CN1208417C - Filter rod forming adhesive for acrylic fibre filter tip and its preparation method - Google Patents
Filter rod forming adhesive for acrylic fibre filter tip and its preparation method Download PDFInfo
- Publication number
- CN1208417C CN1208417C CN 02128960 CN02128960A CN1208417C CN 1208417 C CN1208417 C CN 1208417C CN 02128960 CN02128960 CN 02128960 CN 02128960 A CN02128960 A CN 02128960A CN 1208417 C CN1208417 C CN 1208417C
- Authority
- CN
- China
- Prior art keywords
- forming adhesive
- acrylic fibre
- filter
- rod forming
- solvent oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a filter rod forming adhesive for an acrylic fibre filter tip and a preparation method thereof, which belongs to the technical field of adhesives for cigarette filter tips. The method comprises the following steps: step 1, 0.5 to 3.5 wt% of thermoplastic rubber or thermoplastic styrene butadiene rubber is dissolved into one part of solvent oil; step 2, 8 to 15 wt% of terpene resin, 1 to 5 wt% of rosin resin and/or petroleum resin and 1 to 5 wt% of white oil are added to the other part of the solvent oil and are stirred until being dissolved completely; step 3, products obtained in step 1 and step 2 are uniformly mixed so as to obtain the filter rod forming adhesive for the acrylic fibre filter tip, and the total amount of the solvent oil is from 75 to 82 wt%. The terpene resin, the rosin resin and/or the petroleum resin are added to the forming adhesive to adsorb the abnormal flavor of heated acrylic fibre, so that the sharp taste, the pungent taste and the miscellaneous smell of the smoke gas of cigarettes are eliminated so as to make the cigarette smell become mellow.
Description
Technical field
The invention belongs to cigarette filter bonding agent field, particularly filter rod forming adhesive for acrylic fibre filter tip and preparation method thereof.
Background technology
At present, cigar mill's great majority are as cigarette filter with diacetate fiber.Normally with Cellulose diacetate through reeling off raw silk from cocoons, again cigarette filter rod forming adhesive-glycerine triacetate is sprayed on diacetate fiber silk and/or the tow, make diacetate fiber silk and/or tow then, be shaped to the filter-tip rod through filter-stick forming device.Since with the raw material of diacetate fiber, when lighting cigarette, when being heated, filter tip do not produce peculiar smell as cigarette filter, thus allow the human consumer accept easily, and make the glad use of cigar mill; But higher with diacetate fiber as the raw materials cost of cigarette filter, increased human consumer's expenditure virtually.Another kind is to be sprayed on the third fine fiber yarn and/or the tow with the conventional third fine sizing agent, makes third fine fiber yarn and/or the tow then, is shaped to the filter-tip rod through filter-stick forming device; Its raw materials cost is low, and material is easy to get, and meeting produces peculiar smell but filter tip is heated, and has had a strong impact on human consumer's mouthfeel, and the human consumer can not be accepted.
Summary of the invention
One of purpose of the present invention is the defective that is subjected to the thermogenesis peculiar smell when overcoming with the third long and slender dimension as cigarette filter, a kind of filter rod forming adhesive for acrylic fibre filter tip is provided, by this sizing agent being sprayed onto in the third long and slender dimension, utilize absorption principle to remove the peculiar smell that cigarette is heated and is afterwards produced, and reduce the tar content of cigarette, in order to substitute the diacetate fiber filter tip.
Another object of the present invention provides a kind of preparation method of filter rod forming adhesive for acrylic fibre filter tip.
Filter rod forming adhesive for acrylic fibre filter tip of the present invention, it is formed and content is:
Thermoplastic elastomer or thermoplastic styrene butadiene rubber 0.5～3.5wt%
Terpine resin 8～15wt%
Gum Rosin and/or petroleum resin 1～5wt%
White oil 1～5wt%
Solvent oil 75～82wt%.
Described solvent oil is No. 120 to No. 170 gasoline or their any mixture.
