JP2017161547A - Earth crust composition, radioactivity incompetence processing system, method for manufacturing earth crust composition, and radioactivity incompetence processing method - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide an earth crust composition capable of making radioactive waste incompetent and disposing it relatively easily.SOLUTION: An earth crust composition is a solid phase composition capable of performing hydration reaction obtained by burning a calcium carbonate composite whose main component is calcium carbonate, a silicic acid composite composed of silicate as a main component, and an iron oxide composite composed of an iron oxide material as main component, at least one of the above being derived from radioactive pollution. Concentration of a radioactive material confined in the solid phase composition is made to be equal to or less than a regulation standard.SELECTED DRAWING: Figure 6

Description

  The present invention relates to a crust composition, a radioactivity inactivation treatment system, a method for producing a crust composition, and a radioactivity incapacitance that can reduce the concentration of a radioactive substance to a safety standard or less set in international or domestic standards. The present invention relates to a processing method.

  In Japan, after the great earthquake of March 11, 2011, there was an accident at a nuclear power plant, and as shown in FIG. 1, it is considered that more than 850,000 terabecquerel radioactive material was scattered. Since then, not only high-level radioactive waste, but also low-level radioactive waste and waste associated with decontamination have been generated in large quantities and are still increasing. Specifically, as shown in Fig. 2, radioactive waste is found in radioactive incineration ash and sewage treatment plant sludge that accumulates daily, and from radioactive rubble in the affected areas. Has been confirmed. Radioactive pollutants have also been identified in rivers and oceans.

  Regarding the treatment of radioactive waste, as shown in FIG. 3, there is a nuclear policy outline established before the earthquake, and the Reactor Regulation Law and the Radiation Hazard Prevention Law have been established. Internationally, Japan is a member of the London Convention, and the dumping of radioactive material into the ocean is prohibited. In addition, a clearance system has been introduced, in which the radioactive waste clearance level is set.

  At the time of final disposal of radioactive waste, at present, high-level radioactive waste is subjected to geological disposal of vitrified solids, while low-level radioactive waste is disposed at a shallow depth, shallow underground pits or shallow areas. The middle trench is to be disposed of. As for geological disposal, the management period is more than tens of thousands of years, hundreds of years for marginal depth disposal, about 300 years for shallow pit disposal, and about 50 years for shallow underground trench disposal. Such a disposal method requires very high technology, is expensive, and must be managed for a very long period of time. It is very difficult to dispose of radioactive waste that will increase in the future in this way.

  The present invention has been made on the basis of the background as described above, and a crustal composition, a radioactive disabling treatment system, and a crustal composition that can be disposed of relatively easily by disabling radioactive waste. An object of the present invention is to provide a production method and a radioactivity disabling treatment method.

  The crust composition according to the present invention is a primary composition, a calcium carbonate composition comprising a composition containing calcium carbonate as a main component, and a siliceous composition comprising a siliceous composition as a main component. A solid phase composition capable of hydration reaction comprising a calcined product with an iron oxide composition comprising an iron oxide-based material as a main component, the calcium carbonate composition, the siliceous composition, and the iron oxide At least one of the compositions is derived from radioactive contamination, and as a whole, the composition is configured to include a radioactive substance having a concentration equal to or lower than the legal standard value confined in the solid phase composition. Therefore, the composition can disable radioactive waste and can be disposed relatively easily.

  Here, the amount of heat necessary for the firing is for obtaining the amount of heat necessary for the firing by burning itself during the firing, and the combustion husk itself is a raw material for the solid phase composition. Including. Further, the composition is admixed with a porous material and can adsorb radioactive substances. In addition, the composition may contain a fixing material in which a radioactive substance and a mineral substance are coexistingly fixed, and can contain the radioactive substance inside.

  Further, the crust composition according to the present invention is a secondary composition, which is a calcium carbonate composition composed of a composition mainly composed of calcium carbonate, and a siliceous composition composed mainly of a siliceous composition. A solid phase composition comprising a fired product of a composition and an iron oxide composition containing an iron oxide-based substance as a main component and a hydration-reactive solid-phase composition, and a reaction rate for adjusting a curing rate and / or a hydration rate It is a granular composition obtained by including a conditioning material, wherein at least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination, and the powder as a whole It is configured to contain a radioactive substance having a concentration equal to or lower than the legal standard value confined in the granular composition. Therefore, the crust composition can disable radioactive waste and dispose of it relatively easily.

