CN103979860B - A kind of waterproof light partition plate and preparation method thereof - Google Patents
A kind of waterproof light partition plate and preparation method thereof Download PDFInfo
- Publication number
- CN103979860B CN103979860B CN201410135232.8A CN201410135232A CN103979860B CN 103979860 B CN103979860 B CN 103979860B CN 201410135232 A CN201410135232 A CN 201410135232A CN 103979860 B CN103979860 B CN 103979860B
- Authority
- CN
- China
- Prior art keywords
- powder
- partition plate
- oil
- suitable quantity
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of waterproof light partition plate, it is characterized in that, be made up of the raw material of following weight part: cement 20-25, metakaolin 17-19, type of wire form steel fiber 11-15, naphthalene water reducer 6-8, UEA-H type swelling agent 3-7, paraffin oil 7-9, Nano-class zinc oxide 9-11, vermiculite 13-17, sepiolite 15-18, oil shale waste 16-19, pomelo peel 12-16, auxiliary agent 3-6, suitable quantity of water; The present invention adds Nano-class zinc oxide, can uvioresistant and sterilization, enzyme inhibitor, and a small amount of pomelo peel particle after high temperature carbonization of admixture, can the obnoxious flavour such as formaldehyde in absorbed air, makes the present invention have long-acting effect purified the air of a room and waterproof effect.
Description
Technical field
The present invention relates to building material field, be specifically related to a kind of waterproof light partition plate and preparation method thereof.
Background technology
Light cellular partition board is made up of various industrial waste residues such as innoxious phosphogypsum, lightweight slag, flyash, through a kind of novel energy-conserving walling material of frequency conversion steam pressurized maintenance, the walling that it is a kind of external form as the cassette ceiling, but there is male and female falcon groove on its both sides, only sheet material need be erected during installation, male and female falcon is coated after a small amount of filleting mortar assembled.It has the advantages such as quality is light, intensity is high, multiple environmental protection, heat insulating, sound insulation, breathing damping, fire prevention, rapid construction, reduction body of wall cost, so enjoy favor in architecture indoor finishing field, but shortcomings such as the light cellular partition board ultimate compression strength used in the market is low, tensile strength is weak, anti-cracking performance and hanging ability is not good, production cost is high, sound-insulating weak effect.
Summary of the invention
Object of the present invention is just to provide a kind of waterproof light partition plate and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
A kind of waterproof light partition plate, it is characterized in that, be made up of the raw material of following weight part: cement 20-25, metakaolin 17-19, type of wire form steel fiber 11-15, naphthalene water reducer 6-8, UEA-H type swelling agent 3-7, paraffin oil 7-9, Nano-class zinc oxide 9-11, vermiculite 13-17, sepiolite 15-18, oil shale waste 16-19, pomelo peel 12-16, auxiliary agent 3-6, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: mica powder 5-8, titanium dioxide 3-5, lithium silicate 0.1-0.2, magnesium chloride 2-4, magnesium oxide 1-3, sodium tetraborate 0.02-0.05, Sodium hexametaphosphate 99 0.04-0.08, redispersable latex powder 0.2-0.4, molasses 0.6-2.7, SHP-50 polysiloxane powder hydrophober 1.2-2.4, Oenothera oil 0.02-0.5, dimethyl silicone oil 2.1-3.6, its preparation method to stir adding magnesium oxide powder in 3:2 ratio in 50% magnesium chloride solution to obtain inorganic gel agent, then other leftover materials are pulverized mixing, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
The preparation method of described a kind of waterproof light partition plate, is characterized in that comprising the following steps:
(1) pomelo peel, metakaolin are sent in charring furnace, calcination processing 3-4 hour at 510-615 DEG C, take out, be ground into powder, the powder to gained makes it seethe spray form paraffin oil under condition in air blast, makes it mixing;
(2) vermiculite, sepiolite, oil shale waste are calcined at 610-860 DEG C after 3-6 hour and take out, pulverize, spray 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions to evenly with spraying gun, dipping 10-12 hour;
(3) step (1), (2) reaction mass and other leftover materials are pulverized add suitable quantity of water stirring and evenly mixing and obtain slip, obtained slurry is added wall slab squeezing former is shaping, cutting, natural curing, to obtain final product.
