JP5248702B2 - Life support equipment - Google Patents

Description

  The present invention relates to a life support device that shields radiation such as gamma rays.

  Conventionally, in high radiation environments, radiation shielding means for protecting workers from radiation has been required.

  For example, radiation protection clothing that covers the entire body of the worker and a radiation shielding material that forms the radiation protection clothing are known (see, for example, Patent Documents 1 and 2).

  The invention described in Patent Document 1 uses a moisture permeable material for radiation protective clothing covering almost the entire body of the wearer. The invention described in Patent Document 2 is an air-conditioning garment that can be used for a protective garment, in which a plurality of spacers are attached to the inner surface of the garment body, and thereby air is circulated between the garment body and the body or underwear. It forms a flow passage. By the said structure, the protective clothing which concerns on invention of patent document 1 and 2 has a dehumidification function, and can reduce the discomfort of the wearer by sweating.

JP-A-10-197688 International Publication No. 2005/081822

  When wearing radiation protection clothing, it is necessary to send air for breathing skin between the radiation protection clothing and the wearer's body or oxygen for wearer's breathing. For this reason, the wearer needs to wear a life support device for blowing and exhausting air and oxygen separately from the radiation protective clothing.

  This life support device is a device that is used in an environment where there is a risk of exposure in the same manner as radiation protective clothing. For this reason, it is necessary to take measures to sufficiently shield radiation so that the wearer is not exposed via the life support device. For example, when water or oxygen is irradiated with neutrons contained in radiation, there is a possibility that physical properties will change with a low probability. In addition, fine substances contained in water and oxygen may be radioactively contaminated.

  However, Patent Documents 1 and 2 only disclose a technique related to radiation protective clothing, and do not consider the radiation shielding technique for the life support device described above.

  Therefore, an object of the present invention is to provide a life support device that suitably shields radiation such as neutron rays and gamma rays.

  In order to solve the above-described problems, a life support device according to the present invention includes an endothelial layer that shields scattered X-rays and electron beams, a mesentery layer that is laminated on the endothelial layer and shields gamma rays, and a mesothelial layer. It is characterized by comprising a radiation shielding material comprising a laminated epithelial layer that shields neutron rays, and life support means covered with the radiation shielding material.

  According to the life support device of the present invention, radiation such as neutron rays and gamma rays can be suitably shielded.

The block diagram of the life support apparatus in this embodiment. The functional block diagram of the life support apparatus in this embodiment. The front view of the radiation protection suit equipped with the life support device. The side view of the radiation protection suit equipped with the life support device. The rear view of the radiation protection suit equipped with the life support device. Sectional drawing of a radiation shielding material. VII-VII sectional view taken on the line of FIG. Sectional drawing of the outer skin part of a radiation protective suit. The enlarged view of the IX part of FIG. The flowchart which shows an example of the manufacturing method of a gamma ray shielding material. The flowchart which shows an example of the manufacturing method of the said scattering X-ray and an electron beam shielding material. The image of the scattering X-ray and electron beam shielding material obtained in Example 1. Sectional drawing of the space suit which can apply a life support device. The XIV partial enlarged view of FIG. It is a front view of the radiation protective suit which concerns on 2nd Embodiment. It is a right view of the radiation protective suit which concerns on 2nd Embodiment. It is a left view of the radiation protective suit which concerns on 2nd Embodiment. It is a rear view of the radiation protective suit which concerns on 2nd Embodiment. It is a block diagram of the life support apparatus used with the radiation protective suit which concerns on 2nd Embodiment.

  Embodiments of the present invention will be described with reference to the accompanying drawings.

  FIG. 1 is a configuration diagram of a life support device 1 in the present embodiment.

  FIG. 2 is a functional block diagram of the life support device 1 in the present embodiment.

  FIG. 3 is a front view of the radiation protective suit 30 to which the life support device 1 is attached.

  FIG. 4 is a side view of the radiation protective suit 30 to which the life support device 1 is attached.

  FIG. 5 is a rear view of the radiation protective suit 30 to which the life support device 1 is attached.

  The life support apparatus 1 in the present embodiment is used when working in a high radiation environment such as a nuclear power plant. The life support device 1 is used by being worn by a wearer (operator, wearer of the life support device 1) wearing the radiation protection suit 30. The life support device 1 is attached to the back side of the radiation protective suit 30 as shown in FIG. 5 by, for example, the attachment member 10 shown in FIG.

  As shown in FIG. 1, the life support device 1 includes a main oxygen tank 11, an air tank 12, a water supply tank 13, a respiratory circulation air cooling device 14, a carbon dioxide absorbent 15, and a device control unit 16. , A GPS (Global Positioning System) 17, a micropump unit 18, and a battery unit 19.

  The main oxygen tank (oxygen tank) 11 and the air tank 12 store oxygen and nitrogen, respectively. As shown in FIG. 2, oxygen and nitrogen supplied from the main oxygen tank 11 and the air tank 12 are mixed and used by the wearer as breathing air. Moreover, the air from the life support apparatus 1 is supplied to the supply port 61a provided inside the outer skin part 31 of the radiation protection suit 30 mentioned later for a wearer's skin respiration etc. FIG.

  The water supply tank 13 supplies water to the wearer. The respiratory circulation air cooling device 14 cools the air supplied from the main oxygen tank 11 and the air tank 12, the air exhausted from the radiation protective suit 30, and the water supplied from the water supply tank, thereby reducing the body temperature of the wearer. Adjust. Further, the breathing circulation air cooling device 14 circulates the air discharged by the wearer's breathing. The carbon dioxide absorbent 15 is a cassette type, and the carbon dioxide absorbent 15 mainly includes a carbon dioxide detector 15a and a carbon dioxide concentration adjuster 15b. It absorbs and recirculates carbon dioxide breathed (exhausted) by the wearer exhausted from the radiation protective suit 30.

  The device control unit (control unit) 16 is mainly electrically connected to an electric control unit 16 a provided in the main oxygen tank 11, the air tank 12, the respiratory circulation air cooling device 14, and the carbon dioxide absorbent 15 of the life support device 1. A signal is transmitted and each part is controlled.

  For example, the device control unit 16 controls the wearer wearing the life support device 1 to supply oxygen in the main oxygen tank 11. The device control unit 16 controls to absorb the carbon dioxide breathed by the wearer. The device control unit 16 circulates the air discharged by the wearer's breathing by controlling the breathing circulation air cooling device 14.

