JP2000212024A - Cosmetics - Google Patents

Abstract

PROBLEM TO BE SOLVED: To obtain cosmetics excellent in resistance to water and oil, adhesivity and smoothness, capable of preventing makeup fading due to perspiration and sebum and excellent in lasting of make up by making the cosmetics include a surface treated powder with a specific fluorine containing silicone and silicone oil. SOLUTION: The cosmetics includes (A) the powder (e.g.; inorganic powder, polymer, organic pigments or the like) obtained by treating (e.g.; wet process, dry process or the like) the surface of the powder with the fluorine including silicone of the formula [R1 is a 1-20C alkyl, an aryl; R2 is -R5-Rf (R5 is a 2-6C divalent alkylene; Rf is a 1-12C perfluoroalkyl); R3 is -R5-SiX3 (X is a 1-4C alkoxyl or a halogen); R4 is either one of R1-R3; 1 is 0-500; m and n are each 1-500], and (B) silicone oil (e.g.; dimethylpolysiloxane or the like). The preferable adding amount of the fluorine containing silicone in the component A is 1-50 wt.%, to the powder base, and the preferable compounding amount of the component A and B to a cosmetic is 0.1-99% and 0.1-70%.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

BACKGROUND OF THE INVENTION The present invention relates to water resistance, oil resistance,
The present invention relates to a cosmetic that has excellent smoothness, can prevent makeup collapse due to sweat and sebum, and has excellent makeup durability. More specifically, by mixing the powder obtained by treating the surface of the powder with a specific fluorine-containing silicone, and silicone oil, sweat produced on the skin, the effect of preventing makeup collapse due to sebum is excellent, and The present invention relates to cosmetics having excellent usability, especially fit and smoothness.

[0002]

2. Description of the Related Art Cosmetic forms in which powders for cosmetics are blended include foundation, blusher, eyebrow, eyeshadow, body powder, sunscreen cosmetics and the like.
In recent years, there has been a great demand for these cosmetics for a long-lasting cosmetic effect and a long-lasting sunscreen effect. Accordingly, improvement of water resistance and oil resistance has been required for cosmetic powders to be incorporated in these cosmetics.

[0003] As a method for imparting water resistance to a powder, a method of treating the powder with silicone has conventionally been known.
Specifically, a method in which methyl hydrogen polysiloxane is mixed with a powder and the powder is treated by heating and baking (Japanese Patent Publication No. 45-2915), a method in which methyl hydrogen polysiloxane or dimethyl polysiloxane is dissolved in an organic solvent After that, the powder is treated by adding zinc octylate or the like as a crosslinking catalyst and baking the mixture (Japanese Patent Publication No. 45-18999). The powder is mixed with a metal hydroxide, coated and treated with methyl hydrogen. A method of treating a powder by a mechanochemical reaction using polysiloxane (JP-B-56-43264) is known.
However, these treated powders are not sufficient in water resistance and oil resistance, and have a problem that makeup is easily disintegrated due to sweat and sebum generated on the skin.

[0004] Therefore, in order to improve the water resistance and oil resistance of the powder, and to prevent makeup collapse due to sweat, sebum and the like, a method of treating the powder with a fluorine compound has recently been proposed. Specifically, a method of treating a powder with Teflon (Japanese Patent Publication No. 61-55481), a method of treating a powder with a fluorinated acrylate (Japanese Patent Publication No. 61-48803),
A method of treating a powder with a perfluoroalkyl phosphate diethanolamine salt (Japanese Patent Publication No. 5-86984);
A method of treating a powder with a perfluoroalkylsilane (JP-A-2-218603, JP-A-4-193816) has been proposed.

Since all of these powders are coated with a fluorine compound having an extremely low surface free energy on the surface of the powder, they have water and oil repellency and are not compatible with sweat and sebum. However, the dispersibility of the oil agent contained in the cosmetic is poor, and the agglomeration and color unevenness of the powder are liable to occur, and it is extremely difficult to incorporate the oil into the cosmetic. In addition, these powders have a drawback that, in terms of usability, the smoothness is deteriorated as compared to before the treatment.

