CN102617084A - Inorganic colorized decoration mortar and preparation method thereof - Google Patents
Inorganic colorized decoration mortar and preparation method thereof Download PDFInfo
- Publication number
- CN102617084A CN102617084A CN2011100327202A CN201110032720A CN102617084A CN 102617084 A CN102617084 A CN 102617084A CN 2011100327202 A CN2011100327202 A CN 2011100327202A CN 201110032720 A CN201110032720 A CN 201110032720A CN 102617084 A CN102617084 A CN 102617084A
- Authority
- CN
- China
- Prior art keywords
- decoration mortar
- inorganic color
- color decoration
- aggregate
- mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention which belongs to the technical field of building materials concretely relates to an inorganic colorized decoration mortar and a preparation method thereof. The motor is characterized in that the motor comprises the following components, by weight, 15-40% of cement, 40-70% of an aggregate, 1-30% of an auxiliary material, 0.5-5.0% of nanoscale micropowder, 0.5-4.0% of a thixotropic agent, 0.1-3% of an early strength agent, 1-10% of a dispersant, 0.1-1.5% of a thickener, 0.1-1.5% of a water repellent and 0.01-8% of a coloring agent, wherein the total weight percentage of all the components is 100%. The inorganic colorized decoration mortar prepared by uniformly mixing the components according to above proportions in a factory has the advantages of excellent cohesiveness with a wall base, very good hydrophobicity and permeability, and excellent contamination resistance, and the weatherability and the long-term stability are better than that of organic coatings. The inorganic colorized decoration mortar can be prepared by adding 10-25% of water at a building site and uniformly and mechanically stirring when being used. The mortar can be directly daubed or sprayed on the base, so the mortar has the characteristics of simple construction and easy operation.
Description
Technical field
The invention belongs to wall facing mortar technical field for building, be specifically related to a kind of inorganic color mortar that is used for decorating inner and external walls and preparation method thereof.
Background technology
At present; In the most at home dwelling construction; The in the eyes of wall decorative material of people is nothing more than being various bright organic coatings, is rich in ceramic tile and the stone material of texture etc., and these traditional finishing materials brought many joyous pleased and fine memories once for huge numbers of families' congratulations on the new home.But along with being showing improvement or progress day by day and common people's growth in the living standard of science and technology, people have promoted the demand to novel building technology and type material greatly to the high standard requirement of the attractive in appearance and residence comfort in the construction quality of house, house.Aspect the decoration of exterior wall, novel environmental protection type material is more and more by people's understanding and acceptance in buildings, and people expect that newer decorative material for wall surface brings people's different modeling, simple and unsophisticated, the fresh and new sensation of color.
Simultaneously, along with the development of society, energy-saving heat preserving becomes the requirement of national compulsory; The newly constructed house exterior wall all will be done external thermal insulation system; Owing to the restriction of house land used, especially in the big city, mostly the construction in residential building building is high-rise building again; But for high-rise building, the big limitations of deadweight problem of ceramic tile itself application of this type material on Highrise buildings (external thermal insulation system).And generally by exterior coating that people accepted owing to belong to organic materials, it is poor to exist tangible weathering resistance, be prone to aging, shortcomings such as long construction period, so the variation of decorative material for wall surface is the inevitable outcome of market economy.
Summary of the invention
The object of the invention is to provide a kind of inorganic color decoration mortar and preparation method thereof.This colored mortar is an inorganic materials owing to what adopt, and weather resistance will be higher than coating far away, owing to be directly to spread upon on the overcoat; So also fine with the cohesive force of basal plane, in addition, because the own wt of its material will be well below ceramic tile; So can be as phenomenons such as generations such as ceramic tile cracking come off; This colored mortar has also added advanced hydrophobic material, makes colored mortar have good hydrophobic nature, so there is good provide protection in basic unit.Colored mortar is through selecting the aggregate of different-grain diameter for use, and in construction process, adopts different construction appliances and construction gimmick, can moulding go out various pattern structure, and such graphical configuration has fairly obvious texture and good main body is decorated effect.This mortar can directly be smeared or spray on the basal plane, easy construction, easy handling.