  The GPS (position information acquisition means) 17 detects the current position of the wearer of the life support apparatus 1 (the wearer of the radiation protective suit 30). The device control unit 16 and the GPS 17 can communicate with the management base wirelessly or by wire, and the state of each device of the life support device 1 can be appropriately transmitted to the management base. The management base is a facility that is provided when an operator performs an operation to manage the operation in an integrated manner.

  The micro pump unit 18 supplies air and moisture to a predetermined supply destination. The battery unit 19 supplies power for driving to each part in the life support apparatus 1 that operates electrically.

  The life support device 1 includes an air supply side connection component 21, an exhaust side connection component 22, a helmet side air supply side connection component 23, and a helmet side exhaust side for supplying or exhausting air and moisture to and from the radiation protective suit 30. It has a connection part 24 and a water supply side connection part 25.

  Next, the radiation protective suit 30 to which the life support apparatus 1 in this embodiment is attached will be described.

  As shown in FIG. 3 to FIG. 5, the radiation protective clothing 30 includes an outer skin portion 31 that covers the wearer's head, upper limbs, trunk, and lower limbs, and a helmet 32 that protects the head from above the outer skin portion 31. A glove 34 that protects both hands and a boot 35 that protects both feet.

  The outer skin portion 31 and the helmet 32 are joined by a joint portion 37, the outer skin portion 31 and the globe 34 are joined by a joint portion 38, and the outer skin portion 31 and the boot 35 are joined by a joint portion 39. Further, knee pads 40 (see FIG. 3) and elbow pads 41 (see FIG. 5) are provided at portions corresponding to the wearer's knees and elbows.

  The life support device 1 and the radiation protective clothing 30 (the outer skin portion 31, the glove 34, the boot 35, the knee pad 40 and the elbow pad 41) having such a configuration are formed by the radiation shielding material 51.

  FIG. 6 is a cross-sectional view of the radiation shielding material 51.

  7 is a cross-sectional view taken along line VII-VII in FIG.

  The radiation shielding material 51 is formed by a three-layer structure having an endothelial layer 52, a mesothelial layer 53, and an epithelial layer 54. The radiation shielding material 51 is designed to shield radiation incident from the epithelial layer 54 side. The epithelial layer 54 shields neutron rays, and the mesothelial layer 53 shields gamma rays. When gamma rays come into contact with a substance, scattered X-rays and electron beams are generated by the photoelectric effect and Compton scattering. Therefore, it is configured so that the scattered X-rays and electron beams that may be generated when the gamma rays are shielded by the mesothelial layer 53 are shielded by the endothelial layer 52.

  A mesothelial layer 53 is laminated on the endothelial layer 52. The mesothelial layer 53 faces the endothelial layer 52 and extends while holding a predetermined space between the inner skin layer 52, a partition wall portion 57 extending from the outer layer portion 56 toward the endothelial layer 52, and the partition wall A plurality of hollow layers 55 defined by the portion 57 and the outer layer portion 56 are provided.

  As shown in FIG. 7, the partition wall portion 57 partitions the space between the inner skin layer 52 and the outer layer portion 56 of the mesothelial layer 53 to form a plurality of hollow layers 55 made of gas. A communication hole 57 a is formed in the partition wall portion 57 so that the filler in the plurality of adjacent hollow layers 55 can flow. In the case where the step of filling the hollow layer 55 with a specific filler is not performed, the hollow layer 55 is filled with air when the mesothelial layer 53 is laminated on the endothelial layer 52.

  As shown in FIG. 7, in the present embodiment, the partition wall 57 is formed in a lattice shape. The partition wall 57 holds the space, that is, the hollow layer 55 between the inner skin layer 52 and the outer layer portion 56 of the mesothelial layer 53, and contributes to the reinforcement of the three-layer structure.

  An epithelial layer 54 extending along the outer surface is laminated on the outer surface of the outer layer portion 56 of the mesothelial layer 53. As shown in FIG. 6, the cross section of the outer layer portion 56 and the epithelial layer 54 of the mesothelial layer 53 has a wave shape that protrudes toward the epithelial layer 54 between adjacent partition walls 57. As an example, the thickness l1 of the endothelial layer 52 is 2 mm, the thickness l2 in the partition wall portion 57 of the mesothelial layer 53 is 8 mm, and the thickness l3 of the epithelial layer 54 is 3 mm.

  The epithelial layer 54 is formed by mixing silicon rubber with boron that absorbs neutron beams.

  The middle layer 53 is formed by mixing a unique gamma ray shielding material with silicon rubber. This unique gamma ray shielding material has at least one of bismuth and titanium, silicon, and strontium as essential elements. This gamma ray shielding material will be described in detail later.

  The endothelium layer 52 is formed by mixing silicon rubber with a unique scattering X-ray and electron beam shielding material. This unique scattering X-ray and electron beam shielding material has at least silicon, strontium, magnesium, europium and dysprosium as essential elements. The scattered X-ray and electron beam shielding material will be described in detail later.

  For each of the epithelial layer 54, the mesothelial layer 53, and the endothelial layer 52, silicon rubber and each of the above mixtures are kneaded, vulcanized for molding, and subjected to a crosslinking reaction by applying heat and pressure. The hardness of the silicon rubber can be adjusted. For example, it can be made softer or harder by adjusting the mixing volume ratio of the silicon rubber and the above-mentioned mixture added to the silicon rubber. As an example, the mixing volume ratio of silicon rubber and the mixture added to the silicon rubber is 40:60. The epithelial layer 54 and the endothelial layer 52 are formed in a sheet shape. For the inner skin layer 53, the outer layer portion 56 is formed into a sheet shape, and the partition wall portion 57 protruding from the outer layer portion 56 is integrally formed with the outer layer portion 56 using a mold.

  A sheet-shaped epithelial layer 54 is laminated along the surface of the outer layer portion 56 of the formed mesothelial layer 53. Next, the end portion of the partition wall portion 57 of the mesothelial layer 53 is adhered to the surface of the endothelial layer 52 formed in a sheet shape, thereby laminating the mesothelial layer 53 on the endothelial layer 52. During lamination, the distance between the end portions of the partition wall portion 57 is narrowed, so that the outer layer portion 56 and the epithelial layer 54 of the mesothelial layer 53 can be bent toward the epithelial layer 54 side between the end portions of the partition wall portion 57. it can. Thereby, as shown in FIG. 7, the outer layer part 56 of the mesothelial layer 53 and the cross section of the epithelial layer 54 are formed in a wave shape.