[0006] In addition, silicone oil is blended for the purpose of imparting water repellency to cosmetics. Because silicone oil has excellent water repellency and has a smooth feeling of use,
It is widely used as a cosmetic ingredient. However, silicone oil is not sufficient in water resistance and oil resistance, and there is a problem that cosmetics containing silicone oil easily lose their makeup due to sweat and sebum generated on the skin.

For the purpose of imparting water resistance and oil resistance to cosmetics, cosmetics containing liquid perfluoropolyether (JP-A-61-234928 and JP-A-63-247214), fluorine-modified Cosmetics containing silicone oil (JP-A-5-247214, JP-A-6-12-1)
84312, JP-A-6-234858). However, although these fluorinated oils have water and oil repellency, they have high fluidity and poor adhesion to the skin, and thus cannot sufficiently prevent makeup collapse against a large amount of sweat or sebum. was there.

[0008]

SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to provide a cosmetic which is excellent in water resistance, oil resistance, adhesion and smoothness, can prevent makeup collapse due to sweat and sebum, and is excellent in long-lasting makeup. And

[0009]

Means for Solving the Problems In view of such circumstances, the present inventors have conducted intensive studies, and as a result, by treating the surface of the powder with a specific fluorine-containing silicone, water resistance, oil resistance, A powder with excellent smoothness and good dispersibility in silicone oil can be obtained, and by combining this treated powder with silicone oil, a cosmetic with excellent water resistance, oil resistance, adhesion and smoothness can be obtained. The present invention was completed by finding that a material was obtained.

That is, according to the present invention, (a) the surface of the powder is represented by the general formula (1) wherein R1 is the same or different
To 20 alkyl groups or aryl groups, R2 is -R5-
Rf (wherein, R5 represents a divalent alkylene group having 2 to 6 carbon atoms, Rf represents a perfluoroalkyl group having 1 to 12 carbon atoms.), R3 is -R5-SiX ₃ (wherein, X Represents an alkoxyl group having 1 to 4 carbon atoms or halogen.), R4 is any of R1 or R2 or R3, l, m, and n are integers, and l = 0 to 500, m
= 1 to 500 and n = 1 to 500. By mixing the powder obtained by treating with the fluorine-containing silicone represented by the formula (1) and (b) silicone oil, it is excellent in the effect of preventing makeup collapse caused by sweat and sebum generated on the skin, In particular, the present invention provides cosmetics having excellent fit and smoothness.

[0011]

FIG. 2

Hereinafter, the present invention will be described in detail.

As the powder used in the present invention, any powder which is usually used as a cosmetic can be applied. For example, talc, mica, kaolin, sericite, bentonite, smectite, mica titanium, bismuth oxychloride,
Silicic acid, silicic anhydride, alumina, titanium oxide, fine particle titanium oxide, zinc oxide, zirconium oxide, magnesium oxide, barium sulfate, magnesium sulfate, calcium carbonate, magnesium carbonate, aluminum silicate, magnesium silicate, calcium silicate, silica Barium acid, hydroxyapatite, boron nitride, metal soap, red iron,
Inorganic powders such as yellow iron oxide, black iron oxide, chromium oxide, chromium hydroxide, carbon black, ultramarine, navy blue, nylon,
Polymethyl methacrylate, polyethylene, polystyrene, cellulose, acetylated cellulose, polyurethane, divinylbenzene / styrene copolymer, silicone resin, epoxy resin, melamine resin, polycarbonate resin, vinyl resin, polymer such as silk powder, Red No. 104, Red No. 106, Red No. 201, Red 202
No., Red No. 204, Red No. 205, Red No. 206, Red No. 226, Red No. 227, Red No. 228, Yellow No. 4, Yellow No. 5, Yellow No. 202, Yellow No. 203, Yellow No. 205,
Organic dyes such as Yellow No. 401, Blue No. 1 and Green No. 3 are exemplified. Further, two or more kinds of powders and composites thereof may be used. Similarly, the shape and particle size of the powder are not particularly limited.

