RU2738367C1 - Fire-retardant intumescent material - Google Patents

Fire-retardant intumescent material Download PDF

Info

Publication number
RU2738367C1
RU2738367C1 RU2020114467A RU2020114467A RU2738367C1 RU 2738367 C1 RU2738367 C1 RU 2738367C1 RU 2020114467 A RU2020114467 A RU 2020114467A RU 2020114467 A RU2020114467 A RU 2020114467A RU 2738367 C1 RU2738367 C1 RU 2738367C1
Authority
RU
Russia
Prior art keywords
fire
fabric
composition
polyvinyl chloride
aluminum hydroxide
Prior art date
Application number
RU2020114467A
Other languages
Russian (ru)
Inventor
Наталья Александровна Кейбал
Виктор Федорович Каблов
Тамара Викторовна Крекалева
Анастасия Геннадьевна Степанова
Original Assignee
Федеральное государственное бюджетное образовательное учреж-дение высшего образования "Волгоградский государственный технический университет" (ВолгГТУ)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Федеральное государственное бюджетное образовательное учреж-дение высшего образования "Волгоградский государственный технический университет" (ВолгГТУ) filed Critical Федеральное государственное бюджетное образовательное учреж-дение высшего образования "Волгоградский государственный технический университет" (ВолгГТУ)
Priority to RU2020114467A priority Critical patent/RU2738367C1/en
Application granted granted Critical
Publication of RU2738367C1 publication Critical patent/RU2738367C1/en

Abstract

FIELD: chemistry.
SUBSTANCE: invention relates to fire and heat protection material, which can be used as fire curtains. Disclosed is a fire-retardant intumescent material made in the form of a fabric coated with a polymer coating from a polyvinyl chloride composition containing a phosphoric acid derivative and dioctyl phthalate, wherein the composition further contains chlorinated paraffin, aluminum hydroxide, zinc borate and a phosphorus-boron-containing oligomer, the phosphoric acid derivative used is trichloropropylphosphate, and fabric is basalt fabric with following weight ratio of components of composition, weight parts: polyvinyl chloride 10.0, dioctyl phthalate 5.0, trichloropropylphosphate 35.0, chlorinated paraffin 9.0–14.0, aluminum hydroxide 22.0, zinc borate 13.0, phosphorus-boron-containing oligomer PBO 1.0–6.0.
EFFECT: high adhesion strength of bonding between plastisol-fabric layers and longer duration of fire-retardant material efficiency.
1 cl, 2 tbl, 6 ex

Description

Изобретение относится к огнетеплозащитному материалу, который может использоваться в качестве противопожарных штор. The invention relates to a fireproof material that can be used as fire curtains.

Известен огнезащитный вспучивающийся материал, состоящий из вспучивающейся композиции на основе пластифицированной полимерной массы, содержащей поливинилхлорид, пластификатор, фосфат аммония, пентаэритрит и амид, армированной текстильным материалом (Пат. GB 1408133, МПК C08K3/32, C08К5/52, C08F114/06, 1975).Known fire retardant intumescent material, consisting of an intumescent composition based on a plasticized polymer mass containing polyvinyl chloride, plasticizer, ammonium phosphate, pentaerythritol and amide, reinforced with textile material (US Patent GB 1408133, IPC C08K3 / 32, C08K5 / 52/06, 1975F114 ).

Недостатком данного огнезащитного материала являются сравнительно низкие огнезащитные свойства.The disadvantage of this fire retardant material is the relatively low fire retardant properties.

Известен огнестойкий текстильный материал, представляющий собой текстильное полотно из смеси полиэфирных волокон или с хлопковыми, или с льняными волокнами, или со смесью хлопковых или льняных волокон с шерстяными, с нанесенным на него дискретным покрытием на основе эмульсионного поливинилхлорида, содержащего тальк или мел и трихлорэтилфосфат (Патент РФ №2294411, МПК D06M15/244, D06M13/298, C09K21/14, C09D127/06, D06M101/04, D06M101/12, D06M101/32, C09K21/12, опубл. 27.09.1997).Known fire-resistant textile material, which is a textile fabric from a mixture of polyester fibers or cotton or linen fibers, or with a mixture of cotton or linen fibers with woolen, coated with a discrete coating based on emulsion polyvinyl chloride containing talc or chalk and trichloroethyl phosphate ( RF Patent No. 2294411, IPC D06M15 / 244, D06M13 / 298, C09K21 / 14, C09D127 / 06, D06M101 / 04, D06M101 / 12, D06M101 / 32, C09K21 / 12, publ. 09/27/1997).

