CN208247064U - 一种环保高耐磨防火实木 - Google Patents
一种环保高耐磨防火实木 Download PDFInfo
- Publication number
- CN208247064U CN208247064U CN201820800194.7U CN201820800194U CN208247064U CN 208247064 U CN208247064 U CN 208247064U CN 201820800194 U CN201820800194 U CN 201820800194U CN 208247064 U CN208247064 U CN 208247064U
- Authority
- CN
- China
- Prior art keywords
- solid wood
- fireproof
- environmentally friendly
- resistant fireproof
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本实用新型公开了一种环保高耐磨防火实木，其技术方案要点是：包括实木木皮，所述实木木皮上涂覆有防火涂层，所述防火涂层厚度约为50～100微米；本实用新型提供一种环保高耐磨防火实木，加工工艺范围宽，对外层防火阻极好的能力，有较高的阻隔能力、耐老化性能、耐刮耐磨能力。
Description
【技术领域】
本实用新型属于防火材料技术领域，具体涉及一种环保高耐磨防火实木。
【背景技术】
目前市场上有几种类型的阻燃板，品种多样，性能质量不一，主要有难燃人造板、玻镁板，这些阻燃产品性能根据制作材料不同，而达到的效果也不同，木质材料的防火问题一直是建筑领域内的重要课题，在《建筑设计防火规范GB50016-2014》中明确规定了，各种场所建筑材料的耐火极限，现有建筑材料长时间在高温环境下，仍会被烧毁，而给人们的生命财产带来损失，而市场上能够长时间耐火耐高温的建筑材料，或者成本很高，或者达不到较好的装饰效果。
【发明内容】
本实用新型的目的是克服现有技术的不足，提供一种环保高耐磨防火实木，加工工艺范围宽，对外层防火阻极好的能力，有较高的阻隔能力、耐老化性能、耐刮耐磨能力。
本实用新型技术方案如下：
一种环保高耐磨防火实木，包括实木木皮，所述实木木皮上涂覆有防火涂层，所述防火涂层厚度约为50～100微米；
a、原材料实木木皮预处理,清理表面灰尘、毛边褶皱，整平压合5～10min，风干或40℃～60℃条件烘干；
b、自然冷却至常温时进行第一次底涂纳米级防火涂料5～10g/c㎡，待底涂层自然固化形成膜质结构，再使用40℃～60℃烘干处理；
c、自然冷却至常温时进行第二次涂覆纳米级防火涂料5～10g/c㎡，待涂层自然固化形成膜质结构后形成防火涂层，存放于恒温、恒湿、遮光、避阳的环境内，确保木皮含水率8％-13％以下后，投入下工序；
本申请防火实木采用的防火涂层，该涂料的过程极其方便，充分利用了碳源、磷源等结合体，保证了涂料的防火性能，以及高附着力，同时具有较好的耐磨性，制备的环保高耐磨防火实木，具有很好的A级防火性能，加工工艺范围宽，对外层阻隔有极好的防火能力，有较高的阻隔能力及耐老化性能和耐刮耐磨能力。
优选的，在涂装好的实木木皮上增设热固性防火胶粘剂层，所述热固性防火胶粘剂层的厚度为0.1～0.15mm，所述热固性防火胶粘剂层外侧贴附有防火布或纤维层。所述实木皮外侧贴附的防火布或纤维层的厚度为0.5～1mm。热固性防火胶粘剂用于将防火布或纤维层固定在实木皮外侧，配合实木皮上的防火涂层进一步保护实木皮，能够耐高温。
优选的，所述防火布或纤维层的厚度为0.5～1mm。选择较小厚度的防火布或纤维层设计，能够在结构上对防火涂层起到支撑作用，保持实木整体结构在高温下长时间不形变。
