CN104745035B - One kind emulation multicolor finish containing sand and preparation method thereof and method of application - Google Patents
One kind emulation multicolor finish containing sand and preparation method thereof and method of application Download PDFInfo
- Publication number
- CN104745035B CN104745035B CN201510121833.8A CN201510121833A CN104745035B CN 104745035 B CN104745035 B CN 104745035B CN 201510121833 A CN201510121833 A CN 201510121833A CN 104745035 B CN104745035 B CN 104745035B
- Authority
- CN
- China
- Prior art keywords
- parts
- minutes
- water
- multicolor finish
- containing sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention belongs to technical field of coatings, and in particular to one kind emulation multicolor finish containing sand and preparation method thereof and method of application；It includes what is calculated in parts by weight：90~160 parts of 150~250 parts of emulsion, 10~15 parts of antifreeze, 13~18 parts of coalescents, 0.5~1.5 part of defoamer, 1~2 part of preservative, 2~3 parts of pH adjusting agent, 600~700 parts of color tablets solution, 10~20 parts of thickener B and water.The present invention is aqueous, environmental protective artificial granite paint, not only can arbitrarily prepare the effect that color reaches most of natural granite, fidelity is up to 90%~95%；And cost is low compared with natural granite, safe to use, easy for construction, flow is simple, can be constructed in convex-concave surface；And fidelity is higher compared with common multicolor finish, texture is more preferable.
Description
Technical field
The invention belongs to technical field of coatings, and in particular to a kind of emulation multicolor finish containing sand suitable for external wall and
Its preparation method and method of application.
Background technology
The exterior finish of building plays an important role to the sense organ of building, and the ornament materials of present exterior wall mainly has following several
Kind：Emulsion paint, true mineral varnish, aluminium-plastic panel, clad aluminium, cement plate, ceramic tile, glass, stone material etc..Wherein, with natural ornamental stone
Decorative effect is best, and durable and enjoy great popularity.But come with some shortcomings using natural ornamental stone：It is natural granite, big
The decorative pattern and color category of reason stone are limited, and can be had any different between different geographical；Natural granite, marble own wt compared with
Greatly, the risk to be dropped on external wall using having；Lithotome is limited resources, is increasingly reduced, and exhaustive exploitation
Environment can be damaged.
Because people replace its decorative effect using the coating of natural-like stone.Common more color coatings on the market at present
Although material can accomplish to approach with natural granite effect in color, its surface tactile sensation all the time with natural granite gap compared with
Greatly.
The content of the invention
In order to solve the above problems, it is an object of the invention to provide one kind to emulate multicolor finish containing sand, and the coating applies
Onto exterior wall so that not only color is close to the decorative effect of lithotome for the wall decorated, and texture is also close to natural stone
The decorative effect of material.
The second object of the present invention there is provided the preparation method of emulation multicolor finish containing sand.
The third object of the present invention there is provided the method for application of emulation multicolor finish containing sand.
The present invention is achieved through the following technical solutions：
One kind emulation multicolor finish containing sand, including the following raw material calculated in parts by weight：
Wherein, described color tablets solution is made by the following raw material calculated in parts by weight：
7% 400~500 parts of glue solution of protection
450~700 parts of colored paint
20~40 parts of water
The colored paint is the base paint mixture after at least three kinds of color toners；It is preferred that adjust red base paint 100~120
Part, adjust 180~210 parts of grey base paint and adjust the mixture of 180~210 parts of yellow base paint, in such proportioning color with
Lithotome is more close.Protection glue solution is water-soluble silicate class compound, preferably Ke Naiou：S-482, its weight ratio
For 7%, main function is the independence for protecting color tablets, makes it in the texture with lithotome.
Wherein described emulsion is silicone acrylic emulsion, and preferably Ahmedabad is rich：996AD.The preferred propane diols of antifreeze, coalescents are preferred
Alcohol ester 12, the preferred mineral oil antifoam agent of defoamer, the preferred broad spectrum type preservative of preservative, the preferred AMP-95 of pH adjusting agent, increase
The preferred hydrophobically-modified alkali swelling type thickeners of thick dose of B, the preferred deionized water of water.
It is preferred that the preparation method of the color tablets solution is specially：First glue solution and colored paint are protected by the 7% of the amount
Stir 4~8 minutes under 250~350rpm, then cross 10~30 mesh sieves, finally will sieving gained granular mixture with it is described
The water of amount stirs 4~8 minutes under 250~350rpm, and the color tablets solution is made.
