GB1004748A - Improvements in methods of manufacturing sintered ferrite bodies - Google Patents

Improvements in methods of manufacturing sintered ferrite bodies

Info

Publication number
GB1004748A
GB1004748A GB31511/64A GB3151164A GB1004748A GB 1004748 A GB1004748 A GB 1004748A GB 31511/64 A GB31511/64 A GB 31511/64A GB 3151164 A GB3151164 A GB 3151164A GB 1004748 A GB1004748 A GB 1004748A
Authority
GB
United Kingdom
Prior art keywords
cooling
atmosphere
oxygen content
zinc
ferrite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB31511/64A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Philips Electronics UK Ltd
Original Assignee
Philips Electronic and Associated Industries Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Philips Electronic and Associated Industries Ltd filed Critical Philips Electronic and Associated Industries Ltd
Publication of GB1004748A publication Critical patent/GB1004748A/en
Expired legal-status Critical Current

Abstract

1,004,748. Magnetic compositions. PHILIPS ELECTRONIC & ASSOCIATED INDUSTRIES Ltd. Aug. 4, 1964 [Aug. 5, 1963], No. 31511/64. Heading H1H. A manganese-zinc ferrite is made by a process which includes a complex sintering schedule to achieve the desired oxygen content of the final material. In particular, a method of making a MnZn ferrite comprises presintering a mixture of oxides or equivalent compounds the mixture consisting of 24À5-28À5mol. %MnO, 53-54 mol. % Fe 2 0 3 and balance ZnO, cooling and pulverizing the presintered product, forming a shaped body, sintering between 1370‹ and 1430‹ C. in an atmosphere containing 95% O 2 for between 15 minutes and 3 hours, then cooling the sintered body, initiating a gradual reduction of the oxygen content when the body is between 1250‹ and 1310‹ C., continuing the reduction of oxygen so that at 1150‹ C. the atmosphere contains less than 0.2% 0 2 and cooling to room temperature in this atmosphere, providing means for controlling the evaporation of zinc (e.g. by placing in a ferrite pot of the same composition as the body, or by adding zinc vapour to the atmosphere), heating the body to between 1250‹ and 1310‹ C. in an atmosphere containing between 0.05 and 1% O 2 and maintaining this for 5-10 hours, and cooling to room temperature while the oxygen content does not exceed 0.1%.
GB31511/64A 1963-08-05 1964-08-04 Improvements in methods of manufacturing sintered ferrite bodies Expired GB1004748A (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
NL296282 1963-08-05

Publications (1)

Publication Number Publication Date
GB1004748A true GB1004748A (en) 1965-09-15

Family

ID=19754941

Family Applications (1)

Application Number Title Priority Date Filing Date
GB31511/64A Expired GB1004748A (en) 1963-08-05 1964-08-04 Improvements in methods of manufacturing sintered ferrite bodies

Country Status (12)

Country Link
JP (1) JPS412836B1 (en)
AT (1) AT252592B (en)
BE (1) BE651395A (en)
CH (1) CH464377A (en)
DE (1) DE1471349A1 (en)
DK (1) DK116384B (en)
ES (1) ES302762A1 (en)
FR (1) FR1403510A (en)
GB (1) GB1004748A (en)
LU (1) LU46680A1 (en)
NL (1) NL296282A (en)
SE (1) SE301523B (en)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114085086A (en) * 2021-11-02 2022-02-25 宝钢磁业（江苏）有限公司 Sintering process of iron-rich ultrahigh Bs material

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0400716A1 (en) * 1989-05-26 1990-12-05 Koninklijke Philips Electronics N.V. Soft magnetic magnesium-manganese-zinc-ferrite material and products thereof
CN116751045B (en) * 2023-05-12 2024-09-24 日照亿鑫电子材料有限公司 A cold sintered manganese-zinc ferrite material and preparation method thereof

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114085086A (en) * 2021-11-02 2022-02-25 宝钢磁业（江苏）有限公司 Sintering process of iron-rich ultrahigh Bs material

Also Published As

Publication number Publication date
CH464377A (en) 1968-10-31
FR1403510A (en) 1965-06-18
LU46680A1 (en) 1964-10-03
ES302762A1 (en) 1965-01-01
JPS412836B1 (en) 1966-02-22
BE651395A (en) 1965-02-04
DE1471349A1 (en) 1969-02-27
SE301523B (en) 1968-06-10
DK116384B (en) 1970-01-05
AT252592B (en) 1967-02-27
NL296282A (en)

Similar Documents

Publication Publication Date Title
US3565806A (en) Manganese zinc ferrite core with high initial permeability
GB954775A (en) Improvements in methods of manufacturing sintered ferrite bodies
GB923991A (en) Oxide magnetic material
GB1004748A (en) Improvements in methods of manufacturing sintered ferrite bodies
GB823971A (en) Improvements in or relating to ferromagnetic ferrite materials
GB836674A (en) Improvements in or relating to methods of producing manganese zinc ferrites
GB1060598A (en) Ferromagnetic cores and processes for the preparation thereof
GB1304237A (en)
GB994240A (en) Improvements in or relating to methods of manufacturing magnetic cores and magnetic cores manufactured by such methods
US3065181A (en) Inductor materials
GB1390279A (en) Manganese-zinc ferrites
GB1271706A (en) Improvements in or relating to manganese-zinc ferrite materials
GB959643A (en)
US3778374A (en) Process for producing ferrites
GB1227459A (en)
GB1523910A (en) Method of manufacturing ferrite cores
GB1056315A (en) Process for the manufacture of manganese-zinc ferrites
GB875600A (en) Improvements relating to magnetic cores for use as memory elements
GB1057774A (en) Magnetic oxide material
GB911642A (en) Improvements in or relating to ferromagnetic materials
GB982756A (en) Process for sintering a ferrite body
JP2532159B2 (en) Transformer core for high frequency power supply
GB1070510A (en) Ferromagnetic materials and processes for their manufacture
JPH0544807B2 (en)
GB883291A (en) Improvements in or relating to ferromagnetic ferrite cores