优选的，所述防火布为陶瓷玻纤防火布。本申请的防火布主要为陶瓷玻纤混合材质，混合材料中的陶材料的气孔率为65-75％，短玻纤为长度小于3mm的材料。
优选的，所述纤维层为斜纹、缎纹或平纹碳纤维布，且选择材料克重为150-300g/㎡。150-300g/㎡克重的纤维织布具有较好的结构强度和纹路外观，能够很好的支撑实木结构，长时间在高温下不变形。
优选的，所述热固性防火胶粘剂层为高渗透胶粘剂和高强加硬粘合剂的混合物。高渗透胶粘剂和高强加硬粘合剂混合制成的热固性防火胶粘剂，能够维持在高温下不软化，不挥发。
本实用新型相对于现有技术，有以下优点：
本实用新型的一种环保高耐磨防火实木，具有很好的A级防火性能，加工工艺范围宽，对外层阻隔有极好的防火能力，有较高的阻隔能力及耐老化性能和耐刮耐磨能力；且生产工艺简单，容易控制；又不影响外层表面的外观质量，能有效解决外表面防火效果、氧化、耐磨刮等等问题，可应用于家具、地板材料、饰面板材料MDF,GRG及要求表面防火、防磨刮材料的表面处理。该方法适应现有生产工艺流程，可批量化生产。
【附图说明】
图1是本实用新型实施例1和2结构示意图；
图2是本实用新型实施例3和4结构示意图；
图3是本实用新型实施例5和6结构示意图。
【具体实施方式】
下面结合具体实施例对本实用新型作进一步描述：
一种环保高耐磨防火实木，包括实木木皮1，所述实木木皮1上涂覆有防火涂层2，所述防火涂层2厚度约为50～100微米；在涂装好的实木木皮上增设热固性防火胶粘剂层3，所述热固性防火胶粘剂层3的厚度为0.1～0.15mm，所述热固性防火胶粘剂层3外侧贴附有防火布4或纤维层5；所述防火布4或纤维层5的厚度为0.5～1mm；所述防火布4为陶瓷玻纤防火布；所述纤维层5为斜纹、缎纹或平纹碳纤维布，且选择材料克重为150-300g/㎡；所述热固性防火胶粘剂层3为高渗透胶粘剂和高强加硬粘合剂的混合物。
一种制备环保高耐磨防火实木的方法，包括以下步骤：
实施例1～2：
d、原材料实木木皮1预处理,清理表面灰尘、毛边褶皱，整平压合5～10min，风干或40℃～60℃条件烘干；
e、自然冷却至常温时进行第一次底涂纳米级防火涂料5～10g/c㎡，待底涂层自然固化形成膜质结构，再使用40℃～60℃烘干处理；
f、自然冷却至常温时进行第二次涂覆纳米级防火涂料5～10g/c㎡，待涂层自然固化形成膜质结构后形成防火涂层2，存放于恒温、恒湿、遮光、避阳的环境内，确保木皮含水率8％～13％以下后，投入下工序。
实施例3～4：
a、原材料实木木皮1预处理,清理表面灰尘、毛边褶皱，整平压合5～10min，风干或40℃～60℃条件烘干；
b、自然冷却至常温时进行第一次底涂纳米级防火涂料5～10g/c㎡，待底涂层自然固化形成膜质结构，再使用40℃～60℃烘干处理；
c、自然冷却至常温时进行第二次涂覆纳米级防火涂料5～10g/c㎡，待涂层自然固化形成膜质结构后形成防火涂层2，存放于恒温、恒湿、遮光、避阳的环境内，确保木皮含水率8％～13％以下后，投入下工序；
d、在涂装好的实木皮上添加克重5～10g/c㎡的热固性防火胶粘剂3，再在外侧贴附防火布4。
实施例5～6：
a、原材料实木木皮1预处理,清理表面灰尘、毛边褶皱，整平压合5～10min，风干或40℃～60℃条件烘干；
b、自然冷却至常温时进行第一次底涂纳米级防火涂料5～10g/c㎡，待底涂层自然固化形成膜质结构，再使用40℃～60℃烘干处理；
c、自然冷却至常温时进行第二次涂覆纳米级防火涂料5～10g/c㎡，待涂层自然固化形成膜质结构后形成防火涂层2，存放于恒温、恒湿、遮光、避阳的环境内，确保木皮含水率8％～13％以下后，投入下工序；
d、在涂装好的实木皮上添加克重5～10g/c㎡的热固性防火胶粘剂3，再在外侧贴附纤维层5。
表1：实施例1～6各组分厚度
