RU2360879C1 - Complex additive - Google Patents
Complex additive Download PDFInfo
- Publication number
- RU2360879C1 RU2360879C1 RU2007146730/03A RU2007146730A RU2360879C1 RU 2360879 C1 RU2360879 C1 RU 2360879C1 RU 2007146730/03 A RU2007146730/03 A RU 2007146730/03A RU 2007146730 A RU2007146730 A RU 2007146730A RU 2360879 C1 RU2360879 C1 RU 2360879C1
- Authority
- RU
- Russia
- Prior art keywords
- concrete
- complex additive
- sodium
- sodium thiosulfate
- superplasticizer
- Prior art date
Abstract
Description
Изобретение относится к составу комплексной добавки для бетонной смеси и строительных растворов.The invention relates to the composition of a complex additive for concrete mix and mortar.
Известна комплексная добавка для строительной смеси, включающая релаксол - смесь балластных солей сероочистки коксового газа на основе тиосульфата и роданида натрия, технические лигносульфаты и суперпластификатор С-3 при следующем соотношении компонентов, мас.%: релаксол - 20-50, технические лигносульфаты - 20-40, суперпластификатор С-3 - остальное (RU №2290375, С04В 22/08, С04В 24/24, С04В 24/18, С04В 103/61, опубл. 27.12.2006).A well-known complex additive for building mixtures, including relaxol - a mixture of ballast salts of coke oven gas desulfurization based on sodium thiosulfate and thiocyanate, technical lignosulphates and C-3 superplasticizer in the following ratio, wt.%: Relaxol - 20-50, technical lignosulphates - 20- 40, superplasticizer C-3 - the rest (RU No. 2290375, С04В 22/08, С04В 24/24, С04В 24/18, С04В 103/61, publ. 12/27/2006).
Данная комплексная добавка не обеспечивает достижения передаточной прочности бетона в возрасте 12 часов.This complex additive does not ensure the achievement of the transfer strength of concrete at the age of 12 hours.
Наиболее близкой по технической сущности и достигаемому техническому результату к заявляемой добавке является комплексная добавка, содержащая мас.%: кремний органический пеногаситель - 0,02-0,06, суперпластификатор С-3 - полинафталинметилсульфонат натрия - 0-40, тиосульфат натрия - 40-55, суперпластификатор-лигнопан - 10-20, карбонат натрия - 1-2 (RU 2247092 C1, 27.02.2005, 4 с.).The closest in technical essence and the achieved technical result to the claimed additive is a complex additive containing wt.%: Silicon organic defoamer - 0.02-0.06, superplasticizer S-3 - sodium polynaphthalene methyl sulfonate - 0-40, sodium thiosulfate - 40- 55, superplasticizer-lignopane - 10-20, sodium carbonate - 1-2 (RU 2247092 C1, 02.27.2005, 4 pp.).
Известная добавка также не обеспечивает достижения передаточной прочности бетона в возрасте 12 часов при нормально-влажностных условиях твердения.The known additive also does not ensure the achievement of the transfer strength of concrete at the age of 12 hours under normal humidity conditions of hardening.
В основу изобретения поставлена задача создания комплексной добавки в бетонные смеси и строительные растворы, которая обеспечивает достижение передаточной прочности бетона в возрасте 12 часов и позволяет перейти на беспропарочную технологию производства сборного бетона и железобетона.The basis of the invention is the task of creating a complex additive in concrete mixtures and mortars, which ensures the achievement of the transfer strength of concrete at the age of 12 hours and allows you to switch to the steam-free technology for the production of precast and reinforced concrete.
Поставленная задача решается тем, что комплексная добавка, включающая суперпластификатор - полинафталинметилсульфонат натрия, пеногаситель и тиосульфат натрия, содержит в качестве пеногасителя Troykyd D128 при следующем соотношении компонентов, мас.%:The problem is solved in that the complex additive, including a superplasticizer - sodium polynaphthalene methyl sulfonate, antifoam and sodium thiosulfate, contains Troykyd D128 as an antifoam in the following ratio, wt.%:
Между совокупностью существенных признаков заявляемого изобретения и достигаемым результатом существует причинно-следственная связь.Between the totality of the essential features of the claimed invention and the achieved result, there is a causal relationship.
