CN104098301A - Light-burned dolomite/ montmorillonite composited lightweight partition board, and manufacturing method thereof - Google Patents
Light-burned dolomite/ montmorillonite composited lightweight partition board, and manufacturing method thereof Download PDFInfo
- Publication number
- CN104098301A CN104098301A CN201410271807.9A CN201410271807A CN104098301A CN 104098301 A CN104098301 A CN 104098301A CN 201410271807 A CN201410271807 A CN 201410271807A CN 104098301 A CN104098301 A CN 104098301A
- Authority
- CN
- China
- Prior art keywords
- parts
- partition board
- light
- montmorillonite
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a light-burned dolomite/montmorillonite composited lightweight partition board. The light-burned dolomite/montmorillonite composited lightweight partition board is characterized by comprising the following raw materials in parts by weight: 10-14 parts of cement, 11-15 parts of ceramic, 15-18 parts of low polymer, 9-14 parts of light-burned dolomite, 1-2 parts of dicumyl peroxide, 1.1-2.4 parts of methyl triethoxysilane, 10-13 parts of montmorillonite, 5-8 parts of organic silicon, 19-23 parts of waste porcelain powder, 0.9-1.5 parts of triethyl citrate, 16-18 parts of indocalamus leaves, 3-6 parts of an assistant, and a proper amount of water. According to the invention, lots of industrial waste slag and agricultural wastes are used, so that the production cost is low, a good social and economic benefit is provided, and the prepared lightweight partition board has functions of being free of steam or autoclave curing, high in strength, good in water resistance, thermal-insulating, fire-retardant and the like, and can avoid moisture absorption and efflorescence.
Description
Technical field
The present invention relates to building material field, be specifically related to a kind of light dolomite/montmorillonite Composite light cellular partition board and preparation method thereof.
Background technology
Light cellular partition board is made up of various industrial waste residues such as innoxious phosphogypsum, lightweight slag, flyash, a kind of novel energy-conserving walling material forming through the maintenance of frequency conversion steam pressurized, the walling that it is a kind of external form as the cassette ceiling, but there is male and female falcon groove on its both sides, when installation, only sheet material need be erected, male and female falcon is coated after a small amount of filleting mortar assembled.It has the advantages such as quality is light, intensity is high, multiple environmental protection, heat insulating, sound insulation, breathing damping, fire prevention, rapid construction, reduction body of wall cost, so enjoy favor in architecture indoor finishing field, but the shortcomings such as the light cellular partition board ultimate compression strength using is in the market low, tensile strength weak, anti-cracking performance and hanging ability is not good, production cost is high, sound-insulating weak effect.
Summary of the invention
Object of the present invention is just to provide a kind of light dolomite/montmorillonite Composite light cellular partition board and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
A kind of light dolomite/montmorillonite Composite light cellular partition board, it is characterized in that, made by the raw material of following weight part: cement 10-14, haydite 11-15, low-grade polymer 15-18, light dolomite 9-14, dicumyl peroxide 1-2, Union carbide A-162 1.1-2.4, polynite 10-13, organosilicon 5-8, useless porcelain powder 19-23, triethyl citrate 0.9-1.5, rice-pudding leaf 16-18, auxiliary agent 3-6, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: volcanic ash 6-9, Sodium sulfate anhydrous.min(99) 2-5, magnesium chloride 3-5, magnesium oxide 2-4, polyvinyl alcohol 0.2-0.5, Starso 0.03-0.07, sodium aluminate 0.05-0.6, tartrate 0.8-2.1, organosilicon crylic acid latex 2.1-4.3, 2-imidazolidone 0.04-0.09, silicon carbide 1-3, accelerant CZ 0.03-0.05, Syzygium aromaticum stem oil 1.2-3.2, its preparation method is in 50% magnesium chloride solution, to add the magnesium oxide powder inorganic gel agent that stirs to obtain, then other leftover materials are pulverized and mixed, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
Described low-grade polymer is the novel inorganic silicon-aluminum gelatinized material in a kind of structure with the network-like keyed jointing structure of space three-dimensional, does not adopt " two mills one burn " calcining process of consumption of natural resource and the energy in preparation technology, does not substantially discharge CO
2.The starting material wide material sources of low-grade polymer, easy to prepare, energy consumption is little, has higher mechanical property and very excellent resistance to elevated temperatures simultaneously, broken through the use range of traditional portland and alkali slag cement.The present invention, by low-grade polymer replacing partial cement, not only can reduce cost energy-conserving and environment-protective, and can not weaken again the pectisation of cement.
The preparation method of described a kind of light dolomite/montmorillonite Composite light cellular partition board, is characterized in that comprising the following steps:
(1) rice-pudding leaf is sent in charring furnace, at 485-605 DEG C, 3-4 hour is processed in charing, takes out, and is ground into powder, makes it seethe spray form triethyl citrate under condition, then add Union carbide A-162 stirring and evenly mixing to the powder of gained in air blast;
(2) get low-grade polymer and put into the hydrochloric acid soln of 8-12% and soak 4-5 hour, filter and take out, use clear water repetitive scrubbing, dry, be added to the water, meanwhile, add light dolomite, haydite, grinding obtains slurry;
(3) polynite, useless porcelain powder are calcined after 3-6 hour and taken out at 600-828 DEG C, pulverize, add organosilicon to be mixed to get slurry, granulation, dry for standby;
(4) step (1), (2), (3) reaction mass and the pulverizing of other leftover materials are added to suitable quantity of water stirring and evenly mixing and obtain slip, the slurry making is added to wall slab squeezing former moulding, cutting, natural curing, to obtain final product.
