WO2016052046A1 - 太陽電池およびその製造方法、ならびに太陽電池モジュールおよびその製造方法 - Google Patents

太陽電池およびその製造方法、ならびに太陽電池モジュールおよびその製造方法 Download PDF

Info

Publication number
WO2016052046A1
WO2016052046A1 PCT/JP2015/074656 JP2015074656W WO2016052046A1 WO 2016052046 A1 WO2016052046 A1 WO 2016052046A1 JP 2015074656 W JP2015074656 W JP 2015074656W WO 2016052046 A1 WO2016052046 A1 WO 2016052046A1
Authority
WO
WIPO (PCT)
Prior art keywords
electrode layer
solar cell
main surface
silicon substrate
substrate
Prior art date
Application number
PCT/JP2015/074656
Other languages
English (en)
French (fr)
Inventor
邦裕 中野
訓太 吉河
足立　大輔
Original Assignee
株式会社カネカ
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社カネカ filed Critical 株式会社カネカ
Priority to JP2016551660A priority Critical patent/JP6650407B2/ja
Publication of WO2016052046A1 publication Critical patent/WO2016052046A1/ja
Priority to US15/473,000 priority patent/US20170200839A1/en

Abstract

　太陽電池（１０１）は、結晶シリコン基板（１）を含む光電変換部（４０）の上に電極層（６１）を備える。電極層（６１）が製膜される際に、開口（２２０）を有するマスク板の開口縁部に、基板（１１０）が接するように載置された状態で、デポアップ方式で製膜が行われる。マスク板の開口縁部は、基板（１１０）の第一の主面側と接する部位に、基板（１１０）の周端における撓み角に沿うテーパ面（２１５）を有する。マスク遮蔽領域への回り込みによる電極層の製膜を抑制し、有効面積の大きい太陽電池を作製できる。

Description

太陽電池およびその製造方法、ならびに太陽電池モジュールおよびその製造方法
　本発明は、太陽電池およびその製造方法に関する。さらに、本発明は太陽電池モジュールおよびその製造方法に関する。
　太陽電池では、半導体接合等を有する光電変換部への光照射により発生したキャリア（電子および正孔）を外部回路に取り出すことにより、発電がおこなわれる。単結晶シリコン基板の両面に、導電型シリコン系薄膜を備える結晶シリコン太陽電池は、ヘテロ接合太陽電池と呼ばれている。中でも、結晶シリコン基板上の一方の面にｎ型シリコン系薄膜を備え、他方の面にｐ型シリコン系薄膜を備え、結晶シリコン基板と導電型（ｎ型またはｐ型）シリコン系薄膜との間に真性シリコン薄膜を有するヘテロ接合太陽電池は、変換効率の高い結晶シリコン太陽電池の一形態として知られている。
　ヘテロ接合太陽電池は、単結晶シリコン基板の両面に導電型シリコン系薄膜を備える光電変換部上に透明電極層を有する。透明電極層は、光電変換部での光生成キャリアを金属集電極へ輸送する働きを有する。透明電極層は、ＣＶＤ法や、スパッタ法、イオンプレーティング法等のＰＶＤ法により形成される。この際、透明電極層は、基板表面のみならず、側面や裏面にも回り込んで形成されるため、表裏の透明電極層が接触し、表面と裏面との間の電気的な短絡を生じる。
　表面と裏面の透明電極層間の短絡を防止するために、特許文献１や特許文献２に開示されているように、結晶シリコン基板の周端をマスクで覆いながら透明電極層を形成する方法が知られている。
特開２００１－４４４６１号公報 ＷＯ２０１３／１６１１２７号国際公開パンフレット
　ヘテロ接合太陽電池のように、シリコン基板上に電極層を備える太陽電池の製造において、基板の端部や側面への電極層の着膜を防止するためにマスクを用いて製膜を行う場合、基板とマスクとが十分に密着していないと、基板とマスクとの間の空隙から蒸着粒子が回りこみ、マスク遮蔽領域に着膜が生じる。マスク遮蔽領域の空隙部分に回り込んで電極層が着膜した領域では、他の領域（マスクにより遮蔽されておらず、膜厚が一定の領域）に比して、電極層の被覆率や膜厚が小さくなる傾向がある（以下、他の領域に比して、膜厚および被覆率の少なくともいずれか一方が小さい領域を「遷移領域」と称する場合がある）。
