CN107183779A - The low temperature cigarette reconstituted tobacco prepared based on inorganic salts - Google Patents
The low temperature cigarette reconstituted tobacco prepared based on inorganic salts Download PDFInfo
- Publication number
- CN107183779A CN107183779A CN201710541484.4A CN201710541484A CN107183779A CN 107183779 A CN107183779 A CN 107183779A CN 201710541484 A CN201710541484 A CN 201710541484A CN 107183779 A CN107183779 A CN 107183779A
- Authority
- CN
- China
- Prior art keywords
- tobacco
- reconstituted tobacco
- inorganic salts
- low
- tobacco leaf
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
技术领域technical field
本发明涉及新型卷烟技术领域，具体是一种基于无机盐制备的低温卷烟再造烟叶。The invention relates to the technical field of novel cigarettes, in particular to a low-temperature cigarette reconstituted tobacco leaf prepared based on inorganic salts.
背景技术Background technique
低温卷烟是通过外部加热元件对烟草原料进行加热，而非烟草直接燃烧产生烟雾。这样可以显著的降低传统香烟中的烟草的燃烧和热降解所产生的已知类型的有害烟气成分。外部加热的热源一般包括电池加热热源、燃料炭加热热源以及燃料气加热热源，通常加热的温度200℃-400℃的条件下达到雾化温度。Low-temperature cigarettes use external heating elements to heat tobacco raw materials, rather than directly burning tobacco to produce smoke. This significantly reduces the known types of harmful smoke components produced by the combustion and thermal degradation of tobacco in conventional cigarettes. External heating heat sources generally include battery heating heat sources, fuel charcoal heating heat sources, and fuel gas heating heat sources. Usually, the heating temperature reaches the atomization temperature under the condition of 200°C-400°C.
低温卷烟一般填充物主要为再造烟叶和少量的烟丝等其他辅料成分。为了提高低温卷烟的抽吸口感，较低的温度条件下烟碱等生理满足成分释放不充分，同时，在实际加热过程中，局部温度过高也会导致再造烟叶和烟丝阴燃问题，导致低温卷烟的体验感较差等问题。Low-temperature cigarettes are generally filled with reconstituted tobacco leaves and a small amount of shredded tobacco and other auxiliary materials. In order to improve the smoking taste of low-temperature cigarettes, the release of physiologically satisfying components such as nicotine is insufficient under low temperature conditions. Problems such as poor experience of cigarettes.
发明内容Contents of the invention
本发明为了解决现有技术的不足，提供一种基于无机盐制备的低温卷烟再造烟叶，可提高再造烟叶的耐受温度，并且具有烟草本香充足、生理满足感适当、发烟量大、香气风格特征可调的明显优点。In order to solve the deficiencies of the prior art, the present invention provides a low-temperature cigarette reconstituted tobacco leaf prepared based on inorganic salts, which can increase the tolerance temperature of the reconstituted tobacco leaf, and has sufficient tobacco aroma, appropriate physiological satisfaction, large smoke production, and aroma. The obvious advantage of adjustable style features.
本发明通过以下技术方案予以实现：The present invention is achieved through the following technical solutions:
一种基于无机盐制备的低温卷烟再造烟叶，其特征在于：各组分按照质量百分比配比如下：烟草原料50-95％、发雾剂8-30％、胶粘剂0.5-10％、烟用香料0-8％、无机盐0.1-25％、纤维0.2-20％，所述无机盐为钙盐、镁盐、铝盐中的一种或几种的混合。A low-temperature cigarette reconstituted tobacco leaf prepared based on inorganic salts, characterized in that: the components are proportioned according to the mass percentage as follows: tobacco raw material 50-95%, fogging agent 8-30%, adhesive 0.5-10%, tobacco flavor 0-8%, inorganic salt 0.1-25%, fiber 0.2-20%, the inorganic salt is one or a mixture of calcium salt, magnesium salt and aluminum salt.
进一步的，所述的钙盐为碳酸钙、硫酸钙、草酸钙、磷酸钙、氟化钙中的一种或几种的混合。Further, the calcium salt is one or a mixture of calcium carbonate, calcium sulfate, calcium oxalate, calcium phosphate, and calcium fluoride.
