CN106366799B - The anti-skidding floor coatings of aqueous polyurethane - Google Patents
The anti-skidding floor coatings of aqueous polyurethane Download PDFInfo
- Publication number
- CN106366799B CN106366799B CN201610737776.0A CN201610737776A CN106366799B CN 106366799 B CN106366799 B CN 106366799B CN 201610737776 A CN201610737776 A CN 201610737776A CN 106366799 B CN106366799 B CN 106366799B
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- aqueous polyurethane
- floor coatings
- thickener
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention provides the anti-skidding floor coatings of aqueous polyurethane, including following parts by weight of component：Component A is：20-25.5 parts of hydroxyl acrylic emulsion, 20-24.5 parts of Aqueous acrylic urethane's dispersion, 8-10 parts of pigment, 0.5-1 parts of dispersant, 0.2-0.8 parts of antifoaming agent, 0.8-1.5 parts of Glycerin, 30-35 parts of deionized water, 0.5-0.8 parts of thickener, 10-20 parts of barite, 5-8 parts of wollastonite in powder;B component is：1-20 parts of modified polyisocyanate, 5-8 parts of coalescents.The anti-skidding resin of aqueous polyurethane, it is environmentally protective nontoxic, there is high-strength abrasion-proof, scratch resistance, excellent anti-hydrolytic performance, extremely excellent weatherability, the performances such as skid resistance is good, plentiful good, non yellowing, stable storing.
Description
Technical field
The invention belongs to paint fields, and in particular to the anti-skidding floor coatings of aqueous polyurethane.
Background technology
In order to meet the functional requirement of modern industrialization workshop and human-based management requirement, good work and life cycle are created
Border, more and more workshops, warehouse, Office Area, people's row passageway, classroom, court etc. are beautiful, function admirable using color
Floor coatings.Currently on the market using it is more be epoxy flooring coating and polyurethane floor coatings, this two classes coating all has
Good decorative, chemical-resistant and wearability.But epoxy flooring coating quality is crisp, poor flexibility is easy out after being hit
It splits, and polyurethane coating while keeping excellent properties requires that coating can be adjusted in wide range according to application environment
Case hardness.Therefore, it is a kind of ideal floor coatings that function admirable, dicoration and practicability have concurrently, and what we developed
The anti-skidding floor coatings of aqueous polyurethane can overcome the defect of epoxy flooring coating.
Invention content
The purpose of the present invention is to provide the anti-skidding floor coatings of aqueous polyurethane.
To achieve the above object, the present invention adopts the following technical scheme that：
The anti-skidding floor coatings of aqueous polyurethane, including following parts by weight of component：Component A is：Hydroxyl acrylic emulsion 20-
25.5 parts, 20-24.5 parts of Aqueous acrylic urethane's dispersion, 8-10 parts of pigment, 0.5-1 parts of dispersant, antifoaming agent 0.2-0.8
Part, 0.8-1.5 parts of Glycerin, 30-35 parts of deionized water, 0.5-0.8 parts of thickener, 10-20 parts of barite, wollastonite in powder
5-8 parts;B component is：1-20 parts of modified polyisocyanate, 5-8 parts of coalescents；The weight ratio of component A and B component is：4:1.
The dispersant is：BYK-161；Antifoaming agent is：Polysiloxane；Thickener is：Methacrylate；Film forming
Auxiliary agent is：Dipropylene.
Preferably, the anti-skidding floor coatings of aqueous polyurethane, including following parts by weight of component：Component A is：Hydroxy yogurt
23 parts of liquid, 22 parts of Aqueous acrylic urethane's dispersion, 9 parts of pigment, 0.8 part of dispersant, 0.6 part of antifoaming agent, Glycerin 1
Part, 33 parts of deionized water, 0.6 part of thickener, 15 parts of barite, 6 parts of wollastonite in powder；B component is：Modified polyisocyanate 10
Part, 7 parts of coalescents.
The advantage of the invention is that：The anti-skidding floor coatings of aqueous polyurethane of the present invention, it is environmentally protective nontoxic, there is high intensity
Wear-resisting, scratch resistance, excellent anti-hydrolytic performance, extremely excellent weatherability, the property such as skid resistance is good, plentiful good, non yellowing, stable storing
Energy.
