KR101479642B1 - Hydrogel Pack and method of the same - Google Patents

Abstract

The present invention relates to a hydrogel pack. Such a hydrogel pack comprises 10 to 30 parts by weight of purified water, 1 to 3 parts by weight of glycerin, 2 to 5 parts by weight of butylene glycols, 1 to 3 parts by weight of gum, 0.1 to 10 parts by weight of Hydrolyzed Collagen, 5 to 10 parts by weight of Sodium Hyaluronate, 0.1 to 0.5 parts by weight of 1,2-Hexane diol, Shea Butter), 0.2 to 0.8 parts by weight of allantoin, 1 to 3 parts by weight of calcium lactate, 0.5 to 3 parts by weight of polyglutamic acid, 1 to 3 parts by weight of β-glucan, 1 to 9 parts by weight of oil, 5 to 10 parts by weight of fragrance, 5 to 10 parts by weight of carrageenan, 1 to 3 parts by weight of white sericite, And 5-50 parts by weight of the extract.

Description

Hydrogel pack and method for manufacturing the same

TECHNICAL FIELD The present invention relates to a hydrogel pack and a method of manufacturing the same, and more particularly, to a hydrogel pack and a method for manufacturing the hydrogel pack which are excellent in skin cost by improving components.

Recently, with the improvement of income level and the interest in skin beauty, there have been a lot of various beauty related products being developed.

Hydrogel packs are also one of these cosmetic products and are used for facial skin care.

Originally, pack means "wrap", wrapping the active substance on the face, removing the dirt of the pores cleanly, and supplying the moisture and cosmetic ingredients effectively to the skin, thereby restoring the physiological function of the skin by keeping blood circulation smooth The state is a kind of functional cosmetics.

Since the pack can provide various nutritional ingredients very effectively to the skin, various effects such as moisturizing, soothing, aging, keratin and waste removal, tired skin recovery, elasticity enhancement and whitening can be expected by these cosmetic ingredients.

In addition, when the pack is dried, the pack shrinks and the skin is pulled to form tension on the skin. In addition, the pack can improve the elasticity of the skin and reduce the fine lines by the adhesive force and massage effect.

In addition to the skin cosmetic and health effects of the pack as described above, psychological stability that can relieve the stress accumulated by providing relaxation to the face and body tired by a comfortable mind during the time required for applying the pack to the skin and drying Effect can be expected.

These packs are classified into a peel-off pack, a wash-off pack, and a tissue-off pack depending on the type.

The peel-off pack is a form that removes the dried film after applying a facial to the face and after a certain period of time, and has functions such as moisturizing, restoring skin elasticity, removing sebum and waste products.

The wash-off type is to wash the face with a pack of water and wash it off with water.

Moisturizing, calming, relieving fatigue, and providing nutritional sensation.

And, Tissue Off-Pack is a cream-type pack,

It absorbs some of the nutrients into the skin and wipes away the rest of the pack with tissue.

However, such conventional packs have limitations that generate only normal effects such as moisturization of the skin, recovery of elasticity, removal of sebum and waste products as described above.

Patent Application No. 10-2000-19665 (name: sheet-type hydrogel pack containing two or more water-soluble polymers and method for producing the same)

SUMMARY OF THE INVENTION Accordingly, the present invention has been made to solve the above-mentioned problems, and it is an object of the present invention to provide a hydrogel pack which can be improved in skin protection effect as a hydrogel type pack, will be.

SUMMARY OF THE INVENTION The present invention has been conceived in order to solve the above-mentioned problems, and it is an object of the present invention to provide a method for producing a gum, which comprises 10 to 30 parts by weight of purified water, 1 to 3 parts by weight of glycerin, 2-5 parts by weight of butylene glycol, ), 0.1 to 10 parts by weight of hydrolyzed collagen, 5 to 10 parts by weight of sodium hyaluronate, 1, 2-hexane diol ), 1 to 7 parts by weight of Shea Butter, 0.2 to 0.8 parts by weight of Allantoin, 1 to 3 parts by weight of Calcium Lactate, 1 to 3 parts by weight of polyglutamic acid 1 to 3 parts by weight of beta-glucan, 1 to 9 parts by weight of oil, 5 to 10 parts by weight of fragrance, 5 to 10 parts by weight of carrageenan, 5 to 10 parts by weight of white ceriseite (White Sericite) and 5-50 parts by weight of a natural herbal extract.