These powders may or may not have been previously surface-treated by a known method. Examples of the surface treatment method include oil treatment, metal soap treatment, inorganic compound treatment, amino acid treatment, silicone treatment, fluorine compound treatment, pendant treatment, silane coupling agent treatment,
Titanium coupling agent treatment, N-acylated lysine treatment,
Examples include polyacrylic acid treatment, plasma treatment, and mechanochemical treatment.

The fluorine-containing silicone used in the present invention is
Formula (1) wherein R1 is the same or different and has 1 carbon atom
To 20 alkyl groups or aryl groups, R2 is -R5-
Rf (wherein, R5 is a divalent alkylene group having 2 to 6 carbon atoms)
Rf is a perfluoroalkyl having 1 to 12 carbons
Represents a group. ), R3 is -R5-Six₃(Where X is charcoal
Represents an alkoxyl group having a prime number of 1 to 4 or halogen
You. ), R4 is either R1 or R2 or R3
And l, m, and n are integers, and l = 0 to 500, m
= 1 to 500 and n = 1 to 500. ]
Has structure. Among them, l = 0, m = 1 to 50,
In the structure where n = 1 to 50 and the ratio of m to n is 9: 1 to 2: 3,
Is preferred. More preferably, the ratio of m to n is 3: 1.
１1: 1. Note that the fluorine-containing material represented by the general formula (1) is used.
Silicone structural units can be arranged in blocks even if they are alternated.
May be random. Specifically, R1 is CH
₃, C₂H ₅, C₃H₇, CH (CH₃)₂, C
₄H₉, CH₂CH (CH₃) CH₃, C (C
H₃)₃, C₆H₁₃, C₆H₅Etc. as R5
Is C₂H₄, C₃H ₆, C₄H₈, CH₂CH (CH
₃) CH₂, CH₂CH₂CH (CH₃), C ₆H₁₂
But Rf is CF₃, C₂F₅, C₄F₉,
C₆F₁₃, C ₈F₁₇, C₁₂F₂₅Is X
OCH₃, OC₂H₅, OC₃H ₇, OCH (C
H₃)₂, OC₄H₉, OCH₂CH (CH₃) C
H₃, OC (CH₃)₃, Cl, Br, etc.
You.

[0016]

FIG. 3

The fluorine-containing silicone may be used alone or in combination of two or more of the above compounds.

In the surface treatment used in the present invention, the amount of the fluorinated silicone varies depending on the type of the powder and the fluorinated silicone.
~ 50% by weight is preferred. More preferably, 3 to 20
% By weight. If the amount is less than 1% by weight, the effects of the present invention such as water resistance and oil resistance are not sufficient, and even if the amount exceeds 50% by weight, the effect cannot be expected to be enhanced.

The surface treatment used in the present invention includes a wet method and a dry method. The wet method referred to in the present invention is to disperse the powder in an appropriate solvent, add a fluorine-containing silicone and, if necessary, an acid or alkali,
It refers to a technique obtained by removing the solvent after stirring and mixing, drying, and optionally pulverizing. Examples of solvents include hexane,
Heptane, toluene, xylene, benzene, cyclic silicone, methylene chloride, chloroform, acetone, butanol, propanol, isopropanol, ethanol,
Methanol, water and the like can be mentioned. Also, as the acid,
Hydrochloric acid, nitric acid, sulfuric acid, acetic acid and the like, and alkalis include ammonia, pyridine, amine and the like. Also,
With the dry method, while mixing powder with a stirring and mixing device such as a Henschel mixer, a jet mill, a ball mill, and a super mixer, the fluorinated silicone is added as it is or diluted with an appropriate solvent, and the mixture is dried after stirring and mixing. In some cases, it refers to a technique obtained by grinding. As the solvent for diluting the fluorine-containing silicone, the solvents mentioned in the treatment by the wet method can be used. Other examples include a spray drying method and a fluid granulation method, and any method may be used as long as the surface of the base powder is coated with the fluorine-containing silicone.