The inorganic color mortar that the present invention proposes is characterized in that raw material is: cement 15-40%, aggregate 40-70%, auxiliary material 1.0-30%; Nano level micro mist 0.5-5.0%, thixotropic agent 0.5-4.0%, hardening accelerator 0.1-3%; Dispersion agent 1-10%, thickening agent 0.1-1.5%, hydrophober 0.1-1.5%; Tinting material 0.01-8.0%, each component total amount satisfies 100%.
Cement described in the present invention is silicate cement, ordinary Portland cement, white portland cement, one or more in the aluminate cement.
Aggregate described in the present invention is one or more in white Wingdale, silica sand and the artificial colour aggregate, and the particle diameter of aggregate is between 0.1-5.0mm.
Auxiliary material described in the present invention is a limestone powder, one or both in the flyash.
Nano level micro mist described in the present invention is the calcium carbonate superfine powder powder, ultrafine slag powder, one or more in the super-fine silicon micro-powder.
Thixotropic agent described in the present invention is for receiving base bentonite, one or both in the calcium-base bentonite.
Hardening accelerator described in the present invention is trolamine, one or both of nitrite complex accelerator.
Dispersion agent described in the present invention is a vinyl acetate-ethylene copolymer, vinyl acetate between to for plastic-tertiary monocarboxylic acid ethylene copolymer, one or more in the polyvinylacetate-acrylic copolymer.
Thickening agent described in the present invention is a starch ethers, one or both in the ether of cellulose.
Hydrophober described in the present invention is siloyl group, one or both in the alkali metal complex.
Tinting material described in the present invention is a white titanium pigment, one or more in red stone series pigment and the chromic salts pigment.
Preparing method of the present invention can be divided into following 2 kinds:
1. the preparation of building-site: accurately take by weighing various starting material in proportion, with cement, aggregate, auxiliary material; The nano level micro mist, thixotropic agent, hardening accelerator, dispersion agent; Thickening agent, hydrophober, tinting material adds mixing machine, does and stirs 3-15 minute; Even to material, add water then and stirred 10-20 minute, evenly can make the polychromy mortar to material.
2. a factory's dry mortar preparation: accurately take by weighing various starting material in proportion, cement, aggregate (are handled through dry classification in advance! ), auxiliary material, nano level micro mist, thixotropic agent, hardening accelerator, dispersion agent, thickening agent, hydrophober, tinting material adds dry mixer, stirs, and can make dry mortar.The dry mortar that mixes is carried out metering packing by certain specification, and this packing should possess waterproof and dampproof function is arranged.Using the scene with dry mortar, water mixes in mixing machine in proportion, can make the polychromy mortar.
The present invention detects department's (with reference to JC/T 1024-2007 " wall facing mortar ") through country and detects, and its tensile bond strength is greater than 0.5MPa, and 240 minutes water regain is less than 5.0 grams.
The present invention has following advantage:
1. in dry mortar, add water and be stirred to material and evenly can directly use, this mortar and various basal plane (concrete, sand-cement slurry etc.) have good cohesiveness, incrust and cracking; Not only has good flexibility; Simultaneously, also has good hydrophobic nature, ventilation property and good anti-contamination ability; Compare with organic coating, have better weather resistance and permanent stability.
2. used starting material are common commercially available prod, and buying is suitable for extensively promoting the use of easily.
3. for the mortar of existing market, mortar of the present invention has higher tensile bond strength and lower water regain, and preparation technology is simple simultaneously, is easy to construct at building-site.
Embodiment
Below in conjunction with embodiment technical scheme of the present invention is further described, all mix to stir and all to adopt powerful the stirring, and the detection of the water regain of tensile bond strength and 240 minutes is carried out with reference to JC/T 1024-2007 " wall facing mortar ".
Case study on implementation 1:
A kind of inorganic color decoration mortar, its material composition proportioning (weight percent) is: silicate cement: 26%, white carbonatite aggregate 0.1-0.5 millimeter: 20%; White carbonatite aggregate 0.5-1.0 millimeter: 12%, white carbonatite aggregate 1.0-2.0 millimeter: 15%, white carbonatite aggregate 2.0-3.0 millimeter: 10%; Limestone powder: 5.0%, the calcium carbonate superfine powder powder: 3.0%, sodium bentonite: 2.2%; Trolamine: 0.10%, vinyl acetate-ethylene copolymer: 3.0%, ether of cellulose: 0.4%; Siloyl group hydrophober: 0.8%, iron oxide pigment: 2.5%.To mix by each component of proportioning weighing, add an amount of water mixing then.