  Further, the crust composition according to the present invention is a tertiary composition, a calcium carbonate composition composed of a composition mainly composed of calcium carbonate, and a siliceous composition composed mainly of a siliceous composition. And a solid phase composition capable of hydration reaction obtained by firing an iron oxide composition containing an iron oxide-based material as a main component, and a reaction rate for adjusting a curing rate and / or a hydration reaction rate A paste-like composition comprising a kneaded product of an adjusting material and water, wherein at least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination, As described above, it contains a radioactive substance having a concentration equal to or lower than the legal standard value confined in the paste composition. Therefore, the crust composition can disable radioactive waste and dispose of it relatively easily.

  Further, the crust composition according to the present invention is a quaternary composition, a calcium carbonate composition comprising a composition containing calcium carbonate as a main component, and a siliceous substance comprising a siliceous composition as a main component. A solid phase composition capable of hydration reaction obtained by firing a composition and an iron oxide composition containing an iron oxide-based substance as a main component, and a reaction for adjusting a curing rate and / or a hydration reaction rate A paste-like composition comprising a kneaded product of a speed adjusting material, a fine aggregate, and water, wherein at least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is radioactive. It is derived from contamination, and as a whole, is configured to contain a radioactive substance having a concentration equal to or lower than the legal standard value confined in the paste-like composition. Therefore, the crust composition can disable radioactive waste and dispose of it relatively easily.

  Furthermore, the crust composition according to the present invention is a quinary composition comprising a calcium carbonate composition comprising a composition containing calcium carbonate as a main component, and a siliceous composition comprising a siliceous composition as a main component. A solid phase composition capable of hydration reaction obtained by firing a composition and an iron oxide composition containing an iron oxide-based substance as a main component, and a reaction for adjusting a curing rate and / or a hydration reaction rate A paste-like composition comprising a kneaded product of a speed adjusting material, a fine aggregate, a coarse aggregate, and water, the calcium carbonate composition, the siliceous composition, and the iron oxide composition. At least one of them is derived from radioactive contamination, and as a whole, it is configured to contain a radioactive substance having a concentration equal to or lower than the legal standard value confined in the paste-like composition. Therefore, the crust composition can disable radioactive waste and dispose of it relatively easily.

  The crust composition can be configured to protect the crust composition by providing an impermeable layer such as asphalt, tar or glass on the outside.

  Furthermore, the radioactive disabling treatment system according to the present invention is the primary composition treatment system comprising a calcium carbonate composition comprising a composition mainly composed of calcium carbonate and a siliceous composition. A siliceous composition as a component and an iron oxide composition containing an iron oxide-based material as a main component are calcined and hydrated to produce a solid phase composition for producing a crustal composition. At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination, and as a whole, the radioactive substance having a concentration equal to or lower than the legal standard value confined in the solid phase composition To be included. Moreover, this invention is a manufacturing method of the crust composition used as the said primary composition, and is a radioactivity disabling processing method.

  The radioactivity disabling treatment system according to the present invention is a treatment system for the secondary composition, comprising a calcium carbonate composition comprising a composition mainly composed of calcium carbonate, and a siliceous composition. A solid phase composition for producing a crust composition by a hydration reaction obtained by firing a siliceous composition comprising a main component and an iron oxide composition comprising an iron oxide-based substance as a main component; A calcium carbonate composition, the siliceous composition, and the iron oxide composition are produced by mixing a reaction rate adjusting material for adjusting a curing rate and / or a hydration reaction rate to produce a granular composition. At least one of the above is derived from radioactive contamination, and as a whole, a radioactive substance having a concentration equal to or lower than the legal standard value confined in the above-mentioned granular composition is included. Moreover, this invention is a manufacturing method of the crust composition used as the said secondary composition, and is a radioactivity disabling processing method.

  Further, the radioactive disabling treatment system according to the present invention is a treatment system for the tertiary composition, which mainly comprises a calcium carbonate composition comprising a composition mainly composed of calcium carbonate and a siliceous composition. A solid phase composition for producing a crust composition by hydration reaction obtained by firing a siliceous composition as a component and an iron oxide composition containing an iron oxide-based material as a main component, and curing A paste-like composition is produced by kneading with water and a reaction rate adjusting material for adjusting the rate and / or hydration reaction rate, and the calcium carbonate composition, the siliceous composition, and the iron oxide composition At least one of the substances is derived from radioactive contamination, and as a whole, a radioactive substance having a concentration equal to or lower than the legal standard value confined in the paste-like composition is included. Moreover, this invention is a manufacturing method of the crust composition used as the said tertiary composition, and is a radioactivity disabling processing method.

