KR20080038261A - 구멍 확장성과 연성이 우수한 고강도 박강판 - Google Patents
구멍 확장성과 연성이 우수한 고강도 박강판 Download PDFInfo
- Publication number
- KR20080038261A KR20080038261A KR1020087009196A KR20087009196A KR20080038261A KR 20080038261 A KR20080038261 A KR 20080038261A KR 1020087009196 A KR1020087009196 A KR 1020087009196A KR 20087009196 A KR20087009196 A KR 20087009196A KR 20080038261 A KR20080038261 A KR 20080038261A
- Authority
- KR
- South Korea
- Prior art keywords
- ductility
- less
- steel sheet
- ferrite
- hole expandability
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
Claims (13)
- 질량 %로,C : 0.01 % 이상, 0.20 % 이하,Si : 1.5 % 이하,Al : 1.5 % 이하,Mn : 0.5 % 이상, 3.5 % 이하,P : 0.2 % 이하,S : 0.0005 % 이상, 0.009 % 이하,N : 0.009 % 이하,Mg : 0.0006 % 이상, 0.01 % 이하,O : 0.005 % 이하, 및Ti : 0.01 % 이상, 0.20 % 이하,Nb : 0.01 % 이상, 0.10 % 이하,의 1종 또는 2종을 함유하고, 잔량부가 철 및 불가피적 불순물로 이루어지고, 또한 Mn %, Mg %, S % 및 O %가 식 1 내지 식 3을 만족시키는 동시에, 강 조직이 페라이트, 베이나이트 및 마르텐사이트의 1종 또는 2종 이상으로 이루어지고, 잔류 오스테나이트를 포함하는 조직이고, 또한, MgO, MgS 및 (Nb, Ti)N의 복합 석출물에 있어서, 0.05 ㎛ 이상, 3.0 ㎛ 이하의 석출물이 1 평방 ㎜당 5.0 × 102개 이상, 1.0 × 107개 이하 포함되는 것을 특징으로 하는 구멍 확장성과 연성이 우수한 고강도 박강판.[Mg %]≥([O %]/16 × 0.8)× 24 …(식 1)[S %]≤([Mg %]/24 -[O %]/16 × 0.8+ 0.00012)× 32 …(식 2)[S %]≤ 0.0075/[Mn %] …(식 3)
- 제1항에 있어서, 질량 %로, 또한, Al, Si의 관계가 식 4를 만족시키는 것을 특징으로 하는 구멍 확장성과 연성이 우수한 고강도 박강판.[Si %]+ 2.2 ×[Al %]≥ 0.35 …(식 4)
- 제1항 또는 제2항에 있어서, 질량 %로, 또한, Ti %, C %, Mn % 및 Nb %가 식 5 내지 식 7을 만족시키는 동시에, 강 조직이 베이나이트 및 페라이트의 조직이고, 강도가 980 N/㎟ 초과인 것을 특징으로 하는 구멍 확장성과 연성이 우수한 고강도 박강판.0.9 ≤ 48/12 × C/Ti< 1.7 …(식 5)50227 × C- 4479 × Mn> -9860 …(식 6)811 × C+ 135 × Mn+ 602 × Ti+ 794 × Nb> 465 …(식 7)
- 제1항 또는 제2항에 있어서, 질량 %로, 또한, C %, Si %, Al % 및 Mn % 가 식 8을 만족시키는 동시에, 강 조직이 페라이트와 마르텐사이트의 조직이고, 강도가 590 N/㎟ 초과인 것을 특징으로 하는 구멍 확장성과 연성이 우수한 고강도 박강판.-100 ≤ -300[C %]+ 105[Si %]- 95[Mn %]+ 233[Al %] …(식 8)
- 제4항에 있어서, 상기 강 조직의 결정립에 있어서, 짧은 직경(ds)과 긴 직경(dl)의 비(ds/dl)가 0.1 이상인 결정립이 80 % 이상 존재하는 것을 특징으로 하는 구멍 확장성과 연성이 우수한 고강도 박강판.
