CN105272363A - She inkstone imitated porcelain with golden star and golden halo effects and firing method - Google Patents
She inkstone imitated porcelain with golden star and golden halo effects and firing method Download PDFInfo
- Publication number
- CN105272363A CN105272363A CN201510671475.8A CN201510671475A CN105272363A CN 105272363 A CN105272363 A CN 105272363A CN 201510671475 A CN201510671475 A CN 201510671475A CN 105272363 A CN105272363 A CN 105272363A
- Authority
- CN
- China
- Prior art keywords
- parts
- coat enamel
- cover
- ground
- imitative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the technical field of ceramics, in particular to She inkstone imitated porcelain with golden star and golden halo effects and a firing method. Ground glaze and cover glaze are arranged on a green body of the She inkstone imitated porcelain, and the ground glaze comprises feldspar, calcium carbonate, zinc oxide, manganese oxide, kaolin, ferric oxide and mica; the cover glaze comprises the feldspar, quartz, calcium carbonate, zirconium silicate, kaolin and chrismatite. The She inkstone imitated porcelain with the golden star and golden halo effects can be prepared through matching of the ground glaze and the cover glaze, gradient, regular or irregular texture can also be prepared, the base colors of the fired She inkstone imitated porcelain include blue black and dark green, the glazing colors of the cover glaze on the ground glaze include yellowish brown and golden yellow, and a glaze surface formed by the ground glaze and the cover glaze is smooth and tightly combined with the green body and cannot fall off easily; the She inkstone imitated porcelain prepared with the method can imitate the texture of natural She inkstone, the cover glaze is formed through glaze spraying, each piece of porcelain has unique texture, and demands of users for aesthetic diversity are met.
Description
Technical field
The present invention relates to ceramic technology field, be specifically related to a kind of to there is Venus, dizzy the imitative of effect of gold inhales ink-stone porcelain and method for cooking.
Background technology
Along with the improving constantly of continuous progressive living standards of the people of society, also more and more higher to the requirement of quality of the life, aesthetic diversified demand is also constantly changed.Inhale ink-stone due to its huge number, texture form of diverse from Han dynasty just be familiar with by us utilize, and wherein friable mica and gold stone of swooning has representative and by the kind that the men of literature and writing are liked, wherein friable mica in livid ink-stone, becomes spot distribution golden yellow, as sky twinkLing stars bucket seems very dazzling; The dizzy stone of gold is grand round and round, and as the golden cloud in sunset clouds, the wish of blowing is fallen apart, and Song Rutuan wads a quilt with cotton, and the wish touched rises.It is indefinite that the dizzy size of gold is clear, and gives dim U.S. of a kind of uniqueness.The name of an article has that jade belt gold is dizzy, eyebrow line gold is dizzy, golden flower Jin Yun etc.Mostly be distributed in water side of a ship hole, Venus hole, floating fern hole, Bi Likeng.Although inhale ink-stone like by many scholars, but along with inhaling the minimizing day by day of the raw-material exhaustion of ink-stone and exploitation, the price of inhaling ink-stone is very expensive, general only for the making of high-grade inkstone, study articles, tea set, if therefore can provide and a kind of there is the porcelain inhaling ink-stone grain effect by tool, not only can meet the aesthetic diversified demand of people but also there is positive economic benefit.
Summary of the invention
For overcoming deficiency of the prior art, the invention provides a kind of imitative method for cooking inhaling ink-stone porcelain and magnetized ceramic with Venus, the dizzy effect of gold being applicable to any ceramic body.
For achieving the above object, the technical solution used in the present invention is as follows: have Venus, dizzy the imitative of effect of gold inhales ink-stone porcelain, it is characterized in that, the described imitative base substrate inhaling ink-stone porcelain is provided with ground-coat enamel and glaze material, and the raw material that this ground-coat enamel comprises following weight part is prepared from: feldspar 35-55 part, calcium carbonate 15-25 part, zinc oxide 10-15 part, manganese oxide 5-10 part, kaolin 5-10 part, ferric oxide 1-5 part, mica 1-5 part; The raw material that this cover-coat enamel comprises following weight part is prepared from: feldspar 30-50 part, quartzy 15-25 part, calcium carbonate 15-25 part, zirconium silicate 5-10 part, kaolin 10-15 part, yellow wax stone 1-5 part.