进一步的，所述的镁盐为碳酸镁、氟化镁、磷酸镁、草酸镁、氢氧化镁等中的一种或几种的混合。Further, the magnesium salt is one or a mixture of magnesium carbonate, magnesium fluoride, magnesium phosphate, magnesium oxalate, magnesium hydroxide and the like.
进一步的，所述的铝盐为氢氧化铝、硅酸铝中的一种或几种的混合。Further, the aluminum salt is one or a mixture of aluminum hydroxide and aluminum silicate.
进一步的，所述烟草原料为单种烟叶原料或多种烟叶原料经配方组成。Further, the tobacco raw material is composed of a single tobacco leaf raw material or a plurality of tobacco leaf raw materials through formulating.
进一步的，所述发烟剂为甘油、乙二醇、丙二醇中的一种或几种的混合。Further, the smoking agent is one or a mixture of glycerin, ethylene glycol, and propylene glycol.
进一步的，所述胶粘剂为CMC、海藻酸钠、塔马兰子胶、古尔胶、丙甲基纤维素、大豆卵磷脂中的一种或几种的混合。Further, the adhesive is one or a mixture of CMC, sodium alginate, tamaran gum, gull gum, propylmethylcellulose, and soybean lecithin.
进一步的，所述的纤维为木浆纤维、烟草纤维中的一种或其混合。Further, the fiber is one of wood pulp fiber, tobacco fiber or a mixture thereof.
进一步的，所述的再造烟叶采用稠浆法工艺制备，步骤如下：Further, the reconstituted tobacco leaf is prepared by the thick slurry method, and the steps are as follows:
(1)将烟草原料经粉碎机粉碎成粒度在30-120目烟草粉末；(1) The tobacco raw material is pulverized into tobacco powder with a particle size of 30-120 mesh through a pulverizer;
(2)将制备的各组分混匀后，加入物料总重量50-60％的40-45℃温水搅拌，形成均匀的浆状物；(2) After mixing the prepared components evenly, add 50-60% of the total weight of the material with 40-45°C warm water and stir to form a uniform slurry;
(3)将制备好的浆状物均匀地铺在循环的金属带或环形金属带上进行干燥，干燥温度在50℃-120℃；(3) Spread the prepared slurry evenly on a circulating metal belt or an endless metal belt to dry at a drying temperature of 50°C-120°C;
(4)将金属带上的浆状物干燥后，从金属带上剥离切片处理或者进行切丝处理，得到稠浆法工艺制备的再造烟叶。(4) After the slurry on the metal belt is dried, the metal belt is peeled off and sliced or shredded to obtain reconstituted tobacco leaves prepared by the thick slurry method.
进一步的，所述的再造烟叶采用辊压法工艺制备，步骤如下：Further, the reconstituted tobacco leaf is prepared by a rolling process, and the steps are as follows:
(1)将烟草原料经粉碎机粉碎成粒度在30-120目烟草粉末；(1) The tobacco raw material is pulverized into tobacco powder with a particle size of 30-120 mesh through a pulverizer;
(2)将烟草粉末与解纤后的纤维混合，备用；(2) the tobacco powder is mixed with the fiber after defibrating, for subsequent use;
(3)将胶粘剂、烟用香料、薄片胶、磷酸、发雾剂以及水为溶剂，配置成料液，其中薄片胶占溶剂质量比为1％-18％，磷酸占溶剂质量比为0.3％-5％，水占溶剂质量比为10％-50％，(3) Adhesive, tobacco flavor, flake glue, phosphoric acid, fogging agent and water are used as solvents to configure a feed liquid, wherein the flake glue accounts for 1%-18% by mass of the solvent, and the mass ratio of phosphoric acid to the solvent is 0.3% -5%, the mass ratio of water to solvent is 10%-50%,
(4)将烟草粉末与纤维混合物、无机盐与配置好的料液按比例混合，进行搅拌均匀后，后经三次辊压，再送入干燥器中进行干燥、冷却，分切，得到辊压法制备的再造烟叶。(4) Mix the tobacco powder and fiber mixture, inorganic salt and the prepared material liquid in proportion, after stirring evenly, after rolling three times, then send it into the drier for drying, cooling, and cutting to obtain the rolling method Prepared reconstituted tobacco leaves.