It is preferred that the colored paint includes the following raw material calculated in parts by weight：
700~850 parts of base paint
1~100 part of aqueous color paste
100~250 parts of quartz sand；
Wherein, the quartz sand is 150~200 mesh, and the preferably water-based rust of aqueous color paste is starched.
Wherein, the preparation method of the colored paint is：By the base paint, aqueous color paste and quartz sand under 750850rpm
Stirring 8~15 minutes, the colored paint is made.
It is preferred that the base paint includes the following raw material calculated in parts by weight：
The thickener A is cellulose, and the preferred propane diols of antifreeze, defoamer is mineral oil antifoam agent, and dispersant is sodium
Dipersant, preservative are broad spectrum type preservative, and titanium dioxide is rutile type titanium white, and kaolin is calcined kaolin, thickening
The preferred Ke Naiou of agent A：HE-10K, the preferred fraternal chemical industry of gold of crosslinking agent：KP, mainly provide thixotropy；The preferred alcohol ester of coalescents
12, the preferred AMP-95 of pH adjusting agent, emulsion are that Ahmedabad is rich：996AD.
It is preferred that the 7% protection glue solution by water that parts by weight are 930 parts and 70 parts of Protection glue in 450~
Modulation in 8~15 minutes is stirred under 550rpm to form.
Wherein, the preparation method of the base paint is：
First by the antifreeze of the amount, defoamer, dispersant, preservative and 400~450 parts of water in 250~350rpm
Lower stirring 3~8 minutes, is made mixed liquor；
Again by the titanium dioxide of the amount, kaolin, thickener A, hand over glutinous agent, coalescents and pH adjusting agent and remainder 50~
100 parts of water are added in mixed liquor one, are stirred 25~40 minutes under 1000~1500rpm；
The 7% protection glue solution and emulsion of the amount are eventually adding, is stirred 8~15 minutes under 600~1000rpm,
The base paint is made.
The method for preparing emulation multicolor finish containing sand, first by the emulsion of the amount, antifreeze, coalescents, defoaming
Agent, preservative, pH adjusting agent and water stir 3~8 minutes under 700~1000rpm；
The color tablets solution, thickener B and water of the amount are added, is stirred 3~8 minutes under 250~350rpm, institute is made
State emulation multicolor finish containing sand；
Wherein described thickener B is hydrophobically-modified alkali swelling type thickener.
It is preferred that the color tablets solution and thickener B need to be slowly added to.
The method of application of emulation multicolor finish containing sand, specifically：
Exterior wall putty is scraped Step 1: criticizing one time, is dried 5~8 days；
Step 2: roller coating or spraying exterior wall seal coat one time, are dried 5~8 hours；
Step 3: twice of roller coating or the water-based real color bottom paint of spraying, are dried 5~8 hours；
Step 4: spraying is described to emulate multicolor finish containing sand twice, dry 10~15 hours；
Step 5: spraying water-based finishing varnish one time, dry 5~8 hours；Application finishes..
The present invention is aqueous, environmental protective artificial granite paint, not only can arbitrarily prepare color and most of natural granite
Effect, because adding quartz sand in formula, thus fidelity up to 90%~95%, the cost compared with natural granite
Low, safe to use, easy for construction, flow is simple, can be constructed in convex-concave surface；And the fidelity compared with common multicolor finish
Higher, texture is more preferable.Adherence, hardness, weatherability etc. show excellent.Lifted external wall decorative effect and reduce use into
This, replaces natural granite, marble, solves the shortcomings of poor high cost of granite, security, effect limitednumber；Meanwhile with
Common multicolor finish is compared, and greatly lifts surface tactile sensation and fidelity.
Specific embodiment
With reference to embodiment, the present invention is described in further detail, is managed to help those skilled in the art
The solution present invention.
Embodiment 1
A, 7% protection glue solution is prepared
By 930kg deionized waters and 70kg Protection glues (Ke Naiou：S-482) 500rpm is stirred 10 minutes in mixer,
Obtain the 7% protection glue solution.
