DE1285651B - Process for the production of polyvinyl chloride coatings - Google Patents
Process for the production of polyvinyl chloride coatingsInfo
- Publication number
- DE1285651B DE1285651B DEB65976A DEB0065976A DE1285651B DE 1285651 B DE1285651 B DE 1285651B DE B65976 A DEB65976 A DE B65976A DE B0065976 A DEB0065976 A DE B0065976A DE 1285651 B DE1285651 B DE 1285651B
- Authority
- DE
- Germany
- Prior art keywords
- polyvinyl chloride
- coatings
- dispersions
- production
- carrier liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
Diese Erfindung dient zur Verbesserung bei der 2193 613 bei erhöhter Temperatur eine homogene Herstellung von Polyvinylchlorid-Überzügen aus Lösung von Polyvinylchlorid und Weichmacher her-Organosolen, wobei man unter dieser Bezeichnung gestellt werden.This invention serves to improve the 2193 613 to be homogeneous at elevated temperature Production of polyvinyl chloride coatings from a solution of polyvinyl chloride and plasticizer organosols, whereby one can be put under this designation.
gewöhnlich Polyvinylchlorid-Dispersionen in flüssigen Es wurde nun erfindungsgemäß festgestellt, daß Weichmachern versteht. Zu diesen Dispersionen 5 diese Nachteile der bisherigen Verfahren zum Herwurden relativ geringe Mengen flüchtiger Lösungs- stellen von Polyvinyl-Überzügen durch Auftragen mittel zugegeben, um die physikalischen Eigen- einer Dispersion von Polyvinylchlorid in einer flüchschaften der Dispersionen zu modifizieren zwecks tigen Naphthalin-Derivate enthaltenden Trägerflüssig-Erleichterung der Anwendung auf Oberflächen. keit und Entfernen der Trägerflüssigkeit durch Er-Ob die Polyvinylchlorid-Dispersionen zusätzliche io wärmen dadurch überwunden werden können, daß flüchtige Lösungsmittel enthalten oder nicht, der die Polyvinylchlorid-Dispersionen in einer mindewesentliche Zweck der flüssigen Weichmacher ist, stens 70 Gewichtsprozent eines oder mehrerer Monoals Träger für die Polyvinylchloridteilchen und auch methyl- und/oder Dimethylnaphthaline enthaltenden als Homogenisierungsmittel beim Erhitzen der Zube- flüchtigen Trägerflüssigkeit aufgetragen und auf 130 reitung zu wirken, um einen einheitlichen zusammen- 15 bis 250° C erwärmt werden. Beim Erhitzen auf die hängenden Überzug zu liefern; die Erhitzungstempe- angegebene Temperatur bleibt zunächst die Disperratur liegt üblicherweise im Bereich von 160 bis sion noch erhalten, bis die Methylnaphthaline im 250° C, wobei sie jedoch je nach Art der Dispersion wesentlichen entfernt sind, d. h., erst nachdem das und der Zeitdauer, währenddessen sie der erhöhten Monomethyl- und/oder Dimethylnaphthalin prak-Temperatur ausgesetzt wird, schwankt. Der Weich- 20 tisch völlig verdampft ist, tritt das gewünschte Vermacher dient dazu, dem Polyvinylchlorid im Überzug schmelzen der Polyvinylchloridteilchen zu einer Flexibilität zu verleihen; allgemein verwendete homogenen Schicht ein.Usually polyvinyl chloride dispersions in liquid It has now been found according to the invention that Understands plasticizers. These dispersions 5 suffered from these disadvantages of the previous methods of preparation relatively small amounts of volatile solution points of polyvinyl coatings due to application agent added to the physical property of a dispersion of polyvinyl chloride in a flüchschaften to modify the dispersions for the purpose of naphthalene derivative-containing carrier liquid relief the application on surfaces. ability and removal of the carrier liquid by Er-Ob the polyvinyl chloride dispersions additional heat can be overcome in that Containing volatile solvents or not, which affect the polyvinyl chloride dispersions to a minimum The purpose of the liquid plasticizer is at least 70 percent by weight of one or more monoals Carriers for the polyvinyl chloride particles and also containing methyl and / or dimethyl naphthalenes applied as a homogenizing agent when heating the volatile carrier liquid and applied to 130 Preparation to act to a uniform together- 15 to 250 ° C are heated. When heated to the supply hanging cover; the heating temperature indicated initially remains the disperratur is usually in the range from 160 to sion still obtained until the methylnaphthalenes im 250 ° C, but depending on the type of dispersion, they are substantially removed, d. i.e., only after that and the length of time during which they are exposed to the elevated monomethyl and / or dimethylnaphthalene temperature exposed, fluctuates. When the soft table has completely evaporated, the desired Vermacher steps in serves to melt the polyvinyl chloride particles into one with the polyvinyl chloride in the coating To give flexibility; commonly used homogeneous layer.