  Further, the radioactive disabling treatment system according to the present invention is a treatment system for the quaternary composition, comprising a calcium carbonate composition comprising a composition mainly composed of calcium carbonate, and a siliceous composition. A solid phase composition for producing a crust composition by a hydration reaction obtained by firing a siliceous composition comprising a main component and an iron oxide composition comprising an iron oxide-based substance as a main component; A reaction rate adjusting material for adjusting a curing rate and / or a hydration reaction rate and a fine aggregate are kneaded with water to produce a paste-like composition, and the calcium carbonate composition and the siliceous composition And at least one of the iron oxide composition is derived from radioactive contamination, and as a whole, a radioactive substance having a concentration equal to or lower than a legal standard value confined in the paste-like composition is included. Moreover, this invention is a manufacturing method of the crust composition used as the said quaternary composition, and is a radioactivity disabling processing method.

  The radioactivity disabling treatment system according to the present invention is a treatment system for the quinary composition comprising a calcium carbonate composition comprising a composition mainly composed of calcium carbonate, and a siliceous composition. A solid phase composition for producing a crust composition by a hydration reaction obtained by firing a siliceous composition comprising a main component and an iron oxide composition comprising an iron oxide-based substance as a main component; A reaction rate adjusting material for adjusting a curing rate and / or a hydration reaction rate, a fine aggregate, and a coarse aggregate are kneaded with water to produce a paste-like composition, the calcium carbonate composition, At least one of the siliceous composition and the iron oxide composition is derived from radioactive contamination, and as a whole, a radioactive substance having a concentration equal to or lower than the legal standard value confined in the paste-like composition is included. . Moreover, this invention is a manufacturing method of the crust composition used as the said 5th composition, and is a radioactivity disabling processing method.

  In the present invention, radioactive waste is included in at least one of the materials of the crust composition that is cured by the hydration reaction, and the concentration of the entire radioactive material is set to a predetermined value or less, so that the radioactive waste is disabled and compared. Can be disposed of easily.

It is a figure explaining the background of this invention. It is a figure explaining the background of this invention. It is a figure explaining the background of this invention. It is a figure which shows the structure of this invention. It is a figure which shows the structure of this invention. It is a figure which shows the structure of a crust composition. It is a manufacturing-process figure of a crust composition. It is a manufacturing-process figure of the crust composition of a continuation of FIG. It is a manufacturing-process figure of the crustal composition of a continuation of FIG. It is sectional drawing of the crustal composition body in which the impermeable layer was provided outside.

  Hereinafter, a crustal composition, a radioactivity disabling treatment system, a method for producing a crustal composition, and a radioactivity disabling treatment method according to the present invention will be described with reference to the drawings.

  As shown in FIG. 4, the present invention includes a radioactive disabling treatment system 10. In the radioactive disabling treatment system 10, radioactive contaminants are disabled, and the concentration of the radioactive substance is within the domestic and foreign standard values. The crustal composition 20 of the present invention is produced using a hydration reaction. More specifically, as shown in FIG. 5, the radioactive disabling treatment system 10 is concentrated while concentrating radioactive substances, for example, by incinerating rubble, sludge, sludge and the like containing radioactive pollutants. The radioactive material is mixed with another material, for example, and diluted at the same time, so that the concentration of the radioactive material is within a reference value. In addition, the radioactive disabling processing system 10 fixes and confines the radioactive substance in the crustal composition 20, and confines the radioactive substance so that it is not released to the outside. In this way, the radioactive disabling treatment system 10 can prevent the radioactive material from leaking by using the crust composition 20 to physically confine and fix the radioactive material, and chemically confine and fix the radioactive material. By doing so, elution of radioactive materials can be prevented, and furthermore, by reducing the density of radioactive materials, the absolute amount of radiation can be greatly reduced, and furthermore, radiation levels can be reduced by shielding radiation. Furthermore, overheating can be prevented by reducing the heat density.

  Here, the standard value of the concentration of radioactive material is the date of October 29, 2011 from the Ministry of the Environment, such as “intermediate storage facilities necessary for coping with environmental pollution caused by radioactive material caused by the accident at TEPCO's Fukushima Daiichi Nuclear Power Station” According to the document “Basic Concept”, it is 8,000 Bq / kg or less. Therefore, it is preferable that the crustal structure is produced so as to comply with this and suitable for domestic law. In addition, according to the document “Regarding the clearance system in the Reactor Regulation Law” by NISA radioactive waste regulation section, the following standards are set. Therefore, it is preferable to make the crust structure so as to comply with this because it is suitable in accordance with international rules.