Described thermoplastic elastomer is the YH-792 that Yueyang petrochemical plant is produced, and thermoplastic styrene butadiene rubber is the SBS1401-1 that Yanshan Petrochemical factory produces.
The preparation method of filter rod forming adhesive for acrylic fibre filter tip of the present invention, its step comprises:
(1). thermoplastic elastomer or thermoplastic styrene butadiene rubber are dissolved in the partial solvent oil;
(2). in another part solvent oil, add terpine resin, Gum Rosin and/or petroleum resin, white oil, be stirred to dissolving fully;
(3). the product that step (1) is obtained mixes with the product that step (2) obtains, and is stirred to mix, and obtains filter rod forming adhesive for acrylic fibre filter tip; Wherein the amount of above-mentioned each material is:
Thermoplastic elastomer or thermoplastic styrene butadiene rubber 0.5～3.5wt%
Terpine resin 8～15wt%
Gum Rosin and/or petroleum resin 1～5wt%
White oil 1～5wt%
Solvent oil 75～82wt%.
Because the third long and slender dimension poor heat resistance, so after being heated, emit the third fine peculiar smell own easily, in order to eliminate peculiar smell, the present invention has added terpine resin, Gum Rosin and/or petroleum resin and has adsorbed the peculiar smell that third fibre is heated in forming adhesive, eliminated flue gas pungent, pungent taste and the assorted smell of cigarette, made cigarette gas become pure and mild; And make that the third fibril capsule is bulk, increased the fine surface-area of silk and played the tar effect of falling.
Embodiment
Embodiment 1.
(1). thermoplastic elastomer is dissolved in No. 170 gasoline of part;
(2). in No. 170 gasoline of another part, add terpine resin, Gum Rosin, No. 10 white oils of softening temperature＞100 degree of smashing to pieces, be stirred to dissolving fully;
(3). the product that step (1) is obtained mixes with the product that step (2) obtains, and is stirred to mix, and obtains filter rod forming adhesive for acrylic fibre filter tip; Wherein the amount of above-mentioned each material is:
Thermoplastic elastomer 0.8wt%
Terpine resin 12wt%
Gum Rosin 3wt%
10 white oil 3wt%
No. 170 gasoline 81.2wt%.
The cigarette that has prepared is poured in the cigarette moulding stick machine with filter rod forming adhesive for acrylic fibre filter tip, glue is wrapped on the third fine fiber yarn and/or the tow through machine, bonding, curing, moulding, at skin parcel one deck paper of the third fine fiber yarn and/or tow, be shaped to cigarette filter mouth rod again through bonding.
Embodiment 2.
(1). thermoplastic styrene butadiene rubber is dissolved in No. 150 gasoline of part;
(2). in No. 150 gasoline of another part, add terpine resin, petroleum resin, No. 15 white oils of softening temperature＞100 degree of smashing to pieces, be stirred to dissolving fully;
(3). the product that step (1) is obtained mixes with the product that step (2) obtains, and is stirred to mix, and obtains filter rod forming adhesive for acrylic fibre filter tip; Wherein the amount of above-mentioned each material is:
Thermoplastic styrene butadiene rubber 3wt%
Terpine resin 9wt%
Petroleum resin 5wt%
15 white oil 5wt%
No. 150 gasoline 78wt%.
The cigarette that has prepared is poured in the cigarette moulding stick machine with filter rod forming adhesive for acrylic fibre filter tip, glue is wrapped on the third fine fiber yarn and/or the tow through machine, bonding, curing, moulding, at skin parcel one deck paper of the third fine fiber yarn and/or tow, be shaped to cigarette filter mouth rod again through bonding.
Embodiment 3.
