ES2421172A1

ES2421172A1 - Manufacturing process of construction parts, with natural stone residues, binders and additives (Machine-translation by Google Translate, not legally binding)

Info

Publication number: ES2421172A1
Application number: ES201200198A
Authority: ES
Inventors: Ricardo ABAD GONZÁLEZ
Original assignee: NAIES MICHELE
Current assignee: NAIES MICHELE
Priority date: 2012-02-23
Filing date: 2012-02-23
Publication date: 2013-08-29
Anticipated expiration: 2032-02-23
Also published as: ES2421172B1

Abstract

Manufacturing process of construction parts, with natural stone residues, binders and additives. The aim is to protect the process and manufacture of a new component, which is made with the mixture of a thermosetting polymer and natural stone residues, which is joined to a mixture of magnesium oxychloride (cementitious material) and residues of natural stone. ; where the unión, of both mixtures, occurs with the use of inorganic materials, such as: residues of natural stone; textile or synthetic material; cork; cardboard: expanded polymer: wood or derivatives: etc., which are placed between both mixtures, forming the new component. (Machine-translation by Google Translate, not legally binding)

Description

Procedimiento de fabricación de piezas constructivas, con residuos de piedra natural, aglomerantes y aditivos. Manufacturing process of construction pieces, with natural stone residues, binders and additives.

La presente invención tiene por objeto la protección del "procedimiento de fabricación de piezas constructivas, realizadas, con residuos procedentes de la piedra natural, con aglomerantes y aditivos”. The object of the present invention is the protection of the "manufacturing process of construction pieces, made with residues from natural stone, with binders and additives".

Producto que se emplea en la construcción y que se realiza a través de una mezcla de los siguientes componentes: residuos de la piedra natural, polímeros termoestables, aditivos diversos y una composición de oxicloruro de magnesio con residuos de la piedra natural. También en una cara o caras vistas, se puede o no incorporar una o unas laminas de cristal o fragmentos de cristal, con fines de higiene, limpieza y decorativos. Product that is used in construction and is made through a mixture of the following components: natural stone residues, thermostable polymers, various additives and a composition of magnesium oxychloride with natural stone residues. Also on one side or sided faces, one or some glass sheets or glass fragments may or may not be incorporated, for hygiene, cleaning and decorative purposes.

El producto resultante a cuyo objetivo se orienta, preferencial mente, al procedimiento reivindicado, tiene diferentes aplicaciones en el sector de la construcción, como por ejemplo: encimeras de cocina, revestimiento de paredes, solados, etc. Pero en todos los casos se destaca, como característica técnica, prevalente, la consecución de acabados superficiales duros, uniformes, brillantes o mates, con una gran riqueza, aparencial y cromática. The resulting product whose objective, preferably, is directed to the claimed process, has different applications in the construction sector, such as: kitchen countertops, wall cladding, flooring, etc. But in all cases, the achievement of hard, uniform, bright or matt surface finishes, with great richness, appearance and color, stands out as a technical, prevalent characteristic.

Background of the invention

Es conocido el proceso de moldeo de resinas termoestables, principalmente con poliéster, que consiste en inyectar o depositar la resina sobre un molde, en forma de cubo u otras. Según un procedimiento, conocido, se opera con resinas poliéster, acondicionada con activadores de catálisis de la polimerización y endurecimiento del producto y se mezcla, con ella, áridos de cantera; piedra de granulometría y cromatismo seleccionada; formando, mediante un sistema de vacio, vibrado y compresión, grandes bloques, del orden de unos tres metros cubicas y un peso de unas ocho toneladas, que pasan a un proceso ordinario; de corte en un telar, para conseguir las tablas; que son, posteriormente, calibradas, pulidas y cortadas, a la medida deseada. The process of molding thermostable resins is known, mainly with polyester, which consists of injecting or depositing the resin on a mold, in the form of a cube or others. According to a known procedure, it is operated with polyester resins, conditioned with catalysis activators of the polymerization and hardening of the product and mixed, with it, quarry aggregates; granulometry and chromatism stone selected; forming, by means of a system of vacuum, vibration and compression, large blocks, of the order of about three cubic meters and a weight of about eight tons, which pass into an ordinary process; cutting on a loom, to get the boards; which are subsequently calibrated, polished and cut, to the desired extent.