B, base paint is prepared
Deionized water 450kg, antifreeze 15kg, defoamer 3kg, dispersant 3kg and preservative 3kg are first placed in mixer
Middle 300rpm is stirred 5 minutes, obtains the base paint；
Titanium dioxide 10kg, kaolin 70kg, thickener A4.5kg, crosslinking agent 5kg, coalescents 20kg, pH tune are put into again
Agent 1kg and water 75.5kg is saved, mixing speed is heightened and is stirred 30 minutes to 1200rpm；
The finally protection glue solution 40kg and emulsion 300kg of input 7%, 800rpm are stirred 15 minutes, obtain the basis
Paint.
C, basic paint toning
By obtained base paint 790kg, red aqueous color paste 10kg and 200 mesh sizes quartz sand 200kg, in 800rpm
Stirring 10 minutes, obtains adjusting red base paint；
By obtained base paint 790kg, grey aqueous color paste 10kg and the quartz sand 200kg of 200 mesh sizes, in 800rpm
Stirring 10 minutes, obtain adjusting grey base paint；
By obtained base paint 790kg, yellow aqueous color paste 10kg and the quartz sand 200kg of 200 mesh sizes, in 800rpm
Stirring 10 minutes, obtain adjusting yellow base paint.
D, color tablets solution is prepared
First by 7% protection glue solution 460kg, the red base paint 110kg of tune, tune grey base paint 200kg and tune yellow
Base paint 200kg, stirred 5 minutes in 300rpm, then mixture sieves (10 mesh), becomes granular mixture after sieving；
Water 30kg, 300rpm stirring 5 minutes is eventually adding, the color tablets solution is made.
E, the preparation of the multicolor finish containing sand is emulated
First by emulsion, (Ahmedabad is rich：996AD) 200kg, antifreeze 13kg, coalescents 15kg, defoamer 1kg, water 7kg,
Preservative 1.5kg and pH adjusting agent 2.5kg, stirred under 800rpm 5 minutes, then add color tablets solution 650kg, thickener B
14.5kg and water 95.5kg, 300rpm are stirred 5 minutes.Obtain final finished emulation multicolor finish containing sand.
Embodiment 2
A, 7% protection glue solution is prepared
By 930kg deionized waters and 70kg Protection glues (Ke Naiou：S-482) 450rpm is stirred 8 minutes in mixer, is obtained
To described 7% protection glue solution.
B, base paint is prepared
Deionized water 500kg, antifreeze 10kg, defoamer 2kg, dispersant 2kg and preservative 2kg are first placed in mixer
Middle 250rpm is stirred 3 minutes, obtains the base paint；
Titanium dioxide 8kg, kaolin 60kg, thickener A 3kg, crosslinking agent 3kg, coalescents 10kg, pH regulation are put into again
Agent 1kg and water 50kg, heighten mixing speed and stirred 25 minutes to 1000rpm；
The finally protection glue solution 30kg and emulsion 319kg of input 7%, 600rpm are stirred 8 minutes, obtain the basis
Paint.
C, basic paint toning
By obtained base paint 700kg, red aqueous color paste 100kg and 150 mesh sizes quartz sand 200kg, in
750rpm is stirred 8 minutes, obtains adjusting red base paint；
By obtained base paint 790kg, grey aqueous color paste 100kg and the quartz sand 200kg of 150 mesh sizes, in
750rpm is stirred 8 minutes, obtains adjusting red base paint；
By obtained base paint 790kg, yellow aqueous color paste 100kg and the quartz sand 200kg of 150 mesh sizes, in
750rpm is stirred 8 minutes, obtains adjusting red base paint.
D, color tablets solution is prepared
First by 7% protection glue solution 400kg, the red base paint 130kg of tune, tune grey base paint 220kg and tune yellow
Base paint 220kg, stirred 10 minutes in 250rpm, then mixture sieves (10 mesh), becomes granular mixture after sieving；
Water 30kg, 250rpm stirring 4 minutes is eventually adding, the color tablets solution is made.
E, the preparation of the multicolor finish containing sand is emulated
First by emulsion, (Ahmedabad is rich：996AD) 150kg, antifreeze 15kg, coalescents 18kg, defoamer 1.5kg, water
10kg, preservative 2kg and pH adjusting agent 3kg, stirred under 700rpm 3 minutes, then add color tablets solution 700kg, thickener B
205kg and water 80.5kg, 250rpm are stirred 3 minutes.Obtain final finished emulation multicolor finish containing sand.
Embodiment 3
A, 7% protection glue solution is prepared
By 930kg deionized waters and 70kg Protection glues (Ke Naiou：S-482) 550rpm is stirred 15 minutes in mixer,
Obtain the 7% protection glue solution.
