JPH10272704A - Conveyor belt - Google Patents
Conveyor beltInfo
- Publication number
- JPH10272704A JPH10272704A JP9484897A JP9484897A JPH10272704A JP H10272704 A JPH10272704 A JP H10272704A JP 9484897 A JP9484897 A JP 9484897A JP 9484897 A JP9484897 A JP 9484897A JP H10272704 A JPH10272704 A JP H10272704A
- Authority
- JP
- Japan
- Prior art keywords
- conveyor belt
- vinyl acetate
- acetate copolymer
- ethylene
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、樹脂層と繊維帆布
とを積層してなるコンベアベルトに関する。[0001] The present invention relates to a conveyor belt formed by laminating a resin layer and a fiber canvas.
【０００２】[0002]
【従来の技術】コンベアベルトは、物品を搬送するもの
として、食品、食品加工品等の用途、加工材料、器具部
材等の用途、廃棄物等の用途等に広く用いられている。
このようなコンベアベルトは、耐久性、耐磨耗性等を必
要とするため、樹脂からなる樹脂層と、繊維からなる繊
維帆布とを積層して構成されている。2. Description of the Related Art Conveyor belts are widely used for conveying articles, such as foods, processed foods, processed materials, tools and members, and wastes.
Since such a conveyor belt requires durability, abrasion resistance, and the like, it is configured by laminating a resin layer made of resin and a fiber canvas made of fibers.
【０００３】従来より、このような樹脂層用の樹脂とし
て、天然ゴムやスチレン−ブタジエン共重合体ゴム等が
用いられていたが、多種類・多量の添加剤を配合して性
能を調整しなければならず、時としてこれらの添加剤が
コンベアベルトの表面から溶出して搬送品を汚したり食
品を汚染する等の欠点があった。Conventionally, natural rubber, styrene-butadiene copolymer rubber, and the like have been used as a resin for such a resin layer, but the performance must be adjusted by blending a large number of kinds and a large amount of additives. In some cases, these additives are liable to elute from the surface of the conveyor belt and contaminate the conveyed goods or contaminate foods.
【０００４】そこで、食品等の搬送のために用いられる
コンベアベルトとしては、主として衛生面の観点から、
ポリウレタン、ポリ塩化ビニル、エチレン−酢酸ビニル
共重合体、エチレン−アクリル酸共重合体等の樹脂を表
層とした樹脂コンベアベルト等が広く用いられている。
しかしながら、これらの樹脂を用いた場合には、使用中
に加水分解や劣化が起こり、劣化物が食品等へ移行する
欠点を有していた。[0004] Therefore, as a conveyor belt used for conveying foods and the like, mainly from the viewpoint of hygiene,
BACKGROUND ART Resin conveyor belts and the like having a surface layer of a resin such as polyurethane, polyvinyl chloride, ethylene-vinyl acetate copolymer, and ethylene-acrylic acid copolymer are widely used.
However, when these resins are used, hydrolysis or deterioration occurs during use, and there is a disadvantage that the deteriorated product is transferred to foods and the like.
【０００５】一方、ポリエチレンやポリプロピレン等の
ポリオレフィンは、環境安定性に優れており、このよう
な欠点がないことが知られている。しかしながら、ポリ
オレフィンは、難接着材料であり、コンベアベルトの樹
脂層として用いる場合に必要な繊維帆布との接着が困難
である欠点を有していた。[0005] On the other hand, polyolefins such as polyethylene and polypropylene are known to have excellent environmental stability and have no such disadvantages. However, polyolefin is a difficult-to-adhere material, and has a drawback that it is difficult to adhere to a fiber canvas required when used as a resin layer of a conveyor belt.
【０００６】[0006]
【発明が解決しようとする課題】本発明は、上記に鑑
み、ポリオレフィンと繊維とを強固に接着することによ
り、ポリオレフィンからなる樹脂層と繊維帆布とからな
るコンベアベルトを提供可能とすることを目的とするも
のである。SUMMARY OF THE INVENTION In view of the above, it is an object of the present invention to provide a conveyor belt comprising a resin layer made of polyolefin and a fiber canvas by firmly bonding a polyolefin and a fiber. It is assumed that.