The treated powder of the component (a) can be used alone or in combination of two or more. The compounding amount in the cosmetic is preferably 0.1 to 99% by weight. More preferably, it is 1 to 95% by weight. If it is less than 0.1% by weight, the effect of the present invention, that is, the long-lasting effect of makeup, is not sufficient.
Even if the content exceeds 99% by weight, the effect cannot be expected to be enhanced.

As the silicone oil (b) used in the present invention, any silicone oil commonly used in cosmetics can be used. Specifically, dimethylpolysiloxane, methylphenylpolysiloxane,
Octamethylcyclotetrasiloxane, decamethylcyclopentasiloxane, polyether-modified silicone, amino-modified silicone, alkyl-modified silicone, fluorosilicone, acrylic silicone, silicone resin,
And trimethylsiloxysilicic acid.

The silicone oil (b) can be used alone or in combination of two or more. The compounding amount in the cosmetic is preferably 0.1 to 70% by weight. More preferably, it is 1 to 40% by weight. 0.1% by weight
If it is less than 10, the dispersibility of the treated powder of the component (a) is not sufficient, and even if it is more than 70% by weight, the dispersibility of the treated powder of the component (a) is not improved, and conversely, the effect of keeping the makeup is long. descend.

Other components of the cosmetic of the present invention include:
Depending on the form of the desired cosmetic, it can be used by selecting from components that are blended with ordinary cosmetics. As these components, for example, oils include various hydrocarbons such as squalane, liquid paraffin, petrolatum, light isoparaffin, and heavy liquid isoparaffin, microcrystalline wax, ozokerite, ceresin, beeswax, carnauba wax, waxes such as candelilla wax, etc. , Higher fatty acids such as lauric acid, myristic acid, palmitic acid, oleic acid, stearic acid, isostearic acid, higher alcohols such as lauryl alcohol, cetyl alcohol, hexadecyl alcohol, oleyl alcohol, stearyl alcohol, behenyl alcohol, cetyl isooctanoate, myristine Isopropyl acetate, isopropyl palmitate, octyl dodecyl myristate, cetyl palmitate, glyceryl tri (caprylate / caprate), oley Octyldodecyl acid, glyceryl trioctanoate, isodecyl isononanoate, dioctyl succinate, octyldodecyl lactate, diisostearyl malate, diglyceryl diisostearate, diglyceryl triisostearate, neopentyl glycol dioctanoate, isostearyl myristate, stearic acid Esters such as cholesteryl, trimethylolpropane trioctanoate, and pentaerythrit tetraoctanoate;
Olive oil, jojoba oil, hydrogenated jojoba oil, avocado oil, castor oil, macadamia nut oil, mink oil, oils and fats such as lanolin, fluorocarbons, perfluoropolyethers, fluorine compounds such as fluorinated pitch and fluoroalcohol, and the like.

Other components include various polymers, inorganic powders, organic powders, surfactants, polyhydric alcohols, ethanol, thickeners, preservatives, antioxidants, pH adjusters, chelating agents, fragrances, Examples thereof include an ultraviolet absorber, a bactericide, a humectant, an antiperspirant, and water, and can be blended within a range that does not impair the purpose of the present invention.

Examples of the cosmetics of the present invention include, for example, powder foundation, oily foundation, emulsified foundation, blusher, white powder, pressed powder,
Eyebrow, eyeshadow, eyeliner, mascara,
Examples include lipstick, nail color, makeup base, body powder, cream, milky lotion, lotion, sunscreen cosmetics and the like.

The cosmetic of the present invention can be produced according to a usual method.

[0027]

EXAMPLES The present invention will be described in more detail with reference to examples for a better understanding of the present invention, but the present invention is not limited to these examples.

Example 1 After 100 g of sericite was dispersed in 200 g of toluene, a fluorinated silicone having a structure represented by the formula (2) was added, and the mixture was stirred at 80 ° C. for 2 hours. Thereafter, toluene was distilled off under reduced pressure, dried and pulverized to obtain surface-treated sericite.
Similarly, talc and mica were surface-treated. In addition, 0.5 g, 1 g, 3 g, 2 g,
Each was shaken to 0 g, 50 g, and 100 g to be processed.