Optimize, this ground-coat enamel is prepared from by the raw material of following weight part: feldspar 50 parts, 20 parts, calcium carbonate, 10 parts, zinc oxide, manganese oxide 7 parts, kaolin 7 parts, ferric oxide 3 parts, 3 parts, mica.
Optimize, this cover-coat enamel is prepared from by the raw material of following weight part: feldspar 37 parts, 20 parts, quartz, 20 parts, calcium carbonate, zirconium silicate 10 parts, kaolin 10,3 parts, yellow wax stone.
Optimize, this ground-coat enamel is prepared from by the raw material of following weight part: feldspar 41,22 parts, calcium carbonate, 12 parts, zinc oxide, manganese oxide 5 parts, kaolin 5 parts, ferric oxide 5 parts, 4 parts, mica.
Optimize, this cover-coat enamel is prepared from by the raw material of following weight part: feldspar 46 parts, 18 parts, quartz, 16 parts, calcium carbonate, zirconium silicate 8 parts, kaolin 8,4 parts, yellow wax stone.
Optimize, this ground-coat enamel is prepared from by the raw material of following weight part: feldspar 53,16 parts, calcium carbonate, 13 parts, zinc oxide, manganese oxide 9 parts, kaolin 6 parts, ferric oxide 1 part, 2 parts, mica.
Optimize, the raw material that this cover-coat enamel comprises following weight part is prepared from: feldspar 32 parts, 24 parts, quartz, 16 parts, calcium carbonate, zirconium silicate 10 parts, kaolin 13 parts, 5 parts, yellow wax stone.
The imitative method for cooking inhaling ink-stone porcelain, is characterized in that, use in the claims 1-5 described in any one there is Venus, dizzy the imitative of effect of gold inhales ink-stone porcelain, its concrete steps are as follows:
Step 1, makes ceramic body;
Step 2, ceramic body executes ground-coat enamel, and this ground-coat enamel thickness is 0.5-1.0mm;
Step 3, upper have on the ceramic body of ground-coat enamel spray cover-coat enamel, this cover-coat enamel thickness is 0.1-0.5mm;
Step 4, puts into kiln by the ceramic body of first-class ground-coat enamel and cover-coat enamel, burns till in 1000 DEG C-1080 DEG C.
Further, the imitative ink-stone porcelain that inhales is when making Venus effect, and step 3 cover-coat enamel glaze spraying thickness is 0.1-0.3mm, and cover-coat enamel is that oil droplet shape is sporadicly distributed on ground glaze layer.
Further, the imitative ink-stone porcelain that inhales is when making the dizzy effect of gold, and step 3 cover-coat enamel glaze spraying thickness is 0.4-1.0m, and cover-coat enamel in the form of sheets or block distribution on ground glaze layer and the thickness of every sheet cover-coat enamel successively decreased gradually to surrounding by centre.
From the above-mentioned description of this invention, provided by the invention have Venus, the dizzy effect of gold imitative inhale ink-stone porcelain not only can produce as required there is Venus, dizzy the imitative of effect of gold inhales ink-stone porcelain, also can make gradual change, rule or not specify texture then, the imitative ink-stone porcelain that inhales burnt out has blue or green black, dark green background color, cover-coat enamel on ground-coat enamel in the colour of loess, golden yellow glaze colours, according to design requirement ejection Venus, the dizzy effect of gold, and the glaze paint that ground-coat enamel and cover-coat enamel are formed level and smooth, combines tight, difficult drop-off; What use this kind of method to make imitatively inhales ink-stone porcelain, can imitate the natural texture inhaling ink-stone, and cover-coat enamel is formed by glaze spraying, every part porcelain all has different textures, meet user to aesthetic multifarious demand, this kind porcelain manufacture craft is simple, production cost is low, collocation property is high.
Embodiment
Below by way of embodiment, the invention will be further described.
There is Venus, dizzy the imitative of effect of gold inhales ink-stone porcelain, the described imitative base substrate inhaling ink-stone porcelain is provided with ground-coat enamel and glaze material, and the raw material that this ground-coat enamel comprises following weight part is prepared from: feldspar 35-55 part, calcium carbonate 15-25 part, zinc oxide 10-15 part, manganese oxide 5-10 part, kaolin 5-10 part, ferric oxide 1-5 part, mica 1-5 part; The raw material that this cover-coat enamel comprises following weight part is prepared from: feldspar 30-50 part, quartzy 15-25 part, calcium carbonate 15-25 part, zirconium silicate 5-10 part, kaolin 10-15 part, yellow wax stone 1-5 part.