And further containing 10 to 30 parts by weight of purified water, 1 to 3 parts by weight of glycerin, 2 to 5 parts by weight of butylene glycols, 1 to 3 parts by weight of gum and 1 to 3 parts by weight of hydrolyzed 0.1 to 10 parts by weight of sodium hyaluronate, 0.1 to 0.5 part by weight of 1,2-hexanediol, 1 to 5 parts by weight of Shea Butter 1 1 to 3 parts by weight of calcium lactate, 0.5 to 3 parts by weight of polyglutamic acid, 1 to 3 parts by weight of beta-glucan (allantoin) 1 to 3 parts by weight of oil, 1 to 9 parts by weight of oil, 5 to 10 parts by weight of fragrance, 5 to 10 parts by weight of carrageenan, 1 to 3 parts by weight of white sericite, By weight to prepare a hydrogel pack mixture;

Adding 70 to 200 parts by weight of water to the hydrogel pack mixture to prepare a gel state; And

Applying the gel-state hydrogel pack mixture to a face, drying for 10 to 30 minutes, and then removing the gel-pack.

The hydrogel pack according to the present invention may contain at least one selected from the group consisting of glycerin, butylene glycol, gums, hydrolized collagen, sodium hyaluronate, 1,2-hexanediol, shea butter, allantoin, calcium lactate, polyglutamic It contains at least one of acid, beta-glucan, oil, fragrance, carrageenan, white sericite, and natural herbal extract to prevent skin aging and maintain elasticity and whitening effect.

Hereinafter, the hydrogel pack according to the present invention will be described in detail.

The pack proposed by the present invention is a method using a hydrogel in which a hydrophilic polymer which maintains a three-dimensional crosslinked structure swells very quickly when it comes into contact with an excessive amount of water, so that a large amount of water can be contained in the structure. Such a water-soluble gel crosslinking structure is referred to as a hydrogel.

Such hydrogels can generally be prepared by crosslinking a hydrophilic polymer, and natural polymers and synthetic polymers can be used as raw materials thereof.

The hydrogel pack proposed by the present invention comprises 10 to 40 parts by weight of purified water, 1 to 3 parts by weight of glycerin, 2 to 5 parts by weight of butylene glycols, 0.1 to 10 parts by weight of hydrolyzed collagen, 5 to 10 parts by weight of sodium hyaluronate, 1,2-hexanediol 0.1 , 0.5 to 0.5 parts by weight of polyvinyl alcohol, 1 to 7 parts by weight of shea butter, 0.2 to 0.8 parts by weight of allantoin, 1 to 3 parts by weight of calcium lactate, 0.5 to 3 parts by weight of polyglutamic acid 0.5 1 to 3 parts by weight of beta-glucan, 1 to 9 parts by weight of oil, 5 to 10 parts by weight of fragrance, 5 to 10 parts by weight of carrageenan, 5 to 10 parts by weight of white sericite, 1 to 3 parts by weight of a natural herbal extract, and 5-50 parts by weight of a natural herbal extract.

More specifically, the glycerin has a molecular weight of 92.10, a melting point of 17 ° C and a boiling point of 290 ° C. The glycerin is a trifunctional alcohol, glyceride (a major component of triglyceride) Can be obtained by hydrolysis. Such glycerin is used in cosmetics and is used as a softener.

The amount of the glycerin is preferably 1 to 3 parts by weight, and if the amount of the glycerin is less than 1-3 parts by weight, the skin elasticity improving effect can not reach the expected value, and if it exceeds the skin elasticity, the adverse effect may occur.

The butylene glycol has a specific gravity of 1.004 to 1.007, a boiling point of 207.4 ° C, and a melting point of -77 ° C or less.

Such butylene glycol has been widely used as a moisturizing agent, a solvent, and a fragrance retention agent for creams, lotions, aerosol products, dentifrices and the like because of its wettability, good solubility and antibacterial properties, and low irritation and toxicity to the skin.

If the amount of butylene glycol is less than 2 to 5 parts by weight, the skin elasticity-improving effect can not reach the expected value, and if it exceeds, the adverse effect on the skin beauty may occur due to the excessive pharmacological effect.

Said gum may include various components, but preferably includes a ceratonia siliqua Gum or a xanthan gum.