　遷移領域では、電極層の抵抗や、界面での多重干渉による反射率が高いため、遷移領域の幅が大きくなると、太陽電池性能が低下する傾向がある。また、遷移領域が基板の周端や側面に達すると、裏面側の電極層との短絡が生じやすくなる。したがって、遷移領域の幅はできる限り小さいことが好ましい。
　ヘテロ接合太陽電池等の結晶シリコン太陽電池では、光電変換部への光取り込み効率を高めるために、表面テクスチャを有する結晶シリコン基板が用いられる。そのため、テクスチャの凹部とマスクとの間に、不可避的に空隙が生じ、基板とマスクとを完全に密着させることは困難である。そのため、基板表面がテクスチャを有している場合でも、電極層の遷移領域をできる限り小さくして、表裏の短絡を防止しつつ、太陽電池の有効発電面積を大きくすることが求められている。
　本発明では、開口縁部にテーパ面を有するマスク板上に基板を載置し、鉛直下方側から上方に向けて製膜を行うデポアップ（フェースダウン）方式で電極層の製膜が行われる。
　本発明は、結晶シリコン基板を含む光電変換部の第一の主面上に第一電極層を備える太陽電池の製造方法に関する。結晶シリコン基板の第一の主面側に第一電極層が製膜される工程（第一電極層形成工程）は、開口を有するマスク板の開口縁部に、結晶シリコン基板の第一の主面側が接するように載置された状態で、デポアップ方式により製膜が行われる。第一の主面の周縁がマスクに接触した状態で製膜が行われるため、光電変換部の第一の主面の周端には、透明電極層が形成されない。そのため、表裏の電極間が絶縁される。
　マスク板の開口縁部は、基板と接する部位に、テーパ面を有する。テーパ面が、基板の周端における撓み角θに沿うように設定されることにより、マスク板と基板との接点が増加し、マスクによる遮蔽領域における空隙が減少する。その結果、マスクによる遮蔽領域内で、蒸着粒子の回りこみが生じる領域が減少し、電極層遷移領域の幅が小さくなる。遷移領域の幅は、１．５ｍｍ未満が好ましい。
　マスク板の載置平面とテーパ面とのなす角αは、シリコン基板の周端における撓み角θの０．５倍～２倍の範囲であることが好ましい。シリコン基板の周端における撓み角θは、例えば０．１°～１０°の範囲内である。マスク板上に載置された基板が自重により撓んでいる場合、製膜面である第一の主面側（下方）が凸となるように撓みが生じる。
　本発明の太陽電池の一形態において、光電変換部は、表面テクスチャを有する単結晶シリコン基板の両面に導電型シリコン系薄膜を備える。受光面側の第一電極層は透明電極層であり、光電変換部の裏面側には第二電極層が形成される。この形態では、第一電極層が光電変換部の第一の主面の周端に形成されていないことにより、第一電極層と第二電極層とが絶縁されている。第二電極層は、光電変換部の第二の主面側の周端および側面にも形成されていてもよい。また、第二電極層は、第一の主面側の周端にも形成されていてもよい。この場合、第一の主面側において、第一電極層と第二電極層との最短距離（絶縁領域の幅）は、０より大きく、１．５ｍｍ未満が好ましい。
　受光面側の電極層上にはパターン状の集電極が形成される。パターン集電極は、例えばめっき法により形成できる。第一電極層上にパターン状の金属シードを形成後、第一電極層上の全面に絶縁層を形成し、金属シード上の絶縁層に穿孔を設けることにより、穿孔を介して金属シードと導通する金属電極を、めっき法により形成することができる。
　上記の太陽電池を、封止材により封止することにより、太陽電池モジュールが形成される。
　本発明の方法では、マスク板の開口縁部のテーパ面に基板を載置した状態で、デポアップ方式により電極層が形成されるため、マスク遮蔽領域における基板とマスク板との間の空隙が減少する。そのため、基板に撓みが生じている場合でも、電極層遷移領域の幅を小さくでき、太陽電池の有効面積を拡大できる。また、マスク板にテーパ面が存在するため、マスク板の位置合わせが容易となり、生産性が高められるとともに、基板のハンドリング性が良好となるため、基板の厚みが小さい場合でも、割れや欠け等の不具合を抑制できる。
本発明の太陽電池の一形態を示す模式的断面図である。 電極層の製膜に用いられるマスク板の一形態を表す概略斜視図である。 マスク板上に基板が載置された状態の一例を表す模式的断面図である。 マスク板上に基板が載置された状態の比較例を表す模式的断面図である。 Ａ～Ｆは、それぞれマスク板の開口縁部の形状を示す模式的断面図である。