  Specifically, when there are a plurality of radionuclides in the object, the clearance level is 1 in which the sum of the ratio of the concentration of the evaluation target radionuclide contained in the object to the clearance level of the nuclide is 1 Based on the following: The formula is as follows.

i: Radionuclide to be evaluated i
D (i): Concentration of nuclide i contained in the object C (i): Clearance level of nuclide i (see Table 1 below)

  By the way, as shown in FIG. 6, radioactive pollutants include fish shellfish, vegetables, incinerated ash, sludge sludge, marine mud sand, mud river sand, lake mud sand, roadside trees, debris (concrete, wood, glass, metal , Plastic), contaminated water, ground mud, lake mud sand, marine mud sand, river mud sand, and road surface materials. These contaminants can be classified as shown in Table 2 below.

  As shown in FIG. 7, the crust composition 20 of the present invention is manufactured. In the raw material process, calcium carbonate composition generated from fish and shellfish that became radioactive pollutants, animal carcasses, meat and bones, vegetables, etc., incinerated ash, sludge sludge, lakes that became radioactive pollutants Finely ground geological composition such as mud sand, marine mud sand that became radioactive pollutant, silicic acid composition such as river mud sand, lake mud sand, etc. A powder raw material with mixed components is produced by mixing. The fine geological composition and siliceous composition may be incinerated ash from a thermal power plant, or debris (concrete, wood, glass, metal, plastic) that has become a radioactive pollutant. May be.

  Next, as shown in FIG. 8, in the firing step, the powder raw material obtained in the raw material step is heated to a predetermined temperature and fired to become a hydraulic compound. For example, after reaching a maximum temperature and finishing a predetermined chemical reaction, it is cooled at once with an air quenching cooler to produce a primary composition which is a solid phase composition. At the time of firing, either a radioactive pollutant or a non-radioactive pollutant may be used, but a raw material for fuel such as waste plastic, waste oil, waste white clay, wood scrap, meat-and-bone meal, reclaimed oil, etc. is charged to fire the powder raw material.

  The primary composition, which is a solid phase composition, is prepared by adjusting the concentration of radioactive material in advance for each of the calcium carbonate composition, fine-grained geological composition, siliceous composition, iron oxide raw material, and fuel raw material. By using it, the density | concentration of the radioactive substance as a whole can be made into a predetermined value or less. The primary composition which is a solid phase composition is a calcium carbonate composition, a fine-grained geological composition, a siliceous composition, an iron oxide raw material, one or a plurality of fuel raw materials, and a radioactive pollutant. By adjusting the amount of the non-radioactive contamination material, the concentration of the radioactive substance can be reduced to the predetermined value or less.

  Furthermore, as shown in FIG. 9, in the finishing step, a reaction for adjusting the curing rate and / or the hydration reaction rate of the primary composition, which is the solid phase composition obtained in the firing step, is performed. Speed modifiers, such as gypsum, are added and they are ground to a fine powder, thereby completing the secondary composition that becomes a solidifying binder. By using the above-mentioned primary composition, the concentration of the radioactive material as a whole is set to a predetermined value or less as the secondary composition serving as the solidifying binder.

  The secondary composition to be the solidifying binder becomes a tertiary composition that is a paste-like composition by being kneaded with an appropriate amount of water. The tertiary composition is hydrated, polymerized and cured by being kneaded with water. The water used here may be contaminated water that is a radioactive pollutant or non-radioactive polluted water. The concentration of the radioactive material as a whole can be adjusted to a predetermined value or less depending on what kind of water is used for the tertiary composition. In such a tertiary composition, the concentration of the radioactive substance as a whole is set to a predetermined value or less in a paste-like composition state or a hardened crust composition state.

  Furthermore, the secondary composition to be a solidifying binder is a quaternary composition which is a paste-like composition by adding fine aggregate (sand) and kneading with an appropriate amount of water. This quaternary composition is hydrated, polymerized and cured by being kneaded with water. The water used here may be contaminated water that is a radioactive pollutant or non-radioactive polluted water. Further, as the fine aggregate (sand), radioactive pollutants such as ground mud sand, lake mud sand, marine mud sand and river mud sand may be used, or sand of non-radioactive pollutant material may be used. The concentration of the radioactive material as a whole can be adjusted to a predetermined value or less depending on what kind of water or fine aggregate (sand) is used for the quaternary composition. In such a quaternary composition, the concentration of the radioactive material as a whole is set to a predetermined value or less in a paste-like composition state or a hardened crust composition state.