Such gauges act as a binder to adhere the above-mentioned hydrogel pack components to each other.

If the amount of the gum is less than 1-3 parts by weight, the skin elasticity improvement effect can not reach the expected value, and if it exceeds the expected value, the gum skin effect may be adversely affected due to the excessive pharmacological effect.

Ceratonia siliqua Gum is obtained by crushing the seeds of mature fruit of Ceratonia siliqua. This black locust black locust bean sow seed is divided into seed, endosperm, and embryo parts, and the endosperm part is separated and purified.

It is a neutral polysaccharide with a molecular weight of about 300,000. It is composed of galactose and mannose in a ratio of 1: 4. It is used as a thickening agent with excellent moisturizing ability, a binder, an emulsion stabilizer and a fragrance.

Xanthan gum is a fermented polysaccharide which is a bacterium, Xanthomonas campestris, which accumulates glucose outside the cells by oxidizing glucose.

Such black coal is a black white powder, which is soluble in water, and tasteless, odorless, viscous is very high and shows plasticity. Zanthan has black viscosity.

On the other hand, the hydrolyzed collagen is preferably mixed at a ratio of 10 to 30 parts by weight.

Hydrolyzed collagen means hydrolyzed collagen or a salt thereof obtained by hydrolyzing a bone of a bovine or a pig, skin with an acid, an alkali, and an enzyme individually or in combination.

This hydrolized collagen is used as a skin conditioning agent. It is a hydrolyzate of collagen, which promotes the regeneration of skin fibers, regulates the pH of the skin, and activates skin metabolism.

When the added amount of the hydrolized collagen is less than 10-30 parts by weight, the skin elasticity improving effect can not reach the expectation value, and if it exceeds, the adverse effect on the skin beauty may occur due to the excessive pharmacological effect .

Sodium hyaluronate can be obtained by culturing microorganism strains such as Streptococcus sp. Acetylglucosamine and glucosaccharide are cucopolysaccharides, which are used as a soluble and functional ingredient dissolving and preserving agent. This sodium hyaluronate is a natural moisturizing factor that absorbs moisture and hydrates the skin, prevents evaporation, and provides a moist and elastic skin.

If the added amount of sodium hyaluronate is less than 5-10 parts by weight, the skin elasticity improving effect can not be reached to the expectation value, and if it exceeds, the adverse effect on the skin beauty may occur due to the excessive pharmacological effect .

1,2-Hexane diol refers to a surfactant having both a hydrophobic group and a hydrophilic group with a structure in which one alcohol group is attached to each of the first and second positions of a linear alkyl chain. Such hexanediol is mixed with water and has emulsifying property to oil component, and has moisturizing and repelling ability.

The amount of 1,2-hexanediol is preferably 0.1 to 0.5 parts by weight, and when the amount of the 1,2-hexanediol is less than 0.1 to 0.5 parts by weight, the moisturizing effect can not reach the expected value. If the amount exceeds 1,200 parts by weight, May occur.

And Shea Butter is a fatty acid obtained from the seeds of Mangifolia among the Butyrospermum parkii Kotschy (Sapotaseae), widely distributed in Central Africa. This shea butter is used as a skin conditioning agent to block moisture.

If the addition amount of the shea butter is less than 1 to 7 parts by weight, the skin elasticity improving effect can not reach the expectation value, and if it exceeds, the adverse effect on the skin beauty may occur due to the excessive pharmacological effect have.

Allantoin is a colorless to white crystalline powder with a melting point of 220-238 ° C. These allantoins prevent the skin from swelling, and have the effect of softening and smoothing the skin surface.

If the amount of the allantoin is less than 0.2 to 0.8 part by weight, the skin elasticity improvement effect can not reach the expected value, and if it is exceeded, the adverse effect on the skin beauty may be caused due to the excessive pharmacological effect.

Calcium Lactate is a white powder or granular calcium salt fortifier with no odor or a slight peculiar smell. The formula is C6H10O6Ca.5H2O. 5% soluble in water and more soluble in hot water. This calcium lactate is used to control the acidity of the skin.

If the amount of the calcium lactate is less than 1 to 3 parts by weight, the skin elasticity improving effect can not reach the expected value. If the calcium lactate is exceeded, the skin elasticity can not be expected to be exceeded due to the excessive pharmacological effect .