The present invention has following beneficial effect: the present invention adds Nano-class zinc oxide, can uvioresistant and sterilization, enzyme inhibitor, and a small amount of pomelo peel particle after high temperature carbonization of admixture, can the obnoxious flavour such as formaldehyde in absorbed air, make the present invention have long-acting effect purified the air of a room and waterproof effect.
Embodiment
Described a kind of waterproof light partition plate, it is characterized in that, be made up of the raw material of following weight part: cement 20-25, metakaolin 17-19, type of wire form steel fiber 11-15, naphthalene water reducer 6-8, UEA-H type swelling agent 3-7, paraffin oil 7-9, Nano-class zinc oxide 9-11, vermiculite 13-17, sepiolite 15-18, oil shale waste 16-19, pomelo peel 12-16, auxiliary agent 3-6, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: mica powder 5-8, titanium dioxide 3-5, lithium silicate 0.1-0.2, magnesium chloride 2-4, magnesium oxide 1-3, sodium tetraborate 0.02-0.05, Sodium hexametaphosphate 99 0.04-0.08, redispersable latex powder 0.2-0.4, molasses 0.6-2.7, SHP-50 polysiloxane powder hydrophober 1.2-2.4, Oenothera oil 0.02-0.5, dimethyl silicone oil 2.1-3.6, its preparation method to stir adding magnesium oxide powder in 3:2 ratio in 50% magnesium chloride solution to obtain inorganic gel agent, then other leftover materials are pulverized mixing, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
Making method comprises the following steps:
(1) pomelo peel, metakaolin are sent in charring furnace, calcination processing 3-4 hour at 510-615 DEG C, take out, be ground into powder, the powder to gained makes it seethe spray form paraffin oil under condition in air blast, makes it mixing;
(2) vermiculite, sepiolite, oil shale waste are calcined at 610-860 DEG C after 3-6 hour and take out, pulverize, spray 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions to evenly with spraying gun, dipping 10-12 hour;
(3) step (1), (2) reaction mass and other leftover materials are pulverized add suitable quantity of water stirring and evenly mixing and obtain slip, obtained slurry is added wall slab squeezing former is shaping, cutting, natural curing, to obtain final product.
The technical indicator of being processed the light cellular partition board obtained by above-described embodiment is as follows:
(1) thermal conductivity (medial temperature 25 ± 2 DEG C): 0.075W/ (mk);
(2) ultimate compression strength: 4.7MPa;
(3) high temperature resistant, flat appearance is smooth.
Claims (2)
1. a waterproof light partition plate, it is characterized in that, be made up of the raw material of following weight part: cement 20-25, metakaolin 17-19, type of wire form steel fiber 11-15, naphthalene water reducer 6-8, UEA-H type swelling agent 3-7, paraffin oil 7-9, Nano-class zinc oxide 9-11, vermiculite 13-17, sepiolite 15-18, oil shale waste 16-19, pomelo peel 12-16, auxiliary agent 3-6, suitable quantity of water, described auxiliary agent is made up of following raw materials in part by weight: mica powder 5-8, titanium dioxide 3-5, lithium silicate 0.1-0.2, magnesium chloride 2-4, magnesium oxide 1-3, sodium tetraborate 0.02-0.05, Sodium hexametaphosphate 99 0.04-0.08, redispersable latex powder 0.2-0.4, molasses 0.6-2.7, SHP-50 polysiloxane powder hydrophober 1.2-2.4, Oenothera oil 0.02-0.5, dimethyl silicone oil 2.1-3.6, its preparation method to stir adding magnesium oxide powder in 3:2 ratio in 50% magnesium chloride solution to obtain inorganic gel agent, then other leftover materials are pulverized mixing, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
2. the making method of a kind of waterproof light partition plate according to claim 1, is characterized in that comprising the following steps:
(1) pomelo peel, metakaolin are sent in charring furnace, calcination processing 3-4 hour at 510-615 DEG C, take out, be ground into powder, the powder to gained makes it seethe spray form paraffin oil under condition in air blast, makes it mixing;
(2) vermiculite, sepiolite, oil shale waste are calcined at 610-860 DEG C after 3-6 hour and take out, pulverize, spray 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions to evenly with spraying gun, dipping 10-12 hour;
(3) step (1), (2) reaction mass and other leftover materials are pulverized add suitable quantity of water stirring and evenly mixing and obtain slip, obtained slurry is added wall slab squeezing former is shaping, cutting, natural curing, to obtain final product.