CN102477240A - Floor protective paint - Google Patents
Floor protective paint Download PDFInfo
- Publication number
- CN102477240A CN102477240A CN2010105576315A CN201010557631A CN102477240A CN 102477240 A CN102477240 A CN 102477240A CN 2010105576315 A CN2010105576315 A CN 2010105576315A CN 201010557631 A CN201010557631 A CN 201010557631A CN 102477240 A CN102477240 A CN 102477240A
- Authority
- CN
- China
- Prior art keywords
- parts
- protective paint
- emulsion
- ground
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a material for building decoration, in particular to a ground protection paint. The formula of the floor protective paint is as follows: 10-20 parts of water, 20-40 parts of emulsion, 5-20 parts of titanium dioxide, 3-5 parts of heavy metal powder, 10-15 parts of calcium carbonate, 3-5 parts of kaolin, 3-5 parts of mica powder, 0.5-1 part of wetting dispersant, 0.2-0.4 part of defoaming agent, 0.4-0.6 part of flatting agent, 2.5-3.8 parts of thickening agent, 0.2 part of multifunctional auxiliary agent, 0.8-1.6 parts of film-forming auxiliary agent and 1-4 parts of sterilization mildew inhibitor. The invention is prepared by selecting high-quality natural mineral powder and various assistants and adopting an advanced production process. The product has the characteristics of environmental protection, no toxicity, alkali resistance, mould prevention, bottom fixation and bottom sealing, crack resistance, energy conservation, flame retardance, sound insulation, moisture prevention, leakage stoppage, strong adhesive force, high hardness, dry friction resistance and the like, and various colors can be adjusted by adding color paste.
Description
Technical field:
The present invention relates to a kind of construction and decoration and use material, particularly a kind of ground protective paint.
Background technology:
The ground protective paint has been necessary part in finishing in finishing, can be so that dust minimizing in when finishing room improves construction effect greatly.It is single that but existing ground protective paint usually can have a little toxicity and color, more fatal is to use that the cohesive force of floor tile and cement can reduce after the protective paint.
Summary of the invention:
A kind of ground protective paint that the present invention invents in order to solve the problems of the technologies described above just.The present invention passes through, and technique means realizes: described ground protective paint prescription is following: 10～20 parts in water, 20～40 parts of emulsions, 5～20 parts of white titanium pigments, 3～5 parts of stone flours of a huge sum of money, 10～15 parts in lime carbonate, 3～5 parts of kaolin, 3～5 parts of mica powders, 0.5～1 part of wetting dispersing agent, 0.2～0.4 part of skimmer, 0.4～0.6 part of flow agent, 2.5～3.8 parts of thickening materials, 0.2 part of multifunctional assistant, 0.8～1.6 part of film coalescence aid, 1～4 part of biocide mildewcide.
Described water is deionized water.Described emulsion is mixed by arbitrary proportion by at least a among organosilicon crylic acid latex, pure-acrylic emulsion, the benzene emulsion.Described ground protective paint can also be deployed into required color through adding the different colours mill base.
Above-mentioned ground protective paint production craft step is: a, Jiang Shui place container interior under the stirring of 300 rev/mins of high speed dispersors, evenly drop into thickening material in the water with the mode of spreading throwing; B, then throw successively like wetting dispersing agent, skimmer, multifunctional assistant, film coalescence aid, biocide mildewcide; C, stir and to add white titanium pigment, huge sum of money stone flour, lime carbonate, kaolin and mica powder after 5 minutes and to regulate dispersion machine to 1600 rev/min, high speed dispersion added emulsion after 30～50 minutes; Regulate dispersion machine to 400～500 rev/min, add thickening material, liquid is transferred to viscosity 90～110KU, promptly get.
The present invention selects the fine XPA for use, and natural mineral powder and multiple auxiliary agent adopt advanced production technique to make with extra care and form.At the bottom of this product has environment-protecting asepsis, alkali resistant, mildew-resistant, a solid underseal, characteristics such as cracking resistance, energy-conservation, fire-retardant, sound insulation, protection against the tide, leak stopping, strong adhesion, hardness height, anti-metal to-metal contact, the adding mill base can access shades of colour.