  The life support device 1 and the radiation protective clothing 30 (the outer skin portion 31, the glove 34, the boot 35, the knee pad 40 and the elbow pad 41) are covered (formed) with such a radiation shielding material 51, Any entry of radiation is blocked.

  The outer skin portion 31 of the radiation protective suit 30 will be described in detail.

  FIG. 8 is a cross-sectional view of the outer skin portion 31 of the radiation protective suit 30. In addition, illustration of the helmet 32 is abbreviate | omitted for description.

  FIG. 9 is an enlarged view of a portion IX in FIG.

  The outer skin part 31 has a space 63 between the body surface 62 of the wearer. In addition, illustration of the underwear 64 (refer FIG. 8) which covers a wearer's body surface 62 is abbreviate | omitted for description.

  The endothelial layer 52 formed of silicon rubber, scattered X-rays, and electron beam shielding material also has a heat insulating function. On the outer surface of the endothelial layer 52, that is, on the surface facing the body surface 62 of the wearer, a fiber cloth such as nylon fiber (not shown) is attached inside. Compared with the case where the outer surface of the endothelial layer 52 formed of silicon rubber or the like is exposed, the touch is improved by attaching the fiber cloth, and the radiation protective clothing 30 is easily attached and detached. Further, by using nylon fiber, moisture absorption, quick drying, antibacterial, deodorizing, and heat retaining functions can be added.

  As shown in FIG. 9, a supply port 61 a and an exhaust port 61 b are provided on the outer surface of the endothelial layer 52 with the fiber cloth attached thereto. Although only the supply port 61a is shown in FIG. 9, the exhaust port 61b is provided on the outer surface of the endothelial layer 52 in the left elbow portion that is symmetrical to the IX portion in FIG.

  As shown in FIG. 5, the supply port 61a supplies the air supplied from the life support device 1 to the space 63 between the body surface 62 of the wearer via the supply tube 45a. The exhaust port 61b exhausts the air exhausted from the space 63 through the exhaust tube 45b.

  The supply tube 45 a and the exhaust tube 45 b are fixed to the outer surface of the endothelial layer 52. One end of the supply tube 45 a is connected to the supply side connection component 21 (see FIG. 2) of the life support device 1, and the other end is connected to the supply port 61 a of the radiation protective clothing 30. One end of the exhaust tube 45 b is connected to the exhaust side connection component 22 (see FIG. 2) of the life support device 1, and the other end is connected to the exhaust port 61 b of the radiation protective suit 30.

  By supplying air from the supply port 61a and exhausting air from the exhaust port 61b, the skin respiration of the wearer can be maintained. Moreover, a wearer's body temperature can also be adjusted by adjusting the temperature of the air to supply.

  As shown in FIG. 5, the supply tube 45 a and the exhaust tube 45 b are also connected to a supply port 61 a and an exhaust port 61 b provided in an in-helmet breathing mechanism 32 a (see FIG. 2) provided in the helmet 32. The wearer's breathing air is sent to the breathing mechanism in the helmet 32 through the helmet-side air supply-side connection component 23 and a supply tube (both not shown) connected to the supply port. The breathing air is exhausted from the breathing mechanism in the helmet 32 via the helmet-side exhaust-side connecting component 24 and an exhaust tube (both not shown) connected to the exhaust port.

  The helmet 32 is also provided with a water supply tube (not shown). One end of the water supply tube is connected to the water supply side connection component 25 (FIG. 2), and the other end is connected to a water supply port (not shown) of the radiation protective suit 30.

  In the present embodiment, the hollow layer 55 is filled with helium gas. As a result, the weight of the radiation protective suit 30 can be reduced, and workability is improved. In addition, since the communication hole 57 a is formed in the partition wall 57 that defines the hollow layer 55, helium gas filled in each hollow layer 55 can flow between the hollow layers 55. Therefore, the radiation shielding material 51 can be easily deformed and the wearer's mobility is enhanced. In addition, in the site | part 31a corresponding to a wearer's joint shown in FIG. 3, the quantity of helium gas with which the hollow layer 55 is filled is reduced rather than another site | part. Therefore, the radiation shielding material 51 in the part 31a is easily deformed as compared with other parts. Thereby, a wearer's mobility can further be improved.

  For the knee pad 40 and the elbow pad 41, a radiation shielding material 51 having higher hardness than the outer skin part 31 is used for protecting the knee and elbow. As described above, when the epithelial layer 54, the mesothelial layer 53, and the endothelial layer 52 are formed, the hardness of the radiation shielding material 51 can be increased by changing the ratio of the mixture mixed into the silicon rubber.

  The life support device 1 in the present embodiment has a three-layer structure including an epithelial layer 54 that shields neutron rays, a mesothelial layer 53 that shields gamma rays, and an endothelial layer 52 that shields scattered X-rays and electron beams from the outside. The incident neutron and gamma rays are shielded, and the scattered X-rays and electron beams that may be generated when the gamma rays are shielded can also be shielded. Note that alpha rays and beta rays having a material transmission ability lower than that of neutron rays and gamma rays are also shielded by the radiation shielding material 51.

  In particular, the life support device 1 has a change in physical properties caused by irradiation of water or oxygen supplied to workers in a high radiation environment to which the life support device 1 is attached, or a minute amount contained in water or oxygen. The radioactive contamination of the substance can be suitably suppressed. As a result, the life support device 1 can ensure the safety of the worker.

  In addition, since the life support device 1 includes the GPS 17 and is configured to be able to communicate with the management base, the life support device 1 can grasp the worker's state and can further ensure the worker's safety.

[Gamma ray shielding material]
The unique gamma ray shielding material described above has at least one of bismuth and titanium, silicon, and strontium as essential elements. For example, it contains 20 to 50% by mass of bismuth, 3 to 25% by mass of silicon, and 20 to 50% by mass of strontium. As an example, it contains 20 to 50% by mass of titanium, 3 to 25% by mass of silicon, and 20 to 50% by mass of strontium.

