GB808163A - Improvements relating to sintered frictional materials - Google Patents
Improvements relating to sintered frictional materialsInfo
- Publication number
- GB808163A GB808163A GB4093/57A GB409357A GB808163A GB 808163 A GB808163 A GB 808163A GB 4093/57 A GB4093/57 A GB 4093/57A GB 409357 A GB409357 A GB 409357A GB 808163 A GB808163 A GB 808163A
- Authority
- GB
- United Kingdom
- Prior art keywords
- per cent
- mixture
- weight
- sintered
- phosphorus
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
A brake shoe, drum, or disc is formed by compressing and sintering a mixture containing Fe powder, from 2 to 15 per cent by weight of powdered frictional material selected from asbestos, talc, feldspar and apatite, and P or a reducible phosphorus compound in such amount that the sintered braking means contains 0.1 to 2.5 per cent by weight of P. The phosphorus compound may be ferro-phosphorus or a phosphate of Fe or of the alkali or alkaline earth metals; or red phosphorus may be used. The Fe amounts preferably to 80 to 95 per cent by weight of the mixture and up to 10 per cent Cu may also be present. The mixture is compressed to the desired shape (e.g. 8 tons per sq. cm.) and sintered under reducing conditions, e.g. in hydrogen, at between 1050 DEG C. (the eutectric Fe-P melting point) and 1300 DEG C. Up to 2 per cent of lubricant such as zinc stearate and graphite may also be used in the mixture.
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| SE808163X | 1956-02-11 |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| GB808163A true GB808163A (en) | 1959-01-28 |
Family
ID=20342759
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| GB4093/57A Expired GB808163A (en) | 1956-02-11 | 1957-02-06 | Improvements relating to sintered frictional materials |
Country Status (1)
| Country | Link |
|---|---|
| GB (1) | GB808163A (en) |
Cited By (2)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US3120698A (en) * | 1960-09-15 | 1964-02-11 | Ferro Corp | Powdered metal compositions and method |
| EP0861913A1 (en) * | 1997-02-19 | 1998-09-02 | Basf Aktiengesellschaft | Iron powder containing phosphorus |
-
1957
- 1957-02-06 GB GB4093/57A patent/GB808163A/en not_active Expired
Cited By (3)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US3120698A (en) * | 1960-09-15 | 1964-02-11 | Ferro Corp | Powdered metal compositions and method |
| EP0861913A1 (en) * | 1997-02-19 | 1998-09-02 | Basf Aktiengesellschaft | Iron powder containing phosphorus |
| US6180235B1 (en) | 1997-02-19 | 2001-01-30 | Basf Aktiengesellschaft | Phosphorus-containing iron powders |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| US3836355A (en) | Steel powder containing phosphorus | |
| ES8702460A1 (en) | High carbon friction material | |
| FR2457887A1 (en) | FRICTION MATERIAL, ESPECIALLY USEFUL FOR BRAKES | |
| GB1466328A (en) | Sintered metallic composite material | |
| ES8701562A1 (en) | A manganese sulphide-containing iron powder mixture and a process for the production thereof. | |
| GB808163A (en) | Improvements relating to sintered frictional materials | |
| GB1449978A (en) | Refractory metal-containing bodies | |
| GB1291259A (en) | Improvements in friction mechanisms | |
| ES8301433A1 (en) | Steel-hard carbide macrostructured tools, compositions and methods of forming. | |
| ES445181A1 (en) | Friction materials containing spinel solid solution as friction modifier | |
| US2945759A (en) | Method for measuring the strength of sintered ferrous articles | |
| GB823675A (en) | Friction article and method of producing same | |
| GB807909A (en) | Improved porous sintered metal friction element | |
| GB1028762A (en) | Sintered friction materials | |
| GB656324A (en) | Improvements in or relating to brake shoes | |
| GB967553A (en) | Metal diamond compacts | |
| GB1387232A (en) | Carbon/metal friction composition for brake linings | |
| GB999348A (en) | Improvements in friction linings more particularly for aircraft brakes | |
| GB864769A (en) | Improvements in and relating to friction elements for brake and the like mechanisms | |
| ES432149A1 (en) | Powder-metallurgy of cobalt containing brass alloys | |
| GB1330946A (en) | Composition containing ferrophosphorus duitable for use in the steel industry | |
| GB885144A (en) | Method of producing shaped parts by sintering | |
| GB834946A (en) | Improvements in or relating to metal-bonded graphite | |
| GB533842A (en) | Porous metal articles | |
| US1958740A (en) | Porous metal structure |