[0029]

FIG. 4

Example 2 After 100 g of sericite was dispersed in 200 g of xylene, a fluorinated silicone having a structure represented by the formula (3) was added, and the mixture was stirred at 100 ° C. for 2 hours. Thereafter, xylene was distilled off under reduced pressure, dried and pulverized to obtain surface-treated sericite. Similarly, talc and mica were surface-treated. In addition, 0.5 g, 1 g, 3 g
g, 20 g, 50 g, and 100 g, respectively.

[0031]

FIG. 5

Next, the treated powders of Examples 1 and 2 obtained as described above were evaluated for water / oil repellency and smoothness. The results are shown in Tables 1 to 3. The abscissa indicates the amount (g) of the fluorine-containing silicone added.

(Evaluation method) <Water repellency> 5 ml of purified water was placed in a 10 ml test tube, 0.1 g of the powder of the example was added, and the mixture was shaken 100 times. 3
The state after standing for 0 minutes was visually determined. ：: Mostly floating on the surface of water △: Partly floating on the surface of water, but most of it was dispersed in water. ×: Completely dispersed and precipitated in water. <Oil repellency> 5 ml of squalane was placed in a 10 ml test tube, 0.1 g of the powder of the example was added, and the mixture was shaken 100 times. The state after standing for 30 minutes was visually determined. ：: Most of them floated on the surface of squalane △: Although they partially floated on the surface of squalane, most of them were dispersed in squalane. ×: Completely dispersed and precipitated in squalane. <Smoothness> Sensory evaluation was carried out by 10 expert panelists, and the results were shown according to the following criteria. 〇: 8 or more felt good △: 4 to 7 felt good ×: Less than 4 felt good

[0034]

[Table 1]

[0035]

[Table 2]

[0036]

[Table 3]

From Tables 1 to 3, it was found that the amount of the fluorine-containing silicone added is preferably 1 to 50% by weight, more preferably 3 to 20% by weight, based on the weight of the powder. .

Example 3 After dispersing 100 g of sericite in 200 g of toluene, a fluorine-containing silicone 5 having a structure represented by the formula (2) was prepared.
g was added and stirred at 80 ° C. for 2 hours. Thereafter, toluene was distilled off under reduced pressure, dried and pulverized to obtain surface-treated sericite. Similarly, talc, mica, red iron oxide, yellow iron oxide, black iron oxide, and titanium oxide were surface-treated.

[0039]

FIG. 6

Example 4 After dispersing 100 g of sericite in 200 g of xylene, a fluorine-containing silicone 6 having a structure represented by the formula (3) was prepared.
g was added and stirred at 100 ° C. for 2 hours. Thereafter, xylene was distilled off under reduced pressure, dried and pulverized to obtain surface-treated sericite. Similarly, talc, mica, red iron oxide, yellow iron oxide, black iron oxide, and titanium oxide were surface-treated.

[0041]

FIG. 7

Example 5 After 100 g of sericite treated with 3% methylhydrogenpolysiloxane was dispersed in 200 g of toluene, 5 g of a fluorine-containing silicone having a structure represented by the formula (4) was added, and the mixture was stirred at 85 ° C. for 2 hours. Thereafter, toluene was distilled off under reduced pressure, dried and pulverized to obtain surface-treated sericite. Similarly, talc, mica, red iron oxide, yellow iron oxide, black iron oxide, and titanium oxide were surface-treated.

[0043]

FIG. 8

Comparative Example 1 Comparative Example 1 was prepared using sericite, talc, mica, red iron oxide, yellow iron oxide, black iron oxide, and titanium oxide treated with 5% perfluoroalkyl phosphate ester salt manufactured by Daito Kasei Kogyo.

Comparative Example 2 After 100 g of sericite was dispersed in 200 g of toluene, 6 g of dimethylpolysiloxane (1000 cs) was added, and the mixture was treated in the same manner as in Example 3. Similarly, talc, mica, red iron oxide, yellow iron oxide, black iron oxide, and titanium oxide were subjected to a surface treatment to obtain Comparative Example 2.