The present invention has following beneficial effect: the present invention utilizes industrial residue and agricultural wastes in a large number, production cost is low, there are good economic results in society, make that light cellular partition board has non-evaporating vapour or steam press maintenance, intensity is high, water resisting property good, nonhygroscopic halogen, insulation, the function such as fire-retardant returned.
Embodiment
Described a kind of light dolomite/montmorillonite Composite light cellular partition board, it is characterized in that, made by the raw material of following weight part: cement 10, haydite 11, low-grade polymer 15, light dolomite 9, dicumyl peroxide 1, Union carbide A-162 1.3, polynite 11, organosilicon 5, useless porcelain powder 19, triethyl citrate 0.9, rice-pudding leaf 16, auxiliary agent 3, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: volcanic ash 6, Sodium sulfate anhydrous.min(99) 2, magnesium chloride 4, magnesium oxide 2, polyvinyl alcohol 0.4, Starso 0.03, sodium aluminate 0.2, tartrate 0.8, organosilicon crylic acid latex 2.3,2-imidazolidone 0.04, silicon carbide 1, accelerant CZ 0.03, Syzygium aromaticum stem oil 1.2, its preparation method is in 50% magnesium chloride solution, to add the magnesium oxide powder inorganic gel agent that stirs to obtain, then other leftover materials are pulverized and mixed, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter, at 2-5mm, is dried and be get final product.
Making method comprises the following steps:
(1) rice-pudding leaf is sent in charring furnace, at 485-605 DEG C, 3-4 hour is processed in charing, takes out, and is ground into powder, makes it seethe spray form triethyl citrate under condition, then add Union carbide A-162 stirring and evenly mixing to the powder of gained in air blast;
(2) get low-grade polymer and put into the hydrochloric acid soln of 8-12% and soak 4-5 hour, filter and take out, use clear water repetitive scrubbing, dry, be added to the water, meanwhile, add light dolomite, haydite, grinding obtains slurry;
(3) polynite, useless porcelain powder are calcined after 3-6 hour and taken out at 600-828 DEG C, pulverize, add organosilicon to be mixed to get slurry, granulation, dry for standby;
(4) step (1), (2), (3) reaction mass and the pulverizing of other leftover materials are added to suitable quantity of water stirring and evenly mixing and obtain slip, the slurry making is added to wall slab squeezing former moulding, cutting, natural curing, to obtain final product.
The technical indicator of processing the light cellular partition board obtaining by above-described embodiment is as follows:
(1) unit weight: 515kg/m
3;
(2) ultimate compression strength: 4.57MPa;
(3) high temperature resistant, flat appearance is smooth;
(4) shock resistance: 0.5 meter of 30kg drop, flawless.
Claims (2)
1. light dolomite/montmorillonite Composite light cellular partition board, it is characterized in that, made by the raw material of following weight part: cement 10-14, haydite 11-15, low-grade polymer 15-18, light dolomite 9-14, dicumyl peroxide 1-2, Union carbide A-162 1.1-2.4, polynite 10-13, organosilicon 5-8, useless porcelain powder 19-23, triethyl citrate 0.9-1.5, rice-pudding leaf 16-18, auxiliary agent 3-6, suitable quantity of water, described auxiliary agent is made up of following raw materials in part by weight: volcanic ash 6-9, Sodium sulfate anhydrous.min(99) 2-5, magnesium chloride 3-5, magnesium oxide 2-4, polyvinyl alcohol 0.2-0.5, Starso 0.03-0.07, sodium aluminate 0.05-0.6, tartrate 0.8-2.1, organosilicon crylic acid latex 2.1-4.3, 2-imidazolidone 0.04-0.09, silicon carbide 1-3, accelerant CZ 0.03-0.05, Syzygium aromaticum stem oil 1.2-3.2, its preparation method is in 50% magnesium chloride solution, to add the magnesium oxide powder inorganic gel agent that stirs to obtain, then other leftover materials are pulverized and mixed, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
2. the making method of a kind of light dolomite/montmorillonite Composite light cellular partition board according to claim 1, is characterized in that comprising the following steps:
(1) rice-pudding leaf is sent in charring furnace, at 485-605 DEG C, 3-4 hour is processed in charing, takes out, and is ground into powder, makes it seethe spray form triethyl citrate under condition, then add Union carbide A-162 stirring and evenly mixing to the powder of gained in air blast;
(2) get low-grade polymer and put into the hydrochloric acid soln of 8-12% and soak 4-5 hour, filter and take out, use clear water repetitive scrubbing, dry, be added to the water, meanwhile, add light dolomite, haydite, grinding obtains slurry;
(3) polynite, useless porcelain powder are calcined after 3-6 hour and taken out at 600-828 DEG C, pulverize, add organosilicon to be mixed to get slurry, granulation, dry for standby;
(4) step (1), (2), (3) reaction mass and the pulverizing of other leftover materials are added to suitable quantity of water stirring and evenly mixing and obtain slip, the slurry making is added to wall slab squeezing former moulding, cutting, natural curing, to obtain final product.