JPH1159842A - Conveyer belt - Google Patents
Conveyer beltInfo
- Publication number
- JPH1159842A JPH1159842A JP22719697A JP22719697A JPH1159842A JP H1159842 A JPH1159842 A JP H1159842A JP 22719697 A JP22719697 A JP 22719697A JP 22719697 A JP22719697 A JP 22719697A JP H1159842 A JPH1159842 A JP H1159842A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- polyolefin
- polyester resin
- anhydride
- conveyor belt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、樹脂層と繊維帆布
とを積層してなるコンベアベルトに関する。[0001] The present invention relates to a conveyor belt formed by laminating a resin layer and a fiber canvas.
【０００２】[0002]
【従来の技術】コンベアベルトは、物品を搬送するもの
として、食品、食品加工品等の用途、加工材料、器具部
材等の用途、廃棄物等の用途等に広く用いられている。
このようなコンベアベルトは、耐久性、耐磨耗性等を必
要とするため、樹脂からなる樹脂層と、繊維からなる繊
維帆布とを積層して構成されている。2. Description of the Related Art Conveyor belts are widely used for conveying articles, such as foods, processed foods, processed materials, tools and members, and wastes.
Since such a conveyor belt requires durability, abrasion resistance, and the like, it is configured by laminating a resin layer made of resin and a fiber canvas made of fibers.
【０００３】従来より、このような樹脂層用の樹脂とし
て、天然ゴムやスチレン−ブタジエン共重合体ゴム等が
用いられていたが、多種類・多量の添加剤を配合して性
能を調整しなければならず、時としてこれらの添加剤が
コンベアベルトの表面から溶出して搬送品を汚したり食
品を汚染する等の欠点があった。Conventionally, natural rubber, styrene-butadiene copolymer rubber, and the like have been used as a resin for such a resin layer, but the performance must be adjusted by blending a large number of kinds and a large amount of additives. In some cases, these additives are liable to elute from the surface of the conveyor belt and contaminate the conveyed goods or contaminate foods.
【０００４】そこで、食品等の搬送のために用いられる
コンベアベルトとしては、主として衛生面の観点から、
ポリウレタン、ポリ塩化ビニル、エチレン−酢酸ビニル
共重合体、エチレン−アクリル酸共重合体等の樹脂を表
層とした樹脂コンベアベルト等が広く用いられている。
しかしながら、これらの樹脂を用いた場合には、使用中
に加水分解や劣化が起こり、劣化物が食品等へ移行する
欠点を有していた。[0004] Therefore, as a conveyor belt used for conveying foods and the like, mainly from the viewpoint of hygiene,
BACKGROUND ART Resin conveyor belts and the like having a surface layer of a resin such as polyurethane, polyvinyl chloride, ethylene-vinyl acetate copolymer, and ethylene-acrylic acid copolymer are widely used.
However, when these resins are used, hydrolysis or deterioration occurs during use, and there is a disadvantage that the deteriorated product is transferred to foods and the like.
【０００５】一方、ポリエチレンやポリプロピレン等の
ポリオレフィンは、環境安定性に優れており、このよう
な欠点がないことが知られている。しかしながら、ポリ
オレフィンは、難接着材料であり、コンベアベルトの樹
脂層として用いる場合に必要な帆布との接着が困難であ
る欠点を有していた。[0005] On the other hand, polyolefins such as polyethylene and polypropylene are known to have excellent environmental stability and have no such disadvantages. However, polyolefin is a material that is difficult to adhere to, and has a drawback that it is difficult to adhere to canvas, which is necessary when used as a resin layer of a conveyor belt.
【０００６】[0006]
【発明が解決しようとする課題】本発明は、上記に鑑
み、ポリオレフィンと繊維とを強固に接着することによ
り、ポリオレフィンからなる樹脂層と繊維帆布とからな
るコンベアベルトを提供可能とすることを目的とするも
のである。SUMMARY OF THE INVENTION In view of the above, it is an object of the present invention to provide a conveyor belt comprising a resin layer made of polyolefin and a fiber canvas by firmly bonding a polyolefin and a fiber. It is assumed that.