(1). thermoplastic elastomer is dissolved in No. 120 and No. 170 gasoline in;
(2). in No. 120, another part and No. 170 gasoline, add terpine resin, Gum Rosin, No. 10 white oils of softening temperature＞100 degree of smashing to pieces, be stirred to dissolving fully;
(3). the product that step (1) is obtained mixes with the product that step (2) obtains, and is stirred to mix, and obtains filter rod forming adhesive for acrylic fibre filter tip; Wherein the amount of above-mentioned each material is:
Thermoplastic elastomer 2wt%
Terpine resin 15wt%
Gum Rosin 1wt%
10 white oil 2wt%
No. 120 and No. 170 gasoline 80wt%.
The cigarette that has prepared is poured in the cigarette moulding stick machine with filter rod forming adhesive for acrylic fibre filter tip, glue is wrapped on the third fine fiber yarn and/or the tow through machine, bonding, curing, moulding, at skin parcel one deck paper of the third fine fiber yarn and/or tow, be shaped to cigarette filter mouth rod again through bonding.
Embodiment 4.
(1). thermoplastic elastomer is dissolved in No. 120 and No. 170 gasoline in;
(2). in No. 120, another part and No. 170 gasoline, add terpine resin, Gum Rosin and petroleum resin, No. 10 white oils of softening temperature＞100 degree of smashing to pieces, be stirred to dissolving fully;
(3). the product that step (1) is obtained mixes with the product that step (2) obtains, and is stirred to mix, and obtains filter rod forming adhesive for acrylic fibre filter tip; Wherein the amount of above-mentioned each material is:
Thermoplastic elastomer 2wt%
Terpine resin 15wt%
Gum Rosin and petroleum resin 1wt%
10 white oil 2wt%
No. 120 and No. 170 gasoline 80wt%
Wherein, Gum Rosin accounts for the 70wt% of 1wt%, and petroleum resin account for the 30wt% of 1wt%.
The cigarette that has prepared is poured in the cigarette moulding stick machine with filter rod forming adhesive for acrylic fibre filter tip, glue is wrapped on the third fine fiber yarn and/or the tow through machine, bonding, curing, moulding, at skin parcel one deck paper of the third fine fiber yarn and/or tow, be shaped to cigarette filter mouth rod again through bonding.
Claims (2)
1. filter rod forming adhesive for acrylic fibre filter tip, it is characterized in that: the composition of described sizing agent and content are:
Thermoplastic elastomer or thermoplastic styrene butadiene rubber 0.5～3.5wt%
Terpine resin 8～15wt%
Gum Rosin and/or petroleum resin 1～5wt%
White oil 1～5wt%
Solvent oil 75～82wt%;
Described solvent oil is No. 120, No. 150, No. 170 gasoline or their any mixture;
Described thermoplastic elastomer is the YH-792 that Yueyang petrochemical plant is produced, and thermoplastic styrene butadiene rubber is the SBS1401-1 that Yanshan Petrochemical factory produces.
2. the preparation method of a filter rod forming adhesive for acrylic fibre filter tip as claimed in claim 1, it is characterized in that: described preparation method's step comprises:
(1). thermoplastic elastomer or thermoplastic styrene butadiene rubber are dissolved in the partial solvent oil;
(2). in another part solvent oil, add terpine resin, Gum Rosin and/or petroleum resin, white oil, be stirred to dissolving fully;
(3). the product that step (1) is obtained mixes with the product that step (2) obtains, and is stirred to mix, and obtains filter rod forming adhesive for acrylic fibre filter tip; Wherein the amount of above-mentioned each material is:
Thermoplastic elastomer or thermoplastic styrene butadiene rubber 0.5～3.5wt%
Terpine resin 8～15wt%
Gum Rosin and/or petroleum resin 1～5wt%
White oil 1～5wt%
Solvent oil 75～82wt%;
Described solvent oil is No. 120, No. 150, No. 170 gasoline or their any mixture;
Described thermoplastic elastomer is the YH-792 that Yueyang petrochemical plant is produced, and thermoplastic styrene butadiene rubber is the SBS1401-1 that Yanshan Petrochemical factory produces.