Полинафталинсульфонат натрия адсорбируется на продуктах гидратации портландцемента, прежде всего на эттрингите, и замедляет превращение эттрингита в моносульфоалюминат кальция, что оказывает блокирующий эффект на ранней стадии гидратации и приводит к увеличению длительности индукционного периода. Так как формируемая система условно замкнутых пор является неоднородной и содержит значительное количество пор крупнее 500 микрон, то на ранней стадии твердения снижение однородности структуры цементного камня сопровождается ускорением процессов трещинообразования под нагрузкой и снижением предела прочности при сжатии. Пеногаситель на основе растительных масел Troykyd D128 препятствует вовлечению неорганизованного воздуха и в оптимальной дозировке не приводит к снижению водоредуцирующего действия суперпластификатора. В сочетании с тиосульфатом натрия заявляемая комплексная добавка обеспечивает достижение передаточной прочности бетона в 12 часов без тепловлажностной обработки или с тепловлажностной обработкой при температуре не выше 40°С.Sodium polynaphthalene sulfonate is adsorbed on Portland cement hydration products, primarily on ettringite, and slows down the conversion of ettringite to calcium monosulfoaluminate, which has a blocking effect in the early stage of hydration and leads to an increase in the duration of the induction period. Since the formed system of conditionally closed pores is heterogeneous and contains a significant number of pores larger than 500 microns, at the early stage of hardening, a decrease in the uniformity of the structure of cement stone is accompanied by an acceleration of cracking processes under load and a decrease in compressive strength. The antifoam based on vegetable oils Troykyd D128 prevents the involvement of unorganized air and in the optimal dosage does not reduce the water-reducing effect of the superplasticizer. In combination with sodium thiosulfate, the inventive complex additive ensures that the concrete has a transfer strength of 12 hours without heat and moisture treatment or with heat and moisture treatment at a temperature not exceeding 40 ° C.
На момент подачи заявки, по мнению авторов, заявляемая комплексная добавка неизвестна и обладает мировой новизной.At the time of application, according to the authors, the claimed complex additive is unknown and has a world novelty.
Заявляемая совокупность существенных признаков проявляет новое свойство, которое позволяет получить указанный технический результат.The inventive combination of essential features exhibits a new property that allows you to get the specified technical result.
Заявляемое изобретение промышленно применимо и может быть использовано в производстве бетонов, строительных растворов.The claimed invention is industrially applicable and can be used in the production of concrete, mortar.
Для приготовления комплексной добавки использовалиFor the preparation of complex additives used
полинафталинметилсульфонат натрия - диспербетон № 9505 (регистрационный номер C.A.S - 9084-06-4), тиосульфат натрия (ГОСТ 27068-86), пеногаситель Troykyd D128 на основе растительных масел (US 5685898, 11.11.1997). Тиосульфат натрия измельчали и смешивали с остальными компонентами в заявляемом процентном соотношении.sodium polynaphthalene methyl sulfonate - disperson No. 9505 (registration number C.A.S - 9084-06-4), sodium thiosulfate (GOST 27068-86), antifoam Troykyd D128 based on vegetable oils (US 5685898, 11.11.1997). Sodium thiosulfate was ground and mixed with the remaining components in the claimed percentage.
Для исследования свойств заявляемой добавки были приготовлены бетонные смеси жесткостью 5-7 секунд, содержащие 470 кг/м3 цемента, щебень гранитный Кузнечного месторождения фракции 5-20 и песок речной с модулем крупности 2,2. Для приготовления бетонной смеси использовали цемент Оскольского цементного завода марки ПЦ-500Д0.To study the properties of the inventive additives, concrete mixtures with a hardness of 5-7 seconds were prepared, containing 470 kg / m 3 of cement, granite crushed stone of the Kuznechnoye deposit, fractions 5-20 and river sand with a particle size 2.2. For the preparation of the concrete mixture used cement Oskol cement plant brand PTs-500D0.
Заявляемую добавку предварительно растворяли и вводили в бетонную смесь вместе с водой затворения в количестве 0,8-1,2%. В полученных бетонных смесях определяли жесткость по ГОСТ 10181-2000. Из бетонных смесей готовили образцы бетонов для испытания на раннюю прочность. Образцы твердели при температуре 30°С при 100% влажности и в возрасте 12 часов испытывались на прочность при сжатии по ГОСТ 18105-86. Были также проведены испытания бетонной смеси, изготовленной в соответствии с прототипом, а также бетонной смеси, содержащей 0,375% от массы цемента диспербетона №9505 (опыт №5 в табл.). Результаты проведенных испытаний представлены в таблице.The inventive additive was previously dissolved and introduced into the concrete mixture together with mixing water in an amount of 0.8-1.2%. In the obtained concrete mixtures, the stiffness was determined according to GOST 10181-2000. Concrete samples were prepared from concrete mixtures for testing for early strength. The samples hardened at a temperature of 30 ° C at 100% humidity and at the age of 12 hours were tested for compressive strength according to GOST 18105-86. Tests were also conducted concrete mixture made in accordance with the prototype, as well as concrete mixture containing 0.375% by weight of cement dispersed concrete No. 9505 (experiment No. 5 in the table). The results of the tests are presented in the table.
Из таблицы видно, что заявляемая добавка согласно изобретению обеспечивает в возрасте 12 часов достижение передаточной прочности бетона (32 МПа), при сохранении жесткости бетонной смеси (опыты 2-4).The table shows that the inventive additive according to the invention at the age of 12 hours, the achievement of the transfer strength of concrete (32 MPa), while maintaining the rigidity of the concrete mixture (experiments 2-4).
Данная комплексная добавка позволяет внедрить беспропарочную и малопрогревную технологию производства сборного бетона и железобетона на заводах сборных железобетонных изделий.This complex additive allows the introduction of steamless and low-warming technology for the production of precast concrete and reinforced concrete at prefabricated concrete plants.
Claims (1)