JPS6029666B2 - Manufacturing method for basic magkuro ribbon bricks - Google Patents
Manufacturing method for basic magkuro ribbon bricksInfo
- Publication number
- JPS6029666B2 JPS6029666B2 JP54025435A JP2543579A JPS6029666B2 JP S6029666 B2 JPS6029666 B2 JP S6029666B2 JP 54025435 A JP54025435 A JP 54025435A JP 2543579 A JP2543579 A JP 2543579A JP S6029666 B2 JPS6029666 B2 JP S6029666B2
- Authority
- JP
- Japan
- Prior art keywords
- bricks
- ribbon
- chromite
- basic
- manufacturing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
本発明は耐スポーリング性および耐食性ともに優れた塩
基性リボンドれんがの製造法に関するものである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a method for producing basic ribbon bricks having excellent spalling resistance and corrosion resistance.
塩基性リボンドれんがは亀融もし〈は焼結マグク。Basic ribbon bricks are Kamefu and sintered maguku.
クリンカーを原料として1700午0以上の高温度で焼
結されているため、繊密で、高熱間強度で、高耐食性を
有するものであるが、反面嘘結‘性の良い単一原料より
なるため、マグネシアれんがのごとくスポーリング抵抗
性が劣るものである。そのため、炉外精錬炉のスラグラ
ィン等に使用された場合、熱ショックによる剥落が先行
し、その高耐食性が充分に発揮できず、用途が限定され
ている。本発明は、リボンドれんがにクロム鉱の粗粒を
添加することによりリボンドれんがの最大の弱点である
耐スポーリング性を改善したものである。Because it is sintered at a high temperature of 1,700 degrees or more using clinker as a raw material, it is dense, has high hot strength, and has high corrosion resistance. , it has poor spalling resistance like magnesia brick. Therefore, when used as slag line in an outside-furnace refining furnace, flaking occurs first due to thermal shock, and its high corrosion resistance cannot be fully demonstrated, so its uses are limited. The present invention improves the spalling resistance, which is the biggest weakness of ribbon bricks, by adding coarse particles of chromite to ribbon bricks.
塩基性れんがの原料の中では、ク。ム鉱は熱膨張率の小
さい原料であり、またマグクロダィレクトボンドれんが
をミクロ的に観察した際、クロム鉱の周辺には空隙がよ
く見られる。本発明のリボンドれんがの耐スポーリング
性改善方法は、クロム鉱のこれらの性質を利用すること
によるものである。Among the raw materials for basic bricks, Ku. Chromium ore is a raw material with a small coefficient of thermal expansion, and when macroscopic direct bond bricks are observed microscopically, voids are often seen around chromium ore. The method of improving the spalling resistance of ribbon bricks according to the present invention utilizes these properties of chromite.
従来のリボンドれんがは、マグクロクリンカー単味使用
により、均質で繊密なれんが組織を有しているが、一方
本発明品は、れんが内部に蓄積される熱応力を緩和し易
くする為、れんが組織をわざと不均質にしたものである
。Conventional ribbon bricks have a homogeneous and delicate brick structure due to the single use of maguro clinker, but the product of the present invention has The organization was intentionally made heterogeneous.
ただし、れんが組織を不均質にするあまり、れんが結合
組織の破壊まで至ると、耐食性の面で性能低下をきたす
ので、その不均質化もコントロールが必要である。つま
り、個々のクロム鉱周辺の空隙同志が連絡し合う迄クロ
ム鉱を多く分布した場合、耐食性や強度面で弊害が生じ
てくる。本発明品は、熱膨張率の小さいクロム鉱をでき
るだけ多く添加し、かつれんが結合組織の破壊を最少限
にするため、クロムの粒度を5〜3側に添加量を5〜2
0%に規制している。However, if the brick structure is made too heterogeneous and the connective tissue of the brick is destroyed, the corrosion resistance will deteriorate, so it is necessary to control this heterogeneity. In other words, if a large amount of chromium ore is distributed to the extent that the voids around individual chromium ores communicate with each other, problems will occur in terms of corrosion resistance and strength. In the product of the present invention, in order to add as much chromite as possible, which has a small coefficient of thermal expansion, and to minimize the destruction of the connective tissue of the bricks, the particle size of chromium is set to 5-3 and the amount added is 5-2.
It is regulated at 0%.
そうすることにより、繊密で強固なれんが組織が大勢を
しめ、リボンドれんがの特質である高耐食性がそこなわ
れることなく耐スポーリング性の向上が可能である。0
以下その試験例を示す。By doing so, a dense and strong brick structure is formed, and it is possible to improve the spalling resistance without impairing the high corrosion resistance that is a characteristic of ribbon brick. 0
A test example is shown below.
クロム鉱の添加方法としてまず、リボンドれんがの結合
組織の破壊を最少限にとどめる為、クロム鉱の添加粒度
を5〜3側とし、添加量を検討した。As a method for adding chromite, first, in order to minimize the destruction of the connective tissue of ribbon bricks, the particle size of chromite added was set at 5 to 3, and the amount of addition was investigated.
タ 表1に示す露融マグクロクリンカーと、アフリカ産
のクロム鉱を原料として使用し、表2に示すA,B,C
,D,Eの5種類の配合で、一般的なマグクロダィレク
トボンドれんが製造法と同じ方法で成形、糠成し、れん
が試作を行なった。Using the open melted maguro clinker shown in Table 1 and chromite from Africa as raw materials,
.