Недостатком данного огнестойкого текстильного материала являются сравнительно невысокие огнезащитные свойства.The disadvantage of this fire-resistant textile material is the relatively low fire-retardant properties.

Наиболее близким к заявляемому является огнезащитный вспучивающийся материал (Патент РФ №2091424, МПК С09К21/12, опубл. 27.09.1997). Материал выполнен в виде ткани из стекловолокна с нанесенным на нее полимерным покрытием из поливинилхлоридной композиции, содержащей в качестве аммониевой соли фосфорной кислоты двузамещенный фосфорнокислый аммоний и дополнительно в качестве пластификатора диоктилфталат. Вспучивающимся компонентом в материале являются двузамещенный фосфорнокислый аммоний и пентаэритрит.Closest to the claimed is a fire retardant intumescent material (RF Patent No. 2091424, IPC S09K21 / 12, publ. 09/27/1997). The material is made in the form of a fiberglass cloth with a polymer coating applied to it from a polyvinyl chloride composition containing disubstituted ammonium phosphate as an ammonium salt of phosphoric acid and additionally as a plasticizer dioctyl phthalate. The intumescent component in the material is disubstituted ammonium phosphate and pentaerythritol.

Недостатком данного материала является то, что высокий огнезащитный эффект обеспечивается значительной толщиной покрытия, а не его свойствами.The disadvantage of this material is that a high fire-retardant effect is provided by a significant thickness of the coating, and not by its properties.

Задачей предлагаемого изобретения является разработка огнезащитного вспучивающегося материала с небольшой толщиной покрытия при сохранении огнетеплозащитной эффективности материала.The objective of the present invention is to develop a fire retardant intumescent material with a small coating thickness while maintaining the fire and heat protection efficiency of the material.

Техническим результатом заявленного изобретения является увеличение адгезионной прочности связи между слоями пластизоль-ткань и увеличение длительности огнезащитной эффективности материала.The technical result of the claimed invention is to increase the adhesive strength of the bond between the plastisol-fabric layers and to increase the duration of the fire-retardant efficiency of the material.

Технический результат достигается тем, что в огнезащитном вспучивающемся материале, выполненном в виде ткани с нанесенным на нее полимерным покрытием из поливинилхлоридной композиции, включающей производное фосфорной кислоты и диоктилфталат, при этом композиция дополнительно содержит хлорпарафин, гидроксид алюминия, борат цинка и фосфорборсодержащий олигомер, в качестве производного фосфорной кислоты композиция содержит трихлорпропилфосфат, а в качестве ткани используют базальтовую ткань при следующем массовом соотношении компонентов композиции, мас. ч.: поливинилхлорид 10,0, диоктилфталат 5,0, трихлорпропилфосфат 35,0, хлорпарафин 9,0-14,0, гидроксид алюминия 22,0, борат цинка 13,0, фосфорборсодержащий олигомер ФБО 1,0-6,0.The technical result is achieved by the fact that in a fire retardant intumescent material made in the form of a fabric coated with a polymer coating of a polyvinyl chloride composition containing a phosphoric acid derivative and dioctyl phthalate, the composition additionally contains chlorinated paraffin, aluminum hydroxide, zinc borate and a phosphorus-boron-containing oligomer, as derivative of phosphoric acid, the composition contains trichloropropyl phosphate, and as the fabric is used basalt fabric with the following mass ratio of the components of the composition, wt. including: polyvinyl chloride 10.0, dioctyl phthalate 5.0, trichloropropyl phosphate 35.0, chloroparaffin 9.0-14.0, aluminum hydroxide 22.0, zinc borate 13.0, phosphorusboron-containing oligomer TSF 1.0-6.0.