　図１は、本発明の一実施形態に係るヘテロ接合太陽電池の模式的断面図である。ヘテロ接合太陽電池１０１は、光電変換部４０上の一方の面に第一電極層６１を備え、他方の面に第二電極層６２を備える。ヘテロ接合太陽電池１０１では、第一電極層６１および第二電極層６２はいずれも透明電極層である。第一電極層６１は、光電変換部４０の第一の主面の周端には形成されておらず、第一の主面の周縁には電極層非形成領域６１５が存在する。本発明においては、基板の周縁がマスクにより遮蔽された状態で第一電極層の製膜が行われることにより、電極層非形成領域が形成される。なお、本明細書において、「周端」とは、主面の端縁を指す。「周縁」とは、周端および周端から所定距離（例えば、数十μｍ～数ｍｍ程度）の領域を指す。
［光電変換部］
　ヘテロ接合太陽電池１０１の光電変換部４０は、単結晶シリコン基板１の第一の主面および第二の主面のそれぞれに、第一導電型シリコン系薄膜３１および第二導電型シリコン系薄膜３２を備える。これらの導電型シリコン系薄膜は、いずれか一方がｐ型であり、他方がｎ型である。
　単結晶シリコン基板１の導電型は、ｎ型でもｐ型でもよい。正孔と電子とを比較した場合、電子の方が移動度が大きいため、シリコン基板１がｎ型単結晶シリコン基板である場合は、特に変換特性が高い。シリコン基板１は、少なくとも受光面側、好ましくは両面にテクスチャを有する。テクスチャは、例えば、異方性エッチング技術を用いて形成される。異方性エッチングにより形成されたテクスチャは、四角錘状の凹凸構造を有する。
　テクスチャの高低差は、０．５μｍ～４０μｍ程度であり、好ましくは１μｍ～２０μｍである。テクスチャの高低差が上記範囲内であれば、光散乱により、単結晶シリコンが吸収可能な３００～１２００ｎｍの波長領域の光の光路長が増大されることに加えて、凹凸構造により光が有効に散乱され、界面反射の低減効果が効率的に得られる。テクスチャの高低差は、１０μｍ以下がさらに好ましく、５μｍ以下が特に好ましい。テクスチャの高低差を小さくすることにより、マスク製膜の際の空隙からの蒸着粒子の回り込みを低減できる。
　シリコン基板１の厚みは特に限定されないが、好ましくは１０μｍ～１５０μｍ、より好ましくは３０μｍ～１２０μｍである。シリコン基板の厚みを１５０μｍ以下とすることで、シリコンの使用量が減少するため、低コスト化を図ることができる。また、シリコン基板の厚みが小さいほど、シリコン基板内での光生成キャリアの再結合が低減するため、太陽電池の開放端電圧（Ｖｏｃ）が向上する傾向がある。シリコン基板の厚みは、表面側のテクスチャの凸部側頂点と裏面側の凸部頂点との距離で定義される。
　光電変換部４０は、単結晶シリコン基板１と導電型シリコン系薄膜３１，３２との間に、真性シリコン系薄膜２１，２２を有することが好ましい。単結晶シリコン基板の表面に真性シリコン系薄膜が設けられることにより、単結晶シリコン基板への不純物の拡散を抑えつつ表面パッシベーションを有効に行うことができる。単結晶シリコン基板１の表面パッシベーションを有効に行うために、真性シリコン系薄膜２１，２２は、真性非晶質シリコン薄膜が好ましい。
　上記真性シリコン系薄膜２１，２２の製膜方法としては、プラズマＣＶＤ法が好ましい。プラズマＣＶＤ法によるシリコン系薄膜の製膜条件としては、基板温度１００～３００℃、圧力２０～２６００Ｐａ、高周波パワー密度０．００４～０．８Ｗ／ｃｍ２が好ましく用いられる。シリコン系薄膜の形成に使用される原料ガスとしては、ＳｉＨ４、Ｓｉ２Ｈ６等のシリコン含有ガスとＨ２との混合ガスが好ましく用いられる。
　ｐ型またはｎ型の導電型シリコン系薄膜３１，３２としては、非晶質シリコン、微結晶シリコン（非晶質シリコンと結晶質シリコンを含む材料）や、非晶質シリコン合金、微結晶シリコン合金等が用いられる。シリコン合金としては、シリコンオキサイド、シリコンカーバイド、シリコンナイトライド、シリコンゲルマニウム等が挙げられる。これらの中でも、導電型シリコン系薄膜は、非晶質シリコン薄膜であることが好ましい。
　導電型シリコン系薄膜３１，３２も、真性シリコン系薄膜と同様に、プラズマＣＶＤにより製膜されることが好ましい。導電型シリコン系薄膜の製膜時には、導電型（ｎ型またはｐ型）を調整するためのドーパントガスとして、ＰＨ３やＢ２Ｈ６等が用いられる。導電型決定不純物の添加量は微量でよいため、予めＳｉＨ４やＨ２で希釈されたドーパントガスを用いることが好ましい。導電型シリコン系薄膜の製膜時に、ＣＯ２、ＣＨ４、ＮＨ３、ＧｅＨ４等の異種元素を含むガスを添加すれすることにより、シリコン系薄膜を合金化して、エネルギーギャップを変更することもできる。
［電極層］
　光電変換部４０の導電型シリコン系薄膜３１，３２上には、導電性酸化物を主成分とする透明電極層６１，６２が形成される。導電性酸化物としては、例えば、酸化亜鉛や酸化インジウム、酸化錫等を単独で、あるいは複合酸化物として用いることができる。導電性、光学特性、および長期信頼性の観点から、インジウム系酸化物が好ましく、中でも酸化インジウム錫（ＩＴＯ）を主成分とするものがより好ましく用いられる。透明電極層６１，６２の膜厚は、透明性、導電性、および光反射低減の観点から、１０ｎｍ以上１４０ｎｍ以下であることが好ましい。
