KR102679266B1 - 그라우팅용 지수제 조성물 - Google Patents
그라우팅용 지수제 조성물 Download PDFInfo
- Publication number
- KR102679266B1 KR102679266B1 KR1020230123399A KR20230123399A KR102679266B1 KR 102679266 B1 KR102679266 B1 KR 102679266B1 KR 1020230123399 A KR1020230123399 A KR 1020230123399A KR 20230123399 A KR20230123399 A KR 20230123399A KR 102679266 B1 KR102679266 B1 KR 102679266B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- catalyst
- acrylic monomer
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
본 발명은 주제, 경화제 및 촉매제를 포함하고, 상기 주제에 촉매를 첨가하여 교반한 후 상기 경화제를 혼합하여 사용되는 그라우팅용 지수제 조성물에 관한 것으로서, 주제는, 아크릴 모노머, 트리에탄올아민(Triethanol amine), 멜라민(Melamine), 옥틸페놀 에톡실레이트(Octyl Phenol Ethoxylate), 산화방지제를 포함하고; 경화제는, 물, 소듐실리케이트(Sodium silicate), 소듐퍼설페이트(Sodium persulfate)를 포함하고; 촉매제는, 물, 알콕시아민(Alkoxyamine), 트리에탄올아민(Triethanol amine), 디부틸틴 디아세테이트(Dibutyltin Diacetate);를 포함하는 것을 특징으로 한다.
Description
본 발명은 콘크리트 구조물의 크랙을 보수하기 위한 그라우팅용 지수제 조성물에 관한 것으로서, 더욱 상세하게는 미세 공극을 가지는 크랙으로의 침투성이 우수하고, 누수를 완벽하게 보수할 수 있는 그라우팅용 지수제 조성물에 관한 것이다.
일반적으로 콘크리트 구조물에서, 시공불량, 물리적인 손상, 철근 부식 및 충격 등으로 인한 성능 저하 등으로부터 기인하는 구조적인 크랙(structural crack)과, 소성 수축 및 침하 크랙, 건조 수축 크랙, 동결융해에 의한 크랙 등의 비구조적인 크랙(nonstructural crack)이 발생될 수 있다. 상기와 같은 콘크리트 구조물의 크랙은 구조적 결함, 내구성 저하, 외관 손상, 방수 성능 저하 등과 같은 문제가 발생하고, 크랙이 지속적으로 확산되기 때문에 크랙의 발생시에는 되도록 빨리 적절한 대처가 필요하다.
콘크리트 구조물에서 발생되는 크랙을 보수하기 위한 공법으로 그라우팅 공법(Injector Grouting)이 있다. 그라우팅 공법이란, 크랙 주위에 천공을 형성한 후 천공으로 고단위 에폭시계 또는 우레탄계 지수제를 주입 및 경화시킴으로써 크랙을 보수, 보강, 방수하는 공법이다.
그런데 에폭시계 지수제의 경우, 열과 자외선에 약하고, 인장성 및 탄성이 거의 없기 때문에 경화시 지수제와 크랙면 사이에서 틈새가 발생되어 재누수가 발생하고, 경우에 따라 외력이 가해질 경우 크랙으로부터 탈락 현상이 발생되었다.
또한 우레탄계 지수제의 경우, 주성분이 폴리이소시아네이트와 폴리올 등의 유기물이어서 화재의 위험성이 있고, 조성물의 점도가 비교적 높아 미세한 크랙에 대한 침투성이 부족하고, 건조시에 수축하여 수침투를 적절히 막지 못하게 되었다라는 문제점이 있었다.
본 발명은 상기와 같은 문제점을 해결하기 위하여 창출된 것으로서, 미세한 크랙에 대한 침투성이 우수하고, 경화되었을 때 고탄성 및 불투성을 가짐으로써 크랙 탈락 및 우수한 차수성을 가지며, 강한 기계적 물성을 가짐으로써 보수되는 콘크리트 구조물의 내구성을 유지할 수 있도록 하는, 그라우팅용 지수제 조성물을 제공하는 것을 목적으로 한다.