本发明通过在再造烟叶中主要添加不易溶于水的无机盐作为填充物，降低再造烟叶的黏连性和提高受热的均匀性，无机盐的添加量一般不超过再造烟叶总重量的25％，可提高再造烟叶在新型烟草中的耐热温度，改善再造烟叶在新型烟草的填充量，而且不改变新型烟草的低温受热的吸味。The present invention mainly adds inorganic salts that are not easily soluble in water as fillers in the reconstituted tobacco leaves to reduce the adhesion of the reconstituted tobacco leaves and improve the uniformity of heating. The amount of inorganic salts added generally does not exceed 25% of the total weight of the reconstituted tobacco leaves. The heat-resistant temperature of the reconstituted tobacco leaves in the new tobacco can be increased, the filling amount of the reconstituted tobacco leaves in the new tobacco can be improved, and the low-temperature heating flavor of the new tobacco can not be changed.
采用本发明的有益效果：(1)利用烟草原料，未经过提取工艺，生产工艺简单，操作方便，应用于低温卷烟，烟雾满足感强；(2)高阻燃性无机盐的加入，提高了无机盐在再造烟叶中的固体填充量，提高了低温卷烟耐热温度，提高烟气抽吸舒适性，可以广泛应用在电加热低温卷烟、碳加热低温卷烟中，应用范围更广泛。The beneficial effects of adopting the present invention: (1) the use of tobacco raw materials, without the extraction process, the production process is simple, the operation is convenient, and it is applied to low-temperature cigarettes, and the smoke satisfaction is strong; (2) the addition of high flame-retardant inorganic salts improves the The solid filling amount of inorganic salts in reconstituted tobacco leaves increases the heat-resistant temperature of low-temperature cigarettes and improves the comfort of smoking smoke. It can be widely used in electric heating low-temperature cigarettes and carbon-heating low-temperature cigarettes, and the application range is wider.
具体实施方式detailed description
下面将结合具体实施例，对本发明中的技术方案进行清楚、完整地描述。The technical solutions in the present invention will be clearly and completely described below in conjunction with specific embodiments.
实施例一Embodiment one
一种基于无机盐制备的应用于于低温卷烟的再造烟叶，各组分按照质量百分比配比如下：烟草原料65％、发雾剂20％、胶粘剂6％、碳酸钙8％、烟用香料1％。再造烟叶按照稠浆法生产工艺制造，其厚度为0.10-0.20mm，其中烟草原料由烤烟60％、白肋烟30％和香料10％烟组成，发雾剂为甘油、丙二醇比例为2:1配制，胶粘剂为羟甲基纤维素，采用淡雅香风格的烟用香料。A reconstituted tobacco leaf based on inorganic salts and applied to low-temperature cigarettes. The components are proportioned according to the mass percentage as follows: 65% of tobacco raw materials, 20% of fogging agent, 6% of adhesive, 8% of calcium carbonate, and 1% of tobacco flavoring %. The reconstituted tobacco leaves are manufactured according to the thick pulp production process, and its thickness is 0.10-0.20mm. The tobacco raw materials are composed of 60% flue-cured tobacco, 30% Burley tobacco and 10% spice tobacco. The ratio of glycerin and propylene glycol is 2:1. It is formulated, the adhesive is hydroxymethyl cellulose, and it adopts elegant and fragrant style tobacco flavor.
将制备的稠浆法再造烟叶进行卷烟卷制，用专用低温烟具进行卷烟评价，其香气风格特征为：优雅纯正、香气飘逸、自然醇和、淡雅纯正，同时，通过与未添加碳酸钙的再造烟叶比较，其耐温程度可以提高60℃，大幅度的提高了低温卷烟烟支的耐受温度。The reconstituted tobacco leaves prepared by the thick pulp method were rolled into cigarettes, and the cigarettes were evaluated with special low-temperature smoking utensils. The aroma style characteristics were: elegant and pure, elegant aroma, natural alcohol, elegant and pure. In comparison, its temperature resistance can be increased by 60°C, greatly increasing the temperature resistance of low-temperature cigarettes.