  Furthermore, the secondary composition to be a solidifying binder is a quinary composition which is a paste-like composition by adding fine aggregate (sand) and coarse aggregate (gravel) and kneading with an appropriate amount of water. It becomes. The quinary composition is hydrated, polymerized and cured by being kneaded with water. The water used here may be fresh water, seawater, contaminated water that is a radioactive pollutant, or non-radioactive contaminated water. In particular, when seawater is used and treatment by transoceanic crust reduction is performed, it is preferable because osmotic pressure adjustment between the crustal composition and seawater in contact with the seatime can be performed in advance. Further, as the fine aggregate (sand), radioactive pollutants such as ground mud sand, lake mud sand, marine mud sand and river mud sand may be used, or sand of non-radioactive pollutant material may be used. Further, as the coarse aggregate (gravel), a road surface material that is a radioactive pollutant may be used, or gravel of a non-radioactive pollutant material may be used. The concentration of the radioactive substance as a whole can be adjusted to a predetermined value or less depending on what kind of water, fine aggregate (sand), or coarse aggregate (gravel) is used for the quinary composition. In such a quaternary composition, the concentration of the radioactive material as a whole is set to a predetermined value or less in the state of a paste-like composition or the state of a hardened crust composition.

  By the way, the primary to quinary composition may be mixed with a porous material that adsorbs radioactive substances before being kneaded with water. The porous material is not particularly limited, but for example, Shirasu Porous Glass is preferable. In Shirasu porous glass, the pore diameter can be freely controlled in the range of 1 nm to 50 μm by adjusting the heat treatment conditions, so that the pore diameter can be adjusted according to the size of the intended radioactive substance. Such a porous material may be used, for example, as a filter medium for filtering contaminated water, and the waste material may be mixed into the primary to quinary composition.

  Moreover, the crustal composition 20 obtained by solidifying the fifth composition, which is a paste-like composition, is solidified, for example, in a block shape as shown in FIG. The crust composition 20 may be provided with an impermeable layer 21 on the surface thereof by at least one substance selected from asphalt, tar, and glass. In other words, the crustal composition 20 containing the primary to quinary composition has the concentration of radioactive material as a whole less than a predetermined value, and no longer corresponds to the definition of radioactive pollutant. Therefore, for example, it can be thrown into the ocean and used for fish reefs and the like. In addition, when it is introduced into the deep sea such as a trench through the sea via the sea, it can be extinguished as the plate moves, that is, the crust can be reduced. When thrown into the ocean, it will be exposed to seawater for a long time, and the surface may become brittle. Therefore, as shown in FIG. 10, the crust composition body 20 can prevent the crust composition body 20 from becoming brittle by providing an impermeable layer 21. In addition, the crust composition 20 may be stored in a cavity such as a mining site, or may be replaced and stored by replacement at the time of mining, in addition to being put into the ocean.

Furthermore, as a method for solidifying high-level radioactive substances and highly toxic radioactive substances, ores are artificially synthesized with titanate-based minerals such as hollandite, perovskite, and zirconolite as main components, and molybdenum, Co-fixed transuranium element nuclides such as technetium, ruthenium, plutonium, etc., and co-fixed the fixing material 22 with the primary to quinary composition and the impermeable layer 21 to have a high degree of confinement effect You may do it. For example, the fixing material 22 can be mixed before the kneading with water. In the synthesis of the above artificial ore, for example, rutile (TiO ₂ ) and zircon (ZnO ₂ ) among the precursors are prepared from titanium alkoxide and zirconium alkoxide. All the remaining components are prepared by treating with an alkaline solution and coprecipitating as a mixed solution of nitrate solution. These precursors are mixed with high-level radioactive or highly toxic radioactive liquid waste to form a slurry, which is dried and calcined in a reducing atmosphere at 800 ° C., which is enclosed in a vessel together with titanium powder and heated. Press and fire.

  In the above example, the case where the crust composition 20 is produced by the hydration reaction has been described. However, the present invention includes a single, a pair, a cluster, a ring, a chain, a double chain, a layer, and a three-dimensional network. A solid phase composition obtained by firing a fine-grained geological composition having a particle size of 0.05 mm or less, and a basic component is a metal oxide, and baked and hardened by heat treatment at a high temperature. The sintered body may include a radioactive substance having a concentration equal to or lower than a predetermined value.

10 Radioactive disabling system, 20 Crustal composition, 21 Impermeable layer, 22 High-level radioactive material and highly toxic radioactive material

Claims (50)