Weichmacher sind Ester von Phthalsäure und Phos- Die so erhaltenen Überzüge sind frei von FiIm-Plasticizers are esters of phthalic acid and phos- The coatings obtained in this way are free of fiIm-
phorsäure, beispielsweise Dioctylphthalat, Dinonyl- rissen, wie sie bei dem bekannten Verfahren beimphosphoric acid, for example dioctyl phthalate, dinonyl cracks, as in the known method in
phthalat und Tricresylphosphat. 25 Einbrennen leicht entstehen. Bei diesem Verfahrenphthalate and tricresyl phosphate. 25 Burn-in can easily occur. In this procedure
Obgleich für viele Zwecke die Gegenwart eines bildet sich nämlich zunächst eine Lösung bzw. einAlthough for many purposes the presence of one is namely first a solution or imagination
Weichmachers vorteilhaft ist, stellen diese Substanzen Gel, aus dem dann die Lösungsmittel erst heraus-Plasticizer is advantageous, these substances make gel, from which the solvents only then come out.
bei gewissen Anwendungen einen Nachteil dar, da dampfen müssen unter Schrumpfen des Gels undin certain applications is a disadvantage, since steaming must shrink the gel and
der Weichmacher bei erhöhten Temperaturen sich Gefahr der Rißbildung. Das Einbrennen der erfin-the plasticizer at elevated temperatures is at risk of cracking. The branding of the inven-
aus dem Überzug verflüchtigen kann, so daß dessen 30 dungsgemäßen Dispersion kann in einem größerencan volatilize from the coating, so that its 30 proper dispersion can be in a larger
physikalische Eigenschaften geändert werden. Der Temperaturbereich vorgenommen werden, als diesphysical properties are changed. The temperature range can be made as this
Weichmacher kann auch in irgendein anderes orga- bisher bei den bekannten Zubereitungen mit denPlasticizer can also be used in any other organ- hitherto in the case of the known preparations with the
nisches Material wandern, mit dem der Überzug in üblichen Mengen an Weichmachern möglich war.migrate niche material with which the coating in usual amounts of plasticizers was possible.
Berührung ist, was wiederum zu einer Veränderung Die erfindungsgemäß hergestellten Polyvinylchlorid-Touch is what in turn leads to a change The polyvinyl chloride produced according to the invention
der physikalischen Eigenschaften des Überzugs führt. 35 Überzüge sind auch chemisch widerstandsfähiger undthe physical properties of the coating. 35 coatings are also more chemically resistant and
Ein größerer Nachteil besteht darin, daß die Wider- härter als die bisher bekannten Überzüge. Wird inA major disadvantage is that the hardeners than the previously known coatings. Is in
Standsfähigkeit des Überzuges gegenüber dem Angriff einigen Fällen eine besonders gute Adhäsion anThe ability of the coating to withstand attack has, in some cases, particularly good adhesion
von Chemikalien, wie Säuren, Alkalien und Deter- Metalloberflächen gefordert, so kann zuerst eine derof chemicals such as acids, alkalis and detergent metal surfaces, one of the
gentien, durch die Anwesenheit der Weichmacher bekannten geeigneten Klebgrundierungen aufgetragenGentien, due to the presence of the plasticizers, suitable adhesive primers are applied
erheblich vermindert wird. 40 werden.is significantly reduced. Turn 40.