【０００７】[0007]
【課題を解決するための手段】本発明は、樹脂層と繊維
帆布とを積層してなるコンベアベルトであって、上記樹
脂層は、酸無水物共重合ポリオレフィンからなるもので
あり、上記繊維帆布は、エチレン−酢酸ビニル共重合体
／カルボキシル化変性エチレン−酢酸ビニル共重合体か
らなる接着剤により処理されたものであるコンベアベル
トである。以下に、本発明を詳述する。The present invention relates to a conveyor belt comprising a resin layer and a fiber canvas laminated, wherein the resin layer is made of an acid anhydride copolymerized polyolefin. Is a conveyor belt that has been treated with an adhesive consisting of an ethylene-vinyl acetate copolymer / carboxylated modified ethylene-vinyl acetate copolymer. Hereinafter, the present invention will be described in detail.
【０００８】本発明のコンベアベルトの樹脂層は、酸無
水物共重合ポリオレフィンからなる。上記酸無水物共重
合ポリオレフィンは、酸無水物をポリオレフィンに共重
合させたものである。上記酸無水物としては特に限定さ
れず、例えば、無水マレイン酸、無水フタル酸、無水コ
ハク酸等を挙げることができる。上記ポリオレフィンと
しては特に限定されず、例えば、ポリエチレン、ポリプ
ロピレン等を挙げることができる。上記酸無水物共重合
ポリオレフィンとしては、更に具体的には、例えば、Ａ
ＤＭＥＲ（三井石油化学工業社製）、ＭＯＤＩＣ（三菱
化学社製）等を挙げることができる。[0008] The resin layer of the conveyor belt of the present invention comprises an acid anhydride copolymerized polyolefin. The acid anhydride copolymerized polyolefin is obtained by copolymerizing an acid anhydride with a polyolefin. The acid anhydride is not particularly limited, and examples thereof include maleic anhydride, phthalic anhydride, and succinic anhydride. The polyolefin is not particularly limited, and examples thereof include polyethylene and polypropylene. More specifically, as the acid anhydride copolymerized polyolefin, for example, A
DMER (manufactured by Mitsui Petrochemical Industries, Ltd.), MODIC (manufactured by Mitsubishi Chemical Corporation) and the like can be mentioned.
【０００９】本発明のコンベアベルトの帆布は、繊維か
らなり、エチレン−酢酸ビニル共重合体／カルボキシル
化変性エチレン−酢酸ビニル共重合体からなる接着剤か
らなる接着剤により処理されたものである。上記繊維帆
布としては、例えば、ポリエチレンテレフタレート、ナ
イロン６、綿、レーヨン等の繊維からなるもの等を挙げ
ることができる。The canvas of the conveyor belt of the present invention is made of fibers and treated with an adhesive comprising an adhesive comprising an ethylene-vinyl acetate copolymer / a carboxylated modified ethylene-vinyl acetate copolymer. Examples of the fiber canvas include those made of fibers such as polyethylene terephthalate, nylon 6, cotton, and rayon.
【００１０】上記エチレン−酢酸ビニル共重合体（ＥＶ
Ａ）は、エチレンと酢酸ビニルとを共重合させた熱可塑
性樹脂である。上記カルボキシル化変性エチレン−酢酸
ビニル共重合体は、エチレン−酢酸ビニル共重合体を酸
変性し、エチレン−酢酸ビニル共重合体の性状を維持
し、かつ、接着性、反応性等の機能を付与させた熱可塑
性樹脂である。上記エチレン−酢酸ビニル共重合体／カ
ルボキシル化変性エチレン−酢酸ビニル共重合体として
は、溶剤・水溶化樹脂が、繊維帆布を容易に処理するこ
とができる点で好ましい。上記溶剤・水溶化樹脂として
は、具体的には、例えば、ＥＶＡＦＬＥＸ（三井・デュ
ポンポリケミカル社製）等を挙げることができる。上記
ＥＶＡＦＬＥＸの性質は、酢酸ビニル含有量及びメルト
フローレートによって最も一般に規定されている。The above ethylene-vinyl acetate copolymer (EV)
A) is a thermoplastic resin obtained by copolymerizing ethylene and vinyl acetate. The carboxylated ethylene-vinyl acetate copolymer is obtained by acid-modifying the ethylene-vinyl acetate copolymer, maintaining the properties of the ethylene-vinyl acetate copolymer, and imparting functions such as adhesiveness and reactivity. Thermoplastic resin. As the above-mentioned ethylene-vinyl acetate copolymer / carboxylated modified ethylene-vinyl acetate copolymer, a solvent / water-soluble resin is preferable because a fiber canvas can be easily treated. Specific examples of the solvent / water-soluble resin include EVAFLEX (manufactured by Du Pont-Mitsui Polychemicals). The properties of EVAFLEX are most commonly defined by vinyl acetate content and melt flow rate.