Polyglutamic acid is synthesized by polymerizing N-carboxylic acid anhydride of poly-α-glutamic acid, glutamic acid γ-benzyl ester as a polymer of glutamic acid and debenzylating with hydrogenated hydrogen.

Β-glucan is a kind of polysaccharide, which is a glucose polymer. The glucose unit has a β-glycoside bond as a basic structure at positions 1 and 3, and its structure and physicochemical properties are different depending on the position where glucose is bonded . These beta glycans inhibit the formation and accumulation of body fat in the skin.

When beta-glucan is less than 1 to 3 parts by weight, the skin elasticity-improving effect can not reach the expectation value, and if it exceeds, the adverse effect on the skin beauty may occur due to the excessive pharmacological effect .

On the other hand, the oils are preferably mixed in a proportion of 1 to 9 parts by weight, and preferably include castor oil or PEG-60 hydrogencarbonated castor oil.

If the oil flow is less than 1-9 parts by weight, the skin elasticity-improving effect can not reach the expected value, and if it exceeds the expected level, the skin-cosmetic effect may be adversely affected due to the excessive pharmacological effect.

More specifically, the castor oil has a unique stickiness of the fat channel extracted from castor seeds and has a feeling of stickiness although it has affinity to hair. The main ingredient is contained as glyceride as ricinoleic acid. In the present invention, it is used as a lubricating oil.

And PEG-60 Hydrogenated Castor Oil is a solubilizer which is combined with castor oil and paper.

Piggy-60 Hydrogenated castor oil is a nonionic surfactant obtained by addition polymerization of ethylene oxide to cured castor oil to which hydrogen is added to double bonds of castor oil. Such a Pigment-60 Hydrogenated Castor Oil is used as a softener.

In addition, carrageenan refers to a polysaccharide obtained by hydrothermal extraction from irish moss of red algae. The basic structure is a galactose polymer, which is a type of 6-carrageenan such as κ-carrageenan, λ-carrageenan and ι-carrageenan. . Such carrageenans are used as stabilizers and dispersants.

When the carrageenan is less than 5 to 10 parts by weight, the skin elasticity improvement effect can not reach the expected value. If the carrageenan is less than 5 to 10 parts by weight, the skin elasticity improvement effect can not be achieved.

And white sericite (a hundred sericite) refers to hydrated silicate minerals containing potassium, aluminum and the like. These white serry sites smooth blood circulation and metabolism, activate cell tissue to improve skin elasticity and prevent aging.

When the white sericite is less than 1 to 3 parts by weight, the skin elasticity improvement effect can not reach the expected value, and if it exceeds the expected value, the skin effect may be adversely affected due to the excessive pharmacological effect .

Meanwhile, the natural herb extract is preferably mixed at a ratio of 5-50 parts by weight, and the following natural herb can be mixed.

In other words, natural herb extracts such as licorice root extract, horse rid extract, Sasa extract, black sesame extract, mushroom extract, Angelica keiskei extract, manganese extract, peony extract, gossam extract, golden extract, aloe vera leaf extract, Weaver bamboo stem extract, and Daemyeon safflower extract.

When the natural herbal extract is less than 5 to 50 parts by weight, the skin elasticity improvement effect can not be achieved. If the natural herb extract is exceeded, the skin effect may be adversely affected due to the excessive pharmacological effect.

In more detail, Licorice Extract is a sweetener whose concentration is extracted and concentrated at the roots and stems of licorice or coelenterate, which is 200 times as sweet as sugar. The major component of this licorice extract is glycyrrhizic acid, which is a white or colorless crystalline powder. The licorice extract is used as a wetting agent which is a skin conditioning agent.

Cimicifuga racemosa root extract is a substance extracted from black cohosh. Black cohosh is a botanical name, Cimicifuga racemosa, which is one of the buttercups, and perennial woodland plants )to be. These horse riding extracts are used as skin conditioners.

Sucrose extract (ichido) is a substance extracted from Sasao. Sasa is a perennial herbaceous perennial herbaceous plant belonging to the family Myrtaceae, and its scientific name is Pleuropterus multiflorus TURCZ. Sasso extract is used as a skin conditioner.

Sesamum Indicum (Sesame) Seed Extract contains more than twice as much fiber and calcium as normal sesame seeds. It contains a large amount of essential fatty acids, linolenic acid and oleic acid. Natural vitamin E and antioxidants sesamin and cedar Mollin is rich in nutrients and moisturizing effect on the skin.