Specific implementation mode
Embodiment 1
The anti-skidding floor coatings of aqueous polyurethane, including following parts by weight of component：Component A is：23 parts of hydroxyl acrylic emulsion,
22 parts of Aqueous acrylic urethane's dispersion, 9 parts of pigment, 0.8 part of dispersant, 0.6 part of antifoaming agent, 1 part of Glycerin, go from
33 parts of sub- water, 0.6 part of thickener, 15 parts of barite, 6 parts of wollastonite in powder；B component is：10 parts of modified polyisocyanate, film forming help
7 parts of agent；The weight ratio of component A and B component is：4:1.It prepares according to a conventional method.
The dispersant is：BYK-161；Antifoaming agent is：Polysiloxane；Thickener is：Methacrylate；Film forming
Auxiliary agent is：Dipropylene.
Embodiment 2
The anti-skidding floor coatings of aqueous polyurethane, including following parts by weight of component：Component A is：20 parts of hydroxyl acrylic emulsion,
20 parts of Aqueous acrylic urethane's dispersion, 0.5 part of dispersant, 0.2 part of antifoaming agent, 0.8 part of Glycerin, is gone 8 parts of pigment
30 parts of ionized water, 0.5 part of thickener, 10 parts of barite, 5 parts of wollastonite in powder;B component is：1 part of modified polyisocyanate, film forming
5 parts of auxiliary agent；The weight ratio of component A and B component is：4:1.It prepares according to a conventional method.
The dispersant is：BYK-161；Antifoaming agent is：Polysiloxane；Thickener is：Methacrylate；Film forming
Auxiliary agent is：Dipropylene.
Embodiment 3
The anti-skidding floor coatings of aqueous polyurethane, including following parts by weight of component：Component A is：Hydroxyl acrylic emulsion 25.5
Part, 24.5 parts of Aqueous acrylic urethane's dispersion, 10 parts of pigment, 1 part of dispersant, 0.8 part of antifoaming agent, Glycerin 1.5
Part, 35 parts of deionized water, 0.8 part of thickener, 20 parts of barite, 8 parts of wollastonite in powder;B component is：Modified polyisocyanate 20
Part, 8 parts of coalescents；The weight ratio of component A and B component is：4:1.It prepares according to a conventional method.
The dispersant is：BYK-161；Antifoaming agent is：Polysiloxane；Thickener is：Methacrylate；Film forming
Auxiliary agent is：Dipropylene.
Embodiment 1-3 products obtained therefrom performance test results are as shown in the table：
The foregoing is merely presently preferred embodiments of the present invention, all equivalent changes done according to scope of the present invention patent with
Modification should all belong to the covering scope of the present invention.
Claims (2)
1. the anti-skidding floor coatings of aqueous polyurethane, it is characterised in that：Including following parts by weight of component：Component A is：Hydroxy acrylic acid
20-25.5 parts of lotion, 20-24.5 parts of Aqueous acrylic urethane's dispersion, 8-10 parts of pigment, 0.5-1 parts of dispersant, antifoaming agent
0.2-0.8 parts, 0.8-1.5 parts of Glycerin, 30-35 parts of deionized water, 0.5-0.8 parts of thickener, 10-20 parts of barite,
5-8 parts of wollastonite in powder；B component is：1-20 parts of modified polyisocyanate, 5-8 parts of coalescents；The weight ratio of component A and B component
For：4:1；
The dispersant is：BYK-161；Antifoaming agent is：Polysiloxane；Thickener is：Methacrylate；Coalescents
For：Dipropylene.
2. the anti-skidding floor coatings of aqueous polyurethane according to claim 1, it is characterised in that：Including following parts by weight group
Point：Component A is：23 parts of hydroxyl acrylic emulsion, 22 parts of Aqueous acrylic urethane's dispersion, 9 parts of pigment, 0.8 part of dispersant,
0.6 part of antifoaming agent, 1 part of Glycerin, 33 parts of deionized water, 0.6 part of thickener, 15 parts of barite, 6 parts of wollastonite in powder；B groups
It is divided into：10 parts of modified polyisocyanate, 7 parts of coalescents.