  You may obtain by baking at least 1 sort (s) of bismuth oxide, titanium, and titanium oxide, silicon oxide, and strontium carbonate. When manufacturing the said gamma ray shielding material, you may provide the baking process of mixing and baking at least 1 sort (s) of a bismuth compound and a titanium compound, a silicon compound, and a strontium compound. As an example, this baking step is a step of further mixing and baking boric acid in addition to the above compound.

  Hereinafter, the gamma ray shielding material will be described in detail.

  The gamma ray shielding material has at least one of bismuth and titanium, silicon, and strontium as essential elements. By combining these elements, gamma rays can be well shielded. Moreover, since it is a silicate compound, its specific gravity is lighter than that of lead, and it is also excellent in workability.

  The content of at least one of bismuth (Bi) and titanium (Ti) is, for example, 20 to 50% by mass, preferably 30 to 40% by mass.

  The content of silicon (Si) is, for example, 3 to 25% by mass, preferably 5 to 15% by mass. Strontium (Sr) content is 20-50 mass%, for example, Preferably it is 25-40 mass%.

The gamma ray shielding material may contain oxygen atoms (preferably 5 to 30% by mass, more preferably 10 to 20% by mass) in addition to the above essential elements. Further, it may contain a boron atom, a radiation absorbing atom other than the above (for example, a lanthanoid element such as erbium) or the like, and may further contain impurities inevitable in production.
The gamma ray shielding material preferably contains substantially no lead element from the viewpoint of toxicity. For example, it is 5% by mass or less, preferably 1% by mass or less.

  The shape of the gamma ray shielding material may be appropriately determined according to the method of using the shielding material, and examples thereof include granular (powder), pellet shape, lump shape, film shape, plate shape, and the like. In particular, the shielding material can be powder-processed and mixed with other organic substances (powdered, fibrous) or the like and used for various shielding applications.

  In the case of granular, for example, the average particle diameter may be 0.1 μm to 1000 μm, preferably 1 μm to 100 μm.

  In addition, the gamma ray shielding material may be used alone as a compound containing the essential elements, for example, water, organic solvent (alcohol, ether, etc.), surfactant, resin binder, inorganic particles, organic particles. They may be used in combination with additives such as gamma ray shielding materials other than the above-mentioned original gamma ray shielding materials.

  The gamma ray shielding material can be used in various forms for applications that shield (protect) radiation. For example, it can be used in protective apron, medical apron, protective suit, space suit, wallpaper, exterior wall surface, roofing material, cosmetics, sunscreen, facial cream, medical equipment (mammography, etc.) and the like.

  The suitable manufacturing method of the said gamma ray shielding material is equipped with the baking process of mixing and baking at least 1 sort (s) of a bismuth compound and a titanium compound, a silicon compound, and a strontium compound.

FIG. 10 is a flowchart showing an example of a method for manufacturing the gamma ray shielding material. Specifically, for example,
(I) at least one of bismuth oxide (Bi ₂ O ₃ ), titanium and titanium oxide,
(Ii) silicon oxide, and (iii) strontium carbonate (SrCO ₃ ),
It can manufacture by passing through the process of mixing and sintering. The titanium oxide may be any of titanium monoxide (TiO) and titanium dioxide (TiO ₂ ). The silicon oxide may be any of silicon dioxide (SiO ₂ ) and silicon monoxide (SiO), but as an example, SiO ₂ is preferably used.
The blending ratio is not limited, but for example,
(1) Bismuth oxide 30-60% by mass, preferably 40-50% by mass
5-30% by mass of silicon oxide, preferably 10-20% by mass,
Strontium carbonate 30-60% by weight, preferably 40-50% by weight,
(2) Titanium or titanium oxide 30 to 60% by mass, preferably 40 to 50% by mass
5-30% by mass of silicon oxide, preferably 10-20% by mass,
Strontium carbonate 30-60% by weight, preferably 40-50% by weight,
And so on.

In addition to the raw materials, a boron compound such as boric acid (H ₃ BO ₃ ) may be further added. Thereby, the electron transfer between metals can be made easy at the time of baking, and a redox action can be promoted. Although the compounding quantity of a boric acid is not limited, Preferably it is 0.1-5 mass%, More preferably, it is 0.5-3 mass%.

  After mixing, the raw material may be pulverized by a pulverizer such as a ball mill or a rod mill, or may not be pulverized, but is preferably pulverized.

  The firing temperature may be, for example, 500 to 2000 ° C., preferably 800 to 1500 ° C. in an electric furnace.

  The firing atmosphere may be either an air atmosphere or an inert gas atmosphere, but is preferably an air atmosphere.

  The firing time may be appropriately determined according to the firing temperature, firing atmosphere, and the like, but may be, for example, 10 minutes to 10 hours, preferably 30 minutes to 5 hours. A plasma sintering step may be performed instead of or after the firing step. Thereby, the absorption amount of the gamma ray of the gamma ray shielding material obtained can be improved. Plasma sintering may be performed according to a conventional method. For example, it may be performed at 500 to 2000 ° C. (preferably 700 to 1500 ° C.) with a plasma sintering machine. Although what is necessary is just to determine sintering time suitably according to sintering temperature, For example, 5 minutes-2 hours, Preferably what is necessary is just to be 10 minutes-1 hour.

  The gamma ray shielding material will be described in more detail below using examples. The gamma ray shielding material is not limited to the following examples.

