段の熱処理工程と、その後に温度1500〜1800℃の範囲で第二の熱処理工程を経る。このようにして得られた多孔体は、貫通孔の表面からおおむね垂直方向に内側に向けて多数の柱状結晶を析出したものである(例えば、特許文献2）。
【０００４】
【特許文献１】
WO 94/27929号公報
第3頁、第29頁
【特許文献２】
特開2001-316188号公報
第2頁、第4〜5頁
【０００５】
【発明が解決しようとする課題】
特許文献1のSi3N4粉末を出発原料とするものは、原料費が高くなり安価なSi3N4多孔質体を得ることができない。また、特許文献2の出発原料は、金属珪素と二酸化珪素であり、焼結体の中には柱状結晶が析出している。柱状結晶が析出するメカニズムは、多孔体の流路内に生成した一酸化珪素の気相が残留炭素および窒素と反応して窒化珪素粒子を生成する。生成した窒化珪素粒子は、貫通孔の表面に形成された窒化珪素粒子を核として成長し、貫通孔の内側に向けて柱状結晶を形成するものと考えられている。実施例によれば、得られた柱状結晶は、0.1〜0.8mmの大変長い柱状晶が生成しているので、おそらく、綿状の長い結晶が生成しているものと考えられる。一方、焼結体内部の状態は明記されていないが、焼結体の内部は、球状の結晶が詰まった状態になっているものと推定される。言い換えると、焼結体内部には、柱状晶が生成していないので、気孔率が低く強度が低いものと考えられる。従って、焼結体の表面部から内部に亘って、一様に高気孔率であるSi3N4を得ることが難しい。このような状況で、金属珪素を出発原料とし、安価で気孔率の高いフィルタ用多孔質Si3N4製のセラミックスを提供することが本発明の課題である。
【０００６】
【課題を解決するための手段】
本発明は以下の工程を経て製造される。即ち、Si粉末と、第一の焼結助剤として希土類元素化合物の1種以上であって酸化物換算でSi粉末100質量部に対して7.5〜45質量部の粉末とを混合する混合工程と、当該混合粉末にバインダを添加する添加工程と、当該混合粉末を用いて成形体を作製する成形工程と、当該成形体からバインダを除去する脱バインダ工程と、脱バインダ体を窒素雰囲気中において、1350〜1500℃まで加熱、窒化して窒化体を作製する窒化工程と、窒化体を1750〜1900℃の温度で0.1〜1気圧（0.01〜0.1MPa）の窒素圧中で焼結する焼結工程とを含むことによって、気孔率30〜60％、Si3N4粒子が柱状であってその外径が0.2〜5μmであって、そのアスペクト比が2〜20の多孔質Si3N4を得ることを目的とする製造方法を提供するものである。
【０００７】
まず、Si粉末と第一の焼結助剤粉末との混合は、例えば、水やアルコールの溶媒を加えボールミルやアトライターを用いて行う。Si粉末の粒子径は、0.15μm以上10μm未満の範囲が好ましい。平均細孔径が0.05〜12μmの範囲の多孔質体を得るには、前記の粒子径のSi粉末を用いることが望ましい。第一の焼結助剤は、希土類元素化合物であって、その量が酸化物換算でSi粉末100質量部に対して7.5〜45質量部添加する。その量が7.5質量部より少ないと窒化工程においてSiの一部が窒化せずに残る。また、45質量部を超えると、焼結時に液相量が増え焼結が進むので低気孔率になり、かつ原料費用が高くなる。
【０００８】
原料の第二の焼結助剤として周期律表IIa族、IIIb族、IVb族元素、遷移元素の化合物の1種以上であって、その各元素の酸化物換算でSi粉末100質量部に対して0.05〜5質量部を添加すると、焼結温度を下げることができる。さらには、平均細孔径を小さくすることができる。第二の焼結助剤が0.05質量部未満の場合、第二の焼結助剤添加の効果がなく、5質量部を超えると、平均細孔径が小さくなりすぎて多孔質体としては好ましくない。ここにおいて、周期律表IIa族元素としてはBe、Mg、Ca、Srなどを言い、IIIb族元素としてはB、Al、Gaなどを言い、IVb族元素としてはC、Si、Geなどを言い、遷移元素としてはFe、Ti、Zrなどを言う。