Prepared colored mortar of this case study on implementation and basal plane have good cohesiveness, incrust and cracking, and this mortar not only has good flexibility, also has good hydrophobic nature and anti-contamination ability simultaneously, can play the excellent decoration effect to wall body structure.
Case study on implementation 2:
A kind of inorganic color decoration mortar, its material composition proportioning (weight percent) is: white portland cement: 25%, white carbonatite aggregate 0.1-0.5 millimeter: 25%; White carbonatite aggregate 0.5-1.0 millimeter: 10%, white carbonatite aggregate 2.0-3.0 millimeter: 15%, limestone powder: 10%; Super-fine silicon micro-powder: 4.6%, calcium-base bentonite: 2.8%, nitrite complex accelerator: 0.1%; Vinyl acetate between to for plastic-tertiary monocarboxylic acid ethylene copolymer: 3.0%; Ether of cellulose: 0.3%, alkali metal complex hydrophober: 1.0%, iron oxide pigment: 3.2%.To mix by each component of proportioning weighing, add an amount of water mixing then.
Prepared colored mortar of this case study on implementation and basal plane have good cohesiveness, incrust and cracking, and this mortar not only has good flexibility, also has good hydrophobic nature and anti-contamination ability simultaneously, can play the excellent decoration effect to wall body structure.
Case study on implementation 3:
A kind of inorganic color decoration mortar, its material composition proportioning (weight percent) is: white portland cement: 20%, aluminate cement 7%; White carbonatite aggregate 0.1-0.5 millimeter: 20%, white carbonatite aggregate 0.5-1.0 millimeter: 15%, white carbonatite aggregate 1.0-2.0 millimeter: 20%; Limestone powder: 5.4%, the calcium carbonate superfine powder powder: 3.8%, sodium bentonite: 2%; The nitrite complex accelerator: 0.1%, polyvinylacetate-acrylic copolymer: 2.8%, ether of cellulose 0.3%; Siloyl group hydrophober: 0.8%, white titanium pigment: 2.8%.To mix by each component of proportioning weighing, add an amount of water mixing then.
Prepared colored mortar of this case study on implementation and basal plane have good cohesiveness, incrust and cracking, and this mortar not only has good flexibility, also has good hydrophobic nature and anti-contamination ability simultaneously, can play the excellent decoration effect to wall body structure.
Case study on implementation 4:
A kind of inorganic color decoration mortar, its material composition proportioning (weight percent) is: silicate cement: 25%, aluminate cement: 8%; White carbonatite aggregate 0.1-0.5 millimeter: 30%, white carbonatite aggregate 0.5-1.0 millimeter: 6%, white carbonatite aggregate 1.0-2.0 millimeter: 16%; Flyash: 5%, super-fine silicon micro-powder: 2%, sodium bentonite: 2%; The nitrite complex accelerator: 0.1%, polyvinylacetate-acrylic copolymer: 2.6%, ether of cellulose: 0.5%; Siloyl group hydrophober: 0.7%, iron oxide pigment; 2.1%.To mix by each component of proportioning weighing, add an amount of water mixing then.
Prepared colored mortar of this case study on implementation and basal plane have good cohesiveness, incrust and cracking, and this mortar not only has good flexibility, also has good hydrophobic nature and anti-contamination ability simultaneously, can play the excellent decoration effect to wall body structure.
Case study on implementation 5:
A kind of inorganic color decoration mortar, its material composition proportioning (weight percent) is: white portland cement: 20%, aluminate cement: 7%; Artificial colour aggregate 0.1-0.5 millimeter: 25%, artificial colour aggregate 0.5-1.0 millimeter: 12%, artificial colour aggregate 1.0-2.0 millimeter: 5%; Artificial colour aggregate 3.0-5.0 millimeter: 15%, limestone powder: 4%, calcium carbonate superfine powder powder: 3.2%; Sodium bentonite: 2%, the nitrite complex accelerator: 0.1%, vinyl acetate-ethylene copolymer: 2.8%; Ether of cellulose: 0.3%, siloyl group hydrophober: 0.8%, iron oxide pigment: 2.8%.To mix by each component of proportioning weighing, add an amount of water mixing then.