Se comprende, que, siguiendo el proceso descrito, lo que se consigue es; la formación de bloques sintéticos, equiparables, funcionalmente, a los de la piedra natural y a los efectos de conseguir un producto final, que serán unas piedras planas, como losetas para placados, revestimientos o solados. It is understood that, following the process described, what is achieved is; the formation of synthetic blocks, functionally comparable, to those of natural stone and for the purpose of obtaining a final product, which will be flat stones, such as tiles for plating, cladding or flooring.

Por ello, con dicho procedimiento, se desaprovecha la versatilidad en la obtención de formas propias del moldeo y sobre todo se disipa la economía, que podría obtenerse con respecto al proceso de la piedra natural, por el aprovechamiento de productos residuales, como los detritos de las canteras, comparándolo con el gasto que comporta la formación y elaboración de los bloques y tablas sintéticas. Therefore, with this procedure, the versatility in obtaining forms of the molding is wasted and, above all, the economy is dissipated, which could be obtained with respect to the natural stone process, by the use of residual products, such as detritus of the quarries, comparing it with the expense of the formation and elaboration of the blocks and synthetic tables.

Descripción de la invención Description of the invention

La finalidad de la invención que constituye el objeto de esta patente, consiste en la protección del procedimiento de fabricación de piezas constructivas, con residuos de piedra natural, aglomerantes y aditivos. The purpose of the invention that constitutes the object of this patent is the protection of the manufacturing process of construction pieces, with natural stone residues, binders and additives.

En dicho proceso, se parte, como materia prima, de una mezcla compuesta por un polímetro termoestable, aditivos y cargas inorgánicas; preferentemente de naturaleza silícea o cálcica, dependiendo de la elección de las características finales del producto. Las características técnicas del polímero, como son: la flexibilidad, dureza, tenacidad, brillo, color, etc, pueden ser modificas con aditivos; la reacción de polimerización, puede ser catalizada dependiendo del polímero termoestable y catalizador utilizados; ya sea, a temperatura ambiente, con aminas o a temperaturas altas, con anhídridos o ácidos orgánicos; con el fin de acelerar el proceso de endurecimiento de la pieza moldeada. In said process, the raw material is based on a mixture consisting of a thermosetting multimeter, additives and inorganic fillers; preferably of siliceous or calcium nature, depending on the choice of the final characteristics of the product. The technical characteristics of the polymer, such as: flexibility, hardness, toughness, brightness, color, etc., can be modified with additives; The polymerization reaction can be catalyzed depending on the thermostable polymer and catalyst used; either, at room temperature, with amines or at high temperatures, with anhydrides or organic acids; in order to accelerate the hardening process of the molded part.

El proceso básico de la invención, esta orientado a la producción de piezas, para el sector de la construcción, cuyas características técnicas, prevalentes sean: de carácter estético más bien que mecánico y a la obtención de una importante economía en su producción; para que, dicho producto, esté al alcance de todos. The basic process of the invention is oriented to the production of parts, for the construction sector, whose technical characteristics are prevalent: aesthetic rather than mechanical and to obtain an important economy in its production; so that this product is available to everyone.

Comprende las siguientes operaciones descritas, con la misma secuencia con que se realiza: It comprises the following operations described, with the same sequence with which it is performed:

Colocación de un molde (Fig. 1), sobre una bancada rígida; que esta realizado, con un material antiadherente al polímero termoestable utilizado (polipropileno, polietileno, teflón, pvc; o también, con la utilización de cualquier otro material, depositando, previamente sobre el molde, el desmoldeante adecuado. Placing a mold (Fig. 1), on a rigid bench; that is made, with a non-stick material to the thermosetting polymer used (polypropylene, polyethylene, teflon, pvc; or also, with the use of any other material, previously depositing, on the mold, the appropriate release agent.

Se coloca sobre el molde (Fig. 1) o no, una lámina, de cristal o un triturado de cristal, de diversas granulometrías (Fig. 6-5). It is placed on the mold (Fig. 1) or not, a sheet, of glass or a crushed glass, of various granulometries (Fig. 6-5).

Se vierte, sobre el molde (Fig.1), una mezcla (Fig. 2), que está compuesta por polímero termoestable, aditivos cromáticos y cargas de materia inorgánica, procedente de los residuos de la piedra natural. A mixture (Fig. 2) is poured onto the mold (Fig. 2), which is composed of thermosetting polymer, chromatic additives and inorganic matter fillers, from natural stone residues.