【０００７】[0007]
【課題を解決するための手段】本発明は、樹脂層と繊維
帆布とを積層してなるコンベアベルトであって、上記樹
脂層は、酸無水物共重合ポリオレフィンからなるもので
あり、上記繊維帆布は、溶剤可溶型ポリエステル系樹脂
からなる接着剤により処理されたものであるコンベアベ
ルトである。以下に、本発明を詳述する。The present invention relates to a conveyor belt comprising a resin layer and a fiber canvas laminated, wherein the resin layer is made of an acid anhydride copolymerized polyolefin, Is a conveyor belt that has been treated with an adhesive made of a solvent-soluble polyester resin. Hereinafter, the present invention will be described in detail.
【０００８】本発明のコンベアベルトの樹脂層は、酸無
水物共重合ポリオレフィンからなる。上記酸無水物共重
合ポリオレフィンは、酸無水物をポリオレフィンに共重
合させたものである。上記酸無水物としては特に限定さ
れず、例えば、不飽和ジカルボン酸である無水マレイン
酸、無水ナジン酸等を挙げることができる。上記ポリオ
レフィンとしては特に限定されず、例えば、ポリエチレ
ン、ポリプロピレン等を挙げることができる。上記酸無
水物共重合ポリオレフィンとしては、更に具体的には、
例えば、ＡＤＭＥＲ（三井石油化学工業社製）、ＭＯＤ
ＩＣ（三菱化学社製）等を挙げることができる。[0008] The resin layer of the conveyor belt of the present invention comprises an acid anhydride copolymerized polyolefin. The acid anhydride copolymerized polyolefin is obtained by copolymerizing an acid anhydride with a polyolefin. The acid anhydride is not particularly limited, and examples thereof include unsaturated dicarboxylic acids such as maleic anhydride and nadic anhydride. The polyolefin is not particularly limited, and examples thereof include polyethylene and polypropylene. More specifically, as the acid anhydride copolymerized polyolefin,
For example, ADMER (made by Mitsui Petrochemical Industries, Ltd.), MOD
IC (manufactured by Mitsubishi Chemical Corporation) and the like can be mentioned.
【０００９】本発明のコンベアベルトの帆布は、繊維か
らなり、溶剤可溶型ポリエステル系樹脂からなる接着剤
により処理されたものである。上記繊維帆布としては、
例えば、ポリエチレンテレフタレート、ナイロン６、
綿、レーヨン等の繊維からなるもの等を挙げることがで
きる。上記溶剤可溶型ポリエステル系樹脂は、多価アル
コールと多塩基酸との重縮合により生成するポリエステ
ル系樹脂のうち、溶剤に可溶なものである。溶剤に可溶
なポリエステル系樹脂を用いることにより、帆布を容易
に処理することができる。上記溶剤可溶型ポリエステル
系樹脂としては、例えば、末端にカルボキシル基を導入
したポリエステル系樹脂等を挙げることができる。The canvas of the conveyor belt of the present invention is made of fibers and is treated with an adhesive made of a solvent-soluble polyester resin. As the above textile canvas,
For example, polyethylene terephthalate, nylon 6,
Fibers such as cotton and rayon can be used. The solvent-soluble polyester-based resin is a polyester-soluble resin produced by polycondensation of a polyhydric alcohol and a polybasic acid, which is soluble in a solvent. By using a polyester resin soluble in a solvent, the canvas can be easily treated. Examples of the solvent-soluble polyester resin include a polyester resin having a carboxyl group introduced into a terminal.