【００１１】上記エチレン−酢酸ビニル共重合体／カル
ボキシル化変性エチレン−酢酸ビニル共重合体からなる
接着剤としては、エチレン−酢酸ビニル共重合体／カル
ボキシル化変性エチレン−酢酸ビニル共重合体を主成分
とし、好ましくはエポキシ樹脂及び／又はポリイソシア
ネート化合物等を添加したもの等を挙げることができ
る。上記エポキシ樹脂は、分子中にグリシジルエーテル
基を２個以上有するものであり、具体的には、例えば、
エピコート８１５（油化シェル・エポキシ社製）等を挙
げることができる。上記ポリイソシアネート化合物は、
分子中にイソシアネート基を２個以上有するものであ
り、具体的には、例えば、スミジュールＬ−２５（住友
バイエルウレタン社製）等を挙げることができる。The adhesive composed of the ethylene-vinyl acetate copolymer / carboxylated modified ethylene-vinyl acetate copolymer is mainly composed of ethylene-vinyl acetate copolymer / carboxylated modified ethylene-vinyl acetate copolymer. And preferably those to which an epoxy resin and / or a polyisocyanate compound or the like is added. The epoxy resin has two or more glycidyl ether groups in the molecule, and specifically, for example,
Epicoat 815 (manufactured by Yuka Shell Epoxy) can be used. The polyisocyanate compound,
It has two or more isocyanate groups in the molecule, and specific examples thereof include Sumidur L-25 (manufactured by Sumitomo Bayer Urethane Co., Ltd.).
【００１２】本発明のコンベアベルトは、例えば、以下
のようにして製造することができる。予め上記繊維帆布
を、溶液化又は溶融した上記接着剤に浸漬又はコーティ
ングすることにより、上記繊維帆布に上記接着剤を含浸
し又は塗布する。その後、上記接着剤を乾燥・反応させ
るため、必要に応じて、５０〜１５０℃の温度で数分〜
数十分間加熱する。その後、接着剤処理された上記繊維
帆布と、溶融した上記酸無水物共重合ポリオレフィンと
をラミネートする。The conveyor belt of the present invention can be manufactured, for example, as follows. The fiber canvas is impregnated or coated with the adhesive by previously dipping or coating the fiber canvas in a solution or melted adhesive. Then, to dry and react the adhesive, if necessary, at a temperature of 50 to 150 ° C. for several minutes to
Heat for tens of minutes. Thereafter, the fiber canvas treated with the adhesive and the molten acid anhydride copolymerized polyolefin are laminated.
【００１３】本発明のコンベヤベルトは、高耐久性を有
し、衛生上安全であり、また、搬送物の付着残留が極め
て少ない。従って、本発明のコンベヤベルトは、食品等
の搬送用コンベヤベルトとして好適に用いることができ
る。[0013] The conveyor belt of the present invention has high durability, is hygienically safe, and has extremely little adhered residue of the conveyed material. Therefore, the conveyor belt of the present invention can be suitably used as a conveyor belt for conveying foods and the like.
【００１４】[0014]
【実施例】以下に本発明の実施例を掲げて本発明を更に
詳しく説明するが、本発明はこれらに限定されるもので
はない。The present invention will be described in more detail with reference to examples of the present invention, but the present invention is not limited to these examples.
【００１５】実施例１〜４及び比較例１〜５ ポリエチレンテレフタレート製の繊維帆布を、表１に示
す接着剤に浸漬した後、１５０℃で３分間加熱処理を行
った。その後、接着処理した繊維帆布に、表２に示す樹
脂を押出機を用いてラミネートすることにより、コンベ
アベルトを作製した。Examples 1 to 4 and Comparative Examples 1 to 5 A fiber canvas made of polyethylene terephthalate was immersed in an adhesive shown in Table 1, and then heated at 150 ° C. for 3 minutes. Thereafter, a resin belt shown in Table 2 was laminated on the bonded fiber canvas using an extruder to produce a conveyor belt.