实施例二Embodiment two
一种基于无机盐制备的应用于于低温卷烟的再造烟叶，各组分按照质量百分比配比如下：烟草原料60％、发雾剂18％、胶粘剂7％、碳酸镁2％、碳酸钙4％、烟用香料1％、纤维8％。再造烟叶按照辊压法生产工艺制造，其厚度为0.07-0.18mm，其中烟草原料由烤烟55％、白肋烟35％和香料烟10％组成，发雾剂为甘油、丙二醇比例为3:1配制，胶粘剂为羟甲基纤维素与丙甲基纤维素比例为2:1，采用清香型烟用香料。A reconstituted tobacco leaf used in low-temperature cigarettes prepared based on inorganic salts. The components are proportioned according to the mass percentage as follows: 60% of tobacco raw materials, 18% of fogging agent, 7% of adhesive, 2% of magnesium carbonate, and 4% of calcium carbonate , tobacco flavor 1%, fiber 8%. The reconstituted tobacco leaves are manufactured according to the rolling method production process, and its thickness is 0.07-0.18mm. The tobacco raw materials are composed of 55% flue-cured tobacco, 35% Burley tobacco and 10% oriental tobacco. The ratio of glycerin and propylene glycol is 3:1. It is prepared, the adhesive is hydroxymethyl cellulose and propyl methyl cellulose with a ratio of 2:1, and the fragrance type tobacco spice is used.
制备的辊压法再造烟叶进行卷烟卷制，用专用低温烟具进行卷烟评价，其香气风格特征为：具有以清甜香、青香、木香等为主体香韵的烤烟香气特征；清甜香韵突出；香气清雅而飘逸，同时，通过与未添加碳酸钙的再造烟叶比较，其耐温程度可以提高55℃，大幅度的提高了低温卷烟烟支的耐受温度。The reconstituted tobacco leaves prepared by rolling method were rolled into cigarettes, and the cigarettes were evaluated with special low-temperature smoking sets. The rhyme is prominent; the aroma is elegant and elegant. At the same time, compared with reconstituted tobacco leaves without calcium carbonate, its temperature resistance can be increased by 55°C, which greatly improves the temperature resistance of low-temperature cigarettes.
实施例三Embodiment Three
一种基于无机盐制备的应用于于低温卷烟的再造烟叶，各组分按照质量百分比配比如下：烟草原料64％、发雾剂20％、胶粘剂6％、氢氧化铝2％、碳酸镁3％、碳酸钙1％、草酸钙3％、烟用香料1％。再造烟叶按照稠浆法生产工艺制造，其厚度为0.10-0.20mm，其中烟草原料由烤烟60％、白肋烟30％和香料10％烟组成，发雾剂为甘油、丙二醇比例为3:2配制，胶粘剂为羟甲基纤维素，采用中间香型的烟用香料。A reconstituted tobacco leaf used in low-temperature cigarettes prepared based on inorganic salts. The proportions of the components are as follows: 64% of tobacco raw materials, 20% of fogging agent, 6% of adhesive, 2% of aluminum hydroxide, and 3% of magnesium carbonate. %, calcium carbonate 1%, calcium oxalate 3%, tobacco flavor 1%. The reconstituted tobacco leaves are manufactured according to the thick pulp production process, and its thickness is 0.10-0.20mm. The tobacco raw materials are composed of 60% flue-cured tobacco, 30% Burley tobacco and 10% flavored tobacco. The ratio of glycerin and propylene glycol is 3:2. It is prepared, the adhesive is hydroxymethyl cellulose, and middle-flavored tobacco spices are used.