【００１０】上記溶剤可溶型ポリエステル系樹脂からな
る接着剤としては、上記溶剤可溶型ポリエステル系樹脂
を主成分とし、好ましくはエポキシ樹脂及び／又はポリ
イソシアネート化合物等を添加したもの等を挙げること
ができる。上記エポキシ樹脂としては、分子中にグリシ
ジルエーテル基を２個以上有するものが好ましく、例え
ば、ビスフェノール系エポキシ樹脂、グリセリン型エポ
キシ樹脂、ノボラック型エポキシ樹脂、脂環式エポキシ
樹脂、ポリオレフィン型エポキシ樹脂、エポキシ化大豆
油等を挙げることができる。上記ポリイソシアネート化
合物としては、分子中にイソシアネート基を２個以上有
するものが好ましく、例えば、クロロフェニレンジイソ
シアネート、トリレンジイソシアネート、ジフェニルメ
タンジイソシアネート、ヘキサメチレンジイソシアネー
ト、テトラメチレンジイソシアネート等を挙げることが
できる。Examples of the adhesive comprising the solvent-soluble polyester resin include those containing the above-mentioned solvent-soluble polyester resin as a main component and preferably containing an epoxy resin and / or a polyisocyanate compound. Can be. As the epoxy resin, those having two or more glycidyl ether groups in the molecule are preferable. For example, bisphenol-based epoxy resin, glycerin-type epoxy resin, novolak-type epoxy resin, alicyclic epoxy resin, polyolefin-type epoxy resin, epoxy And soybean oil. As the polyisocyanate compound, those having two or more isocyanate groups in the molecule are preferable, and examples thereof include chlorophenylene diisocyanate, tolylene diisocyanate, diphenylmethane diisocyanate, hexamethylene diisocyanate, and tetramethylene diisocyanate.
【００１１】本発明のコンベアベルトは、例えば、以下
のようにして製造することができる。予め上記繊維帆布
を、溶液化又は溶融した上記接着剤に浸漬又はコーティ
ングすることにより、上記繊維帆布に上記接着剤を含浸
し又は塗布する。その後、上記接着剤を乾燥・反応させ
るため、必要に応じて、５０〜１５０℃の温度で数分〜
数十分間加熱する。その後、接着剤処理された上記繊維
帆布と、溶融した上記酸無水物共重合ポリオレフィンと
をラミネートする。The conveyor belt of the present invention can be manufactured, for example, as follows. The fiber canvas is impregnated or coated with the adhesive by previously dipping or coating the fiber canvas in a solution or melted adhesive. Then, to dry and react the adhesive, if necessary, at a temperature of 50 to 150 ° C. for several minutes to
Heat for tens of minutes. Thereafter, the fiber canvas treated with the adhesive and the molten acid anhydride copolymerized polyolefin are laminated.
【００１２】本発明のコンベヤベルトは、高耐久性を有
し、衛生上安全であり、また、搬送物の付着残留が極め
て少ない。従って、本発明のコンベヤベルトは、食品等
の搬送用コンベヤベルトとして好適に用いることができ
る。[0012] The conveyor belt of the present invention has high durability, is hygienically safe, and has extremely little adhered residue of the conveyed material. Therefore, the conveyor belt of the present invention can be suitably used as a conveyor belt for conveying foods and the like.
【００１３】[0013]
【実施例】以下に本発明の実施例を掲げて本発明を更に
詳しく説明するが、本発明はこれらに限定されるもので
はない。The present invention will be described in more detail with reference to examples of the present invention, but the present invention is not limited to these examples.
【００１４】実施例１〜４及び比較例１〜５ ポリエチレンテレフタレート製の繊維帆布を、表１に示
す接着剤に浸漬した後、１５０℃で３分間加熱処理を行
った。その後、接着処理した繊維帆布に、表２に示す樹
脂を押出機を用いてラミネートすることにより、図１に
示すコンベアベルトを作製した。Examples 1 to 4 and Comparative Examples 1 to 5 Polyethylene terephthalate fiber canvas was immersed in the adhesive shown in Table 1 and then heated at 150 ° C. for 3 minutes. Thereafter, the resin shown in Table 2 was laminated on the bonded fiber canvas using an extruder to produce a conveyor belt shown in FIG.