- 제5항에 있어서, 상기 강 조직의 페라이트의 결정립에 있어서, 입경 2 ㎛ 이상의 결정립이 80 % 이상 존재하는 것을 특징으로 하는 구멍 확장성과 연성이 우수한 고강도 박강판.
- 제1항 또는 제2항에 있어서, 질량 %로, 또한, C %, Si %, Mn % 및 Al %가 식 8을 만족시키는 동시에, 강 조직이 페라이트와 베이나이트의 조직이고, 강도가 590 N/㎟ 초과인 것을 특징으로 하는 구멍 확장성과 연성이 우수한 고강도 박강판.-100 ≤ -300[C %]+ 105[Si %]- 95[Mn %]+ 233[Al %] …(식 8)
- 제7항에 있어서, 상기 강 조직의 결정립에 있어서, 짧은 직경(ds)과 긴 직 경(dl)의 비(ds/dl)가 0.1 이상인 결정립이 80 % 이상 존재하는 것을 특징으로 하는 구멍 확장성과 연성이 우수한 고강도 박강판.
- 제8항에 있어서, 상기 강 조직의 페라이트의 결정립에 있어서, 입경 2 ㎛ 이상의 결정립이 80 % 이상 존재하는 것을 특징으로 하는 구멍 확장성과 연성이 우수한 고강도 박강판.
- 제1항 또는 제2항에 기재한 성분 조성의 강을 Ar3 변태점 이상의 압연 종료 온도에서 압연을 종료하고, 계속해서 20 ℃/초 이상의 냉각 속도로 냉각하고, 300 ℃ 미만에서 권취하고, 강 조직이 페라이트와 마르텐사이트로 이루어지고, 잔류 오스테나이트를 포함하는 조직이고, 강도가 590 N/㎟ 초과인 고강도 박강판을 제조하는 것을 특징으로 하는 구멍 확장성과 연성이 우수한 고강도 박강판의 제조 방법.
- 제1항 또는 제2항에 기재한 성분 조성의 강을 Ar3 변태점 이상의 압연 종료 온도에서 압연을 종료하고, 계속해서 20 ℃/초 이상의 냉각 속도로 650 ℃ 내지 750 ℃까지 냉각하고, 계속해서 상기 온도에서 15초 이하 공냉한 후, 다시 냉각하여, 300 ℃ 미만에서 권취하고, 강 조직이 페라이트와 마르텐사이트로 이루어지고, 잔류 오스테나이트를 포함하는 조직이고, 강도가 590 N/㎟ 초과인 고강도 박강판을 제조하는 것을 특징으로 하는 구멍 확장성과 연성이 우수한 고강도 박강판의 제조 방법.
- 제1항 또는 제2항에 기재한 성분 조성의 강을 Ar3 변태점 이상의 압연 종료 온도에서 압연을 종료하고, 계속해서 20 ℃/초 이상의 냉각 속도로 냉각하고, 300 ℃ 이상, 600 ℃ 이하에서 권취하고, 강 조직이 페라이트와 베이나이트로 이루어지고, 잔류 오스테나이트를 포함하는 조직이고, 강도가 590 N/㎟ 초과인 고강도 박강판을 제조하는 것을 특징으로 하는 구멍 확장성과 연성이 우수한 고강도 박강판의 제조 방법.
- 제1항 또는 제2항에 기재한 성분 조성의 강을 Ar3 변태점 이상의 압연 종료 온도에서 압연을 종료하고, 계속해서 20 ℃/초 이상의 냉각 속도로 650 ℃ 내지 750 ℃까지 냉각하고, 계속해서 상기 온도에서 15초 이하 공냉한 후, 다시 냉각하여, 300 ℃ 이상, 600 ℃ 이하에서 권취하고, 강 조직이 페라이트와 베이나이트로 이루어지고, 잔류 오스테나이트를 포함하는 조직이고, 강도가 590 N/㎟ 초과인 고강도 박강판을 제조하는 것을 특징으로 하는 구멍 확장성과 연성이 우수한 고강도 박강판의 제조 방법.