JPH0680457A - Adhesive for large-sized tile, etc. - Google Patents
Adhesive for large-sized tile, etc.Info
- Publication number
- JPH0680457A JPH0680457A JP23237392A JP23237392A JPH0680457A JP H0680457 A JPH0680457 A JP H0680457A JP 23237392 A JP23237392 A JP 23237392A JP 23237392 A JP23237392 A JP 23237392A JP H0680457 A JPH0680457 A JP H0680457A
- Authority
- JP
- Japan
- Prior art keywords
- cement
- adhesive
- tile
- polymer
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、各種壁材、例えば、コ
ンクリート壁、コンクリート板、石膏ボード、合板、石
綿板、ケイカル板、モルタル板、鉄板、亜鉛引鉄板、合
成樹脂板等の表面に大型タイルや、陶板や、自然石等を
貼着する大型タイル等用接着剤に関する。BACKGROUND OF THE INVENTION The present invention is applied to the surface of various wall materials such as concrete walls, concrete boards, gypsum boards, plywood, asbestos boards, silica sheets, mortar boards, iron plates, zinc-iron plates and synthetic resin plates. The present invention relates to an adhesive for large tiles, porcelain plates, large tiles, etc. for sticking natural stones, etc.
【０００２】[0002]
【従来の技術】従来、上記したタイル等は、寸法が 200
mm × 200 mm まではエポキシ樹脂やポリマーセメント
を用いて壁面等に貼着する一方で、寸法が 200 mm × 3
00 mm以上又は重量が１kg/ 枚以上の大型タイル等の場
合は、図２に示すように、エポキシ樹脂又はポリマーセ
メントと金具を併用している。2. Description of the Related Art Conventionally, the tiles mentioned above have a size of 200
Up to mm × 200 mm, the size is 200 mm × 3 while it is affixed to the wall surface using epoxy resin or polymer cement.
For large tiles of 00 mm or more or weight of 1 kg / sheet or more, as shown in Fig. 2, epoxy resin or polymer cement and metal fittings are used together.
【０００３】即ち、図２において、大型タイル30は、そ
の裏面側に釘掛止穴31を設けており、同釘掛止穴31に、
取付壁面32に打ちつけけた掛止金具33に掛止するように
している。従って、大型タイル30の重量を掛止金具33に
持たせる一方で、大型タイル30をエポキシ樹脂34によっ
て接着することができ、大型タイル30の施工時のずれ落
ちなどを確実に防止することができる。That is, in FIG. 2, the large tile 30 has a nail retaining hole 31 on the back side thereof, and the nail retaining hole 31 has
It is adapted to be hooked on a hooking metal fitting 33 which is struck on the mounting wall surface 32. Therefore, while the weight of the large tile 30 is given to the hook metal 33, the large tile 30 can be adhered by the epoxy resin 34, and slippage during construction of the large tile 30 can be reliably prevented. .
【０００４】[0004]
【発明が解決しようとする課題】しかし、かかる接着方
法は、未だ、以下の課題を有していた。However, such a bonding method still has the following problems.
【０００５】即ち、エポキシ樹脂34は大型タイル30の背
面に水が廻ると、剥離するおそれがある。そのため、掛
止金具33の用いているが、タイル接着作業の他に金具取
付作業を別途必要とし、かつ、掛止金具33が経時的に腐
食し、大型タイル30の落下を生じるおそれもあった。That is, the epoxy resin 34 may be peeled off when water is applied to the back surface of the large tile 30. Therefore, although the hook metal 33 is used, metal fitting installation work is required in addition to the tile adhering work, and the metal hook 33 may be corroded with time, which may cause the large tile 30 to drop. .
【０００６】従って、大型タイル30は、安全性を考慮し
て、建物の一階の取付壁面32にしか取付けることができ
なかった。Therefore, in consideration of safety, the large tile 30 could only be mounted on the mounting wall 32 on the first floor of the building.
【０００７】本発明は、上記した課題を解決することが
できる大型タイル等用接着剤を提供することを目的とす
る。An object of the present invention is to provide an adhesive for large tiles or the like which can solve the above-mentioned problems.
【０００８】[0008]
【課題を解決するための手段】本発明は、ポリマーセメ
ントとセメント系急結剤との混和物からなる大型タイル
等用接着剤に係るものである。The present invention relates to an adhesive for a large tile or the like, which is composed of a mixture of polymer cement and a cement-based quick-setting agent.