Embodiment:
A kind of ground protective paint is by 2 parts of 15 parts of deionized waters, 35 parts of emulsions, 15 parts of white titanium pigments, 4 parts of stone flours of a huge sum of money, 13 parts in lime carbonate, 5 parts of kaolin, 3 parts of mica powders, 0.9 part of wetting dispersing agent, 0.3 part of skimmer, 0.5 part of flow agent, 3.6 parts of thickening materials, 0.2 part of multifunctional assistant, 1.5 parts of film coalescence aid and biocide mildewcides.
Wherein emulsion can adopt organosilicon crylic acid latex, pure-acrylic emulsion, benzene emulsion any one.
The ground protective paint can also add mill base according to different construction color needs, is deployed into required color.
Ground protective paint production craft step is: a, deionized water is placed in the container under the stirring of 300 rev/mins of high speed dispersors, evenly drop into thickening material in the deionized water with the mode of spreading throwing; B, then throw successively like wetting dispersing agent, skimmer, multifunctional assistant, film coalescence aid, biocide mildewcide; C, stir and to add white titanium pigment, huge sum of money stone flour, lime carbonate, kaolin and mica powder after 5 minutes and to regulate dispersion machine to 1600 rev/min, high speed dispersion added emulsion after 30～50 minutes; Regulate dispersion machine to 400～500 rev/min, add thickening material, liquid is transferred to viscosity 90～110KU, promptly get.
The detailed introduction that above specification sheets just carries out the present invention for field personnel of the present invention better understand core of the present invention, this paper also should not be construed limitation of the present invention.All similar or close equal replacements also are interpreted as falling in protection scope of the present invention.
Claims (6)
1. a ground protective paint is characterized in that described protective paint prescription is following: 10～20 parts in water, 20～40 parts of emulsions, 5～20 parts of white titanium pigments, 3～5 parts of stone flours of a huge sum of money, 10～15 parts in lime carbonate, 3～5 parts of kaolin, 3～5 parts of mica powders, 0.5～1 part of wetting dispersing agent, 0.2～0.4 part of skimmer, 0.4～0.6 part of flow agent, 2.5～3.8 parts of thickening materials, 0.2 part of multifunctional assistant, 0.8～1.6 part of film coalescence aid, 1～4 part of biocide mildewcide.
2. ground according to claim 1 protective paint is characterized in that described protective paint prescription is following: 15 parts in water, 35 parts of emulsions, 15 parts of white titanium pigments, 4 parts of stone flours of a huge sum of money, 13 parts in lime carbonate, 5 parts of kaolin, 3 parts of mica powders, 0.9 part of wetting dispersing agent, 0.3 part of skimmer, 0.5 part of flow agent, 3.6 parts of thickening materials, 0.2 part of multifunctional assistant, 1.5 parts of film coalescence aid, 2 parts of biocide mildewcides.
3. ground according to claim 1 protective paint is characterized in that described water is deionized water.
4. ground according to claim 1 protective paint is characterized in that described emulsion is mixed by arbitrary proportion by at least a among organosilicon crylic acid latex, pure-acrylic emulsion, the benzene emulsion.
5. ground according to claim 1 protective paint is characterized in that described ground protective paint can also be deployed into required color through adding the different colours mill base.
6. the production technique of a ground as claimed in claim 1 protective paint is characterized in that said production craft step is: a, Jiang Shui place in the container under the stirring of 300 rev/mins of high speed dispersors, evenly drop into thickening material in the water with the mode of spreading throwing; B, then throw successively like wetting dispersing agent, skimmer, multifunctional assistant, film coalescence aid, biocide mildewcide; C, stir and to add white titanium pigment, huge sum of money stone flour, lime carbonate, kaolin and mica powder after 5 minutes and to regulate dispersion machine to 1600 rev/min, high speed dispersion added emulsion after 30～50 minutes; Regulate dispersion machine to 400～500 rev/min, add thickening material, liquid is transferred to viscosity 90～110KU, promptly get.