　これらの電極層は、ドライプロセス（ＣＶＤ法や、スパッタ法、イオンプレーティング法等のＰＶＤ法）により製膜される。インジウム系酸化物を主成分とする電極層の製膜にはスパッタ法やイオンプレーティング法等のＰＶＤ法が好ましい。マスクを使用せずに、ドライプロセスにより両面の電極層の製膜が行われた場合、表裏の電極層は、製膜時の回り込みによって、光電変換部の側面および他面の周端にも形成される。そのため、表裏の電極層同士が短絡した状態となり、太陽電池の特性が低下する。
（第一電極層の形成方法）
　本発明では、第一電極層６１の製膜時に、基板の周縁がマスクと接触した状態で製膜が行われることにより、第一の主面の周縁は電極層非形成領域６１５となる。そのため、第二電極層６２が側面および反対面の周端に回り込んで製膜されている場合でも、光電変換部４０の第一の主面上に、第一電極層および第二電極層のいずれも形成されていない絶縁領域４０１が存在する。絶縁領域４０１が存在することにより、電極層製膜時の回り込みによる短絡の問題を解決できる。
　本発明の製造方法では、第一の主面側、すなわち第一導電型シリコン系薄膜３１形成面側が下面となるように、マスク板上に基板を載置した状態で、デポアップ方式により第一電極層６１の製膜が行われる。第一電極層形成工程に供される基板は、シリコン基板の第一の主面上に第一導電型シリコン系薄膜３１が形成されていれば、第二の主面側の構成は特に限定されない。基板の第二の主面側には、シリコン系薄膜２２，３２が形成されていてもよく、シリコン系薄膜が形成されていなくてもよい。また、基板の第二の主面側には、シリコン系薄膜上に第二電極層６２が形成されていてもよい。
　デポアップ方式（フェースダウン方式）は、基板の製膜面が鉛直下方となるように基板を配置し、基板下方の蒸着源から上方に飛来する蒸着粒子を基板に着膜させる製膜方式である。デポアップ方式では、製膜の際に製膜室内に堆積するパーティクル等の落下による不良を回避できる。また、開口を有するマスク板上に基板を載置して製膜を行う場合、基板の自重により、基板とマスク板との密着性が高められるため、蒸着粒子の隙間からの回り込みによる着膜が低減される傾向がある。
　図２は、第一電極層の製膜に用いられるマスク板の一形態の概略斜視図である。マスク板２００は、載置平面２１０と、開口壁面２１３に囲まれた開口２２０を有する。開口の形状は基板の形状にあわせたものであり、開口の大きさは基板の大きさよりも小さい。図２では、矩形の開口２２０が図示されているが、基板が多角形状である場合は、開口も多角形状であることが好ましい。
　載置平面２１０と開口２２０との境界部である開口縁部は、載置平面２１０と所定角度αをなすテーパ面２１５となっている。この開口縁部のテーパ面に、第一導電型シリコン系薄膜が接するように基板を載置した状態でドライプロセスにより製膜を行えば、開口２２０の下部からの蒸着粒子が基板中央部に着膜し、第一導電層が形成される。
　図３は、マスク板上に、基板１１０が載置された状態の一例を表す模式的断面図である。基板１１０は、自重によって、製膜面（第一の主面）側が凸となるように撓んでおり、基板の周端における撓み角はθである。マスク板は、下面から上面（載置平面）側に向かって開口２２０が拡径するように、テーパ面２１５が形成されている。テーパ面のテーパ角αは、基板の撓み角θに沿うように設定される。自重による撓み角は、厚み１００μｍの６インチサイズの基板で１°程度であり、厚みが小さくなると、撓み角は急激に大きくなる。また、基板の厚みが同等でも、基板サイズが大きくなると撓み角は大きくなる。
　図４は、開口縁部にテーパ面を有していないマスク板上に、基板が載置された状態の比較例を表す模式的断面図である。自重により撓みを生じた基板１１０は、マスク板の載置平面２１８と開口壁面２１９とのコーナー部２３９で接しており、基板の周縁と載置平面２１８との間には空隙２３７が生じている。開口２２９の下部から飛来する蒸着粒子は、マスク板のコーナー部２３９と基板１１０との隙間から、基板の周縁の空隙２３７へと回りこみ、マスク板で遮蔽された基板の周縁にも透明電極層の着膜が生じる。基板１１０の表面にテクスチャが形成されている場合は、基板とマスク板のコーナー部との間にも多数の隙間が存在し、基板とマスク板とは、テクスチャの凸部の頂点でわずかに接しているのみであるため、基板の周縁と載置平面２１８との間の空隙２３７への回り込みによる着膜量が増大する。