 Sanghwang mushroom extract is a mushroom of mulberry mushroom, and its scientific name is Phellinus linteus. This situation mushroom is recorded in the name of 湯 이 (桑 木 耳) in the title of the bath. Mushroom extract contains mainly Polysaccharide materials such as AHCC and β-glucan, and has excellent anti-aging effect and prevention of skin damage.

Angelica acutiloba root extract is effective in preventing skin aging. In addition, promotes blood circulation by promoting metabolism to supply nutrients to the skin and maintain elasticity.

Mulberry root extract is a material obtained by scraping the outer root bark of mulberry and then removing the inner white skin and drying the dried bark. These extracts of Eucalyptus mellonus have excellent whitening, moisturizing and antioxidant effects as an excellent ingredient for inhibiting tyrosinase, an enzyme that plays an important role in melanin production, to improve and prevent pigmentation caused by sunlight and melanin .

Peony extract is a substance extracted from peony, and peony is a perennial plant of the dicotyledonous plant buttercups. These peony extracts provide nutrition to the skin and have a significant effect on the treatment of freckles and pigmentation and have a whitening effect.

Sophora Extract refers to an extract obtained by extracting Sophora flavescens Aiton (Leguminosae) with the roots as they are, or with roots having roughly peeled roots as a base, with 1,3-butylene glycol, anhydrous ethanol and ethanol . These extracts have excellent antioxidative effect and have an effect of healing skin tissue damaged by external stimuli such as ultraviolet rays.

The golden extract (Scutellaria baicalensis Extract; 黄 芩) is a substance extracted from the roots of gold (Scutellaria baicalensis GEORGE), a perennial herbaceous plant belonging to Lamiaceae. These golden extracts act as a skin stabilizer.

Citrus Grandis (Grapefruit) Seed Extract is extracted from the fruit of the citrus tree (Citrus Grandis). The fruit of the citrus tree has good fragrance and it is good for the skin. It opens the constitution of the dermatitis, it removes the wall sticking to the neck, saponin, sapotoxin, saponarin and the like are contained in the citrus tree, and it is used as the skin conditioner.

Weaver bamboo stem extract (Bambusa Textilis Stem Extract) is a substance extracted from the stem of weaver bamboo. These weaver bamboo stem extracts are used as a skin conditioning agent.

The extract of the Great King Song is a material extracted from the king pine (Pinus palustris Mill). It is a tree that grows about 30 ~ 36m in height and grows about 1m in diameter. It grows diagonally upward in the direction of the branches, and the water tube is formed into a long elliptical shape.

A process of forming a hydrogel pack on a face using the hydrogel pack material composed of these components is as follows. First, 70-200 parts by weight of water is added to the hydrogel pack mixture, and the mixture is mixed well to form a gel.

At this time, since the hydrogel pack has a high hardening speed, the gel-like mixture should be stirred immediately before the hydrogel pack is hardened.

After 10 to 30 minutes of application of the hydrogel pack, the skin-soothing component is absorbed into the skin while the gel-like mixture becomes rubbery. When the rubberized mixture is peeled from under the chin by hand, it is naturally peeled off.

[Example]

25 g of purified water, 1 g of glycerin, 2 g of butylene glycols, 1 g of gum, 0.5 g of hydrolyzed collagen, 5 g of sodium hyaluronate, , 0.2 g of 2-hexane diol, 2 g of Shea Butter, 0.3 g of Allantoin, 1 g of Calcium Lactate, 0.5 g of polyglutamic acid 0.5 1 g of beta-glucan, 2 g of oil, 5 g of fragrance, 5 g of carrageenan, 1 g of white sericite and 5 g of natural herbal extract are mixed to prepare a hydrogel pack mixture.

To 55 g of this hydrogel pack mixture , 100 cc of water is added and mixed to form a gel, which is then applied to the face to a certain thickness. After about 20 minutes, the hydrogel pack is cured and rubberized. The rubberized hydrogel pack is then removed from the face.

After removing the hydrogel pack, it was finished with nutritional cream without washing separately.

[Comparative Example 1]

A hydrogel pack mixture was prepared in the same manner as in the above example, except that no hydrolized collagen was added.

[Comparative Example 2]

A hydrogel pack mixture was prepared in the same manner as in the above example except that allantoin was not added in the above examples.