상기와 같은 목적을 달성하기 위하여, 본 발명에 따른 그라우팅용 지수제 조성물은, 주제, 경화제 및 촉매제를 포함하고, 상기 주제에 촉매를 첨가하여 교반한 후 상기 경화제를 혼합하여 사용하는 것으로서, 상기 주제는, 아크릴 모노머, 트리에탄올아민(Triethanol amine), 멜라민(Melamine), 옥틸페놀 에톡실레이트(Octyl Phenol Ethoxylate), 산화방지제를 포함하고; 상기 경화제는, 물, 소듐실리케이트(Sodium silicate), 소듐퍼설페이트(Sodium persulfate)를 포함하고; 상기 촉매제는, 물, 알콕시아민(Alkoxyamine), 트리에탄올아민(Triethanol amine), 디부틸틴 디아세테이트(Dibutyltin Diacetate);를 포함하는 것을 특징으로 한다.
본 발명에 있어서, 상기 주제는, 상기 아크릴 모노머 100 중량부에, 상기 트리에탄올아민 2-6 중량부, 상기 멜라민 2~10 중량부, 상기 옥틸페놀 에톡실레이트 0.2 내지 1 중량부, 상기 산화방지제 1~3 중량부로 혼합되어 구현되고; 상기 경화제는, 상기 물 100 중량부에, 상기 소듐실리케이트 15~25 중량부, 상기 소듐퍼설페이트 1~3 중량부의 조성비로 혼합되어 구현되고; 상기 촉매제는, 상기 물 100 중량부에, 상기 알콕시아민 20~30 중량부, 상기 트리에탄올아민 40~60 중량부의 조성비로 혼합되어 구현된다.
본 발명에 있어서, 상기 주제는 마이크로시멘트를 더 포함하고, 상기 마이크로시멘트는 상기 아크릴 모노머 100 중량부를 기준으로 10~20 중량부이다.
본 발명에 있어서, 상기 주제는 셀룰로오스 피브릴 그래뉼을 더 포함하고, 상기 셀룰로오스 피브릴 그래뉼은 상기 아크릴 모노머 100 중량부를 기준으로 1~5 중량부이다.
본 발명에 있어서, 상기 주제는 실리카 파우더를 더 포함하고, 상기 실리카 파우더는 상기 아크릴 모노머 100 중량부를 기준으로 1~3 중량부이다.
본 발명에 있어서, 상기 방청조성물은, 프로페놀(propanol), 벤조트리아졸(Benzotriazol), 소듐벤조에이트(Sodium Benzoate), 붕산(Boric acid), 인산나트륨(Mono sodium phosphate)을 혼합하여 구성된다.
본 발명에 있어서, 상기 방청조성물은 상기 아크릴 모노머 100 중량부를 기준으로 0.1~0.6 중량부이다.
본 발명의 그라우팅용 지수제 조성물에 따르면, 점도가 낮아서 미세공극의 크랙으로의 침투성이 우수하고, 촉매제의 양을 조절함으로써 경화시간의 조절이 자유로워 주입 거리를 산정할 수 있다.
또한 경화되는 지수제는 고탄성 및 불투성을 가짐으로써 크랙 탈락 현상이 현저히 개선됨과 동시에 우수한 차수성을 유지할 수 있고, 주위로부터 인가되는 진동 및 충격에도 크랙면 조직과 결착된 상태를 유지할 수 있으며, 경화과정에서 감쇄율이 거의 없어 크랙에 밀실되게 그라우트 됨으로써 지속적인 누수방지 기능을 유지할 수 있다.
그리고 경화된 후 화학적으로 열화되지 않고, 시간이 지나더라도 강한 기계적 물성을 유지할 수 있어 콘크리트 구조물을 내구성을 안정화시킨다.
이하 본 발명에 따른 그라우팅용 지수제 조성물을 상세하게 설명하면 다음과 같다.