　マスク板の開口２２０上の基板１１０に製膜される透明電極層の膜厚はほぼ一定である。基板中央部（マスク板の開口上）で、透明電極層の膜厚が均一に形成される領域を、以下では「主形成領域」と称する。一方、基板周縁のマスク板による遮蔽領域では、基板とマスク板との隙間からの回り込みに起因して透明電極層が形成された遷移領域が存在する。この遷移領域では、主形成領域側から周端方向に向けて、透明電極層の被覆率または膜厚の少なくともいずれか一方が小さくなっている。
　マスク製膜によって、基板の周縁に電極層非形成領域を形成するためには、遷移領域の幅を考慮して、マスクによる遮蔽領域の幅（マスク板の開口の大きさ）を設定する必要がある。図４に示すように、基板とマスク板との間の空隙が大きいと、遷移領域の幅が大きくなるため、マスクにより遮蔽される領域の幅を大きくして、マスクの開口面積を小さくする必要がある。その結果、電極層主形成領域の面積が小さくなり、太陽電池の有効発電面積減少により発電効率が低下する傾向がある。
　これに対して、図３に示すように、マスク板の開口縁部に基板の撓み角に沿うテーパ面２１５が存在し、このテーパ部分に基板の周縁が載置される場合は、基板１１０の周縁２３１の形状がマスク板の形状に沿っているため、空隙が小さくなる。そのため、マスク板による遮蔽領域において、基板とマスク板との隙間からの回り込みによる着膜が生じる範囲、すなわち遷移領域を小さくできる。このように、本発明では、マスク板が、開口縁部において、製膜面と接する部位に、シリコン基板の周端における撓み角に沿うテーパ面を有することにより、基板周縁への蒸着粒子の回り込みが低減され、遷移領域の幅を小さくできる（例えば、１．５ｍｍ未満）。そのため、太陽電池の有効発電面積を増大し、変換効率を高めることができる。
　本発明の方法では、マスク板の開口縁部に、基板の撓み角に沿うテーパ面が存在するため、マスク板上に基板を載置する際の位置合わせが容易となり、生産性を高めることができる。電極層の遷移領域の幅が小さくなり、かつ位置合わせが容易であることから、基板周端への電極の着膜が抑制され、表裏の短絡等の不具合の抑制にも寄与する。さらに、マスク板と基板とがテーパ面で接するため、基板の載置時や取出し時の基板の傷つきを抑制できる。特にシリコン基板の厚みが小さい場合は、マスク板に載置する際に、基板の周縁の欠けや、周端からのクラックが生じ易くなる傾向があるが、マスク板の開口縁部がテーパ面を有していることにより、欠けやクラック等を抑制できる。また、マスク板のテーパ面上に基板が載置されており、マスク板と基板との接点が多く、基板の周縁における局所的な応力が小さい状態で電極層が製膜される。そのため、電極層界面での歪みが小さく、界面接合が良好となり、太陽電池の開放端電圧（Ｖｏｃ）が上昇する傾向がある。
　一般にマスク板は金属製であり熱伝導性が高いため、電極層の製膜中は、マスク板の開口付近に比して、開口縁部付近の雰囲気温度が高くなる傾向がある。本発明の方法では、基板の周縁と基板との間の空隙が少ないため、電極層製膜時には、基板の中央部よりも周縁における温度が高くなる傾向がある。基板温度が高くなると、導電性酸化物は結晶化されやすいため、マスク板に近接して透明電極層が製膜される遷移領域は、電極層主形成領域に比して結晶化度が高くなると推定される。そのため、太陽電池の基板周縁からの水分の侵入等が抑制され、太陽電池の耐久性向上が期待できる。なお、結晶化度の大小は、２５℃の１０％塩酸へ所定時間浸漬後に、表面形状を走査型電気顕微鏡（ＳＥＭ：Ｓｃａｎｎｉｎｇ　Ｅｌｅｃｔｒｏｎ　Ｍｉｃｒｏｓｃｏｐｅ）を用いて倍率５０，０００倍で観察し、表面状態の変化の差を観察することにより判断できる。結晶化度が大きいほど、表面形状に差がでるまでの浸漬時間が長い。
　マスク板は、開口縁部の少なくとも一部にテーパ面が形成されていれば、開口縁部の形状は図２や図３に図示される形態に限定されない。例えば、図５Ａに示すように、開口壁面が存在せず、開口縁部全体がテーパ面２１５からなる形状でもよい。また、図５Ｂに示すように、テーパ面２１５の外周に、載置平面２１０と垂直あるいは所定角度をなす壁面２１６が形成されていてもよい。図５Ｃに示すように、テーパ面２１５と壁面２１６との間に、水平面２１２が形成されていてもよい。特に、図５Ｂや５Ｃに示すように、マスク板が、テーパ面２１５の外周に壁面２１６を有する場合は、マスク板上へ基板を載置する際の位置合わせが容易となる。
　図５Ｄ～Ｆに示すように、基板１４０が上面を凸として撓んでいる場合、マスク板の開口縁部のテーパ面２４５もこれに沿うように形成される。例えば、基板の第二の主面側に先に電極層の製膜が行われた場合は、電極層の界面の応力に起因して、第二の主面側を凸として撓んでいる状態で第一の主面側に電極層が形成される場合がある。このように、マスク板の開口縁部のテーパ面が、上に凸の基板の撓み角に沿うように形成されている場合においても、図５Ｅや５Ｆに示すように、テーパ面２４５の外周には、壁面２４６や水平面２４２が形成されていてもよい。