Se vibra el molde (Fig.1), con la mezcla (Fig. 2); con el objeto de conseguir la expulsión del aire contenido en la mezcla, su compactación y su correcta distribución. The mold is vibrated (Fig. 1), with the mixture (Fig. 2); in order to achieve the expulsion of the air contained in the mixture, its compaction and its correct distribution.

Se deposita en el molde (Fig.1), sobre la mezcla (Fig. 2) una carga de residuo inorgánico (Fig. 3), que procede de: las canteras de piedra natural; material textil o sintético; corcho; cartón; polímero expandido; así como madera o derivados, etc. An inorganic waste load (Fig. 3) is deposited on the mixture (Fig. 1), on the mixture (Fig. 2), which comes from: the natural stone quarries; textile or synthetic material; cork; paperboard; expanded polymer; as well as wood or derivatives, etc.

A continuación, se deposita en el molde (Fig.1), sobre la mezcla (Fig. 2), sobre la carga inorgánica (Fig. 3), una mezcla de oxicloruro de magnesio, con aditivos y residuos de piedra natural (Fig. 4). Next, a mixture of magnesium oxychloride, with additives and natural stone residues (Fig. 2) is placed in the mold (Fig. 1), on the mixture (Fig. 2), on the inorganic filler (Fig. 3). 4).

Se vibra el molde (Fig.1), con la mezcla (Fig. 2), con el residuo inorgánico (Fig. 3) y con la mezcla de oxicloruro de magnesio, aditivos y residuos de piedra natural (Fig. 4). The mold is vibrated (Fig. 1), with the mixture (Fig. 2), with the inorganic residue (Fig. 3) and with the mixture of magnesium oxychloride, additives and natural stone residues (Fig. 4).

El molde (Fig. 1), con todos los componentes (2, 3, 4 y 5), mencionados, se deposita sobre una bancada en reposo, para su curación; o bien se introduce en una cámara de calor, a una temperatura entre 30º a 100º; con el fin de conseguir una catalización y curado más rápido. The mold (Fig. 1), with all the components (2, 3, 4 and 5), mentioned, is deposited on a resting bench, for its cure; or it is introduced into a heat chamber, at a temperature between 30º to 100º; in order to achieve faster catalyzing and curing.

Técnicas: Techniques:

Diversidad formal de los productos finales; ya que el proceso reivindicado, permite la obtención de elementos constructivos de cualquier forma y relieve; incluso, logrando la personalización del mismo, a la demanda del consumidor, aprovechando la versatilidad de la invención. Formal diversity of the final products; since the claimed process, allows to obtain constructive elements of any shape and relief; even, achieving the customization of the same, to the demand of the consumer, taking advantage of the versatility of the invention.

En el proceso de formación sintética de los bloques, solamente se pueden obtener piezas planas, de dimensiones estándar. In the process of synthetic formation of the blocks, only flat pieces of standard dimensions can be obtained.

En la orientación de la producción; ya que el procedimiento reivindicado esta orientado a la fabricación, directa e individualizada, de cada una de los productos. Mientras que el proceso de formación sintética de bloques o tablas, desarrolla la fabricación en serie de un producto o subproducto normalizado. In the orientation of production; since the claimed process is oriented to the manufacture, directly and individually, of each of the products. While the process of synthetic formation of blocks or boards, develops the mass production of a standardized product or by-product.

Económicas: Economic:

La supresión de unas operaciones innecesarias, como son: el aserrado del bloque en un telar y el calibrado, pulido y corte de las tablas, en piezas estándar. The suppression of unnecessary operations, such as: the sawing of the block in a loom and the calibration, polishing and cutting of the boards, in standard parts.

Fabricación directa de un producto, con una mínima manipulación y en un solo proceso, que beneficia directamente al consumidor. Direct manufacturing of a product, with minimal handling and in a single process, which directly benefits the consumer.

Brief description of the drawings

Para complementar la descripción de la invención y facilitar la interpretación de las características funcionales de su objeto, se acompañan los dibujos, en los que se representan, esquemáticamente, los diferentes fases de la realización del proceso de moldeo de elementos constructivos; que constituyen el objeto de esta patente. En dichos dibujos se observa lo siguiente: To complement the description of the invention and to facilitate the interpretation of the functional characteristics of its object, the drawings are attached, in which the different phases of the construction process of molding of construction elements are schematically represented; which constitute the object of this patent. In these drawings the following is observed:

La fig. 1 muestra el molde, que consiste en cuatro paredes y fondo, con las prestaciones, características y medidas del producto que se va a realizar (fig. 1-1). Fig. 1 shows the mold, which consists of four walls and bottom, with the features, characteristics and measurements of the product to be made (fig. 1-1).