이하에서, "상부" 나 "상"이라고 기재된 것은 접촉하여 바로 위에 있는 것뿐만 아니라 비접촉으로 위에 있는 것도 포함할 수 있다. 제1, 제2 등의 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 구성요소들은 용어들에 의해 한정 되어서는 안 된다. 용어들은 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 또한 어떤 부분이 어떤 구성요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 포함할 수 있는 것을 의미한다. 또한, 명세서에 기재된 "...부", "모듈" 등의 용어는 적어도 하나의 기능이나 동작을 처리하는 단위를 의미한다. 어떤 실시예가 달리 구현 가능한 경우에 특정한 공정 순서는 설명되는 순서와 다르게 수행될 수도 있다. 예를 들어, 연속하여 설명되는 두 공정이 실질적으로 동시에 수행될 수도 있고, 설명되는 순서와 반대의 순서로 진행될 수 있다.
본 발명의 그라우팅용 지수제 조성물은, 주제, 경화제 및 촉매제를 포함하고, 상기 주제에 촉매를 첨가하여 교반한 후 상기 경화제를 혼합하여 사용하는 것으로서, 콘크리트 구조물을 이루는 바닥, 벽, 천장 등에 형성된 크랙 또는 공동에 주입되어 누수 차단, 강성 보강 등의 목적으로 사용된다.
주제와 경화제는 혼합될 경우 연쇄중합반응을 일으켜 하이드로겔을 형성함으로써 차수 및 지수 효과를 낼 수 있고, 촉매제는 주제와 경화제의 연쇄중합반응 활성화 에너지를 조절하여 연쇄중합반응 속도를 조절한다.
주제는, 아크릴 모노머, 트리에탄올아민(Triethanol amine), 멜라민(Melamine), 옥틸페놀 에톡실레이트(Octyl Phenol Ethoxylate), 산화방지제, 마이크로시멘트, 셀룰로오스 피브릴 그래뉼, 실리카 파우더(Silica powder), 방청조성물을 포함한다.
이러한 주제는, 아크릴 모노머 100 중량부에, 트리에탄올아민 2-6 중량부, 바람직하게는 4 중량부와, 멜라민 2~10 중량부, 바람직하게는 6 중량부와, 옥틸페놀 에톡실레이트 0.2 내지 1 중량부, 바람직하게는 0.6 중량부와, 산화방지제 1~3 중량부, 바람직하게는 2 중량부와, 마이크로시멘트 10~20 중량부, 바람직하게는 15 중량부와, 셀룰로오스 피브릴 그래뉼 1~5 중량부, 바람직하게는 3 중량부와, 실리카 파우더 1~3 중량부, 바람직하게는 2 중량부와, 방청조성물 0.1~0.6 중량부, 바람직하게는 0.4 중량부의 조성비로 혼합되어 구현된다.
마이크로 시멘트는 콘크리트 구조물의 물성과 동일하기 때문에, 경화된 지수제를 크랙면 견고하게 결착되게 하고, 더 나아가 침투된 미세 크랙을 알카리 회복시킨다. 마이크로 시멘트는 비표면적은 본 발명의 지수제 조성물이 미세 크랙으로 침투될 수 있도록 8,000~12,000 cm2/g 이다. 참고적으로 시판되는 일반적인 마이크로 시멘트는 비표면적이 2,000~3,000cm2/g 이며, 이러한 마이크로 시멘트는 입경이 커서 미세한 크랙 내부로 침투되기가 어렵다.
산화방지제는 경화된 지수제의 산화를 방지하는 것으로서, 아민계, 비스페놀계, 모노페놀계 및 유황계가 있다. 바람직하게 산화방지제는 페놀계 산화방지제, 예를 들면 2.2-메틸렌비스(4-메틸-6-t-부틸페놀)[2.2-Methylenebis(4-methyl-6-t-butylphenol)], 2.6-디-t-부틸-4-메틸페놀(2.6-di-t-Butyl-4-methylphenol) 또는 이들의 혼합물을 사용한다.
셀룰로오스 피브릴 그래뉼은, 목재 또는 비목재 재료로부터 펄프를 기계적 처리하여 펄프 분말을 얻고, 펄프 분말로부터 셀룰로오스 응집체를 추출한 후 덩어리 형태의 셀룰로오스 응집체를 기계적으로 파쇄하고 체 거름함으로써 1~10㎛ 크기의 입도로 얻어진다.