【００１５】実施例１〜４及び比較例１〜５のコンベヤ
ベルトについて、下記の評価を行った。 （１）剥離接着力 ２５ｍｍ幅×１５０ｍｍ長さの試験片を作製し、剥離角
度１８０°、剥離速度５０ｍｍ／分で、室温及び８０℃
の温度条件下で樹脂／繊維帆布間の剥離接着力を測定し
た。 （２）ベルト走行試験 幅５０ｍｍの試験ベルトを作製し、５０ｍｍφ駆動プー
リー・５０ｍｍφ従動プーリー・軸間１ｍの試験装置に
より、走行速度２００ｍ／分で、ベルトの走行試験を行
い、剥離開始までの走行時間により、プーリー屈曲回数
を算出した。これらの結果を表３に示した。The conveyor belts of Examples 1 to 4 and Comparative Examples 1 to 5 were evaluated as follows. (1) Peeling adhesive strength A test piece having a width of 25 mm and a length of 150 mm was prepared, and at a peeling angle of 180 ° and a peeling speed of 50 mm / min, room temperature and 80 ° C.
The peel adhesion between the resin and the fiber canvas was measured under the following temperature conditions. (2) Belt running test A test belt having a width of 50 mm was prepared, and a belt running test was performed at a running speed of 200 m / min using a 50 mmφ driving pulley, a 50 mmφ driven pulley, and a 1 m center-to-shaft testing device, and the belt was driven to start peeling. The number of pulley bending times was calculated based on the time. Table 3 shows the results.
【００１６】[0016]
【表１】 [Table 1]
【００１７】[0017]
【表２】 [Table 2]
【００１８】表１、表２中、１）は、末端−カルボキシ
ル基導入ポリエステル樹脂（東洋紡績社製）、２）は、
エポキシ樹脂（油化シェルエポキシ社製）、３）は、イ
ミダゾール化合物（サンアプロ社製）、４）は、酸無水
物共重合ＬＬＤＰＥ系ポリオレフィン（三井石油化学工
業社製）、５）は、エチレン−オクテン共重合体系ポリ
オレフィン（ダウケミカル社製）をそれぞれ表す。In Tables 1 and 2, 1) is a terminal-carboxyl group-introduced polyester resin (manufactured by Toyobo Co., Ltd.), and 2) is
Epoxy resin (manufactured by Yuka Shell Epoxy), 3) is an imidazole compound (manufactured by San Apro), 4) is an acid anhydride copolymerized LLDPE-based polyolefin (manufactured by Mitsui Petrochemical Industry), 5) is ethylene- Octene copolymer polyolefin (manufactured by Dow Chemical Company) is represented.
【００１９】[0019]
【表３】 [Table 3]
【００２０】[0020]
【発明の効果】本発明のコンベヤベルトは、上述の通り
であるので、高耐久性を有し、衛生上安全であり、か
つ、搬送物の付着残留が極めて少ない。本発明のコンベ
ヤベルトは、食品等の搬送用コンベヤベルトとして好適
に用いることができる。As described above, the conveyor belt of the present invention has high durability, is sanitary safe, and has very little adhered residue of the conveyed material. The conveyor belt of the present invention can be suitably used as a conveyor belt for conveying foods and the like.
【図面の簡単な説明】[Brief description of the drawings]
【図１】本発明のコンベヤベルトの断面構造の概略図で
ある。FIG. 1 is a schematic view of a cross-sectional structure of a conveyor belt of the present invention.
１ 繊維帆布 ２ 樹脂層 ３ コンベヤベルト DESCRIPTION OF SYMBOLS 1 Textile canvas 2 Resin layer 3 Conveyor belt
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 ＦＩ Ｂ２９Ｋ 105:08 ──────────────────────────────────────────────────の Continued on front page (51) Int.Cl. 6 Identification code FI B29K 105: 08
Claims (1)
ベアベルトであって、前記樹脂層は、酸無水物共重合ポ
リオレフィンからなるものであり、前記繊維帆布は、溶
剤可溶型ポリエステル系樹脂からなる接着剤により処理
されたものであることを特徴とするコンベアベルト。1. A conveyor belt in which a resin layer and a fiber canvas are laminated, wherein the resin layer is made of an acid anhydride copolymerized polyolefin, and the fiber canvas is a solvent-soluble polyester-based A conveyor belt characterized by being treated with an adhesive made of a resin.