La fig. 2 simboliza la mezcla del polímetro termoestable con una carga de residuos de piedra natural (fig. 2-2). Fig. 2 symbolizes the mixing of the thermosetting multimeter with a load of natural stone waste (fig. 2-2).

La fig. 3 simboliza la mezcla del polímetro termoestable con la carga del residuo inorgánico de piedra natural (fig. 2-2) y sobre ella el depósito de una carga de material inorgánico (fig. 3-3), que consiste en residuo de piedra natural; material textil o sintético; corcho; cartón; polímetro expandido; madera o derivados de la misma; etc. Fig. 3 symbolizes the mixing of the thermosetting multimeter with the loading of the inorganic waste of natural stone (fig. 2-2) and on it the deposit of a load of inorganic material (fig. 3-3), which consists of waste of natural stone; textile or synthetic material; cork; paperboard; expanded polymeter; wood or derivatives thereof; etc.

La fig. 4 simboliza todo lo que se menciona en la (fig. 3) y además se le añade una mezcla de oxiclororo de magnesio y una carga inorgánica de residuos de piedras naturales (fig. 4-4). Fig. 4 symbolizes everything mentioned in (fig. 3) and also a mixture of magnesium oxychloride and an inorganic load of natural stone residues (fig. 4-4) is added.

La fig. 5 simboliza todo lo mencionado en la (fig. 4) y además el molde (fig. 1-1). Fig. 5 symbolizes everything mentioned in (fig. 4) and also the mold (fig. 1-1).

La fig. 6 simboliza todo lo contemplado en la (fig. 5) y además se observa la posibilidad de incorporar o no, el producto final, una lamina de cristal o fragmentos de cristal, de diversa granulometría y cromatismo (fig. 6-5). Fig. 6 symbolizes everything contemplated in (fig. 5) and also the possibility of incorporating or not, the final product, a glass sheet or glass fragments, of different granulometry and chromatism (fig. 6-5) is observed.

Descripción de un ejemplo práctico de la realización de la invención Description of a practical example of the embodiment of the invention

El procedimiento comprende la utilización de un molde (fig. 1-1), con cuatro paredes y fondo; con la prestación antiadherente o no y con características y medidas adecuadas, para lograr el producto deseado. The procedure includes the use of a mold (fig. 1-1), with four walls and bottom; with the non-stick benefit or not and with appropriate features and measures, to achieve the desired product.

En el fondo del molde (fig. 1-1), se deposita una mezcla, compuesta por un polímetro termoestable y una carga de material inorgánico, consistente en residuos de piedra natural (fig. 2-2). At the bottom of the mold (fig. 1-1), a mixture is deposited, consisting of a thermosetting multimeter and a load of inorganic material, consisting of natural stone residues (fig. 2-2).

Después, se deposita en el molde una carga de material inorgánico (fig. 3-3) con el residuo de la piedra natural; material textil o sintético; corcho; cartón; polímetro expandido; madera o derivados de la misma; etc. Then, a load of inorganic material (fig. 3-3) with the residue of the natural stone is deposited in the mold; textile or synthetic material; cork; paperboard; expanded polymeter; wood or derivatives thereof; etc.

5 Depositamos sobre el molde una nueva mezcla, compuesta por oxicloruro de magnesio y una carga de material inorgánico, procedente de los residuos de la piedra natural (fig. 4-4). 5 We deposit a new mixture on the mold, composed of magnesium oxychloride and a load of inorganic material, from the natural stone residues (fig. 4-4).

Después, procedemos a depositar el molde y su contenido, para su reposo y curación sobre una bancada o en una cámara de calor. Then, we proceed to deposit the mold and its contents, for rest and cure on a bench or in a heat chamber.

Finalmente, procedemos al desmolden, clasificación y paletización, para su comercialización y venta. Finally, we proceed to the demoulding, classification and palletizing, for its commercialization and sale.

Claims

1. Manufacturing process of construction pieces, with natural stone residues, binders and additives and characterized in that it comprises:

A) Establish a mold (figure 1) with the appropriate shape and measures.