Weichmacherhaltige Polyvinylchlorid - Überzüge Es sei bemerkt, daß die erfindungsgemäß zu ver-Plasticizer-containing polyvinyl chloride coatings It should be noted that the inventively
können weiterhin dazu neigen, schneller bei erhöhten wendenden Organosolzubereitungen in üblicher Weisecan also tend to turn faster with increased turning organosol preparations in the usual way
Temperaturen zu erweichen als nicht weichgemachte mit Hilfe bekannter Mischeinrichtungen pigmentiertTemperatures to soften as unplasticized pigmented using known mixing devices
Überzüge und werden bei erhöhter Temperatur un- werden können. Auf die Oberflächen können dieCoatings and will become un- at elevated temperature. The
erwünscht klebrig. Die Berührung von Lösungs- 45 Dispersionen in üblicher Weise durch Sprühen,desirably sticky. The contact of solution dispersions in the usual way by spraying,
mitteln mit dem Überzug kann außerdem einen Teil Tauchen, Walz-Auftragen u. dgl. aufgebracht werden,by means of the coating, a part of dipping, roller application and the like can also be applied,
oder den gesamten Weichmacher auslaugen, was Die Dispersionen können als weitere Zusätze nochor leach out all of the plasticizer, which The dispersions can still be used as additional additives
wiederum eine unerwünschte Änderung in den physi- andere Bestandteile, wie synthetische Harze, ober-in turn, an undesirable change in the physical other components, such as synthetic resins,
kalischen Eigenschaften ergibt. flächenaktive Mittel, Polyvinylchlorid-Stabilisatorencalic properties results. surfactants, polyvinyl chloride stabilizers
Es wurde aber schon festgestellt, daß bei einem 50 und relativ geringe Mengen der üblichen Weichdünnen Polyvinylchlorid-Überzug, beispielsweise bis macher ebenso wie andere organische Lösungsmittel zu 0,25 mm Dicke, ein gänzlich zu einer Einheit zu- von niedrigerem Siedepunkt als die methylsubstisammengewachsener Überzug ohne jeglichen Weich- tuierten Naphthaline enthalten. Die Menge an zumacherzusatz ausreichend flexibel ist. Hierbei ver- gegebenem Weichmacher wird mit der Härte des wendet man Organosole des Polymers, die einge- 55 Überzugs schwanken, der hergestellt werden soll, brannt werden. Bekannt ist auch, Polyvinylchlorid- jedoch immer geringer sein als die normalen Weichpulver in Tetrahydronaphthalin in Verbindung mit machermengen; die angewendete Menge soll beieinem flüssigen sogenannten aktiven Mittel, wie spielsweise beträchtlich weniger als 50 Gewichts-Benzylalkohol oder Dimethylphthalat, zu dispergieren prozent des Polyvinylchlorids betragen. Wie erwähnt, und diese Dispersion auf einer Unterlage einzu- 60 können in die Dispersionen auch Pigmente und brennen. Streckmittel eingearbeitet werden; behandelte Tone,But it has already been established that with a 50 and relatively small amounts of the usual soft thin polyvinyl chloride coating, for example up to macher as well as other organic solvents 0.25 mm thick, a boiling point that is entirely one unit lower than that of the methyl substances grown together Coating without any softening contains naphthalenes. The amount of additive is sufficiently flexible. The plasticizer given here is determined by the hardness of the if organosols of the polymer are used, which vary in the coating to be produced, to be burned. It is also known that polyvinyl chloride is always lower than normal soft powder in tetrahydronaphthalene in conjunction with macher amounts; the applied amount should be one liquid so-called active agents, such as considerably less than 50% by weight benzyl alcohol or dimethyl phthalate, percent of the polyvinyl chloride to be dispersed. As mentioned, and to incorporate this dispersion on a base, pigments and can also be incorporated into the dispersions burn. Extenders are incorporated; treated clays,
Es wurde jedoch festgestellt, daß die Verwendung wie Bentonit-Tone, sind als Streckmittel besondersIt has been found, however, that uses, such as bentonite clays, are special as extenders
von Tetrahydronaphthalin als einziges Dispersions- brauchbar.of tetrahydronaphthalene as the only dispersion usable.