В предлагаемом огнезащитном вспучивающемся материале используют следующие компоненты: The proposed intumescent fire retardant material uses the following components:

Поливинилхлорид (ПВХ)– эмульсионный Slovinil E-671основа пластизоля.Polyvinyl chloride (PVC) - emulsion Slovinil E-671 plastisol base.

Диоктилфталат (ДОФ), трихлорпропилфосфат (ТХПФ), хлорпарафин (Хлорпарафин ХП-470) - пластификаторы. Dioctyl phthalate (DOP), trichloropropyl phosphate (TCPP), chloroparaffin (Chloroparaffin HP-470) are plasticizers.

Гидроксид алюминия, борат цинка - наполнители-антипирены.Aluminum hydroxide, zinc borate - fire retardant fillers.

В качестве модифицирующей добавки повышающей огнестойкость и адгезию к ткани используется фосфорборсодержащий олигомер ФБО (ТУ 40-461-806-66-07).As a modifying additive that increases fire resistance and adhesion to tissue, a phosphorusboron-containing oligomer FBO (TU 40-461-806-66-07) is used.

В качестве основы использовалась базальтовая ткань ТБК-100 (ТУ 2574-309-00149363-2008).Basalt fabric TBK-100 (TU 2574-309-00149363-2008) was used as a basis.

Использование в качестве модифицирующей добавки фосфорборсодержащего олигомера ФБО при заявленном составе композиции, придает огнезащитному материалу повышенную огнестойкость. Присутствие в составе композиции ФБО препятствует деструкции огнезащитного материала при воздействии высокой температуры за счет образования на поверхности более прочного защитного коксового слоя. Кроме того, происходит непосредственная доставка фосфорборсодержащего олигомера в зону термического воздействия и коксообразования, где происходит ингибирование радикально-цепных процессов окисления. При этом пенококс выполняет теплозащитную функцию, препятствует прогреву и деструкции материала. The use of a phosphorusboron-containing oligomer TSF as a modifying additive with the claimed composition of the composition gives the fire retardant material increased fire resistance. The presence of the TSF in the composition prevents the destruction of the fire retardant material when exposed to high temperatures due to the formation of a more durable protective coke layer on the surface. In addition, there is a direct delivery of the phosphorusboron-containing oligomer to the zone of thermal action and coke formation, where radical-chain oxidation processes are inhibited. At the same time, the coke foam performs a heat-shielding function, prevents the heating and destruction of the material.

Огнестойкость огнезащитного материала достигается благодаря использованию компонентов, обеспечивающих снижение горючести за счет синергетического действия. К синергистам фосфорборсодержащего олигомера ФБО - замедлителя горения можно отнести, гидроксид алюминия, борат цинка и галогенсодержащие соединения-пластификаторы. Кроме этого, используемые добавки выполняют несколько функций, т. е. одновременно могут является: замедлителями горения, пластификаторами, наполнителями и др. Например, большой эффект может быть получен введением наполнителя, разлагающегося с поглощением тепла. Классическим примером такого наполнителя является гидроксид алюминия Al(OH)3, от которого отщепляется вода. В этом случае тепло расходуется как на нагрев наполнителя, так и на разложение наполнителя и нагрев образующейся воды до температуры пламени. The fire resistance of the fire retardant material is achieved through the use of components that reduce flammability through a synergistic action. The synergists of the phosphorusboron-containing oligomer TSF, a combustion retarder, include aluminum hydroxide, zinc borate and halogen-containing plasticizer compounds. In addition, the additives used perform several functions, that is, they can simultaneously be: flame retardants, plasticizers, fillers, etc. For example, a great effect can be obtained by introducing a filler that decomposes with heat absorption. A classic example of such a filler is aluminum hydroxide Al (OH) 3 , from which water is split off. In this case, heat is consumed both for heating the filler and for decomposition of the filler and heating the resulting water to the flame temperature.

Также ФБО выполняет роль промотора адгезии – повышая прочность связи полимерного покрытия из поливинилхлоридной композиции с базальтовой тканью.The TSF also plays the role of an adhesion promoter - increasing the bond strength of the polymeric coating made of polyvinyl chloride composition with basalt fabric.