<Example 1 of gamma ray shielding material>
SiO ₂ (manufactured by Iwai Chemicals) 12.58% by mass, SrCO ₃ (manufactured by Honjo Chemical Co., Ltd.) 42.42% by mass, Bi ₂ O ₃ (manufactured by Iwai Chemicals) 43.85% by mass, and H ₃ BO ₃ 1.15% by mass (manufactured by Iwai Chemicals) was placed in a ball mill mixer and mixed for 1 hour. Next, it was placed in an electric furnace and baked in the air at 900 ° C. for 2 hours. After firing, it was naturally cooled to room temperature and pulverized with a ball mill mixer until the average particle size became 7 μm (see FIG. 10). Thereby, the gamma ray shielding material of Example 1 was obtained. In addition, when the composition ratio of the gamma ray shielding material of Example 1 was measured, Bi was 37.05 mass%, Si was 9.68 mass%, Sr was 35.12 mass%, O (oxygen atom) was 13.94 mass%, and the rest It was an impurity. When the specific gravity was measured, it was 4.78 g / cm ³ . When measured by fluorescent X-ray analysis, it was estimated that Example 1 was Bi ₂ O ₃ + SrSiO ₃ .
<Example 2 of gamma ray shielding material>
SiO ₂ (manufactured by Iwai Chemicals) 12.58% by mass, SrCO ₃ manufactured by Honjo Chemical Co., Ltd. 42.42% by mass, Ti (manufactured by Tohotech) 43.85% by mass, and H ₃ BO ₃ (Iwai Chemicals) 1.15% by mass was put into a ball mill mixer and mixed for 1 hour. Subsequently, it sintered at 1000 degreeC with the plasma sintering machine (The product name "SPS-1030" by SPS Shintec Co., Ltd.) for about 30 minutes. Thereby, the gamma ray shielding material (pellet shape, thickness 3 mm) of Example 2 was obtained.
In addition, when the composition ratio of the gamma ray shielding material of Example 2 was measured, it was Ti 37.95 mass%, Si 6.45 mass%, Sr 27.37 mass%, O (oxygen atom) 17.73 mass%, and the rest It was an impurity.
When the specific gravity was measured, it was 4.67 g / cm ³ . When measured by fluorescent X-ray analysis, it was estimated that Example 2 was SrTiO _2.6 + TiO + SrSiO ₃ .
<Comparative example of gamma ray shielding material>
A lead plate (thickness 1 mm, commercial product) and an aluminum plate (thickness 3 mm, commercial product) were used as Comparative Example 1 and Comparative Example 2, respectively.

<Gamma ray shielding performance test of gamma ray shielding material>
The gamma ray shielding material of Example 1 was further processed into a pellet shape (thickness 3 mm) by plasma sintering. Under the following conditions, the samples of Examples and Comparative Examples were irradiated with gamma rays, and the shielding rate was measured. The results are shown in Table 1.

Conditions (Laser: CO ₂ , Power: 1W, Magnet: 10A, Energy: 1.7MeV,
(Current: 200mA, Coll: 3mmφ, DTCT: NaI6)

  From the above results, in the gamma ray shielding performance, Examples 1 and 2 of the unique gamma ray shielding material are not as effective as the lead plate (Comparative Example 1) as the gamma ray shielding performance in consideration of the thickness. It can be seen that it has a sufficiently high shielding rate at a practical thickness and has a good gamma ray shielding ability. In particular, when compared with the aluminum of Comparative Example 2, it can be seen that it exhibits a higher shielding rate and has a sufficient gamma ray shielding ability.

  The original gamma ray shielding material has a specific gravity that is significantly lighter than the specific gravity of lead (11.34), can be easily deformed into a granular or plate shape, and has excellent workability. Therefore, it turns out that it can be used for various uses and forms.

The unique gamma ray shielding material can also shield scattered X-rays and electron beams.
[Scattering X-ray and electron beam shielding material]
The unique scattering X-ray and electron beam shielding materials described above have at least silicon, strontium, magnesium, europium and dysprosium as essential elements. For example, silicon 5-30 mass%, strontium 30-60 mass%, magnesium 1-20 mass%, europium 0.1-5 mass%, and dysprosium 0.1-5 mass% are contained. As an example, it is obtained by firing at least silicon oxide, strontium carbonate, magnesium oxide, europium oxide and dysprosium oxide. In this case, after firing, plasma sintering may be performed to obtain at least silicon oxide, strontium carbonate, magnesium oxide, europium oxide, and dysprosium oxide. When manufacturing the said scattering X-ray and an electron beam shielding material, the silicon | silicone compound, a strontium compound, a magnesium compound, a europium compound, and a dysprosium compound are mixed, for example, and the baking process of baking is provided. The baking step may be a step of mixing and baking boric acid in addition to the above compound. Furthermore, you may provide the process of plasma-sintering.

  Hereinafter, the scattering X-ray and the electron beam shielding material will be described in detail.

  The scattered X-ray and electron beam shielding material has at least silicon, strontium, magnesium, europium and dysprosium as essential elements. By combining these elements, X-rays can be shielded at a practical level. It can also absorb ultraviolet rays. Furthermore, since it is a silicate-based compound, it has a lighter specific gravity than lead and is excellent in workability.

The content of silicon (Si) is preferably 5 to 30% by mass, more preferably 10 to 20% by mass.
The content of strontium (Sr) is preferably 30 to 60% by mass, more preferably 40 to 50% by mass.

The content of magnesium (Mg) is preferably 1 to 20% by mass, more preferably 5 to 10% by mass.
The content of europium (Eu) is preferably 0.1 to 5% by mass, more preferably 0.5 to 3% by mass.

  The content of dysprosium (Dy) is preferably 0.1 to 5% by mass, more preferably 0.5 to 3% by mass.

  The scattered X-ray and electron beam shielding material may contain oxygen atoms (preferably 10 to 50% by mass, more preferably 20 to 40% by mass) in addition to the essential elements. Further, it may contain a boron atom, a radiation absorbing atom other than the above (for example, a lanthanoid element such as erbium) or the like, and may further contain impurities inevitable in production.

  In the said scattering X-ray and electron beam shielding material, it is preferable that lead element is not included substantially from a harmful viewpoint. For example, it is 5% by mass or less, preferably 1% by mass or less.

  The shape of the scattering X-ray and the electron beam shielding material may be appropriately determined according to the method of using the shielding material, and examples thereof include granular (powder), pellet, lump, film, and plate. . In particular, the shielding material can be powder-processed and mixed with other organic substances (powdered, fibrous) or the like and used for various shielding applications.

  In the case of granular, for example, the average particle diameter may be 0.1 μm to 1000 μm, preferably 1 μm to 100 μm.

  In addition, the scattered X-ray and electron beam shielding material may be used alone as a compound containing the essential elements, for example, water, organic solvent (alcohol, ether, etc.), surfactant, resin binder, inorganic You may use together with additives, such as particle | grains, organic particle | grains, a scattering X-ray other than the said original scattering X-ray, and an electron beam shielding material, and an electron beam shielding material. In particular, in the unique scattering X-ray and electron beam shielding material, it is preferable to use a titanium compound such as titanium or titanium oxide in combination. Thereby, the ultraviolet shielding property can be further improved.