Specific embodiment one:
Ground-coat enamel is prepared from by the raw material of following weight part: feldspar 50 parts, 20 parts, calcium carbonate, 10 parts, zinc oxide, manganese oxide 7 parts, kaolin 7 parts, ferric oxide 3 parts, 3 parts, mica;
Cover-coat enamel is prepared from by the raw material of following weight part: feldspar 37 parts, 20 parts, quartz, 20 parts, calcium carbonate, zirconium silicate 10 parts, kaolin 10,3 parts, yellow wax stone.
What use the present embodiment to burn out imitatively inhales ink-stone porcelain, has livid background color, the cover-coat enamel glaze colours in the colour of loess on ground-coat enamel, is especially applicable to making having dizzy the imitative of effect of gold and inhaling ink-stone porcelain
Specific embodiment two:
Ground-coat enamel is prepared from by the raw material of following weight part: feldspar 41,22 parts, calcium carbonate, 12 parts, zinc oxide, manganese oxide 5 parts, kaolin 5 parts, ferric oxide 5 parts, 4 parts, mica;
Cover-coat enamel is prepared from by the raw material of following weight part: feldspar 46 parts, 18 parts, quartz, 16 parts, calcium carbonate, zirconium silicate 8 parts, kaolin 8,4 parts, yellow wax stone.
The imitative ink-stone porcelain that inhales using the present embodiment to burn out has dark green background color, cover-coat enamel in golden yellow glaze colours on ground-coat enamel, and especially applicable making has the imitative of Venus effect and inhales ink-stone porcelain.
Specific embodiment three:
Ground-coat enamel is prepared from by the raw material of following weight part: feldspar 53,16 parts, calcium carbonate, 13 parts, zinc oxide, manganese oxide 9 parts, kaolin 6 parts, ferric oxide 1 part, 2 parts, mica;
The raw material that cover-coat enamel comprises following weight part is prepared from: feldspar 32 parts, 24 parts, quartz, 16 parts, calcium carbonate, zirconium silicate 10 parts, kaolin 13 parts, 5 parts, yellow wax stone.
What use the present embodiment to burn out imitatively inhales ink-stone porcelain, and have livid background color, cover-coat enamel in pale yellow glaze colours on ground-coat enamel, applicable making has gradual change or the imitative of effect of decorative patterns inhales ink-stone porcelain.
The imitative method for cooking inhaling ink-stone porcelain described in specific embodiment one to three, is characterized in that, use in the claims 1-5 described in any one there is Venus, dizzy the imitative of effect of gold inhales ink-stone porcelain, its concrete steps are as follows:
Step 1, makes ceramic body;
Step 2, ceramic body executes ground-coat enamel, and this ground-coat enamel thickness is 0.5-1.0mm;
Step 3, upper have on the ceramic body of ground-coat enamel spray cover-coat enamel, this cover-coat enamel thickness is 0.1-0.5mm;
Step 4, puts into kiln by the ceramic body of first-class ground-coat enamel and cover-coat enamel, burns till in 1000 DEG C-1080 DEG C.
When making have a Venus effect imitative and inhaling ink-stone porcelain, step 3 cover-coat enamel glaze spraying thickness is 0.1-0.3mm, and cover-coat enamel is that oil droplet shape is sporadicly distributed on ground glaze layer.
When making have a dizzy effect of gold imitative and inhaling ink-stone porcelain, step 3 cover-coat enamel glaze spraying thickness is 0.4-1.0m, and cover-coat enamel in the form of sheets or block distribution on ground glaze layer and the thickness of every sheet cover-coat enamel successively decreased gradually to surrounding by centre.
When making have a fade effect imitative and inhaling ink-stone porcelain, step 3 cover-coat enamel glaze spraying thickness is 0.2-0.8m, and cover-coat enamel in the form of sheets or block distribution on ground glaze layer and the thickness of every sheet cover-coat enamel successively decreased gradually to opposite side by side.
Above are only some embodiments of the present invention, but design concept of the present invention is not limited thereto, all changes utilizing this design the present invention to be carried out to unsubstantiality, all should belong to the behavior of invading scope.