【０００９】
混合粉末にバインダを添加する工程は、成形時に粉末同士をバインダで固めるための準備工程と位置づけることが出来る。バインダの量や材料は目的によって異なる。バインダとしては、ポリビニルアルコールまたはその変性物、でんぷんまたはその変性物、メチルセルロース、カルボキシメチルセルロース、ヒドロキシメチルセルロース、ポリエチレングリコール、プロピレングリコール、グリセリンなどである。
【００１０】
成形体を製作する工程は、所望の形状に成形して、焼結体の形状を最終製品の形状に近付けようとする工程である。成形する工程においては、ハニカムや円板など最終製品の形状を作ることを目的とする。ハニカムなどを作製するときは、バインダ量を多くして押し出し成形するのが通常である。またプレス成形する場合は、押し出し成形に比較すると少量のバインダを添加して成形する。そのとき重要なのは、低い密度の成形体を製作することである。低密度の成形体を得れば、バインダを除去した脱バインダ体も低密度となり、その結果、高気孔率の焼結されたフィルタ用多孔質Si3N4を得ることができる。
【００１１】
ただし、一般的に脱バインダ体の相対密度は40〜60％の範囲が望ましい。相対密度が40％未満であると、脱バインダ体の強度が弱くなり取り扱いが困難である。逆に、相対密度が60％を越えると、焼結体の気孔率が小さくなって本発明の目的とする高気孔率のセラミックスを製造できない。脱バインダ体が高気孔率であるほど、粒子が成長する空間が広がるのでSi3N4粒子のアスペクト比は理論上大きくなる。なお、相対密度とは、気孔を含めたものの密度を理論密度で割った値である。また、相対密度は、重量と寸法測定または油含浸法によって求めた体積の値から算出した成形密度を、窒化珪素と添加物の重量加重平均である理論密度で割ることによって求める。
【００１２】
脱バインダ工程は、添加したバインダを除去する工程である。金属珪素は酸化しやすくかつ酸化すると窒化が困難なので、不活性雰囲気中で脱バインダする。不活性雰囲気として例えばアルゴンや窒素雰囲気、温度は300〜500℃に保持して、添加したバインダを除去する。低い圧力の方が、バインダが蒸発しやすく望ましい。一方ではバインダは種々な有機物質などに分解し、炉壁などに付着するので雰囲気を制御する上では1気圧が実用的である。時間は成形体の大きさや形状によるが、保持時間1〜5時間で昇温時間を入れると概略5〜20時間が好ましい。
【００１３】
窒化工程は、脱バインダ体中のSiを窒化してSi3N4を含む成形体にする工程のことである。この工程では、殆どすべての珪素が窒化しSi3N4となる。温度は、1350〜1500℃の範囲で、窒素雰囲気の圧力は3〜10気圧（0.3〜1MPa）の範囲、時間は2〜10時間の範囲が望ましい。Siの融点は1414℃なので、この温度以下で窒化して表面層をまず窒化した後この温度を超えた温度で窒化する。また、温度が1350℃未満の場合は、窒化の反応速度が遅く実用的ではない。このようにしてSiをほぼ100％の窒化率で窒化してSi3N4にすると、Si脱バインダ体の1.66倍の重量となると共に、窒化によりSi3N4の体積も増加し気孔率が減少する。得られる窒化体は、α型結晶で球状のSi3N4粒子で構成されている。この時、例えば相対密度が50％の脱バインダ体は、窒化工程では相対密度が30％へと減少してしまう。
【００１４】
窒化工程が無い場合は、焼結温度がSiの融点を超えるので溶融し、脱バインダ体の形状が崩れてしまう。従って窒化工程は、金属珪素を窒化する工程であると共にアスペクト比を高め、針状結晶のSi3N4からなる焼結体を得るための一つの重要な工程である。窒化工程が、3〜10気圧（0.3〜1MPa）の窒素雰囲気中でなされることが好ましい。高い圧力では反応速度が速くなるが、圧力が高くなると装置に要する費用や、操作性が悪くなるので、3〜10気圧の範囲が望ましい。
【００１５】