Заявленные количества фосфорборсодержащего олигомера ФБО, позволяют получить огнетеплозащитный материал, обладающий улучшенными огнезащитными и адгезионными характеристиками.The declared amounts of phosphorusboron-containing oligomer TSF, make it possible to obtain a fire-heat-protective material with improved fire-retardant and adhesion characteristics.

В таблице 1 приведены составы приготовленных смесей.Table 1 shows the compositions of the prepared mixtures.

Таблица 1Table 1

Ингредиент, мас.ч.Ingredient, parts by weight Контрольный примерTest case Номер составаSquad number 1one 22 33 44 55 66 ПВХPvc 10ten 10ten 10ten 10ten 10ten 10ten 10ten ДОФDOF 55 55 55 55 55 55 55 ТХПФThpf 3535 3535 3535 3535 3535 3535 3535 Хлорпарафин ХП-470Chloroparaffin HP-470 1515 1414 1313 1212 11eleven 10ten 9nine Гидроксид алюминияAluminum hydroxide 2222 2222 2222 2222 2222 2222 2222 Борат цинкаZinc borate 1313 1313 1313 1313 1313 1313 1313 ФБОTSF -- 1one 22 33 44 55 66

Огнезащитный вспучивающийся материал изготавливается следующим образом.Fire retardant intumescent material is manufactured as follows.

Все сухие ингредиенты в рецептуре тщательно перемешиваются. Затем при перемешивании небольшими порциями добавляется смесь пластификаторов, предварительно перемешанная. Полученная однородная масса выдерживается в течение 24 часов для вызревания. В это время происходит набухание частиц ПВХ под воздействием пластификатора, что увеличивает вязкость и облегчает процесс желирования. Полученную пасту еще раз перемешивают перед дальнейшим желированием пластизоля. Для исследования полученного огнезащитного вспучивающегося материала пластизоль наносят на базальтовую ткань. Огнезащитный вспучивающийся материал выдерживался в сушильном шкафу 10-15 минут при температуре 150-165 0С. Толщина покрытия составляла 0,65 мм.All dry ingredients in the recipe are thoroughly mixed. Then, while stirring, a mixture of plasticizers, pre-mixed, is added in small portions. The resulting homogeneous mass is aged for 24 hours for ripening. At this time, the PVC particles swell under the influence of the plasticizer, which increases the viscosity and facilitates the gelation process. The resulting paste is mixed again before further gelling of the plastisol. To study the resulting fire retardant intumescent material, plastisol is applied to basalt fabric. The intumescent fire retardant material was kept in an oven for 10-15 minutes at a temperature of 150-165 0 C. The thickness of the coating was 0.65 mm.

Готовые образцы подвергали необходимым испытаниям.The finished samples were subjected to the necessary tests.

Огне-, теплозащитные и адгезионные свойства предлагаемого материала приведены в таблице 2.Fire, heat-shielding and adhesive properties of the proposed material are shown in table 2.

Таблица 2table 2

ПоказательIndex Контрольный примерTest case Номер составаSquad number 1one 22 33 44 55 66 Время прогрева образца до 100 оС, сSample heating time up to 100 о С, s 5,05.0 8,08.0 8,08.0 10,010.0 11,011.0 8,08.0 7,07.0 Температура после прогрева в течение 60 с, оСTemperature after warming up for 60 s, о С 265,0265.0 232,0232.0 225,0225.0 196,3196.3 164,3164.3 182,1182.1 195,1195.1 Адгезионная прочность при отслаивании, НPeeling adhesion strength, N 12,712.7 13,813.8 14,714.7 19,719.7 18,218.2 15,015.0 13,013.0

Оценка длительности теплозащитной эффективности образцов огнезащитного материала при высокотемпературном нагреве проводилась на образцах, размером 10х10см.The assessment of the duration of the heat-shielding efficiency of samples of fire-retardant material at high-temperature heating was carried out on samples with a size of 10x10 cm.

Оценка скорости прогрева образцов огнезащитного материала при высокотемпературном нагреве (теплостойкость) проводилась следующим образом: определялось время прогрева обратной стороны образца до температуры 100°C. The assessment of the heating rate of the samples of fire retardant material during high-temperature heating (heat resistance) was carried out as follows: the heating time of the reverse side of the sample to a temperature of 100 ° C was determined.