Hydration reaction comprising a calcined product of a calcium carbonate composition comprising calcium carbonate as a main component, a siliceous composition comprising silicate as a main component, and an iron oxide composition comprising iron oxide as a main component. A possible solid phase composition comprising:
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A crust composition comprising a radioactive substance having a concentration equal to or lower than a legal standard value confined in the solid phase composition as a whole.   The crustal composition according to claim 1, wherein a porous material is mixed therein.   The crustal composition according to claim 1 or 2, wherein a fixing material obtained by coexisting and fixing a radioactive substance and a mineral substance is mixed. Hydration reaction comprising a calcined product of a calcium carbonate composition comprising calcium carbonate as a main component, a siliceous composition comprising silicate as a main component, and an iron oxide composition comprising iron oxide as a main component. Possible solid phase compositions;
A granular composition obtained by including a reaction rate adjusting material for adjusting a curing rate and / or a hydration reaction rate,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A crustal composition comprising a radioactive substance having a concentration equal to or lower than a legal standard value confined in the powdered composition as a whole.   The crustal composition according to claim 4, wherein a porous material is mixed therein.   The crustal composition according to claim 4 or 5, wherein a fixing material obtained by coexisting and fixing a radioactive substance and a mineral substance is mixed. Hydration reaction comprising a calcined product of a calcium carbonate composition comprising calcium carbonate as a main component, a siliceous composition comprising silicate as a main component, and an iron oxide composition comprising iron oxide as a main component. Possible solid phase compositions;
A reaction rate adjusting material for adjusting the curing rate and / or the hydration reaction rate;
A paste-like composition comprising a kneaded product with water,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A crust composition comprising a radioactive substance having a concentration equal to or lower than a legal standard value confined in the paste composition as a whole.   The crust composition according to claim 7, wherein a porous material is mixed therein.   The crustal composition according to claim 7 or 8, wherein a fixing material obtained by coexisting and fixing a radioactive substance and a mineral substance is mixed. Hydration reaction comprising a calcined product of a calcium carbonate composition comprising calcium carbonate as a main component, a siliceous composition comprising silicate as a main component, and an iron oxide composition comprising iron oxide as a main component. Possible solid phase compositions;
A reaction rate adjusting material for adjusting the curing rate and / or the hydration reaction rate;
Fine aggregate,
A paste-like composition comprising a kneaded product with water,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A crust composition comprising a radioactive substance having a concentration equal to or lower than a legal standard value confined in the paste composition as a whole.   The crust composition according to claim 10, wherein a porous material is mixed.   The crustal composition according to claim 10 or 11, wherein a fixing material obtained by coexisting and fixing a radioactive substance and a mineral substance is mixed. Hydration reaction comprising a calcined product of a calcium carbonate composition comprising calcium carbonate as a main component, a siliceous composition comprising silicate as a main component, and an iron oxide composition comprising iron oxide as a main component. Possible solid phase compositions;
A reaction rate adjusting material for adjusting the curing rate and / or the hydration reaction rate;
Fine aggregate,
Coarse aggregate,
A paste-like composition comprising a kneaded product with water,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A crust composition comprising a radioactive substance having a concentration equal to or lower than a legal standard value confined in the paste composition as a whole.   The crust composition according to claim 13, wherein a porous material is mixed therein.   The crust composition according to claim 13 or 14, wherein a fixing material in which a radioactive substance and a mineral substance are co-fixed is mixed.   The crustal composition according to any one of claims 13 to 15, wherein the crustal composition is provided with an impermeable layer on the outside.   The crustal composition according to claim 16, wherein the impermeable layer is at least one substance selected from asphalt, tar, and glass. A calcium carbonate composition containing calcium carbonate as a main component, a siliceous composition containing silicate as a main component, and an iron oxide composition containing iron oxide as a main component are calcined to cause a hydration reaction. To produce a solid phase composition for producing a crust composition,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A radioactivity disabling treatment system that contains radioactive substances having a concentration equal to or lower than the legal standard value confined in the solid phase composition as a whole.   The amount of heat necessary for the firing is obtained by combusting itself during the firing to obtain the amount of heat necessary for the firing, and the combustion husk itself adds a fuel raw material that is a raw material of the solid phase composition at the time of firing. The radioactivity disabling processing system according to claim 18.   20. The radioactive disabling treatment system according to claim 18 or 19, wherein a porous material is mixed.   21. The radioactive disabling treatment system according to claim 18, wherein a fixing material in which a radioactive substance and a mineral substance are coexistingly fixed is mixed. Hydration obtained by firing a calcium carbonate composition containing calcium carbonate as a main component, a siliceous composition containing silicate as a main component, and an iron oxide composition containing iron oxide as a main component A solid phase composition for reacting to produce a crust composition;