[Comparative Example 3]

The hydrogel pack mixture was prepared in the same manner as in the above example, except that the hydrolized collagen and the arachidonic acid and the natural herb extract were not added.

[Test Example 1]

Moisture measurement

The hydrogel pack mixture prepared in the above Examples and Comparative Examples 1 and 2 was applied to the face, cured, the hydrogel pack was removed, and the water content of the face was measured and shown in Table 1.

For the measurement method, subjects were subjected to daily hydrogel pack treatment after cleansing, applied to temperature and humidity for 20 minutes in a constant temperature and humidity room, and then measured for 6 weeks at intervals of one week. The measuring instrument was a Comeometer (CM820PC).

Moisture measurement result Example Comparative Example 1 Comparative Example 2 Comparative Example 3 1 week 80 65 63 53 2 weeks 85 69 67 56 3 weeks 83 72 70 59 4 weeks 88 76 72 61 5 weeks 89 78 75 65 6 weeks 90 79 77 68

From the results shown in the above Table 1, it can be seen that the example according to the present invention is remarkably superior in the water-containing effect as compared with Comparative Examples 1 to 3. In particular, the hydrolized collagen and the arachidon and the natural herb extract Which is higher than that of Comparative Example 3, which is not higher than about 40%.

[Test Example 2]

Whitening effect measurement

The hydrogel pack mixture prepared in the above Examples and Comparative Examples 1 and 2 was applied to the face, cured, and then the hydrogel pack was removed. The number of melanin in the basal layer of the facial skin was measured and shown in Table 2.

The subjects were subjected to hydrogel pack treatment each day and then measured for 6 weeks at intervals of one week. Measuring instrument was Mexameter MX-16.

Whitening measurement result Example Comparative Example 1 Comparative Example 2 Comparative Example 3 1 week 450 485 479 490 2 weeks 440 483 476 485 3 weeks 436 481 475 486 4 weeks 430 479 471 485 5 weeks 425 476 469 487 6 weeks 421 474 465 486

From the results shown in Table 2, it can be seen that the number of melanin pigments is significantly reduced in Examples according to the present invention as compared with Comparative Examples 1 to 3, indicating that the whitening effect is excellent. In particular, it can be seen that the whitening effect is remarkably superior to that of Comparative Example 3 in which neither hydrolized collagen nor arachidon nor natural herb extract is added.

[Test Example 3]

Elasticity measurement

The hydrogel pack mixture prepared in the above Examples and Comparative Examples 1 and 2 was applied to the face, cured, and then the hydrogel pack was removed. The elasticity of the facial skin was measured and shown in Table 3.

The skin elasticity of the subject was measured before the experiment, and the subjects were subjected to the hydrogel pack treatment every day for 6 weeks at intervals of one week. Both sides of the measurement area were measured and the mean value was used after 3 measurements. The measuring instrument was a cutometer (SEM474).

Elasticity measurement result Example Comparative Example 1 Comparative Example 2 Comparative Example 3 1 week 0.119 0.119 0.120 0.120 2 weeks 0.121 0.124 0.123 0.123 3 weeks 0.126 0.123 0.124 0.124 4 weeks 0.131 0.125 0.126 0.123 5 weeks 0.135 0.126 0.128 0.124 6 weeks 0.140 0.128 0.129 0.127

As can be seen from the results of Table 1, the elasticity of the example according to the present invention increased sharply from 0.119 to 0.142, while the elasticity of Comparative Examples 1 to 3 did not increase significantly compared with the initial value. In particular, in the case of Comparative Example 3 in which neither hydrolized collagen nor arachidon nor natural herb extracts were added, the increase in elasticity is weak.

[Test Example 4]

Wrinkle measurement

The hydrogel pack mixture prepared in the above Examples and Comparative Examples 1 and 2 was applied to the face, cured and then the hydrogel pack was removed and the wrinkles of the face were measured and shown in Table 4.

In the measurement method, the subject was transcribed to 1 cm under the eyes of the subjects before the experiment, and the wrinkles were measured for 6 weeks at intervals of one week after the treatment with the hydrogel packs each day. The measuring instrument was an Image Analyzer (KIT-500), and the change in the number of wrinkles, depth and length was measured.

