DE19626868A1

DE19626868A1 - Gold@ crystals preparation

Info

Publication number: DE19626868A1
Application number: DE1996126868
Authority: DE
Inventors: Guenter Dipl Phys Wolf
Original assignee: Individual
Current assignee: Individual
Priority date: 1996-07-04
Filing date: 1996-07-04
Publication date: 1998-01-08
Anticipated expiration: 2016-07-05
Also published as: DE19626868C2

Abstract

Process for preparing gold crystals comprises adding mercury to pure gold or to gold doped with other elements; heating the mixture to a predetermined temperature; annealing the mixture for a period at this temperature; cooling at a defined rate to a predetermined final temperature; and using this temperature as a starting point either for the addition of a solvent (especially HNO3), to dissolve out the mercury, or for the removal of mercury by vapourisation or vacuum distillation. The gold starting material may be pure gold or it may be doped or mixed with other elements such as silver. The gold is e.g. filed to increase the surface area so that the gold dissolves rapidly in the mercury. The mixture of gold and mercury can be heated to temperatures up to 357 deg C at normal pressure and to higher temperatures under elevated pressures. The Au/Hg solution is annealed for a time at the prevailing temperature and pressure, then cooled either continuously or stepwise to a specified temperature to cause crystallisation of the gold. Finally, the Hg is removed either by addition of a solvent such as HNO3 or by vapourisation or vacuum distillation of the Hg.

Description

Kristallzüchtungen werden aus den verschiedensten Phasen und mit den verschiedensten Verfahren durchgeführt.Crystal growths are made up of different phases and with the performed a wide variety of processes.

Goldkristalle kann man elektolytisch züchten, über die Gasphase oder durch Züchtung aus der Schmelze. Bei den ersten zwei Verfahren sind die Kristallstrukturen nicht abwechslungsreich und mit denen - in der Natur vorkommenden - nicht zu vergleichen. Beim dritten Verfahren handelt es sich um einen festen Körper und einzelne freie Kristalle gibt es nicht.Gold crystals can be grown electrolytically, via the gas phase or by breeding from the melt. The first two methods are Crystal structures not varied and with those - in nature occurring - not to be compared. The third method is there is no solid body and individual free crystals.

Gegenstand der Erfindung ist es nun Goldkristalle zu züchten, die sich einzeln darstellen, den Kristallen in der Natur gleichen und mehr noch, das Gesamtspektrum der vorkommenden Goldkristalle zu ergänzen und zu erweitern. Zum einen wird es dadurch möglich, in der Geologie, Mineralogie und in der Kristallographie Rückschlüsse auf die Natur der Goldkristalle zu ziehen, und zum anderen kann man in der Schmuck industrie verschiedene Schmuckgegenstände mit dünnem Kristallansatz versehen um dadurch Mattierungseffekte bzw. Reliefe zu erzielen.The object of the invention is to grow gold crystals, which are detail, resemble the crystals in nature and more, that To complete and complete the entire spectrum of the occurring gold crystals expand. For one thing, it makes it possible in geology, Mineralogy and in crystallography draw conclusions about the nature of the Gold crystals can be drawn, and on the other hand you can find in the jewelry various jewelry items with a thin crystal base provided to achieve matting effects or reliefs.

Erfindungsgemäß werden die Goldkristalle nun dadurch erzeugt, daß das Gold mit Hilfe des Quecksilbers aufgelöst wird und es sich dadurch in der flüssigen Phase befindet. Von diesem Punkt ausgehend, ist für das breite Spektrum der Goldkristalle jede Variante offen.According to the invention, the gold crystals are now produced in that the Gold is dissolved with the help of mercury and it is thereby in the liquid phase. Starting from this point is for the broad Spectrum of gold crystals every variant open.

In dieser Phase ist es nun möglich Gold-, Platin-, usw.-Schmuck in die Lösung zu tauchen. Die nachfolgende Temperung und Abkühlung läßt nun auf der Oberfläche der Schmuckstücke Kristallstrukturen entstehen. Das anschließende chemische Entfernen des Quecksilbers bewirkt ebenfalls Kristallisationseffekte. Natürlich ist es auch möglich, nach dem definierten Abkühlen und Erreichen des angestrebten Temperatur endpunktes der Lösung, das Quecksilber mit Hilfe einer Vacuumdestillation zu entfernen. Dadurch wird wieder ein anderer Kristalleffekt erzielt bzw. das Schmuckstück, falls notwendig, vor der chemischen Reaktion der Säure geschützt (Silberschmuck).In this phase it is now possible to use gold, platinum, etc. jewelry in the Solution to dive. The subsequent tempering and cooling now leaves Crystal structures develop on the surface of the jewelry. The subsequent chemical removal of the mercury causes also crystallization effects. Of course, it is also possible after defined cooling and reaching the desired temperature endpoint of the solution, the mercury using a Remove vacuum distillation. This will make another one Crystal effect achieved or the piece of jewelry, if necessary, before chemical reaction of the acid protected (silver jewelry).