本発明でアスペクト比とは、柱状粒子の長径と短径との比率を言い、一般的にはアスペクト比が高い方が焼結体の強度が高くなる。本発明の焼結体は、弗硝酸で処理すると焼結助剤が溶解してSi3N4の粒子がばらばらになる。この一つ一つの粒子をSEMなどで観察し、柱状粒子の幅と長さを測定してアスペクト比を定める。Si3N4の柱状晶は概略六角柱である。
【００１６】
焼結工程は、気孔率、平均細孔径及びアスペクト比を定める最終工程である。焼結条件のうち温度は1750〜1900℃、保持時間は0.25〜5時間、窒素圧力は0.1〜1気圧（0.01〜0.1MPa）である。この発明では、0.1〜1気圧（0.01〜0.1MPa）の低窒素圧を利用してSi3N4を積極的に分解させるので柱状晶が細くなり、気孔率及びアスペクト比を高くしようとする点に大きな特徴がある。また、焼結時に焼結助剤が液相となり、その液相に解けたSi3N4からβ型のSi3N4が成長して柱状晶が生じる。従って、柱状晶の伸びを阻害するものに突き当たると成長が停止するので、窒化体の気孔率が高い方が高いアスペクト比の焼結体を得ることができる。さらに好ましい範囲は0.1〜0.5気圧(0.01〜0.05MPa)である。Si3N4の分解が進み、より気孔率の高い焼結体を得ることができるので望ましい。
【００１７】
本発明の多孔質Si3N4は、上記の工程を経て得られた焼結体であって、次の特徴を持つ。気孔率30〜60％の範囲が好ましい理由は以下の通りである。気孔率が30％未満の場合は流体の流量が不足し、60％を越えると焼結体の強度が低すぎて実用化できない。しかしながら、気孔率が高いと液体の透過量が増えるので、経済上気孔率が高い方が望ましい。Si3N4粒子が柱状であってその外径が0.2〜5μmであることが好ましい。0.2μm未満の場合は小さすぎて強度が不足し、5μmを越えると丸い粒子となり柱状ではなくなる。Si3N4粒子のアスペクト比は、2〜20の範囲が好ましい。その理由は、2未満であると強度が不足し、20を超えるものは製造が難しい。このような構成とすることにより、使用済みのフィルタが液体の逆流により再生しやすくなる。おそらく柱状晶の上に堆積した異物は、他の部分との絡み合いなどが少ないために除去しやすくなると考えられる。
【００１８】
本発明のフィルタ用多孔質Si3N4は、Si粉末と第一の焼結助剤として希土類元素化合物の1種以上の粉末を出発原料とするものである。第一の焼結助剤が酸化物換算でSi粉末100質量部に対して7.5〜45質量部であり、気孔率30〜60％、Si3N4粒子が柱状であってその外径が0.2〜5μmであって、そのアスペクト比が2〜20の多孔質Si3N4である。これにさらに、第二の焼結助剤として周期律表IIa族、IIIb族、IVb族元素、遷移元素の化合物の1種以上であってその各元素の酸化物換算でSi粉末100質量部に対して0.05〜5質量部とを加えたものである。
【００１９】
平均細孔径は、0.05〜12μmが好ましい。平均細孔径が0.05μm未満の焼結体を工業的に製造するのは難しい。また、平均細孔径が12μmを超えると、本発明の目的であるフィルタ効果が小さくなる。このような微細な平均細孔径は、出発原料である金属Si粒子が0.15μm以上10μm未満の大きさであることと、減圧窒素雰囲気で焼結することによって得られる。
【００２０】
【発明の実施の形態】
以下、本発明の実施の形態を説明する。
（実施例1）
焼結時の窒素圧力の効果を確認した。平均粒径が1μmの市販のSi粉末100質量部に対して第一の焼結助剤として7.5質量部のY2O3を添加し、エタノールを溶媒としてボールミルを用いて15時間混合した。得られたスラリーを大気中で自然乾燥し、その乾燥粉末にプレス成形用の有機バインダを添加した。次いで直径25mmで高さが3mmのSiの成形体を作製し、窒素雰囲気中にて400℃に加熱し、2時間保持して脱バインダ処理を行った後、窒素雰囲気中3気圧(0.3MPa)において1400℃まで加熱して、5時間保持してSi3N4からなる窒化体を得た。
【００２１】