  The unique scattering X-ray and electron beam shielding material can be used in various forms for the purpose of shielding (protecting) radiation. For example, it can be used in protective apron, medical apron, protective suit, space suit, wallpaper, exterior wall surface, roofing material, cosmetics, sunscreen, facial cream, medical equipment (mammography, etc.) and the like. Since not only X-rays but also ultraviolet rays can be shielded, it can be applied to cosmetics, sunscreens and the like.

  The manufacturing method of the said scattering X-ray and an electron beam shielding material is equipped with the baking process of mixing and baking a silicon compound, a strontium compound, a magnesium compound, a europium compound, and a dysprosium compound.

  FIG. 11 is a flowchart showing an example of a method for producing the scattered X-ray and electron beam shielding material.

Specifically, for example, a step of mixing and sintering silicon oxide, strontium carbonate (SrCO ₃ ), magnesium oxide (MgO), europium oxide (Eu ₂ O ₃ ), and dysprosium oxide (Dy ₂ O ₃ ). It can manufacture by passing.

The silicon oxide may be any of silicon dioxide (SiO ₂ ), silicon monoxide (SiO), etc., but as an example, SiO 2 is preferably used.

The blending ratio is not limited, but for example,
20 to 60% by mass of silicon oxide, preferably 30 to 50% by mass,
20-60% by weight of strontium carbonate, preferably 30-50% by weight,
Magnesium oxide 5 to 40% by mass, preferably 10 to 30% by mass,
Europium oxide 0.1-5% by weight, preferably 0.2-1% by weight and dysprosium oxide 0.1-5% by weight, preferably 0.2-1% by weight,
And it is sufficient.

In addition to the raw materials, a boron compound such as boric acid (H ₃ BO ₃ ) may be further added. Thereby, the electron transfer between metals can be made easy at the time of baking, and a redox action can be promoted. Although the compounding quantity of a boric acid is not limited, Preferably it is 0.1-5 mass%, More preferably, it is 0.5-3 mass%.

  After mixing, the raw material may be pulverized by a pulverizer such as a ball mill or a rod mill, or may not be pulverized, but is preferably pulverized.

  The firing temperature may be, for example, 500 to 2000 ° C., preferably 1000 to 1500 ° C. in an electric furnace.

  The firing atmosphere may be either an air atmosphere or an inert gas atmosphere, but is preferably an air atmosphere.

  The firing time may be appropriately determined according to the firing temperature, firing atmosphere, and the like, but may be, for example, 10 minutes to 10 hours, preferably 30 minutes to 5 hours.

  Moreover, it is preferable to add a plasma sintering process after the said baking process. Thereby, the absorption amount of the X-rays of the obtained scattering X-rays and electron beam shielding material can be improved.

Plasma sintering may be performed according to a conventional method. For example, it may be performed at 500 to 2000 ° C. (preferably 700 to 1500 ° C.) with a plasma sintering machine.
Although what is necessary is just to determine sintering time suitably according to sintering temperature, For example, 5 minutes-2 hours, Preferably what is necessary is just to be 10 minutes-1 hour.

  The scattering X-ray and electron beam shielding material will be described in more detail below using examples. The scattered X-rays and electron beam shielding materials are not limited to the following examples.

<Example 1 of scattering X-ray and electron beam shielding material>
SiO ₂ (manufactured by Iwai Chemicals) 40% by mass, SrCO ₃ (manufactured by Honjo Chemical Co., Ltd.) 38.2% by mass, MgO (manufactured by Ube Materials) 20% by mass, Eu ₂ O ₃ (manufactured by Neomag) 0. 4% by mass, 0.4% by mass of Dy ₂ O ₃ (manufactured by Neomag) and 1% by mass of H ₃ BO ₃ (manufactured by Iwai Chemicals) were placed in a ball mill mixer and mixed for 1 hour. Next, it was put in an electric furnace and fired under conditions of 1300 ° C. and 2 hours in an air atmosphere. After firing, it was naturally cooled to room temperature and pulverized with a ball mill mixer until the average particle size became 7 μm (see FIG. 11). Thereby, the scattered X-ray and electron beam shielding material of Example 1 were obtained. FIG. 12 is an image of the scattered X-ray and electron beam shielding material obtained in Example 1.

  In addition, when the composition ratio of the scattered X-ray and the electron beam shielding material of Example 1 was measured, Si 13.3% by mass, Sr 42.4% by mass, Mg 6.23% by mass, Eu 0.84% by mass, Dy 1.83% by mass. , O (oxygen atom) 31.3% by mass, and the rest were impurities.

When the specific gravity was measured, it was 3.7 g / cm ³ . When measured by qualitative analysis and X-ray fluorescence analysis using an X-ray diffractometer, it was estimated that Example 1 was Sr ₂ MgSi ₂ O7 · Eu ³⁺ , Dy ³⁺ .

<Example 2 of scattering X-ray and electron beam shielding material>
The scattered X-rays and electron beam shielding material obtained in Example 1 were further sintered at 1000 ° C. for about 30 minutes with a plasma sintering machine (product name “SPS-1030” manufactured by SPS Shintec Co., Ltd.). After sintering, it was naturally cooled to room temperature to obtain the scattered X-ray and electron beam shielding material (pellet shape, thickness 3 mm) of Example 2.

<Comparative example of scattering X-ray and electron beam shielding material>
A lead plate (thickness 0.3 mm, commercial product) and an aluminum plate (thickness 3 mm, commercial product) were used as Comparative Example 1 and Comparative Example 2, respectively.

<X-ray shielding performance of scattered X-rays and electron beam shielding materials (measurement of X-ray transmittance)>
The scattered X-ray and electron beam shielding material of Example 1 were further processed into a pellet shape (thickness 3.95 mm) with a press. By the transmission method, the X-ray transmittance of the samples of Examples 1 and 2 and Comparative Examples 1 and 2 was measured under the condition of a measurement energy of 50 keV, and the linear absorption coefficient was calculated from the transmittance. The linear absorption coefficient is calculated by dividing the natural logarithm of transmittance by the thickness (cm) of the sample. The obtained measurement results are shown in Table 2.

<Ultraviolet shielding ability of scattering X-ray and electron beam shielding material: ultraviolet transmission measurement>
The ultraviolet transmittance of Example 1 was measured with an ultraviolet-visible spectrophotometer (UV2400PC, manufactured by Shimadzu Corporation). As a result, the transmittance was 20% or less in the wavelength range of 250 nm to 400 nm.