【０００９】ここに、ポリマーセメントとしては、粘着
性があり、硬化後は水の影響を受けにくいポリマーセメ
ントを用いるものであり、例えば、アクリル酸エステル
共重合体を主成分とする複合ポリマーエマルジョンを、
セメント、珪砂、鉄粉等を主成分とした主材に混合して
生成したポリマーセメントがある。Here, as the polymer cement, a polymer cement that is sticky and is not easily affected by water after curing is used. For example, a composite polymer emulsion containing an acrylic ester copolymer as a main component is used. ,
There is a polymer cement produced by mixing it with a main material mainly composed of cement, silica sand, iron powder and the like.
【００１０】一方、セメント急結剤としては、セメント
と水和反応を生じ、初期材令ではカルシウムアルミネー
ト水和物を形成し、長期材令ではカルシウムシリケート
水和物と水酸化カルシウムを生成する、長期的に安定し
た水和物を用いることができる。On the other hand, as a cement quick-setting agent, a hydration reaction occurs with cement, forming calcium aluminate hydrate in the early age, and forming calcium silicate hydrate and calcium hydroxide in the long age. A long-term stable hydrate can be used.
【００１１】また、上記接着剤において、セメント系急
結剤の混和量は、ポリマーセメント中のセメント量の３
〜10重量％とするのが好ましい。In the above adhesive, the amount of the cement type quick-setting admixture is 3 times the amount of the cement in the polymer cement.
It is preferably about 10% by weight.
【００１２】[0012]
【実施例】以下、添付図である図１に示す実施例を参照
して、本発明に係る大型タイル等用接着剤Ａについて説
明する。EXAMPLE An adhesive A for a large tile or the like according to the present invention will be described below with reference to the example shown in FIG.
【００１３】図１において、10は一定の厚みを有するコ
ンクリート製壁材を示している。In FIG. 1, reference numeral 10 denotes a concrete wall material having a constant thickness.
【００１４】一方、同コンクリート製壁材10には、同壁
材10に接着しようとする自然石等からなる大型タイル11
が配設されている。On the other hand, the concrete wall material 10 has a large tile 11 made of natural stone or the like which is to be bonded to the wall material 10.
Is provided.
【００１５】そして、図１に示すように、大型タイル11
は、それぞれ、以下に説明する組成を有するポリマーセ
メントとセメント系急結剤との混和物からなる大型タイ
ル等用接着剤12を、約１〜２mmの厚みで用いてコンクリ
ート製壁材10に強力に接着することができる。Then, as shown in FIG. 1, the large tile 11
Is an adhesive 12 for large tiles, which is composed of a mixture of polymer cement and a cement-based quick-setting admixture having the composition described below, each having a thickness of about 1 to 2 mm, and is strong against the concrete wall material 10. Can be glued to.
【００１６】なお、本実施例では、足掛かりのための接
着剤13,14 として、同様にポリマーセメントからなる接
着剤を、予め、約 0.5 mm の厚さで、コンクリート製壁
材10の表面と、大型タイル11の背面に塗布して硬化さ
せ、その後、上記した大型タイル等用接着剤12を用い
て、大型タイル11をコンクリート製壁材10へ迅速かつ強
力に貼着することができる。In this embodiment, as the adhesives 13 and 14 for the stepping, an adhesive also made of polymer cement is preliminarily applied to the surface of the concrete wall material 10 with a thickness of about 0.5 mm. The large tile 11 can be applied to the back surface of the large tile 11 and cured, and then the large tile 11 can be quickly and strongly attached to the concrete wall material 10 using the adhesive 12 for large tiles and the like.