B) Deposit on the mold (figure 1) a mixture of natural stone waste, resin and the corresponding additive (figure 2-2).

C) Proceed to its vibration.

D) Deposit on the content (Figure 2-2), which is inside the mold (Figure 1), a load of inorganic material, which is observed (Figure 3-3).

E) Respect the catalytic time of the mixture.

F) Deposit on the content 2-3 (figure 3), which is inside the mold (figure 1), a mixture of natural stone residues with a cementitious product (figure 4-4).

G) Perform a vibrate.

H) Allow the construction piece to cure, in order to achieve its hardening.

I) The mold (figure 1) that is used to carry out the manufacturing process of construction pieces, with natural stone residues, binders and additives, as contemplated in claim 1 and in section A), is characterized in that it contemplates the dimensions and shape of the product and is made with: polypropylene, polyethylene, teflon, pvc, metal or glass; which are materials in which the mixture does not adhere and in which the release agent is deposited, if necessary.

2.2.: Procedimiento de fabricación de piezas constructivas, con residuos de piedra natural, aglomerantes y aditivos, que se depositan en el molde reivindicado en la reivindicación n° 1 y que se caracteriza porque se realiza a través de una mezcla de resina epoxy y residuos de piedra natural (Fig. 2) con unas proporciones que oscilan entre el 5% al 50% de resina y entre el 95% al 50% de residuos de piedra natural y a la que se añade el aditivo que consiste en un pigmento que colorea toda la mezcla, con el color deseado y una proporción máxima de un 20% del peso de la resina. Manufacturing process of construction pieces, with natural stone residues, binders and additives, which are deposited in the mold claimed in claim 1 and characterized in that it is carried out through a mixture of epoxy resin and natural stone residues (Fig. 2) with proportions ranging from 5% to 50% resin and between 95% to 50% natural stone waste and to which the additive consisting of a pigment that colors the entire mixture is added, with the desired color and a maximum proportion of 20% of the resin weight.

3.3.: Procedimiento de fabricación de piezas constructivas, con residuos de piedra natural, aglomerantes y aditivos y se caracteriza por que sobre el contenido reivindicado en la reivindicación n° 2 que se contempla en la figura n° 2, que está sobre el molde reivindicado en la reivindicación n° 1 y se contempla en la figura n° 1, se deposita una carga de material inorgánico (Fig. 3.3) que se extiende y cubre toda la superficie vista y que consiste en un granulado de piedra natural; una lamina de material textil o sintético; corcho; cartón, madera; polexpan; metal o los residuos de estos materiales mencionados. Con una dimensión máxima de 20 mm. Material inorgánico que queda adherido a la mezcla reivindicada en la reivindicación n° 2 y que se contempla en la figura 3.2 y que se observa en la figura 3.3 y sirve de unión fundamental para completar la pieza constructiva. Manufacturing process of construction pieces, with natural stone residues, binders and additives and characterized in that on the content claimed in claim 2 which is contemplated in figure 2, which is on the mold claimed in claim No. 1 and is contemplated in Figure No. 1, a load of inorganic material is deposited (Fig. 3.3) that extends and covers the entire exposed surface and consists of a natural stone granulate; a sheet of textile or synthetic material; cork; chipboard; polexpan; metal or waste of these mentioned materials. With a maximum dimension of 20 mm. Inorganic material that is adhered to the mixture claimed in claim 2 and which is contemplated in Figure 3.2 and which is observed in Figure 3.3 and serves as a fundamental union to complete the construction piece.

4.Four.: Procedimiento de fabricación de piezas constructivas, con residuos de piedra natural, aglomerantes y aditivos y se caracteriza por que sobre el contenido reivindicado en la reivindicación n° 3, que se contempla en la figura 3.3.2, que esta en el molde reivindicado en la reivindicación n° 1 y que contempla la figura n° 1, se deposita una mezcla de residuos de piedra natural, oxicloruro de magnesio, pigmento e hidrofugante (Fig. 4.4) y en las siguientes proporciones: a) residuos de piedra natural, 50% al 80%; b) oxicloruro de magnesio, 50% al 20%; e) pigmento e hidrofugante, el 20% y 10% respectivamente, del peso del oxicloruro de magnesio mencionado. Manufacturing process of construction pieces, with natural stone residues, binders and additives and characterized in that on the content claimed in claim 3, which is contemplated in Figure 3.3.2, which is in the mold claimed in the claim 1 and which contemplates figure 1, a mixture of natural stone, magnesium oxychloride, pigment and hydrophobic residues is deposited (Fig. 4.4) and in the following proportions: a) natural stone residues, 50% at 80%; b) magnesium oxychloride, 50% to 20%; e) pigment and hydrofugante, 20% and 10% respectively, of the weight of the magnesium oxychloride mentioned.