Comparative Example 3 Comparative Example 3 was made of sericite, talc, mica, red iron oxide, yellow iron oxide, black iron oxide, and titanium oxide treated with 3% methylhydrogenpolysiloxane manufactured by Toishoku Pigment.

Next, examples of cosmetics containing the treated powder of the present invention and silicone oil will be described. In addition,
The mixing ratio of the components is% by weight.

Example 6 (Emulsion type foundation) Using the treated powder of Example 3, an emulsion type foundation having the composition shown in Table 4 was produced. The production method is as follows.

(Preparation method) After uniformly dissolving the oil phase at room temperature,
The powder is added to this and dispersed with a homomixer. The aqueous phase was added to this with stirring and emulsified to obtain an emulsified foundation.

Example 7 (Emulsified Foundation) An emulsified foundation having the composition shown in Table 4 was produced in the same manner as in Example 6 using the treated powder of Example 4.

Example 8 (Emulsified Foundation) An emulsified foundation having the composition shown in Table 4 was produced in the same manner as in Example 6, except that the treated powder of Example 5 was used.

Comparative Example 4 (Emulsified Foundation) An emulsified foundation having the composition shown in Table 4 was produced in the same manner as in Example 6 using the treated powder of Example 3.

Comparative Example 5 (Emulsion Foundation) An emulsified foundation having the composition shown in Table 4 was produced in the same manner as in Example 6 using the treated powder of Comparative Example 1.

Comparative Example 6 (Emulsion Foundation) Using the treated powder of Comparative Example 2, an emulsion foundation having the composition shown in Table 4 was produced in the same manner as in Example 6.

Comparative Example 7 (Emulsion Foundation) An emulsified foundation having the composition shown in Table 4 was produced in the same manner as in Example 6 using the treated powder of Comparative Example 3.

Next, Example 6 obtained as described above was used.
The emulsified foundations of Comparative Examples Nos. 8 to 8 and Comparative Examples 4 to 7 were evaluated for their long-lasting makeup against sweat and sebum, feeling of use, presence or absence of aggregation, and stability. Table 5 shows the results.

(Evaluation method) <Cosmetic durability and feeling of use> Sensory evaluation was carried out by 10 expert panelists, and the results were shown by the following criteria. 〇: 8 or more felt good Δ: 4 to 7 felt good ×: Less than 4 felt good <Presence or absence of aggregation> Regarding the emulsion type foundation immediately after production, the presence or absence of aggregation was visually observed. Judged. 〇: No aggregation ×: Aggregation <Stability> The emulsified foundation after storage at 40 ° C. for one month was evaluated according to the following criteria. 〇: Disperses evenly when shaken lightly ×: Does not disperse evenly when shaken strongly

[0058]

[Table 4]

[0059]

[Table 5]

As is clear from Table 5, the emulsified foundations of the present invention (Examples 6 to 8) are blended with the treated powder of the present invention and silicone oil to give a feeling of use,
The stability was excellent, and the durability was extremely good.
On the other hand, the emulsified foundation (Comparative Example 5) in which the perfluoroalkylphosphate ester-treated powder was blended was inferior in stability, and the emulsified foundation (Comparative Examples 6 and 7) in which the silicone-treated powder was blended was The makeup durability was poor. Further, the emulsified foundation (Comparative Example 4) in which the treated powder of Example 3 and an oil other than silicone oil were blended (Comparative Example 4) did not disperse the treated powder in the oil and was inferior in stability. From this, the necessity of combining and combining the treated powder of the present invention and silicone oil has become clear.