【００１７】即ち、本実施例で用いる大型タイル等用接
着剤12において、ポリマーセメントは粘着性があり、硬
化後は水の影響を受けにくい性質を有するものであり、
一方、セメント系急結剤は、ポリマーセメント中のセメ
ントと水和反応を起こして、初期材令ではカルシウムア
ルミネート水和物を生成し、長期材令ではカルシウムシ
リケート水和物と水酸化カルシウムとからなる長期的に
安定した水和物を生成することができるものである。That is, in the adhesive 12 for large tiles and the like used in this embodiment, the polymer cement is tacky and has a property of being less susceptible to water after curing,
On the other hand, the cement-based quick-setting agent causes a hydration reaction with the cement in the polymer cement to produce calcium aluminate hydrate in the early age, and calcium silicate hydrate and calcium hydroxide in the long age. It is possible to produce a stable hydrate consisting of
【００１８】従って、大型タイル11を圧着によってコン
クリート製壁材10へ接着した際、セメント急結剤が速や
かにポリマーセメント中のセメントを凝結するので、ポ
リマーセメントが硬化するまで、セメント急結剤の作用
によって、大型タイル11のずれを確実に防止することが
できる。その後、ポリマーセメントが十分に硬化する
と、長期的に安定した接着力を発揮するので、大型タイ
ル11を確実に長期間にわたって接着することができる。Therefore, when the large tile 11 is adhered to the concrete wall material 10 by pressure bonding, the cement quick-setting agent promptly sets the cement in the polymer cement, so that the cement quick-setting agent is not cured until the polymer cement is hardened. By the action, the displacement of the large tile 11 can be surely prevented. After that, when the polymer cement is sufficiently hardened, a stable adhesive force is exhibited for a long period of time, so that the large tile 11 can be reliably adhered for a long period of time.
【００１９】具体的には、450 mm×450 mm、厚さが12 m
m 、重量が７kg/ 枚の自然石からなる大型タイル11でも
容易かつ迅速に貼着することができる。Specifically, it is 450 mm × 450 mm and the thickness is 12 m.
Even large tiles 11 made of natural stone with a weight of 7 m and a weight of 7 kg / piece can be easily and quickly applied.
【００２０】これによって、従来不可欠であった掛止金
具等を不要とすることができる。As a result, it is possible to eliminate the previously required indispensable metal fittings and the like.
【００２１】次に、上記した大型タイル等用接着剤12の
製造に用いるポリマーセメントとしては、例えば、酸化
珪素、酸化カルシウム、酸化鉄を主成分とした主材Ｍ
に、少なくともアクリル酸エステル共重合体を主成分と
してなる複合ポリマーエマルジョンＰを４：１の混合比
率で混和して生成したものを用いることができ、以下
に、具体的成分及び配合割合を示す。Next, as the polymer cement used for manufacturing the above-mentioned adhesive 12 for large tiles, for example, a main material M containing silicon oxide, calcium oxide and iron oxide as main components is used.
Can be used by mixing the composite polymer emulsion P containing at least an acrylic ester copolymer as a main component at a mixing ratio of 4: 1. Specific components and blending ratios are shown below.
【００２２】 （複合ポリマーエマルジョンＰ) （実施例１） （実施例２） なお、上記白色セメントの成分重量比は、以下の通りで
あった。(Composite Polymer Emulsion P) (Example 1) (Example 2) The component weight ratio of the white cement was as follows.
【００２３】 ポリマーセメントは、複合ポリマーエマルジョンＰを攪
拌容器に入れ、主剤Ｍを徐々に加えながらハンドミキサ
ーで攪拌して製造した。[0023] The polymer cement was produced by putting the composite polymer emulsion P in a stirring container and stirring the main agent M gradually with a hand mixer.
【００２４】そして、このようにして製造したポリマー
セメント中に、セメント系急結剤を、上記した主剤Ｍ中
に含まれる白色セメントの全量に対して、５重量％添加
して混合して大型タイル等用接着剤12を製造した。Then, in the polymer cement thus produced, a cement type quick-setting agent is added in an amount of 5% by weight with respect to the total amount of the white cement contained in the above-mentioned main agent M and mixed to prepare a large tile. Adhesive 12 for equality was manufactured.
【００２５】ここで、セメント系急結剤としては、各種
形態のものを用いることができるが、本実施例では、以
下の組成のものを用いた。Here, various types of cement-type quick-setting agents can be used, but in this example, the one having the following composition was used.
【００２６】 また、上記組成において、Ｒ2 Ｏ＝Ｎａ2 Ｏ＋ 0.658Ｋ
2 Ｏである。[0026] Further, in the above composition, R 2 O = Na 2 O + 0.658K
2 O.
【００２７】さらに、上記セメント系急結剤の物理的性
質は、かさ比重が 0.8〜1.0 であり、真比重が 2.7であ
り、粉末度 (cm2/g)が 5360 である。Further, the physical properties of the cement type quick-setting admixture are such that the bulk specific gravity is 0.8 to 1.0, the true specific gravity is 2.7, and the fineness (cm 2 / g) is 5360.