5.5.: Procedimiento de fabricación de piezas constructivas, con residuos de piedra natural, aglomerantes y aditivos, y que se caracteriza porque el molde, reivindicado en la reivindicación n° 1 , que se contempla con la figura 1, se deposita una lamina de cristal o fragmentos del mismo (Fig. 6.5). Cuando es una lámina cubre en su totalidad el fondo del molde reivindicado en la reivindicación n° 1 y contemplado en la figura 1, y cuando son fragmentos cubren todo el fondo del molde reivindicado en la reivindicación n° 1 y que se contempla en la figura 1 y tiene longitud y espesor máximo de 20 mm. Method of manufacturing construction pieces, with natural stone residues, binders and additives, and characterized in that the mold, claimed in claim 1, which is contemplated with Figure 1, is deposited a glass sheet or fragments of the same (Fig. 6.5). When it is a sheet it completely covers the bottom of the mold claimed in claim 1 and contemplated in figure 1, and when they are fragments they cover the entire bottom of the mold claimed in claim 1 and contemplated in the figure 1 and has a maximum length and thickness of 20 mm.

SPANISH OFFICE OF THE PATENTS AND BRAND

Application no .: 201200198

SPAIN

Date of submission of the application: 23.02.2012

Priority Date:

REPORT ON THE STATE OF THE TECHNIQUE

51 Int. Cl.: See Additional Sheet

RELEVANT DOCUMENTS

Categoría Category: 56 Documentos citados Reivindicaciones afectadas 56 Documents cited Claims Affected

X X: FR 2923174 A1 (NAIES MICHELE) 08.05.2009, 1-2 FR 2923174 A1 (NAIES MICHELE) 08.05.2009, 1-2

página 2, líneas 15-23; página 4, líneas 25-30. page 2, lines 15-23; page 4, lines 25-30.

X X: BASE DE DATOS WPI EN EPOQUE, AN 2010-J45154, KR 100967077 B (MOON T M) 1 WPI DATABASE IN EPOQUE, AN 2010-J45154, KR 100967077 B (MOON T M) one

01.07.2010, resumen. 01.07.2010, summary.

A TO: ES 2342113 T3 (TONCELLI DARIO) 01.07.2010, 1-5 ES 2342113 T3 (TONCELLI DARIO) 01.07.2010, 1-5

reivindicación 1. claim 1.

A TO: FR 2795359 A1 (MORIN SYSTEME ET ARCHITECTONIQ) 29.12.2000 1-5 FR 2795359 A1 (MORIN SYSTEME ET ARCHITECTONIQ) 29.12.2000 1-5

Categoría de los documentos citados X: de particular relevancia Y: de particular relevancia combinado con otro/s de la misma categoría A: refleja el estado de la técnica O: referido a divulgación no escrita P: publicado entre la fecha de prioridad y la de presentación de la solicitud E: documento anterior, pero publicado después de la fecha de presentación de la solicitud Category of the documents cited X: of particular relevance Y: of particular relevance combined with other / s of the same category A: reflects the state of the art O: refers to unwritten disclosure P: published between the priority date and the date of priority submission of the application E: previous document, but published after the date of submission of the application

El presente informe ha sido realizado • para todas las reivindicaciones • para las reivindicaciones nº: This report has been prepared • for all claims • for claims no:

Fecha de realización del informe 27.06.2013 Date of realization of the report 27.06.2013: Examinador J. García Cernuda Gallardo Página 1/4 Examiner J. García Cernuda Gallardo Page 1/4

REPORT OF THE STATE OF THE TECHNIQUE

Application number: 201200198

CLASSIFICATION OBJECT OF THE APPLICATION B28B1 / 087 (2006.01)

C04B24 / 32 (2006.01) B28B1 / 087 (2006.01) Minimum documentation sought (classification system followed by classification symbols)

