CN105819802A - 一种耐热免烧砖的改进制备方法 - Google Patents
一种耐热免烧砖的改进制备方法 Download PDFInfo
- Publication number
- CN105819802A CN105819802A CN201610152775.XA CN201610152775A CN105819802A CN 105819802 A CN105819802 A CN 105819802A CN 201610152775 A CN201610152775 A CN 201610152775A CN 105819802 A CN105819802 A CN 105819802A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- weight portion
- baking
- brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种耐热免烧砖的改进制备方法，包括以下步骤：一、将发电厂烧结灰粉碎至粒径为10mm的块料；二、将35份重量份且块料为10mm的发电厂烧结灰与25重量份的煤渣粉，25重量份的普通砂，为8重量份的水泥，7重量份且粒径为15mm的氧化钙，5重量份的硅酸钙，1.5重量份的硫酸钠，1重量份的硅酸钠，5重量份的水溶性不饱和树脂及2重量份的龟粉加入15重量份的水混合搅拌成潮湿状的物料；三、用免烧砖成型机在25MPa的压力下将上述潮湿状的物料压制成型免烧砖；四、用喷水法在常温下自然干燥养护四周。与现有技术相比，其以发电厂烧结灰为主要原料，有利于环保，并使得制成的免烧砖具有强度高，耐热温度高，绝热性强，容重小，比强度高，耐久性好的优点。
Description
技术领域
本发明是专利号为201310014176.8，申请日为2013年01月15日，名称为“一种免烧砖的配方及其制作方法”的发明专利的分案申请，涉及一种免烧砖，具体涉及一种耐热免烧砖的改进制备方法。
背景技术
我国是砖体消耗大国，也是砖体的生产大国，普通粘土砖是传统的墙体材料，主要用用耕地下层粘土为原料，砌成长方体砖坯后在砖窑中明火煅烧而成，这种砖是目前城市及农村最常用的建筑材料，为了保护日益减少的耕地，国家已明令禁止粘土砖的生产，过去，也曾尝试用水泥砖代替粘土砖，但水泥砖的生产和使用成本较高，同时还存在自身自量大，不适应高层建筑使用的缺陷，近年来国内开发一种免烧砖，其主要采用粉煤灰与水泥搅拌后压制成形，这种采用粉煤灰与水泥搅拌压制成型的免烧砖存在成本高，强度低，耐久性差，耐热温度低，抗冻性能不好，砖体重的缺陷。
我国是以燃烧发电为主的国家，每年由于燃烧发电会排放大量的垃圾焚烧残留物，即垃圾发电厂烧结灰，这种垃圾发电氧化钙造成严重的污染和危害,且垃圾发电厂烧结灰中含有部分铁和氧化钙等有用成分，如果能够回收利用，将节省了很多宝贵的资源。
有鉴于此，本发明人对上述缺陷进行深入研究，遂由本案产生。
发明内容
本发明提出一种耐热免烧砖的改进制备方法,其解决了发电厂烧结灰处理成本高，不利于环保的问题,同时利用发电厂烧结灰含有少量的铁粉和氧化钙等制砖有用物质，提高了砖的强度、交联性及粘连性,使得制成的免烧砖的抗压强度达到18.1Mpa,耐热温度为1013℃，具有强度高，耐热温度高，绝热性强，容重小，比强度高，耐久性好的优点。
为达到上述目的，本发明是通过以下技术方案实现的：一种耐热免烧砖的改进制备方法，包括以下步骤：
一、发电厂烧结灰粉碎：将发电厂烧结灰粉碎至粒径为10mm的块料；
二、配料搅拌：将重量份为35份且块料为10mm的发电厂烧结灰与重量份为25份的煤渣粉，重量份为25份的普通砂，重量份为8份的水泥，重量份为7份且粒径为15mm的氧化钙，重量份为5份的硅酸钙，重量份为1.5份的硫酸钠，重量份为1份的硅酸钠，重量份为5份的水溶性不饱和树脂及重量份为2份的龟粉加入重量份为15份的水混合搅拌成潮湿状的物料；
三、压制成形：用免烧砖成型机在25MPa的压力下将上述潮湿状的物料压制成型免烧砖；
四、养护：用喷水法在常温下自然干燥养护四周。
通过采用前述技术方案，本发明的有益效果是：其采用发电厂烧结灰为主要原料，不仅废物利用消除了烧结飞灰对环境的污染,有利于环保；且发电厂烧结飞灰中含有少量的铁粉和氧化钙等制砖有用物质，铁粉有助于提高砖的强度，而且能缩短6～8小时的烧结时间，氧化钙可提高砖的交联性及粘连性，降低免烧砖所需氧化钙的重量份比，减少材料成本；在配方中加入了水溶性不饱水脂,水溶性不饱和树脂进一步提高了砖的交联性及粘连性，有效减少了氧化钙的用量，进一步降低了成本，提高了强度；在配方中加入了硅酸钙对其进行改性，使所得的产品的抗压强度达到18.1Mpa,耐热温度为1013℃，具有耐热温度高，绝热性强，容重小，比强度高，耐久性好。
具体实施方式
本发明的一种耐热免烧砖的改进制备方法，包括以下步骤：
一、发电厂烧结灰粉碎：将发电厂烧结灰粉碎至粒径为10mm的块料；
二、配料搅拌：将重量份为35份且块料为10mm的发电厂烧结灰与重量份为25份的煤渣粉，重量份为25份的普通砂，重量份为8份的水泥，重量份为7份且粒径为15mm的氧化钙，重量份为5份的硅酸钙，重量份为1.5份的硫酸钠，重量份为1份的硅酸钠，重量份为5份的水溶性不饱和树脂及重量份为2份的龟粉加入重量份为15份的水混合搅拌成潮湿状的物料；
三、压制成形：用免烧砖成型机在25MPa的压力下将上述潮湿状的物料压制成型免烧砖；
四、养护：用喷水法在常温下自然干燥养护四周。
本发明的一种耐热免烧砖的改进制备方法，其以发电厂烧结灰为主要原料，不仅废物利用消除了烧结飞灰对环境的污染,有利于环保；且发电厂烧结飞灰中含有少量的铁粉和氧化钙等制砖有用物质，铁粉有助于提高砖的强度，而且能缩短6～8小时的烧结时间，氧化钙可提高砖的交联性及粘连性，降低免烧砖所需氧化钙的重量份比，减少材料成本；在配方中加入了水溶性不饱水脂,水溶性不饱和树脂进一步提高了砖的交联性及粘连性，有效减少了氧化钙的用量，进一步降低了成本，提高了强度；在配方中加入了硅酸钙对其进行改性，使所得的产品的抗压强度达到18.1Mpa,耐热温度为1013℃，具有耐热温度高，绝热性强，容重小，比强度高，耐久性好。
Claims (1)
1.一种耐热免烧砖的改进制备方法，其特征在于：包括以下步骤：
一、发电厂烧结灰粉碎：将发电厂烧结灰粉碎至粒径为10mm的块料；
二、配料搅拌：将重量份为35份且块料为10mm的发电厂烧结灰与重量份为25份的煤渣粉，重量份为25份的普通砂，重量份为8份的水泥，重量份为7份且粒径为15mm的氧化钙，重量份为5份的硅酸钙，重量份为1.5份的硫酸钠，重量份为1份的硅酸钠，重量份为5份的水溶性不饱和树脂及重量份为2份的龟粉加入重量份为15份的水混合搅拌成潮湿状的物料；
三、压制成形：用免烧砖成型机在25MPa的压力下将上述潮湿状的物料压制成型免烧砖；
四、养护：用喷水法在常温下自然干燥养护四周。