  From the above results, in the X-ray transmittance measurement, Examples 1 and 2 do not reach the lead which is very excellent as the X-ray shielding material of Comparative Example 1, but have a sufficiently low transmittance at a practical thickness. It can be obtained and has a good linear absorption coefficient. In particular, when compared with the aluminum of Comparative Example 2, it can be seen that it has a sufficiently good linear absorption coefficient.

  In addition, it can be seen that Example 1 of the unique scattering X-ray and electron beam shielding material has a good ultraviolet shielding performance because of its low ultraviolet transmittance. Furthermore, it is also effective for electron beams.

  In addition, the unique scattering X-ray and electron beam shielding material has a specific gravity that is significantly lighter than the specific gravity of lead (11.34), can be easily deformed into a granular or plate shape, and has excellent workability. Therefore, it turns out that it can be used for various uses and forms.

  Although the embodiments of the present invention have been described above, the present invention is not limited to the above-described embodiments, and various modifications and changes can be made based on the technical idea of the present invention. As an example, the gamma ray shielding function may be further enhanced by filling the hollow layer 55 with a substance containing a gamma ray shielding material. As another example, the hollow layer 55 may not be formed in the mesothelial layer 53, and the mesothelial layer 53 may be formed in a sheet shape in the same manner as the endothelial layer 52 and the epithelial layer 54.

  For example, the epithelial layer 54 may be added with beryllium, cadmium, gadolinium, or the like, instead of boron, as a mixture added to silicon rubber.

  As described above, the gamma ray shielding material used as an essential element for forming the mesothelium layer 53 having at least one of bismuth and titanium, silicon, and strontium also has a function of shielding scattered X-rays and electron beams. Therefore, when forming the endothelial layer 52, silicon rubber may be mixed with at least one of bismuth and titanium, silicon, and strontium. That is, the endothelial layer 52 may be formed of the same material as the mesothelial layer 53.

  In the radiation protective suit 30, an airtight maintenance layer for preventing oxygen leakage due to internal pressure may be provided between the inner skin layer 52 of the outer skin portion 31 and the body surface 62 of the wearer. In this case, the supply port 61 a for supplying air is provided on the surface of the airtight maintaining layer so as to supply air between the airtight maintaining layer and the body surface 62. Similarly, in the space suit 100 according to the third embodiment, an airtight maintenance layer may be provided between the radiation protection unit 102 and the cooling undergarment 103. Moreover, you may apply the life support apparatus 1 to a space suit.

  FIG. 13 is a cross-sectional view of a space suit to which the life support device 1 can be applied. The life support device 1 is not shown.

  The space suit 100 includes a space environment protection unit 101 that covers the entire body of the wearer, a radiation protection unit 102 that covers the entire body of the wearer inside the space environment protection unit 101, and a cooling underwear 103. The space environment protection unit 101 has a multilayer structure having heat insulation and cosmic ray resistance, and protects the wearer from the space environment. The cooling undergarment 103 prevents an abnormal increase in body temperature due to wearing of a space suit. The radiation protection unit 102 is formed of the radiation shielding material 51 described above, and protects the wearer from radiation such as neutron rays, gamma rays, scattered X-rays, and electron beams. The glove 104 and the boot 105 that protect the wearer's hands and both toes are also composed of a space environment protection unit 101 and a radiation protection unit 102 as in the other parts.

  FIG. 14 is an enlarged view of the XIV portion of FIG.

  As a feature different from the outer skin portion 31 of the radiation protective suit 30 shown in FIG. 9, a mercury layer 111 is provided along the outer surface of the endothelial layer 52. A space 113 is formed between the mercury layer 111 and the body surface 112 of the wearer via a cooling undergarment 103 (not shown). The mercury layer 111 includes a mercury holding layer 115, and the mercury in the mercury layer 111 is held between the endothelial layer 52 by the mercury holding layer 115 formed of silicon rubber or the like. By providing the mercury layer 111, the expansion of the body in the weightless space can be suppressed.

  A nylon fiber cloth (not shown) is affixed on the surface of the mercury holding layer 115. Thereby, attachment / detachment becomes easy, and moisture absorption, quick drying, antibacterial, deodorizing, and heat retaining functions can be added. A supply port 117 for supplying air to the space 113 between the body surface 112 of the wearer and the body surface 112 of the wearer is provided on the surface of the mercury holding layer 115 on which the nylon fiber cloth is attached. A tube (not shown) extending from the supply port 117 is connected to the life support device 1 used together with the space suit, and is configured to send air supplied from the oxygen tank of the life support device 1 to the supply port 117. The supply port 117 and the tube extending from the supply port 117 are fixed to the surface of the mercury holding layer 115. By supplying air from the supply port 117, the wearer's skin respiration can be maintained. Moreover, a wearer's body temperature can also be adjusted by adjusting the temperature of the air to supply.

  The hollow layer 55 is filled with mercury. Thereby, the expansion | swelling suppression function of the body by the mercury layer 111 can further be reinforced.

  Mercury filled in each hollow layer 55 can flow through the communication hole 57a. Moreover, in the site | part corresponding to a wearer's joint, the quantity of the mercury with which the hollow layer 55 is filled is reduced rather than the other site | part. Therefore, a wearer's mobility can be improved.

  In the space suit 100, the radiation protection part 102 that covers the entire body of the wearer is formed by the radiation shielding material 51 inside the space environment protection part 101, but is not limited thereto. For example, the radiation shielding material 51 may be hardened without providing the radiation protection portion 102 inside the space environment protection portion 101, and the hardened radiation shielding material 51 may be used for forming the space environment protection portion 101.

  A radiation protective suit according to the second embodiment is shown in FIGS. 15 is a front view of the radiation protective suit 110, and FIG. 16 is a right side view of the radiation protective suit 110. FIG. 17 is a left side view of the radiation protective suit 110. FIG. 18 is a rear view of the radiation protective suit 110. The radiation protection suit 110 has the same configuration as the radiation protection suit 10 described above, but a different configuration will be described. As shown in FIGS. 15 to 18, the radiation protective clothing 110 is provided with a cushion material between the wearer and the endothelial layer. The cushion material 140 is made of urethane or silicone and protects the shoulder, chest, waist and back of the wearer.