さらに、その窒化体を1850℃で2時間保持し、他は表1に示す条件で焼結し、得られたSi3N4焼結体の気孔率及び平均細孔径を水銀ポロシメータ(カンタ・クロム社製オートスキャン60ポロシメータ−）にて測定した。得られた焼結体を弗硝酸で溶解し、Si3N4粒子をばらばらにした。個々のSi3N4粒子を走査型電子顕微鏡で観察し、アスペクト比を求めた。その結果を表1に示す。特に1気圧（0.1MPa)以下の窒素圧で焼結すると、30％以上の高い気孔率のセラミックスを得ることができた。アスペクト比は、窒素圧が高くなるに従い高くなる傾向にある。
【００２２】
【表１】
Figure 0003698143
【００２３】
（実施例2）
第一の焼結助剤である希土類元素化合物の添加量の効果を確認した。平均粒径が1μmの市販のSi粉末に表2に示す量の焼結助剤を添加し、エタノールを溶媒としてボールミルを用いて15時間混合した。得られたスラリーを大気中で自然乾燥し、その乾燥粉末にプレス成形用の有機バインダを添加する。次いで直径25mm、厚さ3mmのSi成形体を作製し、窒素雰囲気中で350℃に加熱し5時間保持して脱バインダ処理を行った。
【００２４】
次に、5気圧(0.5MPa)の窒素雰囲気中において1380℃まで加熱し7時間保持して窒化体を得た。さらに、その窒化体を窒素雰囲気中0.5気圧(0.05MPa)とし、1835℃で2時間保持して焼結した。得られたSi3N4焼結体の気孔率および平均細孔径を水銀ポロシメータにて実施例１と同様に測定した。その結果を表2にまとめて示す。特に、0.5気圧（0.05MPa）の窒素圧力で焼結しているので、実施例1と同様に30％以上の気孔率を得ることができた。また表2から、希土類元素化合物の添加量に比例して焼結体中のSi3N4粒子の高いアスペクト比の組織が得られた。この中で、気孔率の高い試料24のものが、実用上最も優れていた。
【００２５】
【表２】
Figure 0003698143
【００２６】
（実施例3）
第一の焼結助剤と第二の焼結助剤を同時に加えた効果を調べた。平均粒径が0.15μmの市販のSi粉末と、第一の焼結助剤として25質量部のY2O3と、第二の焼結助剤として表3に示す量を添加し、エタノールを溶媒として20時間混合した。得られたスラリーを大気中で自然乾燥し、その乾燥粉末にプレス成形用の有機バインダを添加した。次いで直径25mm、厚さ3mmのSi成形体を作製し、窒素雰囲気中にて450℃に加熱し4時間保持して脱バインダ処理を行った後、3気圧の窒素雰囲気中において1400℃まで加熱し5時間保持して窒化体を得た。
【００２７】
さらに、その窒化体を窒素圧が0.3気圧(0.03MPa)で、焼結の保持時間は2時間とし焼結温度を表3に示すとおりの条件で焼結した。得られたSi3N4焼結体の気孔率および平均細孔径を水銀ポロシメータにて測定した。その結果を表3にまとめて示す。この時、第二の焼結助剤をわずかに添加しただけでも、液相量は多くなり、液相生成温度が低下するためにSi3N4の粒成長が抑制される。その結果、気孔率は低下するが、微細な平均細孔径をもつ。この中で試料32、34のものは、気孔率が高く優れたフィルタであった。
【００２８】
【表３】
Figure 0003698143
【００２９】
（実施例4）
成形体を脱バインダ処理した時の気孔率である脱バインダ体気孔率と焼結時の窒素圧力を変化させて試料を作製した。平均粒径が9μmの市販のSi粉末に第一の焼結助剤として15質量部のY2O3を添加し、エタノールを溶媒として0.5時間混合する。得られたスラリーを大気中で自然乾燥し、その乾燥粉末にプレス成形用の有機バインダを添加する。次いで直径25mm、厚さ3mmのSi成形体をプレス成形圧を変えて作製し、窒素雰囲気中にて400℃に加熱し、3時間保持して脱バインダ処理を行った。この実施例では、脱バインダ処理をしたものの気孔率を測定して表4に示した。その後、5気圧の窒素雰囲気中において1450℃まで加熱し、3時間保持して窒化体を得た。
【００３０】