　テーパ面のテーパ角、すなわち載置平面２１０，２４０とテーパ面２１５，２４５とのなす角αは、基板の周端における撓み角θに近いことが好ましい。具体的には、テーパ角αは、撓み角θの０．５倍～２倍が好ましく、０．７倍～１．５倍がより好ましい。撓み角θは特に限定されないが、一般には０．１°～１０°程度の範囲である。
　上記のように、マスク板上でデポアップ方式により製膜された第一電極層６１は、主形成領域６１１の外周に遷移領域６１３を有し、その外周が非形成領域６１５となっている。
（第二電極層）
　ヘテロ接合太陽電池では、光電変換部４０の第二の主面上（導電型シリコン系薄膜３２上）に、第二電極層６２が形成される。第二電極層の製膜は、第一電極層の製膜の前後いずれに行ってもよい。図１に示すように、第一の主面の周縁に電極層非形成領域６１５が存在するため、第二電極層６２が、光電変換部４０の第二の主面の周端まで形成され、光電変換部の側面および第一の主面の周端にまで回り込んで形成されている場合でも、第一の主面の周縁には、第一電極層および第二電極層のいずれも製膜されていない絶縁領域４０１が形成される。
　なお、第一電極層の製膜と同様に、第二の主面の周縁をマスクで被覆した状態で第二電極層を製膜してもよい。この場合、光電変換部の側面および第一の主面の周端への回り込みが防止できるため、第一電極層と第二電極層との短絡をより確実に防止できる。
　一方、マスクを用いずに第二電極層６２を製膜して、光電変換部の側面および第一の主面の周端への第二電極層の回り込みが生じた場合でも、本発明においては、第一電極層の遷移領域の幅が小さいため、第一電極層と第二電極層との短絡を防止できる。また、第一電極層の製膜時にのみマスクを用いる場合、両方の電極層の製膜時にマスクを用いる場合に比べて、マスクの位置合わせの回数が半減するため、太陽電池の生産効率が高められる。この形態では、第二の主面上には絶縁領域が存在せず、周端にも第二電極層が形成されているため、光電変換部の周縁におけるキャリア回収効率が高められる。そのため、光電変換部の両面に絶縁領域を有する場合に比して、生産効率が高められる上に、変換効率の向上が期待できる。
　第二電極層が、第一の主面に回り込んで形成されている場合、第一の主面における絶縁領域４０１の幅、すなわち第一透明電極層の遷移領域の端部から第二透明電極層までの最短距離は、０より大きくする必要がある。絶縁領域の幅は、１．５ｍｍ未満であることが好ましい。
［集電極］
　ヘテロ接合太陽電池では、光生成キャリアを有効に取り出すために、透明電極層６１，６２上に、金属集電極が形成される。受光面側の集電極は、所定のパターン状に形成される。裏面側の集電極は、パターン状でもよく、透明電極層上の略全面に形成されていてもよい。図１に示す形態では、受光面側の透明電極層６１上にパターン集電極７が形成され、裏面側の透明電極層６２上の全面に裏面金属電極層８が形成されている。透明電極層上の全面に金属電極層を形成する方法としては、各種ＰＶＤ法やＣＶＤ法等のドライプロセス、ペーストの塗布、めっき法等が挙げられる。裏面金属電極層としては、近赤外から赤外域の波長領域の光の反射率が高く、かつ導電性や化学的安定性が高い材料を用いることが望ましい。このような特性を満たす材料としては、銀、銅、アルミニウム等が挙げられる。
　パターン集電極は、導電性ペーストを印刷する方法や、めっき法等により形成される。導電性ペーストが用いられる場合、インクジェット、スクリーン印刷、スプレー等により集電極が形成される。生産性の観点からはスクリーン印刷が好ましい。スクリーン印刷においては、金属粒子と樹脂バインダーからなる導電ペーストをスクリーン印刷によって印刷する工程が好ましく用いられる。
　めっき法によりパターン集電極を形成する場合、電極層上に、パターン状の金属シード７１を形成し、金属シードを起点としてめっき法により、金属電極７２が形成されることが好ましい。透明電極層６１上への金属電極の析出を抑制するために、透明電極層６１上には、絶縁層９が形成されることが好ましい。
　絶縁層９は、第一の主面の周端まで形成されていることが好ましい。絶縁層が第一の主面の周端まで形成されている場合（すなわち、第一の主面の全領域にわたって絶縁層が形成されている場合）、電極層非形成領域６１５上にも絶縁層が存在するため、めっき法により金属電極７２が形成される際に、光電変換部４０をめっき液から化学的および電気的に保護できる。そのため、めっき液中の不純物等の結晶シリコン基板への拡散を抑制でき、太陽電池の長期信頼性の向上が期待できる。