B28B, C04B

Electronic databases consulted during the search (name of the database and, if possible, terms of search used) INVENES, WPI, EPODOC, XPESP, TXTEP1, TXTGB1, TXTUS2, TXTUS3, TXTUS4

State of the Art Report Page 2/4

WRITTEN OPINION

Application number: 201200198

Date of Completion of Written Opinion: 06.27.2013

Statement

Novedad (Art. 6.1 LP 11/1986) Novelty (Art. 6.1 LP 11/1986): Reivindicaciones Reivindicaciones 3-5 1-2 SI NO Claims Claims 3-5 1-2 IF NOT

Actividad inventiva (Art. 8.1 LP11/1986) Inventive activity (Art. 8.1 LP11 / 1986): Reivindicaciones Reivindicaciones 3-5 1-2 SI NO Claims Claims 3-5 1-2 IF NOT

The application is considered to comply with the industrial application requirement. This requirement was evaluated during the formal and technical examination phase of the application (Article 31.2 Law 11/1986).

Opinion Base.-

This opinion has been made on the basis of the patent application as published.

State of the Art Report Page 3/4

WRITTEN OPINION

Application number: 201200198

1. Documents considered.-

The documents belonging to the state of the art taken into consideration for the realization of this opinion are listed below.

Documento Document: Número Publicación o Identificación Fecha Publicación Publication or Identification Number publication date

D01 D01: FR 2923174 A1 (NAIES MICHELE) 08.05.2009 FR 2923174 A1 (NAIES MICHELE) 05.08.2009

D02 D02: KR 100967077 B1 (MOON T M) 01.07.2010 KR 100967077 B1 (MOON T M) 01.07.2010

D03 D03: ES 2342113 T3 (TONCELLI DARIO) 01.07.2010 ES 2342113 T3 (TONCELLI DARIO) 01.07.2010

D04 D04: FR 2795359 A1 (MORIN SYSTEME ET ARCHITECTONIQ) 29.12.2000 FR 2795359 A1 (MORIN SYSTEME ET ARCHITECTONIQ) 29.12.2000

2. Statement motivated according to articles 29.6 and 29.7 of the Regulation of execution of Law 11/1986, of March 20, on Patents on novelty and inventive activity; quotes and explanations in support of this statement

The application refers to a manufacturing process of construction pieces with natural stone residues, binders and additives characterized in that it comprises establishing a mold with the appropriate shape and measures, depositing in it a mixture of waste and natural stone, resin and additive, proceed to its vibration, deposit a load of inorganic material on the contents, allow the catalysis of the mixture to pass, deposit a mixture of natural stone residues with a cementitious product on the mold content, perform a vibration, allow the piece to harden it, all in a mold of polypropylene, polyethylene, teflon, PVC, metal or glass (reiv. 1). The process includes a mixture of epoxy resin and natural stone residues (reiv. 2). Document D01 refers to a manufacturing process for building parts based on a mixture of granules and natural stone dust, binders and additives. It includes the elaboration of a mold in which an anti-adhesive is placed and in which the mixture is incorporated, a vibration, removal of the piece and removal of the non-adhesive (p. 2 line 1523). The film consists of a plastic material such as polypropylene, polyethylene, PVC, Teflon and the binder may consist of a thermosetting polymer such as epoxy resin (page 4 line 25-30). With these characteristics, those of claims 1 and 2 of the application are anticipated. Document D02 refers to a rock dust introduced into a mold with high strength concrete and subsequently subjected to vibration and curing. Concrete contains resin powder and other additives. These data anticipate the content of claim 1 of the application. Document D03 refers to an installation for the manufacture of conglomerated articles in the form of slabs of stone material, in which the initial mixture is deposited inside a tray mold, in a second station a vibrocompression machine operates in vacuum, a third station to harden the binder of the initial mixture and transfer media (reiv. 1). The components of the initial mixture are not specified. Document D04 refers to a method of manufacturing wall cladding plates. It consists of placing in a mold a mortar that includes hydraulic binder, sand, fibers, metacaolin, plasticizer and water and vibrating said mortar (p. 1 line. 28-37). A mixture of waste and natural stone with resin is not mentioned in the mortar content. It is considered that claims 1 and 2 of the application do not meet the requirements of novelty and inventive activity, while claims 3-4 do meet said requirements, in accordance with art. 6.1 and 8.1 of the L.P.

State of the Art Report Page 4/4