B, base paint is prepared
Deionized water 400kg, antifreeze 20kg, defoamer 5kg, dispersant 5kg and preservative 5kg are first placed in mixer
Middle 350rpm is stirred 8 minutes, obtains the base paint；
Titanium dioxide 15kg, kaolin 80kg, thickener A5kg, crosslinking 15kg, coalescents 255kg, pH regulation are put into again
Agent 1kg and water 100kg, heighten mixing speed and stirred 40 minutes to 1500rpm；
The finally protection glue solution 45kg and emulsion 289kg of input 7%, 1000rpm are stirred 15 minutes, obtain the basis
Paint.
C, basic paint toning
By obtained base paint 749kg, red aqueous color paste 1kg and 200 mesh sizes quartz sand 250kg, in 850rpm
Stirring 15 minutes, obtains adjusting red base paint；
By obtained base paint 749kg, grey aqueous color paste 1kg and the quartz sand 250kg of 200 mesh sizes, in 850rpm
Stirring 15 minutes, obtains adjusting red base paint；
By obtained base paint 749kg, yellow aqueous color paste 1kg and the quartz sand 250kg of 200 mesh sizes, in 850rpm
Stirring 15 minutes, obtains adjusting red base paint.
D, color tablets solution is prepared
First by 7% protection glue solution 500kg, the red base paint 120kg of tune, tune grey base paint 180kg and tune yellow
Base paint 1800kg, stirred 8 minutes in 350rpm, then mixture sieves (20 mesh), becomes granular mixture after sieving；
Water 20kg, 350rpm stirring 8 minutes is eventually adding, the color tablets solution is made.
E, the preparation of the multicolor finish containing sand is emulated
First by emulsion, (Ahmedabad is rich：996AD) 208.5kg, antifreeze 103kg, coalescents 13kg, defoamer 0.5kg, water
5kg, preservative 1kg and pH adjusting agent 2kg, stirred under 1000rpm 8 minutes, then add color tablets solution 600kg, thickener B
10kg and water 1kg, 3500rpm are stirred 8 minutes.Obtain final finished emulation multicolor finish containing sand.
Embodiment 4
A, 7% protection glue solution is prepared
By 930kg deionized waters and 70kg Protection glues (Ke Naiou：S-482) 500rpm is stirred 10 minutes in mixer,
Obtain the 7% protection glue solution.
B, base paint is prepared
Deionized water 420kg, antifreeze 18kg, defoamer 4kg, dispersant 4kg and preservative 4kg are first placed in mixer
Middle 300rpm is stirred 5 minutes, obtains the base paint；
Titanium dioxide 12kg, kaolin 75kg, thickener A 4kg, crosslinking agent 4kg, coalescents 20kg, pH regulation are put into again
Agent 1kg and water 90kg, heighten mixing speed and stirred 30 minutes to 1200rpm；
The finally protection glue solution 40kg and emulsion 300kg of input 7%, 800rpm are stirred 15 minutes, obtain the basis
Paint.
C, basic paint toning
By obtained base paint 850kg, red aqueous color paste 50kg and 200 mesh sizes quartz sand 100kg, in 800rpm
Stirring 10 minutes, obtains adjusting red base paint；
By obtained base paint 850kg, grey aqueous color paste 50kg and the quartz sand 100kg of 200 mesh sizes, in 800rpm
Stirring 10 minutes, obtain adjusting grey base paint；
By obtained base paint 850kg, yellow aqueous color paste 50kg and the quartz sand 100kg of 200 mesh sizes, in 800rpm
Stirring 10 minutes, obtain adjusting yellow base paint.
D, color tablets solution is prepared
First by 7% protection glue solution 460kg, the red base paint 100kg of tune, tune grey base paint 190kg and tune yellow
Base paint 210kg, stirred 5 minutes in 300rpm, then mixture sieves (10 mesh), becomes granular mixture after sieving；
Water 40kg, 300rpm stirring 5 minutes is eventually adding, the color tablets solution is made.
E, the preparation of the multicolor finish containing sand is emulated
First by emulsion, (Ahmedabad is rich：996AD) 200kg, antifreeze 14kg, coalescents 12kg, defoamer 1kg, water 8kg,
Preservative 1.5kg and pH adjusting agent 2.5kg, stirred under 800rpm 5 minutes, then add color tablets solution 643kg, thickener B
18kg and water 100kg, 300rpm are stirred 5 minutes.Obtain final finished emulation multicolor finish containing sand.