셀룰로오스 피브릴 그래뉼은 기계적 강도가 매우 크고, 인장탄성계수가 강철이나 케볼라와 비슷할 정도의 100~160 Gpa 을 가지므로, 본 발명의 지수제의 기계적 강도는 물론 인장강도를 증가시킬 수 있다. 또한 셀룰로오스 피브릴 그래뉼은 넓은 비표면적을 가지면서 수분을 흡수하는 성질을 가짐으로써, 주제와 경화제의 수화반응을 지연시키는데 일조를 한다. 또한 셀룰로오스 피브릴 그래뉼은 친수성을 가지므로 주제에 혼합된 마이크로 시멘트 입자와의 부착성능이 우수하다.
실리카 파우더는 백색 무취 분말로서, 본 발명의 지수제 조성물이 경화되어 얻어지는 지수제의 시인성을 향상시킨다. 다시 말해 실리카 파우더에 의하여 지수제는 백색을 띠며, 사용자는 육안으로 크랙 주입부에 지수제 조성물이 충분히 주입되었는지 여부를 판단할 수 있다. 또한, 실리카 파우더는 경화된 지수제의 압축강도 및 굴곡강도를 향상시키고, 건조에 따른 수축율을 낮출 수 있어 경화되는 지수제가 수축됨에 발생되는 재누수 문제를 방지한다.
방청조성물은, 프로페놀(propanol), 벤조트리아졸(Benzotriazol), 소듐벤조에이트(Sodium Benzoate), 붕산(Boric acid), 인산나트륨(Mono sodium phosphate)을 혼합하여 구성된다. 방청조성물은, 프로페놀 100 중량부에, 벤조트리아졸 10 내지 20 중량부, 바람직하게는 15 중량부와, 소듐벤조에이트 2 내지 10 중량부, 바람직하게는 6 중량부와, 붕산 2 내지 20 중량부, 바람직하게는 10 중량부와, 인산나트륨 6~10 중량부, 바람직하게는 8 중량부의 조성비로 혼합되어 구현된다. 이러한 방청조성물은, 콘크리트 구조물을 구성하는 철근이 부식되는 것을 방지함으로써 기계적 강도를 유지할 수 있도록 한다.
경화제는, 물, 소듐실리케이트(Sodium silicate), 소듐퍼설페이트(Sodium persulfate)를 포함한다. 이러한 경화제는, 물 100 중량부에, 소듐실리케이트 15~25 중량부, 바람직하게는 20 중량부와, 소듐퍼설페이트 1~3 중량부, 바람직하게는 2 중량부의 조성비로 혼합되어 구현된다.
촉매제는 주제와 경화제의 연쇄중합반응 활성화 에너지를 조절하여 연쇄중합반응 속도를 조절하는 것으로서, 물, 알콕시아민(Alkoxyamine), 트리에탄올아민(Triethanol amine), 디부틸틴 디아세테이트(Dibutyltin Diacetate)를 포함한다. 이러한 촉매제는, 물 100 중량부에, 알콕시아민 20~30 중량부, 바람직하게는 25 중량부, 트리에탄올아민 40~60 중량부, 바람직하게는 50 중량부, 디부틸틴 디아세테이트 40~60 중량부, 바람직하게는 50 중량부의 조성비로 혼합되어 구현된다.
촉매제는 주제 100 중량부를 기준으로 2 내지 4 중량부를 포함한다. 촉매제의 함량이 2 중량부 보다 적을 경우 주제의 겔화가 지나치게 지연되고, 반면에 함량이 4 중량부 보다 많은 경우 크랙내로 방수액이 충분한 깊이로 침투되기 전에 주제의 겔화가 진행되어 크랙 내부 깊이에서 방수막이 형성되지 못하게 된다.
이러한 촉매제는 주제에 혼합될 때 양을 조절함으로써 경화시간을 자유롭게 조절할 수 있고, 이에 따라 크랙 내로 주제 및 경화제의 주입 거리를 산정할 수 있다.
이와 같이, 본 발명에 따른 그라우팅용 지수제 조성물은, 상기 조성물 및 조성비를 포함함으로써 점도가 낮아서 미세공극의 크랙으로의 침투성이 우수하고, 촉매제의 양을 조절함으로써 경화시간의 조절이 자유로워 주입 거리를 산정할 수 있다.