Нагрев образца проводился открытым пламенем плазматрона Multiplaz-3500 (ГОСТ 12.2.007.8-75 «Устройства электросварочные и для плазменной обработки»), на поверхности создавалась температура 2000 °C. Образец закреплялся в штативе под углом 90° к пламени плазматрона. Для уменьшения стока тепла и уменьшения погрешности опыта образец по краю изолировался асбестом. The sample was heated with an open flame of the Multiplaz-3500 plasmatron (GOST 12.2.007.8-75 "Electric welding and plasma treatment devices"), a temperature of 2000 ° C was created on the surface. The sample was fixed in a tripod at an angle of 90 ° to the plasma torch flame. To reduce the heat sink and to reduce the experimental error, the sample was insulated along the edge with asbestos.

Для измерения температуры на необогреваемой поверхности образца использовался пирометр марки С-300.3 «Фотон» (ГОСТ 28243-96 «Пирометры. Общие технические требования»). Принцип работы пирометра основан на измерении мощности теплового излучения объекта измерения преимущественно в диапазонах инфракрасного излучения и видимого света.To measure the temperature on the unheated surface of the sample, a S-300.3 "Photon" pyrometer (GOST 28243-96 "Pyrometers. General technical requirements") was used. The principle of operation of the pyrometer is based on measuring the power of the thermal radiation of the measurement object, mainly in the infrared and visible light ranges.

Адгезионную прочность при отслаивании определяли по ГОСТ Р 57514-2017.Peeling adhesion strength was determined according to GOST R 57514-2017.

Таким образом, огнезащитный вспучивающийся материал, выполненный в виде базальтовой ткани с нанесенным на нее полимерным покрытием из поливинилхлоридной композиции, содержащей поливинилхлорид, диоктилфталат, трихлорпропилфосфат, хлорпарафин, гидроксид алюминия, борат цинка и фосфорборсодержащий олигомер, при заявленном соотношении компонентов, обладает большей длительностью огнезащитной эффективности и высокими адгезионными показателями.Thus, a fire retardant intumescent material made in the form of a basalt fabric with a polymer coating applied to it from a polyvinyl chloride composition containing polyvinyl chloride, dioctyl phthalate, trichloropropyl phosphate, chloroparaffin, aluminum hydroxide, zinc borate and phosphorus-boron-containing oligomer has a flame retardant efficiency, with the stated ratio of components and high adhesion rates.

Claims (2)

Огнезащитный вспучивающийся материал, выполненный в виде ткани с нанесенным на нее полимерным покрытием из поливинилхлоридной композиции, включающей производное фосфорной кислоты и диоктилфталат, отличающийся тем, что композиция дополнительно содержит хлорпарафин, гидроксид алюминия, борат цинка и фосфорборсодержащий олигомер, в качестве производного фосфорной кислоты композиция содержит трихлорпропилфосфат, а в качестве ткани используют базальтовую ткань при следующем массовом соотношении компонентов композиции, мас.ч.: Fire retardant intumescent material made in the form of a fabric coated with a polymer coating of a polyvinyl chloride composition comprising a phosphoric acid derivative and dioctyl phthalate, characterized in that the composition additionally contains chlorinated paraffin, aluminum hydroxide, zinc borate and a phosphorus-boron-containing oligomer, as a derivative of phosphoric acid, the composition contains trichloropropyl phosphate, and basalt fabric is used as the fabric with the following mass ratio of the components of the composition, parts by weight: ПоливинилхлоридPolyvinyl chloride 10,0 10.0 ДиоктилфталатDioctyl phthalate 5,0 5.0 ТрихлорпропилфосфатTrichloropropyl phosphate 35,0 35.0 ХлорпарафинChloroparaffin 9,0-14,0 9.0-14.0 Гидроксид алюминияAluminum hydroxide 22,0 22.0 Борат цинкаZinc borate 13,0 13.0 Фосфорборсодержащий олигомер ФБОPhosphorus-boron-containing oligomer TSF 1,0-6,01.0-6.0
RU2020114467A 2020-04-23 2020-04-23 Fire-retardant intumescent material RU2738367C1 (en)