Example 9 Powder Foundation Using the treated powder of Example 3, a target powder foundation was obtained. (Preparation method) The treated powder of Example 3 was mixed, pulverized and transferred to a Henschel mixer. The remaining components were mixed by heating and homogenized, mixed with a pigment, pulverized again and passed through a sieve. This was compression-molded on a metal plate to obtain a powder foundation. Composition (%) 1 Surface treated talc 34.5 2 Surface treated mica 10.0 2 Surface treated sericite 30.0 3 Surface treated titanium oxide 10.0 4 Surface treated bengara 2.0 4 Surface treated yellow iron oxide 3.0 4 Surface treated black iron oxide 0.15 Squalane 4.06 Dimethylpolysiloxane 6.0 7 Preservative 0.28 Fragrance 0.2

Example 10 Blush The desired blush was obtained in the same manner as in Example 9 except that the treated powder of Example 3 was used. Composition (%) 1 Surface-treated talc 60.6 2 Surface-treated mica 20.0 3 Surface-treated titanium oxide 5.0 4 Surface-treated Bengala 2.05 Squalane 8.06 Dimethylpolysiloxane 1.07 Methylphenylpolysiloxane 3.0 8 Preservatives 0.2 9 Fragrances 0.2

Example 11 Powder Eye Shadow An intended powder eye shadow was obtained in the same manner as in Example 9 except that the treated powder of Example 3 was used. Composition (%) 1 Surface treated sericite 28.0 2 Surface treated mica 54.6 3 Surface treated bengala 1.0 4 Surface treated yellow iron oxide 2.0 5 Glyceryl trioctanoate 6.0 6 Methylphenyl polysiloxane 8.0 7 Preservatives 0.2 8 Fragrances 0.2

Example 12 Pressed Powder Using the treated powder of Example 3, the same procedure as in Example 9 was carried out to obtain the desired pressed powder. Composition (%) 1 Surface treated sericite 30.0 2 Surface treated talc 57.89 3 Surface treated red iron oxide 0.2 4 Surface treated yellow iron oxide 0.5 5 Surface treated black iron oxide 0.01 6 Surface treated titanium oxide 3 0.07 Glyceryl trioctanoate 4.08 Dimethylpolysiloxane 4.09 Preservative 0.2 10 Fragrance 0.2

The cosmetics obtained in Examples 9 to 12 were all excellent in use feeling and stability, and had extremely good cosmetic durability.

[0066]

EFFECT OF THE INVENTION The cosmetic of the present invention is excellent in the effect of preventing makeup collapse due to sweat and sebum, and has a feeling of use, especially a feeling of fit.
Excellent in smoothness.

Continued on the front page (51) Int.Cl. ⁷ Identification symbol FI Theme coat II (reference) // C08J 3/12 C08J 3/12 Z F term (reference) 4C083 AB232 AB242 AB432 AC022 AC102 AC422 AC902 AD151 AD152 AD162 BB25 CC01 CC05 CC12 CC14 DD17 DD31 EE06 4F070 AA02 AA13 AA18 AA32 AA45 AA46 AA50 AA53 AA54 AA60 AC92 BA08 BB02 DC02 DC05 DC11

Claims (3)

[Claims] (1) The surface of a powder is represented by the following general formula (1): wherein R1 is the same or different alkyl or aryl group having 1 to 20 carbon atoms, R2 is -R5-Rf (wherein R5
Represents a divalent alkylene group having 2 to 6 carbon atoms, and Rf represents a perfluoroalkyl group having 1 to 12 carbon atoms. ), R
3 -R5-SiX ₃ (wherein, X represents an alkoxyl group or a halogen having 1 to 4 carbon atoms.), R4 is either R1 or R2 or R3, l, m, n is a integer Where l = 0 to 500, m = 1 to 500, n = 1 to
500. ] A cosmetic obtained by mixing a powder obtained by treating with a fluorine-containing silicone represented by the formula (1) and (b) silicone oil. FIG. 2. In the structure of the general formula (1), 1 = 0, m = 1
-50, n = 1-50, and the ratio of m to n is 9: 1 to 2: 3
The cosmetic according to claim 1, wherein 3. In the structure of the general formula (1), 1 = 0, m = 1
-50, n = 1-50, and the ratio of m to n is 3: 1 to 1: 1
The cosmetic according to claim 1, wherein