　絶縁層９は、光電変換部の側面にも形成されていることが好ましい。インターコネクタを介して複数の太陽電池を接続してモジュール化する際、光電変換部側面とインターコネクタとが接触した場合でも、側面に絶縁層が形成されていれば、インターコネクタとの短絡が防止されるため、太陽電池モジュールの変換効率を向上できる。
　金属シード７１上に、めっき法により金属電極７２を形成するためには、金属シードとめっき液とを導通させる必要がある。そのため、金属シード７１上の絶縁層９には、穿孔９ｈを設ける必要がある。絶縁層に穿孔を形成する方法としては、レジストを用いて絶縁層をパターニングする方法が挙げられる。また、レーザ照射、機械的な孔開け、化学エッチング等の方法により、絶縁層に穿孔を形成してもよい。
　上記の他に、絶縁層の穿孔を介してめっき金属電極を形成する方法として、下記の技術等を採用できる。
　透明電極上に絶縁層を形成後、絶縁層を貫通する溝を設けて透明電極層の表面または側面を露出させ、透明電極層の露出面に光めっき等により金属シードを析出させた後、この金属シードを起点としてめっきにより金属電極層を形成する（特開２０１１－１９９０４５号参照）。
　凹凸を有する金属シード上に、絶縁層を形成することにより、絶縁層が不連続となるため、穿孔が形成される。この穿孔を起点としてめっきにより金属電極を形成する（ＷＯ２０１１／０４５２８７号）。
　低融点材料を含有する金属シード上に絶縁層を形成後、または絶縁層形成時に、加熱により低融点材料を熱流動させて、金属シード上の絶縁層に穿孔を形成し、この穿孔を起点としてめっきにより金属電極を形成する（ＷＯ２０１３／０７７０３８号）。
　絶縁層として自己組織化単分子膜を形成後、金属シード上の自己組織化単分子膜が剥離除去されることにより、絶縁層に穿孔が形成される（金属シードが露出した状態となる）。露出した金属シードを起点としてめっきにより金属電極を形成する。透明電極層上には自己組織化単分子膜が形成されているため、透明電極層上への金属電極の析出が抑制される（ＷＯ２０１４／０９７８２９号）。
　これらの方法によれば、レジストを用いる必要がないため、材料コストおよびプロセスコスト面でより有利である。また、低抵抗の金属シードを設けることにより、透明電極層と集電極との間の接触抵抗を低下させることができる。
　また、本発明においては、マスク板と基板とがテーパ面で接した状態で電極層の製膜が行われ、基板の載置時や取出し時の基板の傷つきや端面でのクラックの発生等が抑制されるため、基板周縁の電極層（特に遷移領域）上や電極層非形成領域上に形成される絶縁層のカバレッジが良好となる。そのため、基板周縁等の不所望の箇所へのめっき金属の析出が抑制される傾向がある。
　以上、ヘテロ接合太陽電池の受光面側の透明電極層をマスク製膜する例を中心に説明したが、裏面側の透明電極層をマスク製膜し、受光面側はマスクを用いずに全面に透明電極層を製膜してもよい。また、本発明は、ヘテロ接合太陽電池以外でも、シリコン基板を含む光電変換部上に電極層と集電極を備える各種の太陽電池にも適用できる。
　本発明の太陽電池は、実用に供するに際して、封止材により封止して、モジュール化されることが好ましい。太陽電池のモジュール化は、適宜の方法により行われる。例えば、集電極にタブ等のインターコネクタを介してバスバーが接続されることによって、複数の太陽電池セルが直列または並列に接続され、封止材およびガラス板により封止されることによりモジュール化が行われる。
　１．　結晶シリコン基板
　２１，２２．　真性シリコン系薄膜
　３１，３２．　導電型シリコン系薄膜
　６１，６２．　電極層
　７．　集電極
　７１．　シード層
　７２．　金属電極
　８．　裏面電極
　９．　絶縁層
　９ｈ．　穿孔
　４０．光電変換部
　１０１．ヘテロ接合太陽電池
　１１０，１３０．　基板
　２００．　マスク板
　２１０，２３０　載置平面
　２１５，２４５　テーパ面
　４０１．　絶縁領域
　６１１．　主形成領域
　６１３．　遷移成領域
　６１５．　電極層非形成領域

Claims (16)

  1. 　結晶シリコン基板を含む光電変換部の第一の主面上に第一電極層を備える太陽電池の製造方法であって、
    　結晶シリコン基板の第一の主面側に第一電極層が製膜される第一電極層形成工程において、開口を有するマスク板の開口縁部に、結晶シリコン基板の第一の主面側が接するように載置された状態で、デポアップ方式で製膜が行われることにより、第一の主面の周端への着膜が防止され、
    　前記マスク板の開口縁部は、前記結晶シリコン基板の第一の主面側と接する部位に、前記結晶シリコン基板の周端における撓み角に沿うテーパ面を有する、太陽電池の製造方法。
  2. 　前記結晶シリコン基板の第一の主面側が凸となるように撓んだ状態で、前記第一電極層形成工程が実施され、
    　前記マスク板の開口縁部のテーパ面は、前記マスク板の下面から載置平面側に向かって開口が拡径するように形成されている、請求項１に記載の太陽電池の製造方法。