将制备的稠浆法再造烟叶进行卷烟卷制，用专用低温烟具进行卷烟评价，其香气风格特征为：具有正甜香、木香、辛香等为主体香韵的烤烟香气特征；正甜香韵突出；香气丰富而悬浮，同时，通过与未添加碳酸钙的再造烟叶比较，其耐温程度可以提高59℃，大幅度的提高了低温卷烟烟支的耐受温度。The reconstituted tobacco leaves prepared by the thick pulp method were rolled into cigarettes, and the cigarettes were evaluated with special low-temperature smoking utensils. The aroma style characteristics were: the aroma characteristics of flue-cured tobacco with positive sweetness, woody aroma, and spicy aroma as the main aroma; positive sweetness The rhyme is prominent; the aroma is rich and suspended. At the same time, compared with reconstituted tobacco leaves without calcium carbonate, its temperature resistance can be increased by 59 ° C, which greatly improves the temperature resistance of low-temperature cigarettes.
实施例四Embodiment four
一种基于无机盐制备的应用于于低温卷烟的再造烟叶的制备，各组分按照质量百分比配比如下：烟草原料55％、发雾剂18％、胶粘剂7％、草酸钙6％、碳酸钙5％、烟用香料2％、纤维7％。再造烟叶按照辊压法生产工艺制造，其厚度为0.07-0.18mm，其中烟草原料由烤烟55％、白肋烟30％和香料烟15％组成，发雾剂为甘油、丙二醇比例为3:1配制，胶粘剂为羟甲基纤维素与丙甲基纤维素比例为2:1，采用浓香型烟用香料。A preparation of reconstituted tobacco leaves used in low-temperature cigarettes based on inorganic salts. The proportions of the components are as follows: 55% of tobacco raw materials, 18% of fogging agent, 7% of adhesive, 6% of calcium oxalate, calcium carbonate 5%, tobacco flavor 2%, fiber 7%. The reconstituted tobacco leaves are manufactured according to the rolling method production process, and its thickness is 0.07-0.18mm. The tobacco raw materials are composed of 55% flue-cured tobacco, 30% Burley tobacco and 15% oriental tobacco. The ratio of glycerin and propylene glycol is 3:1. It is prepared, the adhesive is hydroxymethyl cellulose and propyl methyl cellulose in a ratio of 2:1, and a strong flavor tobacco flavor is used.
制备的辊压法再造烟叶进行卷烟卷制，用专用低温烟具进行卷烟评价，其香气风格特征为：具有以焦甜香、木香、焦香等为主体香韵的烤烟香气特征；焦甜香韵突出；香气浓郁而沉溢，同时，通过与未添加碳酸钙的再造烟叶比较，其耐温程度可以提高56℃，大幅度的提高了低温卷烟烟支的耐受温度。The reconstituted tobacco leaves prepared by rolling method were rolled into cigarettes, and the cigarettes were evaluated with special low-temperature smoking sets. The rhyme is prominent; the aroma is rich and deep. At the same time, compared with the reconstituted tobacco leaves without calcium carbonate, its temperature resistance can be increased by 56°C, which greatly improves the temperature resistance of low-temperature cigarettes.
表1考察不同实施例与常规产品在不同温度下的耐温情况Table 1 investigates the temperature resistance of different embodiments and conventional products at different temperatures
上述实施例中，所述烟草原料为单种烟叶原料或多种烟叶原料经配方组成，例如烤烟、白肋烟、香料烟、晾晒烟、晒红烟等，所述的烟草原料可以包括烟梗原料。In the above embodiments, the tobacco raw material is a single tobacco leaf raw material or a variety of tobacco leaf raw materials formulated by formula, such as flue-cured tobacco, burley tobacco, oriental tobacco, air-cured tobacco, sun-cured red tobacco, etc., and the tobacco raw material may include tobacco stems raw material.
以上所述，仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何属于本技术领域的技术人员在本发明揭露的技术范围内，可轻易想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求的保护范围为准。The above is only a specific embodiment of the present invention, but the scope of protection of the present invention is not limited thereto, any changes or substitutions that can be easily imagined by those skilled in the art within the technical scope disclosed in the present invention, All should be covered within the protection scope of the present invention. Therefore, the protection scope of the present invention should be determined by the protection scope of the claims.
Claims (10)