Mixing with a reaction rate adjusting material for adjusting the curing rate and / or hydration reaction rate to produce a granular composition,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A radioactivity disabling treatment system that includes radioactive substances having a concentration equal to or lower than the legal standard value confined in the powdered composition as a whole.   The amount of heat necessary for the firing is obtained by combusting itself during the firing to obtain the amount of heat necessary for the firing, and the combustion husk itself adds a fuel raw material that is a raw material of the solid phase composition at the time of firing. The radioactivity disabling processing system according to claim 22.   24. The radioactive disabling system according to claim 22 or 23, wherein a porous material is mixed.   The radioactive disabling treatment system according to any one of claims 22 to 24, wherein a fixing material in which a radioactive substance and a mineral substance are coexistently fixed is mixed. Hydration obtained by firing a calcium carbonate composition containing calcium carbonate as a main component, a siliceous composition containing silicate as a main component, and an iron oxide composition containing iron oxide as a main component A solid phase composition for reacting to produce a crust composition;
A reaction rate adjusting material for adjusting the curing rate and / or the hydration reaction rate;
Kneaded with water to produce a paste-like composition,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A radioactivity disabling treatment system characterized by containing a radioactive substance having a concentration equal to or lower than a legal standard value confined in the paste-like composition as a whole.   The amount of heat necessary for the firing is obtained by combusting itself during the firing to obtain the amount of heat necessary for the firing, and the combustion husk itself adds a fuel raw material that is a raw material of the solid phase composition at the time of firing. The radioactivity disabling processing system according to claim 26.   28. The radioactive disabling system according to claim 26 or 27, wherein the porous material is mixed at least before kneading with water.   29. The radioactive disabling treatment system according to claim 26, wherein the fixing material in which the radioactive substance and the mineral are coexistingly fixed is mixed at least before kneading with water. Hydration obtained by firing a calcium carbonate composition containing calcium carbonate as a main component, a siliceous composition containing silicate as a main component, and an iron oxide composition containing iron oxide as a main component A solid phase composition for reacting to produce a crust composition;
A reaction rate adjusting material for adjusting the curing rate and / or the hydration reaction rate;
Fine aggregate,
Kneaded with water to produce a paste-like composition,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A radioactivity disabling treatment system characterized by containing a radioactive substance having a concentration equal to or lower than a legal standard value confined in the paste-like composition as a whole.   The amount of heat required for the firing is for burning itself during the firing to obtain the amount of heat necessary for the firing, and the fuel shell itself is also added during the firing as a raw material for the solid phase composition The radioactivity disabling processing system according to claim 30, wherein:   32. The radioactive disabling system according to claim 30 or 31, wherein the porous material is mixed at least before kneading with water.   The radioactive disabling system according to any one of claims 30 to 32, wherein the fixing material in which the radioactive substance and the mineral substance are coexistently fixed is mixed at least before kneading with water. Hydration obtained by firing a calcium carbonate composition containing calcium carbonate as a main component, a siliceous composition containing silicate as a main component, and an iron oxide composition containing iron oxide as a main component A solid phase composition for reacting to produce a crust composition;
A reaction rate adjusting material for adjusting the curing rate and / or the hydration reaction rate;
Fine aggregate,
Coarse aggregate,
Kneaded with water to produce a paste-like composition,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A radioactivity disabling treatment system characterized by containing a radioactive substance having a concentration equal to or lower than a legal standard value confined in the paste-like composition as a whole.   The amount of heat required for the firing is for burning itself during the firing to obtain the amount of heat necessary for the firing, and the fuel shell itself is also added during the firing as a raw material for the solid phase composition The radioactivity disabling processing system according to claim 34, wherein:   36. The radioactive disabling system according to claim 34 or 35, wherein the porous material is mixed at least before kneading with water.   37. The radioactive disabling system according to any one of claims 34 to 36, wherein a fixing material in which a radioactive substance and a mineral substance are coexistently fixed is mixed at least before kneading with water.   38. The radioactivity disabling treatment system according to any one of claims 34 to 37, wherein an impermeable layer is formed outside a molded article of the paste-like composition.   39. The radioactive disabling system according to claim 38, wherein the impermeable layer is at least one substance selected from asphalt, tar, and glass. A calcium carbonate composition containing calcium carbonate as a main component, a siliceous composition containing silicate as a main component, and an iron oxide composition containing iron oxide as a main component are calcined to cause a hydration reaction. To produce a solid phase composition for producing a crust composition,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A method for producing a crustal composition that includes a radioactive substance having a concentration equal to or less than a legal standard value confined in the solid phase composition as a whole. Hydration obtained by firing a calcium carbonate composition containing calcium carbonate as a main component, a siliceous composition containing silicate as a main component, and an iron oxide composition containing iron oxide as a main component A solid phase composition for reacting to produce a crust composition;