Im folgenden wird die Erfindung anhand eines Beispieles näher erläutert. Eine bestimmte Goldmenge wird pur oder mit anderen Elementen gemischt (Patentanspruch 2, 3), dann vorzugsweise durch feilen oder raspeln zerkleinert (Patentanspruch 4). Auf diese Weise wird die Oberfläche vergrößert, damit das Quecksilber das Gold schnell auflösen kann.The invention is explained in more detail below using an example. A certain amount of gold becomes pure or with other elements mixed (claim 2, 3), then preferably by filing or shredded shredded (claim 4). In this way the Enlarged surface so that the mercury quickly dissolves the gold can.

Dieses Gemenge wird dann erhitzt. Die Temperaturskala reicht bis 357°C bei normalem Luftdruck, und kann durch Erhöhung des Druckes erweitert werden (Patentanspruch 5). - Lösephase.This mixture is then heated. The temperature scale extends up to 357 ° C at normal air pressure, and can be expanded by increasing the pressure be (claim 5). - release phase.

Die Lösung wird dann bei unterschiedlichen Temperaturen, Zeiten und Drucken getempert (Patentanspruch 5, 6). Diese Arbeitsphase dient dazu, die Kristallisation zu beginnen. Die Keimbildungsgeschwindigkeit hängt von der Temperatur stark ab, und von der Zeit - bei hochviskosen Medien - experimentell merklich von der Zeit ab.The solution is then at different temperatures, times and Printing annealed (claim 5, 6). This work phase serves to start crystallization. The nucleation rate depends strongly dependent on the temperature and on the time - with highly viscous media - experimentally noticeable from time.

Hält man eine bestimmte Keimbildungstemperatur der Lösung konstant, bzw. senkt die Temperatur definiert ab, kann man erreichen, daß große Kristalle gezüchtet werden. Ansonsten entstehen kleinere Formen (Patentanspruch 7, 8). - Diese beschriebene Phase ist die Kristallbildung durch Veränderung der Zustandsvariablen - Temperatur und Druck.If you keep a certain nucleation temperature of the solution constant, or lowers the temperature in a defined manner, one can achieve that large Crystals are grown. Otherwise, smaller shapes are created (Claim 7, 8). - This phase described is the crystal formation by changing the state variables - temperature and pressure.

Durch Zugabe von vorzugsweise Salpetersaure wird dann das Quecksilber chemisch als Salz aufgelöst. Auch hier kommt es noch zur Kristallbildung, da weiterhin noch Gold im Quecksilber gelöst ist. Für die Ausgestaltung der Kristallformen spielt ebenfalls die Konzentration der Salpetersäure eine entscheidende Rolle. (Patentanspruch 9, 10). - (Ähnlich der Abkühlrate s. o.).The mercury is then added by adding preferably nitric acid chemically dissolved as salt. Here too there is crystal formation, because gold is still dissolved in the mercury. For the design the crystal forms also play the concentration of nitric acid a crucial role. (Claim 9, 10). - (Similar to the cooling rate s. O.).

Das Entfernen von dem Quecksilber kann auch durch Vacuumdestillation erfolgen (Patentanspruch 11).Removal of the mercury can also be done by vacuum distillation take place (claim 11).

Claims

1. A process for the production of gold crystals, characterized in that pure gold or gold is doped with other elements, mercury is added, in order to then be heated to a certain temperature, there is annealed for a time, and then to a certain cooling rate to be brought to a defined final temperature, which then serves as the starting point for the addition of solvents (preferably nitric acid) in order to dissolve the mercury or serves as the starting point for removing the mercury by means of evaporation or a vacuum distillation.

2. The method according to claim 1, characterized, that the gold is used pure or as a doping or mixture of silver contains.

3. The method according to one or more of claims 1 to 2, characterized, that the gold is doped or mixed with other elements.

4. The method according to one or more of claims 1 to 3, characterized, that the gold, or the mixture in different sizes and shapes is used.

5. The method according to one or more of claims 1 to 4, characterized, that the gold at different dissolution temperatures, with different pressures is brought.

6. The method according to one or more of claims 1 to 5, characterized, that different annealing times are used.

7. The method according to one or more of claims 1 to 6, characterized, that the solution evenly or intermittently and with or without Stopovers is cooled.

8. The method according to one or more of claims 1 to 7, characterized, that after cooling, different final temperatures are maintained will.

9. The method according to one or more of claims 1 to 8, characterized, that acid or another solvent for mercury is used and their concentrations vary.

10. The method according to one or more of claims 1 to 9, characterized, that nitric acid is used and its concentration varies.

11. The method according to one or more of claims 1 to 10, characterized, that after the cooling process the mercury evaporates, evaporates or is removed by vacuum distillation.