또한 경화되는 지수제는 고탄성 및 불투성을 가짐으로써 크랙 탈락 현상이 현저히 개선됨과 동시에 우수한 차수성을 유지할 수 있고, 주위로부터 인가되는 진동 및 충격에도 크랙면 조직과 결착된 상태를 유지할 수 있으며, 경화과정에서 감쇄율이 거의 없어 크랙에 밀실되게 그라우트 됨으로써 지속적인 누수방지 기능을 유지할 수 있다.
그리고 경화된 후 화학적으로 열화되지 않아 시간이 지나더라도 기계적 물성을 유지할 수 있어 콘크리트 구조물을 내구성을 안정화시킨다.
전술한 본 발명의 설명은 예시를 위한 것이며, 본 발명이 속하는 기술분야의 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 쉽게 변형이 가능하다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다. 예를 들어, 단일형으로 설명되어 있는 각 구성 요소는 분산되어 실시될 수도 있으며, 마찬가지로 분산된 것으로 설명되어 있는 구성 요소들도 결합된 형태로 실시될 수 있다.
본 발명의 범위는 후술하는 특허청구범위에 의하여 나타내어지며, 특허청구범위의 의미 및 범위 그리고 그 균등개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.
Claims (7)
- 주제, 경화제 및 촉매제를 포함하고, 상기 주제에 상기 촉매제를 첨가하여 교반한 후 상기 경화제를 혼합하여 사용하는 것으로서,
상기 주제는, 아크릴 모노머, 트리에탄올아민(Triethanol amine), 멜라민(Melamine), 옥틸페놀 에톡실레이트(Octyl Phenol Ethoxylate), 산화방지제를 포함하고;
상기 경화제는, 물, 소듐실리케이트(Sodium silicate), 소듐퍼설페이트(Sodium persulfate)를 포함하고;
상기 촉매제는, 물, 알콕시아민(Alkoxyamine), 트리에탄올아민(Triethanol amine), 디부틸틴 디아세테이트(Dibutyltin Diacetate);를 포함하고,
상기 주제는, 상기 아크릴 모노머 100 중량부에, 상기 트리에탄올아민 2-6 중량부, 상기 멜라민 2~10 중량부, 상기 옥틸페놀 에톡실레이트 0.2 내지 1 중량부, 상기 산화방지제 1~3 중량부로 혼합되어 구현되고,
상기 경화제는, 상기 물 100 중량부에, 상기 소듐실리케이트 15~25 중량부, 상기 소듐퍼설페이트 1~3 중량부의 조성비로 혼합되어 구현되고,
상기 촉매제는, 상기 물 100 중량부에, 상기 알콕시아민 20~30 중량부, 상기 트리에탄올아민 40~60 중량부의 조성비로 혼합되어 구현되고,
상기 주제는, 1~10㎛ 크기의 입도를 가진, 상기 아크릴 모노머 100 중량부를 기준으로 1~5 중량부의 셀룰로오스 피브릴 그래뉼을 더 포함하고,
상기 주제는, 상기 아크릴 모노머 100 중량부를 기준으로 0.1~0.6 중량부의 방청조성물을 더 포함하고,
상기 방청조성물은, 프로페놀(propanol) 100 중량부에, 벤조트리아졸(Benzotriazol) 10 내지 20 중량부, 소듐벤조에이트(Sodium Benzoate) 2 내지 10 중량부, 붕산(Boric acid) 2 내지 20 중량부, 인산나트륨(Mono sodium phosphate) 6~10 중량부를 혼합하여 구성되는 것을 특징으로 하는, 그라우팅용 지수제 조성물. - 삭제
- 제1항에 있어서,
상기 주제는 마이크로시멘트를 더 포함하고,
상기 마이크로시멘트는 상기 아크릴 모노머 100 중량부를 기준으로 10~20 중량부인 것을 특징으로 하는, 그라우팅용 지수제 조성물. - 삭제
- 제3항에 있어서,
상기 주제는 실리카 파우더를 더 포함하고,
상기 실리카 파우더는 상기 아크릴 모노머 100 중량부를 기준으로 1~3 중량부인 것을 특징으로 하는, 그라우팅용 지수제 조성물. - 삭제
- 삭제