Wrinkle measurement result Example Comparative Example 1 Comparative Example 2 Comparative Example 3 amount
(%) Length
(%) Sum
(%) amount(%) Length(%) Sum(%) amount(%) Length(%) Sum(%) amount(%) Length(%) Sum(%) 1 week 17.3 4.3 10.8 5.5 -8.3 -1.4 3.2 4.5 3.9 -1.2 2.5 2.9 2 weeks 8.3 25.5 33.8 -2.3 4.6 1.2 2.5 5.2 3.9 0.5 0.9 1.4 3 weeks 15.2 26.3 20.7 8.6 5.2 6.9 6.5 5.6 6.1 5.2 2.1 7.3 4 weeks 9.5 0.5 5.0 9.5 3.5 6.5 -0.5 3.1 1.3 2.4 3.2 5.6 5 weeks 2.6 26.8 14.7 6.3 4.5 5.4 1.4 4.1 2.8 -2.3 -0.7 -3.0 6 weeks 10.1 23.1 16.6 4.5 10.5 7.5 5.2 2.5 3.9 6.3 1.6 7.9 Average 10.5 17.7 14.1 5.4 3.4 4.4 3.1 4.2 2.0 1.8 1.6 1.7

As can be seen from the results of Table 1, the improvement according to the present invention improves the number of wrinkles by 10.5% on average and the improvement on length by 17.7%, which is an overall improvement of 14.1% .

On the other hand, in Comparative Examples 1 to 3, the effect on the number and length of wrinkles was not significantly increased when compared with the initial values. In particular, in Comparative Example 3 in which neither hydrolized collagen nor arachidon nor natural herb extract was added, the effect of improving wrinkles was weak.

Claims (4)

10 to 30 parts by weight of purified water, 1 to 3 parts by weight of glycerin, 2 to 5 parts by weight of butylene glycols, 1 to 3 parts by weight of gum and 1 to 3 parts by weight of Hydrolyzed Collagen ), 0.1 to 10 parts by weight of sodium hyaluronate, 5 to 10 parts by weight of sodium hyaluronate, 0.1 to 0.5 parts by weight of 1,2-hexanediol, 1 to 5 parts by weight of shea butter, 1 to 3 parts by weight of calcium lactate, 0.5 to 3 parts by weight of polyglutamic acid, 0.5 to 3 parts by weight of beta-glucan, 1 to 3 parts by weight of oil, 1 to 9 parts by weight of oil, 5 to 10 parts by weight of fragrance, 5 to 10 parts by weight of carrageenan, 1 to 3 parts by weight of white sericite, ≪ / RTI >
The above natural herb extracts can be used as a herb extract, a horse extract, a mulberry extract, a black sesame extract, a mushroom extract, a ginger extract, a manganese extract, a peony extract, a peony extract, A stem extract, and a royal persimmon extract. The method according to claim 1,
The gourd is a hydrogel pack comprising a carob bean gum (Ceratonia siliqua Gum) or xanthan gum. delete 10 to 30 parts by weight of purified water, 1 to 3 parts by weight of glycerin, 2 to 5 parts by weight of butylene glycols, 1 to 3 parts by weight of gum and 1 to 3 parts by weight of Hydrolyzed Collagen ), 0.1 to 10 parts by weight of sodium hyaluronate, 5 to 10 parts by weight of sodium hyaluronate, 0.1 to 0.5 parts by weight of 1,2-hexanediol, 1 to 5 parts by weight of shea butter, 1 to 3 parts by weight of calcium lactate, 0.5 to 3 parts by weight of polyglutamic acid, 0.5 to 3 parts by weight of beta-glucan, 1 to 3 parts by weight of oil, 1 to 9 parts by weight of oil, 5 to 10 parts by weight of fragrance, 5 to 10 parts by weight of carrageenan, 1 to 3 parts by weight of white sericite,
Aloe vera leaf extract, royal jelly extract, Weaver bamboo stem extract, Daemyeongseong extract, Ganoderma lucidum extract, Root extract, Horse extract, Sasa extract, Black sesame extract, And 5 to 50 parts by weight of a natural herb extract containing at least one of the extracts, to prepare a hydrogel pack mixture;
Adding 70 to 200 parts by weight of water to the hydrogel pack mixture to prepare a gel state; And
Applying the gel-state hydrogel pack mixture to the face, drying for 10 to 30 minutes, and removing the gel.