mittel nicht zufriedenstellend ist, da beim Einbrennen Der Zweck der Zugabe des niedrigersiedendenmedium is not satisfactory, as the stoving purpose of adding the lower boiling point
der aufgebrachten Schicht Reißen des Filmes mit 65 Lösungsmittels besteht darin, die Rheologie der Dis-the applied layer tearing the film with 65 solvent consists in the rheology of the dis-
einem Krokodilhauteffekt vorherrscht. persion zwecks Erleichterung seiner Anwendung zua crocodile skin effect prevails. persion to facilitate its use
Verwendet man als Weichmacher z. B. Amyl- modifizieren, wie es mit den bekannten OrganosolenIs used as a plasticizer z. B. Modify amyl, as is the case with the known organosols
naphthaline, so kann gemäß USA.-Patentschrift üblicherweise praktiziert wird.naphthalenes, it is commonly practiced according to U.S. Patent.
Die Einbrennbedingungen zur Herstellung zusammenhängender, gleichmäßiger Überzüge können von 30 Minuten bei 1300C bis 40 Sekunden bei 300° C schwanken, je nach der Dicke des aufgebrachten Filmes und der thermischen Kapazität des Untergrunds, auf den der Film aufgebracht wurde.The baking conditions for the production of cohesive, uniform coatings can vary from 30 minutes at 130 0 C to 40 seconds at 300 ° C, depending on the thickness of the applied film, and the thermal capacity of the substrate on which the film was applied.
Das erfindungsgemäße Verfahren eignet sich auch zum Überziehen von Aluminium-, Stahl- oder anderen Metallstreifen in einem kontinuierlichen Ablauf, wobei die Streifen mit oder ohne Grundierung durch eine Walzenauftragsmaschine oder eine andere geeignete Auftragsvorrichtung beschichtet und die Überzüge durch Leiten durch einen Ofen gehärtet werden.The method according to the invention is also suitable for coating aluminum, steel or others Metal strips in a continuous flow, the strips with or without primer through a roller application machine or another suitable application device coated and the Coatings are cured by passing them through an oven.
100 g gepulvertes Polyvinylchlorid, 200 g gemischte Methylnaphthaline (Siedebereich 209 bis 265° C), 14 g Titandioxyd (Rutil), 10 g Baryt und 2 g Dibutylzinnlaurat werden in einer Kugelmühle 40 Stunden vermählen. Die erhaltene Dispersion wird auf eine geeignet grundierte Stahltafel gesprüht und 10 Minuten auf 180° C erhitzt. Die eingebrannten Überzüge weisen eine Dicke von 0,00508 cm auf und sind chemisch widerstandsfähig mit hervorragenden Eigenschäften. 100 g powdered polyvinyl chloride, 200 g mixed methylnaphthalenes (boiling range 209 to 265 ° C), 14 g titanium dioxide (rutile), 10 g barite and 2 g dibutyltin laurate are put in a ball mill for 40 hours marry. The dispersion obtained is sprayed onto a suitably primed steel panel and 10 minutes heated to 180 ° C. The stoved coatings are 0.00508 cm thick and are chemically resistant with excellent properties.
Die in dem obigen Beispiel verwendeten gemischten Methylnaphthaline sind ein handelsübliches alkyliertes Naphthalin-Produkt, das ungefähr 60% Monomethylnaphthalin und ungefähr 15 °/o Dimethylnaphthalin enthält und einen Kauri-Butanolwert von und ein spezifisches Gewicht von 0,987 besitzt.The mixed methylnaphthalenes used in the above example are commercially available alkylated naphthalene product which is approximately 60% monomethylnaphthalene and approximately 15% dimethylnaphthalene and has a Kauri-Butanol value of and a specific gravity of 0.987.
Claims (2)