GB1210790A - Fibrillatable filaments and bulk yarn of improved dyeability - Google Patents
Fibrillatable filaments and bulk yarn of improved dyeabilityInfo
- Publication number
- GB1210790A GB1210790A GB1231969A GB1231969A GB1210790A GB 1210790 A GB1210790 A GB 1210790A GB 1231969 A GB1231969 A GB 1231969A GB 1231969 A GB1231969 A GB 1231969A GB 1210790 A GB1210790 A GB 1210790A
- Authority
- GB
- United Kingdom
- Prior art keywords
- composition
- polyimine
- backbone
- fibrillatable
- atoms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
1,210,790. Artificial resin composition. ALLIED CHEMICAL CORP. 7 March, 1969 [1 April, 1968], No. 12319/69. Headings C3P and C3R. A composition comprises, in wt. per cent: (a) a polyimine-polyamide graft copolymer, 5-80; and (b) polyolefin(s) and/or polyester(s), 95-20. Graft copolymer (a) has a polyamine backbone wherein imino N-atoms are separated on average by # 5 chain atoms, and carry polyamide side-chains having 3-18 chain atoms between amide and carboxyl gps., with number average M.W. #500 but # ¢ M.W. of backbone; (a) may be prepared by polymerizing a lactam under non-alkaline conditions with a polyimine of M.W. #20,000, e.g. 50,000-500,000; 0À1-25 mol. polyimine is used per 100 mol. lactam; (a) preferably comprises a polycaprolactam side-chain on a polyethylenimine backbone. For (b) lists of suitable polyolefins and polyesters are given, preferred being isotactic polypropylene and/or polyethylene terephthalate. The composition may be prepared by melting a mixture of the polymers, preferably under a dry inert atmosphere, or by forming a solution of the polymers and either precipitating the mixture by adding a non-solvent, or evaporating the solvent. A fibrillatable strand may be obtained by forming a sheet or film of the composition and cutting into strips, or by extruding a monofilament of the composition. Subsequently performed may be stretching, crushing between rollers, and fibrillation by passage through an air jet stream. The split fibres have enhanced dyeability by acid dyes.
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| US71793568A | 1968-04-01 | 1968-04-01 |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| GB1210790A true GB1210790A (en) | 1970-10-28 |
Family
ID=24884112
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| GB1231969A Expired GB1210790A (en) | 1968-04-01 | 1969-03-07 | Fibrillatable filaments and bulk yarn of improved dyeability |
Country Status (5)
| Country | Link |
|---|---|
| BE (1) | BE730512A (en) |
| DE (1) | DE1915772A1 (en) |
| FR (1) | FR2007355A1 (en) |
| GB (1) | GB1210790A (en) |
| NL (1) | NL6904612A (en) |
Cited By (3)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| EP0122304A1 (en) * | 1983-04-15 | 1984-10-24 | General Electric Company | Polyetherimide-polypropylene blends |
| US6677015B2 (en) | 2000-12-21 | 2004-01-13 | Degussa Ag | Molding composition with good capability for blow molding |
| US6726999B2 (en) | 2000-12-21 | 2004-04-27 | Degussa Ag | Free flowing polyester molding composition |
-
1969
- 1969-03-07 GB GB1231969A patent/GB1210790A/en not_active Expired
- 1969-03-25 NL NL6904612A patent/NL6904612A/xx unknown
- 1969-03-26 BE BE730512D patent/BE730512A/xx unknown
- 1969-03-26 FR FR6908997A patent/FR2007355A1/fr not_active Withdrawn
- 1969-03-27 DE DE19691915772 patent/DE1915772A1/en active Pending
Cited By (3)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| EP0122304A1 (en) * | 1983-04-15 | 1984-10-24 | General Electric Company | Polyetherimide-polypropylene blends |
| US6677015B2 (en) | 2000-12-21 | 2004-01-13 | Degussa Ag | Molding composition with good capability for blow molding |
| US6726999B2 (en) | 2000-12-21 | 2004-04-27 | Degussa Ag | Free flowing polyester molding composition |
Also Published As
| Publication number | Publication date |
|---|---|
| BE730512A (en) | 1969-09-01 |
| FR2007355A1 (en) | 1970-01-09 |
| NL6904612A (en) | 1969-10-03 |
| DE1915772A1 (en) | 1969-10-30 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| CA1332642C (en) | Process for the preparation of thermoplastic fibres | |
| US4424257A (en) | Self-crimping multi-component polyamide filament wherein the components contain differing amounts of polyolefin | |
| Lemstra et al. | Speciality products based on commodity polymers | |
| US3546319A (en) | Blends of polyamides,polyester and polyolefins containing minor amounts of elastomers | |
| Gogolewski et al. | High-modulus fibres of nylon-6 prepared by a dry-spinning method | |
| US8313678B2 (en) | Preparing method of microporous high density polyethylene film | |
| US4228218A (en) | Polymer composite material | |
| CA1224297A (en) | Graft-modified ultrahigh-molecular-weight polyethylene and process for producing same | |
| JP3347835B2 (en) | Method for producing microporous polyolefin membrane | |
| Endo et al. | Polyethylene‐polycarbonate blends: Interface modification, phase morphology and measurement of orientation development during cast film and tubular extrusion by infrared dichroism | |
| JPH0987413A (en) | Production of finely porous membrane of polyolefin | |
| CA2218602A1 (en) | Uniaxially shrinkable biaxially oriented polypropylene films | |
| NL8901253A (en) | POLYMERIC FILAMENTS, TAPES AND FILMS WITH HIGH MODULUS, HIGH STRENGTH AND HIGH MELTING TEMPERATURE AND A METHOD FOR THE PRODUCTION THEREOF. | |
| JP2001172420A (en) | Polyolefin microporous membrane and method for producing the same | |
| NZ229218A (en) | Polymer composition comprising a polypropylene and an isotactic but-1-ene polymer | |
| MY113608A (en) | Microporous film of high molecular weight polyolefin and process for producing same | |
| GB1161585A (en) | Stretched Opalescent Films consisting of Thermoplastic Polymers | |
| US3182100A (en) | Monofilament polyamide fishline composition | |
| GB1164582A (en) | Improvements relating to Graft Copolymers | |
| GB1210790A (en) | Fibrillatable filaments and bulk yarn of improved dyeability | |
| US3334153A (en) | Mixture of polyamide, polystyrene, and polyamide-styrene graft copolymer | |
| EP0139141B1 (en) | Production of stretched polymeric material having high strength and high modulus | |
| GB1201101A (en) | A method of producing non-sticky filamentary material consisting of copolyamide | |
| JP3009495B2 (en) | Polyolefin microporous membrane and method for producing the same | |
| GB1306974A (en) | Synthetic fine filament bundle and island-in-a-sea- type composite filament usable for manufacturing the bundle and processes of manufacturing the same |
Legal Events
| Date | Code | Title | Description |
|---|---|---|---|
| PS | Patent sealed | ||
| PLNP | Patent lapsed through nonpayment of renewal fees |