  3. 　前記結晶シリコン基板の周端における撓み角θが０．１°～１０°であり、前記マスク板の載置平面と前記テーパ面とのなす角αが、０．５θ～２θである、請求項１または２に記載の太陽電池の製造方法。
  4. 　前記結晶シリコン基板の厚みが、１０μｍ～１５０μｍである、請求項１～３のいずれか１項に記載の太陽電池の製造方法。
  5. 　前記第一電極層形成工程において、結晶シリコン基板の第一の主面側のマスク板による遮蔽領域に、マスク板の開口側から結晶シリコン基板の周端方向に向けて、前記第一電極層の被覆率または膜厚の少なくともいずれか一方が小さくなっている遷移領域が形成され、
    　前記遷移領域の幅が、０より大きく、１．５ｍｍ未満である、請求項１～４のいずれか１項に記載の太陽電池の製造方法。
  6. 　さらに、
    　前記第一電極層上に、パターン状の金属シードが形成される工程；
    　前記第一電極層上の全面に絶縁層が形成される工程；および
    　前記金属シードと導通する金属電極が、めっき法により形成される工程、をこの順に有し、
    　前記金属電極は、前記絶縁層に設けられた穿孔を介して、前記金属シードと導通される、請求項１～５のいずれか１項に記載の太陽電池の製造方法。
  7. 　前記太陽電池において、前記結晶シリコン基板は表面テクスチャを有する単結晶シリコン基板であり、前記光電変換部は単結晶シリコン基板の両面に導電型シリコン系薄膜を備え、前記第一電極層は透明電極層であり、
    　前記結晶シリコン基板の第二の主面上に第二電極層が製膜される第二電極層形成工程をさらに有し、
    　前記第一電極層形成工程において、第一電極層が光電変換部の第一の主面の周端に形成されていないことにより、前記太陽電池は、第一電極層と第二電極層とが絶縁されている、請求項１～６のいずれか１項に記載の太陽電池の製造方法。
  8. 　前記第二電極層形成工程において、前記結晶シリコン基板の第二の主面側の周端および側面にも、前記第二電極層が形成される、請求項７に記載の太陽電池の製造方法。
  9. 　前記第二電極層形成工程において、前記第二電極層が前記結晶シリコン基板の第一の主面側の周端にも形成され、
    　前記結晶シリコン基板の第一の主面側において、前記第一電極層と前記第二電極層との最短距離が、０より大きく、１．５ｍｍ未満である、請求項８に記載の太陽電池の製造方法。
  10. 　請求項１～９のいずれか１項に記載の方法により太陽電池が製造される工程；および前記太陽電池が封止材により封止される工程、をこの順に有する、太陽電池モジュールの製造方法。
  11. 　表面テクスチャを有する単結晶シリコン基板の両面に導電型シリコン系薄膜を備える光電変換部と、前記光電変換部の第一の主面上の第一透明電極層と、前記光電変換部の第二の主面上の第二透明電極層とを有する太陽電池であって、
    　前記第二透明電極層は、光電変換部の第二の主面の周端および側面ならびに光電変換部の第一の主面の周端にも形成されており、
    　前記第一透明電極層が光電変換部の第一の主面の周端に形成されていないことにより、前記第一透明電極層と前記第二透明電極層とが絶縁されており、
    　前記第一透明電極層は、第一の主面の中央部における主形成領域と、主形成領域から光電変換部の周端方向に向けて、被覆率または膜厚の少なくともいずれか一方が小さくなっている遷移領域とを有し、
    　前記第一透明電極層は、前記遷移領域における結晶化度が、前記主形成領域における透明電極の結晶化度よりも大きい、太陽電池。
  12. 　前記遷移領域の幅が、０より大きく、１．５ｍｍ未満である、請求項１１に記載の太陽電池。
  13. 　前記光電変換部の第一の主面において、前記第一透明電極層と前記第二透明電極層との最短距離が、０より大きく、１．５ｍｍ未満である、請求項１１または１２に記載の太陽電池。
  14. 　前記シリコン基板の厚みが、１０μｍ～１５０μｍである、請求項１１～１３のいずれか１項に記載の太陽電池。
  15. 　前記第一透明電極層上に、パターン状の金属シード、前記第一透明電極層上の全面に形成された絶縁層、および前記金属シードと導通する金属電極を備え、
    　前記金属電極は、前記絶縁層に設けられた穿孔を介して、前記金属シードと導通されている、請求項１１～１４のいずれか１項に記載の太陽電池。
  16. 　請求項１１～１５のいずれか１項に記載の太陽電池が封止材により封止されている、太陽電池モジュール。
PCT/JP2015/074656 2014-09-30 2015-08-31 太陽電池およびその製造方法、ならびに太陽電池モジュールおよびその製造方法 WO2016052046A1 (ja)