Mixing with a reaction rate adjusting material for adjusting the curing rate and / or hydration reaction rate to produce a granular composition,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A method for producing a crustal composition that includes a radioactive substance having a concentration equal to or lower than a legal standard value confined in the above-mentioned granular composition as a whole. Hydration obtained by firing a calcium carbonate composition containing calcium carbonate as a main component, a siliceous composition containing silicate as a main component, and an iron oxide composition containing iron oxide as a main component A solid phase composition for reacting to produce a crust composition;
A reaction rate adjusting material for adjusting the curing rate and / or the hydration reaction rate;
Kneaded with water to produce a paste-like composition,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A method for producing a crustal composition characterized in that a radioactive substance having a concentration equal to or lower than a legal standard value confined in the paste-like composition as a whole is contained. Hydration obtained by firing a calcium carbonate composition containing calcium carbonate as a main component, a siliceous composition containing silicate as a main component, and an iron oxide composition containing iron oxide as a main component A solid phase composition for reacting to produce a crust composition;
A reaction rate adjusting material for adjusting the curing rate and / or the hydration reaction rate;
Fine aggregate,
Kneaded with water to produce a paste-like composition,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A method for producing a crustal composition characterized in that a radioactive substance having a concentration equal to or lower than a legal standard value confined in the paste-like composition as a whole is contained. Hydration obtained by firing a calcium carbonate composition containing calcium carbonate as a main component, a siliceous composition containing silicate as a main component, and an iron oxide composition containing iron oxide as a main component A solid phase composition for reacting to produce a crust composition;
A reaction rate adjusting material for adjusting the curing rate and / or the hydration reaction rate;
Fine aggregate,
Coarse aggregate,
Kneaded with water to produce a paste-like composition,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A method for producing a crustal composition characterized in that a radioactive substance having a concentration equal to or lower than a legal standard value confined in the paste-like composition as a whole is contained. Hydration reaction by firing a calcium carbonate composition containing calcium carbonate as a main component, a siliceous composition containing silicate as a main component, and an iron oxide composition containing iron oxide as a main component A solid phase composition for producing a crustal composition,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A radioactivity disabling treatment method in which a radioactive substance having a concentration equal to or lower than a legal standard value confined in the solid phase composition as a whole is contained. Hydration obtained by firing a calcium carbonate composition containing calcium carbonate as a main component, a siliceous composition containing silicate as a main component, and an iron oxide composition containing iron oxide as a main component A solid phase composition for reacting to produce a crust composition;
Mixing with a reaction rate adjusting material for adjusting the curing rate and / or hydration reaction rate to produce a granular composition,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A radioactivity disabling treatment method in which a radioactive substance having a concentration equal to or lower than a legal standard value confined in the powdered composition is contained as a whole. Hydration obtained by firing a calcium carbonate composition containing calcium carbonate as a main component, a siliceous composition containing silicate as a main component, and an iron oxide composition containing iron oxide as a main component A solid phase composition for reacting to produce a crust composition;
A reaction rate adjusting material for adjusting the curing rate and / or the hydration reaction rate;
Kneaded with water to produce a paste-like composition,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A radioactive disabling treatment method characterized by containing a radioactive substance having a concentration equal to or lower than a legal standard value confined in the paste-like composition as a whole. Hydration obtained by firing a calcium carbonate composition containing calcium carbonate as a main component, a siliceous composition containing silicate as a main component, and an iron oxide composition containing iron oxide as a main component A solid phase composition for reacting to produce a crust composition;
A reaction rate adjusting material for adjusting the curing rate and / or the hydration reaction rate;
Fine aggregate,
Kneaded with water to produce a paste-like composition,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A radioactive disabling treatment method characterized by containing a radioactive substance having a concentration equal to or lower than a legal standard value confined in the paste-like composition as a whole. Hydration obtained by firing a calcium carbonate composition containing calcium carbonate as a main component, a siliceous composition containing silicate as a main component, and an iron oxide composition containing iron oxide as a main component A solid phase composition for reacting to produce a crust composition;
A reaction rate adjusting material for adjusting the curing rate and / or the hydration reaction rate;
Fine aggregate,
Coarse aggregate,
Kneaded with water to produce a paste-like composition,
At least one of the calcium carbonate composition, the siliceous composition, and the iron oxide composition is derived from radioactive contamination,
A radioactive disabling treatment method characterized by containing a radioactive substance having a concentration equal to or lower than a legal standard value confined in the paste-like composition as a whole. Legislation in which a hydratable solid phase composition comprising a layered silicate as a main component and a fired product of a fine geological composition having a particle size of 0.05 mm or less is confined in the solid phase composition as a whole. Containing radioactive material derived from radioactive contamination at a concentration below the standard value,
A crustal composition characterized in that at least one of the layered silicate and / or the fine-grained geological composition is derived from radioactive contamination.