表2中のAは従来から一般的なりポンドれんがに相当す
るものである。クロム鉱5〜3肋を20%以下に限定し
た理由は、20%以上添加した場合れんが組織が劣化し
、リボンドれんがの特質である高耐食性が保てなくなる
からである。A in Table 2 corresponds to the conventionally common pound brick. The reason why the content of 5-3 ribs of chromite is limited to 20% or less is that if 20% or more is added, the brick structure will deteriorate and the high corrosion resistance, which is a characteristic of ribbon-bonded bricks, will not be maintained.
A,B,C,D,Eの5種類の配合で試作され*たれん
がの品質を表3に示す。Table 3 shows the quality of the bricks produced in five different combinations: A, B, C, D, and E.
従来のリボンドれんがAに比較して、B,C,D,Eは
いずれも耐スポーリング性が向上しており、特にクロム
鉱を20%添加したEは格段に改良されている。また、
B,C,D,Eの耐食性は従来のリボンドれんがとほと
んど遜色ない結果である。表 1 原料の化学組成
(重量 ※ )表 2 配
合(1)表 3 れんが品質 (1)
※ 並形 片面加熱−空冷 くり返し
※※ 20×20×150の仇の試料を1650℃溶融
スラグ(0a/Si02=1)中に30分間浸潰しその
被食率を求めAを100とした時の港損指数次に添加す
るクロム鉱の粒度が5〜3職で適切かどうかを確認する
ため、添加量を20%に限定し、添加する粒度を表4の
ごとく検討した。Compared to the conventional ribbon brick A, all of B, C, D, and E have improved spalling resistance, and in particular, E with 20% chromite added is significantly improved. Also,
The corrosion resistance of B, C, D, and E is almost comparable to that of conventional ribbon bricks. Table 1 Chemical composition of raw materials
(Weight *)Table 2
Case (1) Table 3 Brick quality (1) *Normal size One side heating-air cooling Repeated ** A 20 x 20 x 150 sample was immersed in 1650℃ molten slag (0a/Si02=1) for 30 minutes. Port loss index when calculating the eclipse rate and setting A to 100 Next, in order to check whether the particle size of the chromium ore to be added is appropriate for 5 to 3 jobs, limit the amount added to 20% and express the particle size to be added. We considered the following.
試作方法は前述のA,C,D,Eと同様に表1の原料を
使用し一般的なマグクロダイレクトボンドれんが製造法
によるものである。FおよびG配合により試作されたれ
んがの品質を表5に示す。The trial manufacturing method used the raw materials shown in Table 1 in the same manner as A, C, D, and E described above, and was based on the general method for manufacturing magcro direct bond bricks. Table 5 shows the quality of the bricks prototyped using the F and G combinations.
FおよびGとも従来品Aに比鮫すれば耐スポーリング性
は良好であるが、表3中のEほどではなく、また耐食性
が若干劣化する。つまりこの結果は、クロム鉱の粒度を
小さくすることにより、クロム鉱の数が増え、リボンド
れんがの結合組織の破壊個所が多くなったことを示して
いる。また、耐スポーリング性の向上のため一定量のク
ロム鉱を添加する場合のクロム鉱の粒度は5〜3側が有
効であることを示している。Both F and G have good spalling resistance when compared to conventional product A, but are not as good as E in Table 3, and the corrosion resistance is slightly deteriorated. In other words, this result shows that by reducing the particle size of chromite, the number of chromite increased and the number of locations where the connective tissue of the ribbon bricks was destroyed increased. Furthermore, it has been shown that when adding a certain amount of chromite to improve spalling resistance, it is effective to set the particle size of chromite on the 5 to 3 side.
表4 配合(2)
表5 れんが品質 ‘2)
以上のごとくして発明された本発明品は、特に高温度で
操業されるAOD炉,VOD鍋,ASEA−SKF鍋,
VAD鍋,DH炉,RH炉等の主損傷個所の内張り耐火
物として優れている。Table 4 Mixture (2) Table 5 Brick quality '2) The product of the invention invented as described above is suitable for use in AOD furnaces, VOD pots, ASEA-SKF pots, etc., which are operated at particularly high temperatures.
Excellent as a refractory lining for main damaged areas of VAD pots, DH furnaces, RH furnaces, etc.
例えば、表4,表5中のEれんがをASEA−SKF鍋
のスラグラィンおよびAOD炉の羽□でテストした結果
スポーリング損傷が少なく、従釆のりボンドれんがの場
合に比べてそれぞれ約20%のライフアップを達成した
。For example, when the E bricks in Tables 4 and 5 were tested with the slag line of an ASEA-SKF pot and the blade of an AOD furnace, they showed less spalling damage, and each had a life of approximately 20% compared to the case of the subordinate glue bond bricks. Achieved up.
Claims (1)
3mmのクロム鉱を5〜20%添加した混練、成形、焼
結してなる塩基性マグクロリボンドれんがの製法。1 Electro-fused or sintered magcro clinker with a particle size of 5~
A method for producing basic magurobond bricks by kneading, molding, and sintering to which 5 to 20% of 3 mm chromite is added.