さらに、その窒化体を1835℃で3.5時間保持しその他の条件は表4に示す条件で焼結した。得られたSi3N4焼結体の気孔率及び平均細孔径を水銀ポロシメータにて測定した。その結果を表4にまとめて示す。特に、大粒径の原料を用いるため、大きな平均細孔径をもつ多孔体が得られた。また、多孔質Si3N4の気孔率は、脱バインダ体の気孔率よりも、焼結時の窒素圧力への依存の方が大きいことを示している。この中で試料44は気孔率が高く優れていた。
【００３１】
【表４】
Figure 0003698143
【００３２】
【発明の効果】
本発明の方法は、出発原料としてSi3N4ではなく、Si粉末と希土類元素の化合物を用いることで原料を安価なものとし、安価なフィルタ用多孔質Si3N4を得ることができる。また、焼結工程を1750〜1900℃の窒素雰囲気であって0.1〜1気圧の低圧窒素雰囲気とすることで、焼結中にSi3N4が分解し、それによって気孔率を高く維持し、かつSi3N4のアスペクト比を高く維持することができる。本発明のフィルタ用多孔質体Si3N4は、高温特性と耐薬品性に優れているので、腐食性液体中の異物除去用フィルタ、高温で使用されるフィルタ、腐食性の高い雰囲気で使用される触媒担体として有用である。

Claims (7)

  1. (a)Si粉末と、第一の焼結助剤として希土類元素化合物の1種以上であって酸化物換算でSi粉末100質量部に対して7.5〜45質量部の粉末とを混合して混合粉末を得る混合工程と、
    (b)当該混合粉末にバインダを添加する添加工程と、
    (c)当該混合粉末を用いて成形体を作製する成形工程と、
    (d)当該成形体を窒素雰囲気中にて300〜500℃に加熱してバインダを除去する脱バインダ工程と、
    (e)当該脱バインダ体を窒素雰囲気中において、1350〜1500℃まで加熱、窒化して窒化体を作製する窒化工程と、
    (f)当該窒化体を1750〜1900℃の温度で0.1〜1気圧（0.01〜0.1MPa）の窒素圧中で焼結する焼結工程とを含むことによって、
    気孔率30〜60％、Si3N4粒子が柱状であってその外径が0.2〜5μmであって、そのアスペクト比が2〜20とすることを特徴とするフィルタ用多孔質Si3N4の製造方法。
  2. 前記混合工程は、さらに第二の焼結助剤として周期律表IIa族、IIIb族、IVb族元素、遷移元素の化合物の1種以上であってその各元素の酸化物換算でSi粉末100質量部に対して0.05〜5質量部を混合することを特徴とする請求項1記載のフィルタ用多孔質Si3N4の製造方法。
  3. 前記窒化工程が、3〜10気圧（0.3〜1MPa)の窒素雰囲気中でなされることを特徴とする請求項1または2記載のフィルタ用多孔質Si3N4の製造方法。
  4. 当該焼結工程の窒素圧力が0.1〜0.5気圧（0.01〜0.05MPa）の圧力であることを特徴とする請求項1〜3のいずれかに記載のフィルタ用多孔質Si3N4の製造方法。
  5. Si粉末と第一の焼結助剤として希土類元素化合物の1種以上の粉末を出発原料とするフィルタ用多孔質Si3N4であって、前記第一の焼結助剤が酸化物換算でSi粉末100質量部に対して7.5〜45質量部であり、気孔率30〜60％、Si3N4粒子が柱状であってその外径が0.2〜5μmであって、そのアスペクト比が2〜20の多孔質Si3N4であることを特徴とするフィルタ用多孔質Si3N4。
  6. 前記出発原料は、さらに第二の焼結助剤として周期律表IIa族、IIIb族、IVb族元素、遷移元素の化合物の1種以上であってその各元素の酸化物換算でSi粉末100質量部に対して0.05〜5質量部とを加えたものであることを特徴とする請求項５記載のフィルタ用多孔質Si3N4。
  7. 当該フィルタ用多孔質Si3N4の平均細孔径が0.05〜12μmであることを特徴とする請求項5〜6のいずれかに記載のフィルタ用多孔質Si3N4。
JP2003012370A 2003-01-21 2003-01-21 フィルタ用多孔質Ｓｉ３Ｎ４とその製造方法 Expired - Fee Related JP3698143B2 (ja)