【００１６】実施例１〜４及び比較例１〜５のコンベヤ
ベルトについて、下記の評価を行った。 （１）剥離接着力 ２５ｍｍ幅×１５０ｍｍ長さの試験片を作製し、剥離角
度１８０°、剥離速度５０ｍｍ／分で、室温及び６０℃
の温度条件下で樹脂／繊維帆布間の剥離接着力を測定し
た。 （２）ベルト走行試験 幅５０ｍｍの試験ベルトを作製し、５０ｍｍφ駆動プー
リー・５０ｍｍφ従動プーリー・軸間１ｍの試験装置に
より、走行速度２００ｍ／分で、ベルトの走行試験を行
い、剥離開始までの走行時間により、プーリー屈曲回数
を算出した。これらの結果を表３に示した。The conveyor belts of Examples 1 to 4 and Comparative Examples 1 to 5 were evaluated as follows. (1) Peeling adhesive strength A test piece having a width of 25 mm and a length of 150 mm was prepared.
The peel adhesion between the resin and the fiber canvas was measured under the following temperature conditions. (2) Belt running test A test belt having a width of 50 mm was prepared, and a belt running test was performed at a running speed of 200 m / min using a 50 mmφ driving pulley, a 50 mmφ driven pulley, and a 1 m center-to-shaft testing device, and the belt was driven to start peeling. The number of pulley bending times was calculated based on the time. Table 3 shows the results.
【００１７】[0017]
【表１】 [Table 1]
【００１８】[0018]
【表２】 [Table 2]
【００１９】表１、表２中、１）は、エチレン−酢酸ビ
ニル共重合体（ＶＡ＝２８％、三井・デュポンポリケミ
カル社製）、２）は、カルボキシル化変性エチレン−酢
酸ビニル共重合体、３）は、ＴＤＩ−ＴＭＰアダクト体
（住友バイエルウレタン社製）、４）は、酸無水物共重
合ＬＬＤＰＥ系ポリオレフィン（三井石油化学工業社
製）、５）は、エチレン−オクテン共重合体系ポリオレ
フィン（ダウケミカル社製）をそれぞれ表す。In Tables 1 and 2, 1) is an ethylene-vinyl acetate copolymer (VA = 28%, manufactured by DuPont-Mitsui Polychemicals) and 2) is a carboxylated modified ethylene-vinyl acetate copolymer. 3) is a TDI-TMP adduct (manufactured by Sumitomo Bayer Urethane Co.), 4) is an acid anhydride copolymerized LLDPE-based polyolefin (manufactured by Mitsui Petrochemical Industries, Ltd.), and 5) is an ethylene-octene copolymerized polyolefin. (Manufactured by Dow Chemical Company).
【００２０】[0020]
【表３】 [Table 3]
【００２１】[0021]
【発明の効果】本発明のコンベヤベルトは、上述の通り
であるので、高耐久性を有し、衛生上安全であり、か
つ、搬送物の付着残留が極めて少ない。本発明のコンベ
ヤベルトは、食品等の搬送用コンベヤベルトとして好適
に用いることができる。As described above, the conveyor belt of the present invention has high durability, is sanitary safe, and has very little adhered residue of the conveyed material. The conveyor belt of the present invention can be suitably used as a conveyor belt for conveying foods and the like.
【図１】本発明のコンベヤベルトの断面構造の概略図で
ある。FIG. 1 is a schematic view of a cross-sectional structure of a conveyor belt of the present invention.
１ 繊維帆布 ２ 樹脂層 ３ コンベヤベルト DESCRIPTION OF SYMBOLS 1 Textile canvas 2 Resin layer 3 Conveyor belt
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 ＦＩ Ｃ０９Ｊ 131/04 Ｃ０９Ｊ 131/04 Ｓ ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 6 Identification code FI C09J 131/04 C09J 131/04 S
Claims (1)
ベアベルトであって、前記樹脂層は、酸無水物共重合ポ
リオレフィンからなるものであり、前記繊維帆布は、エ
チレン−酢酸ビニル共重合体／カルボキシル化変性エチ
レン−酢酸ビニル共重合体からなる接着剤により処理さ
れたものであることを特徴とするコンベアベルト。1. A conveyor belt comprising a resin layer and a fiber canvas laminated, wherein the resin layer is made of an acid anhydride copolymerized polyolefin, and the fiber canvas is an ethylene-vinyl acetate copolymer. A conveyor belt which has been treated with an adhesive comprising a coalesced / carboxylated modified ethylene-vinyl acetate copolymer.