Above-described embodiment, simply presently preferred embodiments of the present invention, is not used for limiting the scope of the present invention, therefore all with this
The equivalent change or modification that feature and principle described in invention claim are done, all should be included in scope of the invention as claimed
Within.
Product of the present invention is in the case of using supporting finish paint, wherein several main physical property are as shown in the table：
As seen from the above table, the present invention not only has an appearance and texture of natural granite, and adherence, water resistance, resistance to
Alkalescence is identical with natural granite, and is all shown and natural granite identical in QUV tests and cold cycling test
Energy.
Claims (8)
1. one kind emulation multicolor finish containing sand, it is characterised in that including the following raw material calculated in parts by weight：
Wherein, described color tablets solution is made by the following raw material calculated in parts by weight：
7% 400~500 parts of glue solution of protection
450~700 parts of colored paint
20~40 parts of water
The preparation method of the color tablets solution is specially：First by the 7% of amount protection glue solution and colored paint in 250~
Stirred under 350rpm 4~8 minutes, then cross 10~30 mesh sieves, finally by the water of gained granular mixture and the amount that sieves
Stirred 4~8 minutes under 250~350rpm, the color tablets solution is made；
The colored paint is the base paint mixture after at least three kinds of color toners, wherein, the 7% protection glue solution amount of attaching most importance to hundred
Divide ratio.
2. emulation multicolor finish containing sand as claimed in claim 1, it is characterised in that the colored paint includes what is calculated in parts by weight
The following raw material：
700~850 parts of base paint
1~100 part of aqueous color paste
100~250 parts of quartz sand；
Wherein, the quartz sand is 150~200 mesh.
3. emulation multicolor finish containing sand as claimed in claim 2, it is characterised in that the preparation method of the colored paint is：
The base paint, aqueous color paste and quartz sand are stirred 8~15 minutes under 750~850rpm, the colored paint is made.
4. multicolor finish containing sand is emulated as described in any one in claim 1,2 or 3, it is characterised in that the basic enamel-cover
Include the following raw material calculated in parts by weight：
The thickener A is cellulose, wherein, 7% protection glue solution is weight percentage.
5. emulation multicolor finish containing sand as claimed in claim 1, it is characterised in that the 7% protection glue solution is by parts by weight
Water and 70 parts of Protection glue for 930 parts stir modulation in 8~15 minutes under 450~550rpm and formed.
6. emulation multicolor finish containing sand as claimed in claim 4, it is characterised in that the preparation method of the base paint is：
First by the antifreeze of the amount, defoamer, dispersant, preservative and 400~450 parts of water, stirred under 250~350rpm
3~8 minutes, mixed liquor is made；
Again by the titanium dioxide of the amount, kaolin, thickener A, friendship glutinous agent, coalescents and PH conditioning agents and remainder 50~100
Part water is added in the mixed liquor, is stirred 25~40 minutes under 1000~1500rpm；
The 7% protection glue solution and emulsion of the amount are eventually adding, stirs 8~15 minutes, is made under 600~1000rpm
The base paint, wherein, 7% protection glue solution is weight percentage.
7. prepare the method for emulating the multicolor finish containing sand in claim 1-6 described in any one, it is characterised in that：
First by the emulsion of the amount, antifreeze, coalescents, defoamer, preservative, pH adjusting agent and water in 700~1000rpm
Lower stirring 3~8 minutes；
The color tablets solution, thickener B and water of the amount are added, is stirred 3~8 minutes under 250~350rpm, is made described imitative
True multicolor finish containing sand；
Wherein described thickener B is hydrophobically-modified alkali swelling type thickener.
8. the method for application of the multicolor finish containing sand is emulated in claim 1-6 described in any one, it is characterised in that specific
For：
Exterior wall putty is scraped Step 1: criticizing one time, is dried 5~8 days；
Step 2: roller coating or spraying exterior wall seal coat one time, are dried 5~8 hours；
Step 3: twice of roller coating or the water-based real color bottom paint of spraying, are dried 5~8 hours；
Step 4: spraying is described to emulate multicolor finish containing sand twice, dry 10~15 hours；
Step 5: spraying water-based finishing varnish one time, dry 5~8 hours；Application finishes.