【００２８】そして、かかるセメント系急結剤は、温度
が20°で湿度が50％の雰囲気で、混練後15分で大型タイ
ル等用接着剤12を凝結することができた。The cement type quick setting agent was able to set the adhesive 12 for a large tile or the like 15 minutes after the kneading in an atmosphere having a temperature of 20 ° and a humidity of 50%.
【００２９】かかる大型タイル等用接着剤12について耐
水性試験を行ったところ、常態付着強度は 27.9 kg/cm2
であり、水中浸漬 3000 時間後の付着強度も同様に 27.
3 kg/cm2であった。即ち、付着強度は殆ど変わっておら
ず、大型タイル等用接着剤12は大型タイル11を長期間に
わたって安全に貼着することができることが分かる。A water resistance test was conducted on the adhesive 12 for large tiles, etc., and the adhesive strength under normal conditions was 27.9 kg / cm 2
Similarly, the adhesion strength after 3000 hours of immersion in water is 27.
It was 3 kg / cm 2 . That is, it can be seen that the adhesive strength remains almost unchanged, and the large-sized tile adhesive 12 can safely adhere the large-sized tile 11 for a long period of time.
【００３０】[0030]
【効果】本発明に係る大型タイル等用接着剤は、ポリマ
ーセメントとセメント系急結剤との混和物からなる。こ
こに、ポリマーセメントとは、粘着性があり、硬化後は
水の影響を受けにくいポリマーセメントをいい、セメン
ト急結剤としては、セメントと水和反応を生じ、初期材
令ではカルシウムアルミネート水和物を形成し、長期材
令ではカルシウムシリケート水和物と水酸化カルシウム
を生成する、長期的に安定した水和物を生成可能なもの
である。[Effect] The adhesive for large tiles according to the present invention comprises a mixture of polymer cement and a cement-based quick-setting agent. Here, the polymer cement is a polymer cement that is sticky and is not easily affected by water after curing.As a cement quick-setting agent, a hydration reaction occurs with the cement, and calcium aluminate water is used in the initial age. It is capable of forming a hydrate, which forms a hydrate and produces calcium silicate hydrate and calcium hydroxide in the long-term age, which is stable in the long term.
【００３１】従って、大型タイルを圧着によってコンク
リート製壁材へ接着した際、セメント急結剤が速やかに
ポリマーセメント中のセメントを凝結するので、ポリマ
ーセメントが硬化するまで、セメント急結剤の作用によ
って、大型タイルのずれを確実に防止することができ
る。その後、ポリマーセメントが十分に硬化すると、長
期的に安定した接着力を発揮するので、大型タイルを確
実に長期間にわたって接着することができるTherefore, when a large tile is adhered to a concrete wall material by crimping, the cement quick-setting agent rapidly sets the cement in the polymer cement, so that the action of the cement quick-setting agent until the polymer cement hardens. Therefore, it is possible to reliably prevent the displacement of the large tile. After that, when the polymer cement is sufficiently hardened, it exerts a stable adhesive force in the long term, so that large tiles can be reliably adhered over a long period of time.
【図面の簡単な説明】[Brief description of drawings]
【図１】本発明に係る大型タイル等用接着剤による大型
タイルの貼着作業の説明図である。FIG. 1 is an explanatory diagram of a work of attaching a large tile with an adhesive for large tiles according to the present invention.
【図２】従来の大型タイルの貼着作業の説明図である。FIG. 2 is an explanatory view of a pasting work of a conventional large tile.
Ｐ 複合ポリマーエマルジョン Ｍ 主剤 10 コンクリート製壁材 11 大型タイル 12 大型タイル等用接着剤 13 接着剤 14 接着剤 P Complex polymer emulsion M Main agent 10 Concrete wall material 11 Large tile 12 Adhesive for large tile 13 Adhesive 14 Adhesive
Claims (2)
混和物からなる大型タイル等用接着剤。1. An adhesive for large tiles, which comprises a mixture of polymer cement and a cement-based quick-setting agent.
メント中のセメント量の３〜10重量％としたことを特徴
とする請求項１記載の大型タイル等用接着剤。2. The adhesive for large tiles according to claim 1, wherein the amount of the cement type quick-setting admixture is 3 to 10% by weight of the amount of cement in the polymer cement.