Claims (10)
1. have Venus, dizzy the imitative of effect of gold inhales ink-stone porcelain, it is characterized in that, the described imitative base substrate inhaling ink-stone porcelain is provided with ground-coat enamel and glaze material,
The raw material that this ground-coat enamel comprises following weight part is prepared from: feldspar 35-55 part, calcium carbonate 15-25 part, zinc oxide 10-15 part, manganese oxide 5-10 part, kaolin 5-10 part, ferric oxide 1-5 part, mica 1-5 part;
The raw material that this cover-coat enamel comprises following weight part is prepared from: feldspar 30-50 part, quartzy 15-25 part, calcium carbonate 15-25 part, zirconium silicate 5-10 part, kaolin 10-15 part, yellow wax stone 1-5 part.
2. according to claim 1 there is Venus, dizzy the imitative of effect of gold inhales ink-stone porcelain, it is characterized in that, this ground-coat enamel is prepared from by the raw material of following weight part: feldspar 50 parts, 20 parts, calcium carbonate, 10 parts, zinc oxide, manganese oxide 7 parts, kaolin 7 parts, ferric oxide 3 parts, 3 parts, mica.
3. according to claim 1 and 2 there is Venus, dizzy the imitative of effect of gold inhales ink-stone porcelain, it is characterized in that, cover-coat enamel is prepared from by the raw material of following weight part: feldspar 37 parts, 20 parts, quartz, 20 parts, calcium carbonate, zirconium silicate 10 parts, kaolin 10,3 parts, yellow wax stone.
4. according to claim 1 there is Venus, dizzy the imitative of effect of gold inhales ink-stone porcelain, it is characterized in that: described ground-coat enamel is prepared from by the raw material of following weight part: feldspar 41,22 parts, calcium carbonate, 12 parts, zinc oxide, manganese oxide 5 parts, kaolin 5 parts, ferric oxide 5 parts, 4 parts, mica.
5. according to claim 1 or 4 there is Venus, dizzy the imitative of effect of gold inhales ink-stone porcelain, it is characterized in that, this cover-coat enamel is prepared from by the raw material of following weight part: feldspar 46 parts, 18 parts, quartz, 16 parts, calcium carbonate, zirconium silicate 8 parts, kaolin 8,4 parts, yellow wax stone.
6. according to claim 1 there is Venus, dizzy the imitative of effect of gold inhales ink-stone porcelain, it is characterized in that, described ground-coat enamel is prepared from by the raw material of following weight part: feldspar 53,16 parts, calcium carbonate, 13 parts, zinc oxide, manganese oxide 9 parts, kaolin 6 parts, ferric oxide 1 part, 2 parts, mica.
7. according to claim 1 or 6 there is Venus, dizzy the imitative of effect of gold inhales ink-stone porcelain, it is characterized in that: the raw material that described cover-coat enamel comprises following weight part is prepared from: feldspar 32 parts, 24 parts, quartz, 16 parts, calcium carbonate, zirconium silicate 10 parts, kaolin 13 parts, 5 parts, yellow wax stone.
8. the imitative method for cooking inhaling ink-stone porcelain, is characterized in that, use in the claims 1-5 described in any one there is Venus, dizzy the imitative of effect of gold inhales ink-stone porcelain, its concrete steps are as follows:
Step 1, makes ceramic body;
Step 2, ceramic body executes ground-coat enamel, and this ground-coat enamel thickness is 0.5-1.0mm;
Step 3, upper have on the ceramic body of ground-coat enamel spray cover-coat enamel, this cover-coat enamel thickness is 0.1-0.5mm;
Step 4, puts into kiln by the ceramic body of first-class ground-coat enamel and cover-coat enamel, burns till in 1000 DEG C-1080 DEG C.
9. the imitative method for cooking inhaling ink-stone porcelain according to claim 8, is characterized in that: the described imitative ink-stone porcelain that inhales is when making Venus effect, and step 3 cover-coat enamel glaze spraying thickness is 0.1-0.3mm, and cover-coat enamel is that oil droplet shape is sporadicly distributed on ground glaze layer.
10. the imitative method for cooking inhaling ink-stone porcelain according to claim 8, it is characterized in that: the described imitative ink-stone porcelain that inhales is when making the dizzy effect of gold, step 3 cover-coat enamel glaze spraying thickness is 0.4-1.0m, and cover-coat enamel in the form of sheets or block distribution on ground glaze layer and the thickness of every sheet cover-coat enamel successively decreased gradually to surrounding by centre.