  As shown in FIG. 16, a life support device 130 can be attached to the back side of the radiation protective suit 110. The configuration of the life support device 130 is shown in FIG. The life support device 130 includes a first air tank 131, a second air tank 132, and a respiratory circulation air cooling device 134. Oxygen is sent from the first air tank 131 and the second air tank 132 into the helmet 12 through the supply port 135 and a tube connected to the supply port 135 so that the wearer can breathe. In addition, as will be described later, the air from the life support device 130 is also supplied to the inside of the inner skin portion 2 for the skin respiration of the wearer and the like. The water supply tank 138 supplies moisture to the wearer.

  The liquid food tank 139 supplies liquid food to the wearer. The breathing circulation air cooling device 134 adjusts the body temperature of the wearer by cooling the air supplied from the first air tank 131 and the second air tank 132. Moreover, since the life support device 130 is equipped with the cassette type carbon dioxide absorption part 136, the carbon dioxide discharged by the wearer can be processed. In addition, a device control unit 137 that controls various components, a micro pump unit 138, a power supply unit 133, a GPS (Global Positioning System) of the device control unit 137, and the like are provided in the life support device 130.

  The first air tank 131 is an air tank composed of a cassette-type cylinder, which combines a check valve and an air hose, detects air pressure by the equipment control unit 137, and supplies air. The second air tank 132 is an air tank composed of a cassette type cylinder, which combines an electromagnetic valve and an air hose, measures the amount of oxygen by the device control unit 137, and supplies oxygen. The first air tank 131 or the second air tank 132 may be covered as the above-described radiation shielding material as a life support means.

  The power supply unit 133 uses a lithium ion battery and allows the lithium ion battery to be replaced. The power supply unit 133 may replace batteries other than lithium ion batteries, and these batteries are rechargeable. The power supply part 133 may be comprised from batteries other than lithium ion. The power supply unit 133 further includes a circulation fan unit that is used for an exhaust part and adjusts an increase in carbon dioxide of the helmet 12, and a circulation composed of a small pump device that operates cooling air to adjust the body temperature to the body part of the radiation protective suit 110. The pump unit includes a cooling device that encloses liquid nitrogen in a cooling device on a thermos bottle and sends intake air into a space having a cooling fan.

  The carbon dioxide absorption unit 136 always absorbs (adsorbs) and circulates the concentration of discharged carbon dioxide during breathing in the helmet 12. Further, the breathing circulation cooling air 134 has a function of enabling air cooling using liquid nitrogen.

  The device control unit 137 has a thermostat function, a communication function, and a GPS function, and uses electricity from the power supply unit 133 to manage the solenoid valve valve opening / closing, concentration measurement, GPS / communication / thermostat function by computer management. It is what. The device control unit 137 protects the radiation shielding material described above so as to cover it, and adds a function that allows unit replacement. Moreover, the life support device 130 packages each part of the life support device 130 with silicon and a shielding material.

  In the present embodiment, the hollow layer 5 of the radiation protective suit 110 may be filled with other liquid or gas instead of helium or mercury.

The radiation protective clothing 110 can absorb a shock to the wearer and can be fixed to the wearer's body by providing a cushioning material between the wearer and the endothelial layer.

DESCRIPTION OF SYMBOLS 1 Life support device 11 Main oxygen tank 12 Air tank 13 Water supply tank 14 Breathing circulation air cooling device 15 Carbon dioxide absorber 16 Equipment control part 17 GPS
18 Micro-pump unit 19 Battery unit 30 Radiation protective clothing 51 Radiation shielding material 52 Endothelial layer 53 Middle skin layer 54 Epithelial layer 55 Hollow layer 56 Outer layer portion 57 Partition portion 57a Communication hole 110 Radiation protective clothing 130 Life support device 131 First air tank 132 Second Air Tank 133 Power Supply Unit 134 Respiratory Circulation Air Cooling Device 135 Supply Port 136 Carbon Dioxide Absorbing Material 137 Device Control Unit 138 Micropump Unit 138 Water Supply Tank 139 Liquid Food Tank

Claims (12)

An endothelium layer formed from silicon rubber to which at least silicon, strontium and magnesium are added, which shields scattered X-rays and electron beams;
It is formed of silicon rubber laminated on the endothelial layer, shielding at least one of gamma rays, added with at least one of bismuth and titanium, silicon, and strontium. A plurality of hollow layers, and a corrugated mesothel layer having a partition wall partitioning the hollow layers,
A radiation shielding material comprising a corrugated epithelial layer formed from silicon rubber added with at least boron, which is laminated on the mesothelial layer, shields neutron rays, and
A life support device comprising life support means covered with the radiation shielding material. The life support means includes at least an oxygen tank, a carbon dioxide absorbent, a respiratory circulation air cooling device, and a control unit.
The control unit controls the wearer wearing the life support device to supply oxygen in the oxygen tank, and controls to absorb the carbon dioxide breathed by the wearer. 2. The life support device according to claim 1, wherein the air discharged by the wearer's breathing is circulated by controlling the air cooling means.   The life support apparatus according to claim 2, wherein the life support means further includes position information acquisition means for acquiring position information of a wearer wearing the life support apparatus and transmitting the position information.   The life support apparatus according to claim 2 or 3, wherein the life support means further includes a water supply tank that supplies moisture to a wearer wearing the life support apparatus. The life support apparatus according to any one of claims 1 to 4, wherein the hollow layer is filled with a substance containing a gamma ray shielding material. 6. The life support apparatus according to claim 5, wherein the gamma ray shielding material is in any of a granular shape, a pellet shape, a lump shape, a film shape, and a plate shape. 6. The life support device according to claim 5, wherein the gamma ray shielding material is one of water, an organic solvent, a surfactant, a resin binder, inorganic particles, and organic particles. The life support device according to any one of claims 1 to 7, wherein the partition wall includes a communication hole that allows the filler in the adjacent hollow layers to communicate with each other via the partition wall. The life support apparatus according to any one of claims 1 to 8, wherein a mixing volume ratio between the silicon rubber and a substance added to the silicon rubber is 40:60. The life support apparatus according to claim 1, wherein the hardness of the silicon rubber is adjusted by changing a ratio of a substance added to the silicon rubber. The life support apparatus according to any one of claims 1 to 10, wherein the hollow layer is filled with air or liquid. The life support apparatus according to claim 1, wherein the life support means is only the oxygen tank.