FR2314158A1 - Unfired refractory bonded with feldspathoid material - formed by reacting clay and alkali, mixing with refractory and heating at low temp - Google Patents

Unfired refractory bonded with feldspathoid material - formed by reacting clay and alkali, mixing with refractory and heating at low temp

Info

Publication number
FR2314158A1
FR2314158A1 FR7517902A FR7517902A FR2314158A1 FR 2314158 A1 FR2314158 A1 FR 2314158A1 FR 7517902 A FR7517902 A FR 7517902A FR 7517902 A FR7517902 A FR 7517902A FR 2314158 A1 FR2314158 A1 FR 2314158A1
Authority
FR
France
Prior art keywords
refractory
alkali
feldspathoid
mixing
heating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
FR7517902A
Other languages
French (fr)
Inventor
Joseph Davidovits
Jacques Lavau
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CORDI
Original Assignee
CORDI
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CORDI filed Critical CORDI
Priority to FR7517902A priority Critical patent/FR2314158A1/en
Priority to BE2055014A priority patent/BE841637A/en
Priority to DE19762621814 priority patent/DE2621814A1/en
Publication of FR2314158A1 publication Critical patent/FR2314158A1/en
Withdrawn legal-status Critical Current

Abstract

In the mfr. of refractory articles, intergranular bonding is obtd. using a synthetic felspathoid material, obtd. by reaction between a clay and an alkali in a few mins. at 100-200 degrees C. The felspathoid material is mixted with the refractory material in amts. of 1-5 wt.% as a dry powder. The refractory articles can be made without a firing step yet can be used at 1400 degrees C. Pieces of large dimensions and of complicated shapes can be produced in reproducible shapes and sizes without unpredictable shrinkages and crystallographic transformations etc. Used for saggars and other plates for firing ceramics, for cores for metal castings, etc.
FR7517902A 1975-06-09 1975-06-09 Unfired refractory bonded with feldspathoid material - formed by reacting clay and alkali, mixing with refractory and heating at low temp Withdrawn FR2314158A1 (en)

Priority Applications (3)

Application Number Priority Date Filing Date Title
FR7517902A FR2314158A1 (en) 1975-06-09 1975-06-09 Unfired refractory bonded with feldspathoid material - formed by reacting clay and alkali, mixing with refractory and heating at low temp
BE2055014A BE841637A (en) 1975-06-09 1976-05-10 PROCESS FOR THE MANUFACTURE OF MOLDED REFRACTORY ARTICLES, AND PRODUCTS RESULTING FROM THIS PROCESS
DE19762621814 DE2621814A1 (en) 1975-06-09 1976-05-15 PROCESS FOR THE MANUFACTURING OF FIRE-RESISTANT MOLDED PIECES AND ARTICLES MADE TO MEASURE THE SAME

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
FR7517902A FR2314158A1 (en) 1975-06-09 1975-06-09 Unfired refractory bonded with feldspathoid material - formed by reacting clay and alkali, mixing with refractory and heating at low temp

Publications (1)

Publication Number Publication Date
FR2314158A1 true FR2314158A1 (en) 1977-01-07

Family

ID=9156206

Family Applications (1)

Application Number Title Priority Date Filing Date
FR7517902A Withdrawn FR2314158A1 (en) 1975-06-09 1975-06-09 Unfired refractory bonded with feldspathoid material - formed by reacting clay and alkali, mixing with refractory and heating at low temp

Country Status (3)

Country Link
BE (1) BE841637A (en)
DE (1) DE2621814A1 (en)
FR (1) FR2314158A1 (en)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1983003093A1 (en) * 1982-03-08 1983-09-15 Michel Davidovics Method for manufacturing decorated, enamelled ceramic by monofiring, with geopolymer silico-aluminates
EP0494015A1 (en) * 1991-01-03 1992-07-08 Societe Nationale Des Poudres Et Explosifs High-temperature thermal insulating materials and process for their manufacture

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1983003093A1 (en) * 1982-03-08 1983-09-15 Michel Davidovics Method for manufacturing decorated, enamelled ceramic by monofiring, with geopolymer silico-aluminates
EP0494015A1 (en) * 1991-01-03 1992-07-08 Societe Nationale Des Poudres Et Explosifs High-temperature thermal insulating materials and process for their manufacture
FR2671343A1 (en) * 1991-01-03 1992-07-10 Poudres & Explosifs Ste Nale HIGH TEMPERATURE THERMAL INSULATING MATERIALS AND METHOD FOR MANUFACTURING THERMAL INSULATION MATERIALS.

Also Published As

Publication number Publication date
BE841637A (en) 1976-09-01
DE2621814A1 (en) 1976-12-16

Similar Documents

Publication Publication Date Title
GB990840A (en) Light refractory brick
GB1268982A (en) Alumina refractories
FR2314158A1 (en) Unfired refractory bonded with feldspathoid material - formed by reacting clay and alkali, mixing with refractory and heating at low temp
GB1123602A (en) Production of refractory bodies
GB717555A (en) Improvements in or relating to shaped silicon nitride bodies and their manufacture
GB682432A (en) New porous materials suitable for use as thermal and acoustic insulators and process for their manufacture
ZA721295B (en) Process for manufacturing granular,expanded ceramic materials
GB1432091A (en) Method of treating heavy metal-containing residues
JPS51126979A (en) Process for utilizing sodium aeetate trihy drate as a chief component of heat accumulator for room heating
GB1005437A (en) Improvements in and relating to light-weight fireproof products
GB1373441A (en) Brick production
FR2269505A1 (en) White facing bricks of low porosity - made by mixing white firing clay with glass powder, moulding and firing
JPS51124608A (en) An installation method of plastic refractory blocks
Kalugina et al. Large ceramic blocks from loams
ES419175A1 (en) Process of making burnt refractory bricks
GB847852A (en) A pozzolanic material and concrete produced therewith
GB758917A (en) Improvements in or relating to kiln furniture
GB575106A (en) Improvements in or relating to furnace hearths
GB1035354A (en) Improvements in and relating to bricks
Jelinek et al. Low temperature thermal expansion and specific heat properties of structural materials
GB1008929A (en) Method of in situ fabrication of a monolith refractory lining or the like
GB921526A (en) Refractory basic or neutral bricks and furnace linings
GB1420764A (en) Production o fcellular ceramics and shaped articles made thereof
GB1095751A (en) Improvements in or relating to refractory bricks, blocks and like articles
Fischer Present stage of development of fused lime refractories

Legal Events

Date Code Title Description
TP Transmission of property
ST Notification of lapse