本实用新型的环保高耐磨防火实木的制备方法中，所使用的纳米级防火涂料是通过以下制备方法获得：
(1)、制备A组份溶液，具体方法如下：
(a)、现将铝酸酯偶联剂粉末溶于适量的甲醇中，而后加入KH560硅烷偶联剂，制备铝酸酯硅烷偶联剂溶液；
(b)、将交联剂甲基三甲氧硅烷和二甲基二甲氧基硅烷扩链剂加入适量的甲醇溶剂稀释搅拌，制得用于对B组份起到催化、分散、流平作用的反应溶液；
(c)、将上述(a)、(b)两种溶液混合于密闭恒温16～20℃的高速搅拌容器内，高速混合搅拌20～30min后，观察溶液的溶解度至透明无浑浊状物，恒温存放，既得用于催化反应的A组份溶液；
(2)、制备B组份，具体方法如下：
(d)、首先将纯净蒸馏水加热至60～70℃，将抗氧剂BHT264加入热水中并搅拌5～10min，待抗氧剂完全溶解冷却至常温待用；
(e)、将聚己内酯二醇、聚四氢呋喃二醇、丁二醇按照配方组份质量分数要求取少量依次加入恒温16～20℃容器内并缓慢添加工业溶剂乙酸乙酯进行稀释搅拌15～25min，而后加入IPDI、PEG、分散稀释剂丙二醇单甲醚，并缓慢加入工业酒精乙醇进行稀释配比，再搅拌共混20～30min，然后加入缓蚀剂PBTCA和固化催化剂1,4-二甲基哌嗪并共混搅拌10-15min，加入溶解完全的抗氧剂溶液和流平消泡剂聚醚改性有机硅油；
(f)、将步骤(e)溶液，密闭容器内注入氮气排除容器内多余空气，密闭高速搅拌20～30min，得到B组份，冷却至常温，待用；
(3)、制备纳米防火涂料：
(g)、将A、B两个组份的常温溶液进行共混高速搅拌1～2h，搅拌结束后待涂料中的气泡自然散逸完全，即是本实用新型纳米防火涂料。
表2：实施例1～6中A组分构成
表3：实施例1～6中B组分构成
表4：实施例1～6所得纳米防火隔热油漆涂料与市场现有涂料对比例1～2做对比测试(标准参考：GB12441-2005饰面型防火涂料规范)
本实用新型的一种制备环保高耐磨防火实木，制备方法环保，高耐磨防火实木皮，在实木皮上设置防火涂层，而防火涂层由A、B两种组份共混而成：所述的A组份为B组份所用的相关交联剂、偶联剂、扩链剂或稀释溶剂等；所述A组份交联剂、偶联剂、扩链剂按照三种原料投入质量比的80-95％、1-5％、3-5％经均混搅拌、甲醇溶解而成制得，并存放于恒温16℃密闭容器内；所述B组份为聚合反应型聚酯聚氨酯水溶液，原材料采购广泛，均为常见的化学品，且成本低廉；制备工艺简单，操作方法便捷，反应条件宽松，制作该涂料的过程极其方便，充分利用了碳源、磷源等结合体，保证了涂料的防火性能，以及高附着力，制备的环保高耐磨防火实木，具有很好的A级防火性能，加工工艺范围宽，对外层阻隔有极好的防火能力，有较高的阻隔能力及耐老化性能和耐刮耐磨能力；且生产工艺简单，容易控制；又不影响外层表面的外观质量，能有效解决外表面防火效果、氧化、耐磨刮等等问题，可应用于家具、地板材料、饰面板材料MDF,GRG及要求表面防火、防磨刮材料的表面处理，该方法适应现有生产工艺流程，可批量化生产。
Claims (5)
1.一种环保高耐磨防火实木，其特征在于：包括实木木皮，所述实木木皮上涂覆有防火涂层，所述防火涂层厚度约为50～100微米,在涂装好的实木木皮上增设热固性防火胶粘剂层，所述热固性防火胶粘剂层的厚度为0.1～0.15mm，所述热固性防火胶粘剂层外侧贴附有防火布或纤维层。
2.根据权利要求1所述的一种环保高耐磨防火实木，其特征在于：所述防火布或纤维层的厚度为0.5～1mm。
3.根据权利要求1所述的一种环保高耐磨防火实木，其特征在于：所述防火布为陶瓷玻纤防火布。
4.根据权利要求1所述的一种环保高耐磨防火实木，其特征在于：所述纤维层为斜纹、缎纹或平纹碳纤维布，且选择材料克重为150-300g/㎡。
5.根据权利要求1所述的一种环保高耐磨防火实木，其特征在于：所述热固性防火胶粘剂层为高渗透胶粘剂和高强加硬粘合剂的混合物。