Prepared colored mortar of this case study on implementation and basal plane have good cohesiveness, incrust and cracking, and this mortar not only has good flexibility, also has good hydrophobic nature and anti-contamination ability simultaneously, can play the excellent decoration effect to wall body structure.
Case study on implementation 6:
A kind of inorganic color decoration mortar, its material composition proportioning (weight percent) is: silicate cement: 21%, aluminate cement: 7%; Quartz sand aggregate 0.1-0.5 millimeter: 25%, quartz sand aggregate 0.5-1.0 millimeter: 12%, quartz sand aggregate 1.0-2.0 millimeter: 10%; Quartz sand aggregate 2.0-3.0 millimeter: 10%, limestone powder: 3%, calcium carbonate superfine powder powder: 3.2%; Sodium bentonite: 2%, the nitrite complex accelerator: 0.1%, vinyl acetate-ethylene copolymer: 2.8%; Ether of cellulose: 0.3%, siloyl group hydrophober: 0.8%, iron oxide pigment: 2.8%.To mix by each component of proportioning weighing, add an amount of water mixing then.
Prepared colored mortar of this case study on implementation and basal plane have good cohesiveness, incrust and cracking, and this mortar not only has good flexibility, also has good hydrophobic nature and anti-contamination ability simultaneously, can play the excellent decoration effect to wall body structure.
Claims (11)
1. an inorganic color decoration mortar is characterized in that being made up of cement, aggregate, auxiliary material, nano level micro mist, thixotropic agent, hardening accelerator, dispersion agent, thickening agent, hydrophober, tinting material, and the weight proportion of each material is: cement 15-40%; Aggregate 40-70%, auxiliary material 1.0-30%, nano level micro mist 0.5-5.0%; Thixotropic agent 0.5-4.0%, hardening accelerator 0.1-3%, dispersion agent 1.0-10%; Thickening agent 0.1-1.5%; Hydrophober 0.1-1.5%, tinting material 0.01-8.0%, each component total amount satisfies 100%; And each component of aforementioned proportion mixed through the dry mixed mode of machinery.During use,, the building site evenly can make the inorganic color decoration mortar after adding water 10-25% with mechanical stirring.
2. inorganic color decoration mortar according to claim 1 is characterized in that said cement is silicate cement, ordinary Portland cement, white portland cement, one or more in the aluminate cement.
3. inorganic color decoration mortar according to claim 1 is characterized in that described aggregate is one or more in white Wingdale, silica sand and the artificial colour aggregate, and the particle diameter of aggregate is between 0.1-5.0mm.
4. inorganic color decoration mortar according to claim 1 is characterized in that described auxiliary material is a limestone powder, one or both in the flyash.
5. inorganic color decoration mortar according to claim 1 is characterized in that described nano level micro mist is the calcium carbonate superfine powder powder, ultrafine slag powder, one or more in the super-fine silicon micro-powder.
6. inorganic color decoration mortar according to claim 1 is characterized in that described thixotropic agent is for receiving base bentonite, one or both in the calcium-base bentonite.
7. inorganic color decoration mortar according to claim 1 is characterized in that described hardening accelerator is trolamine, one or both of nitrite complex accelerator.
8. inorganic color decoration mortar according to claim 1 is characterized in that described dispersion agent is a vinyl acetate-ethylene copolymer, vinyl acetate between to for plastic-tertiary monocarboxylic acid ethylene copolymer, one or more in the polyvinylacetate-acrylic copolymer.
9. inorganic color decoration mortar according to claim 1 is characterized in that described thickening agent is a starch ethers, one or both in the ether of cellulose.
10. inorganic color decoration mortar according to claim 1 is characterized in that described hydrophober is siloyl group, one or both in the alkali metal complex.
11. inorganic color decoration mortar according to claim 1 is characterized in that described tinting material is a white titanium pigment, one or more in red stone series pigment and the chromic salts pigment.