CN117565237A - 一种墓碑石材翻新的方法 - Google Patents
一种墓碑石材翻新的方法 Download PDFInfo
- Publication number
- CN117565237A CN117565237A CN202311636822.4A CN202311636822A CN117565237A CN 117565237 A CN117565237 A CN 117565237A CN 202311636822 A CN202311636822 A CN 202311636822A CN 117565237 A CN117565237 A CN 117565237A
- Authority
- CN
- China
- Prior art keywords
- stone
- tombstone
- cleaning
- paint
- renewing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种墓碑石材翻新的方法，步骤包括：清洁墓碑石材表面；覆盖花纹、文字部分表面；将翻新涂料覆盖墓碑石材表面，所述的翻新涂料为液体玻璃、乙醇或水；翻新涂料干燥、凝结成膜；待表膜硬化后，使用细砂纸对需要处理的地方进一步打磨即可。本发明的墓碑石材翻新的方法，能简单有效地使得石材表面获得崭新的效果，并且能够较长时间地保持表面效果。
Description
技术领域
本发明涉及一种表面处理方法，尤其涉及一种石材表面处理的方法。
背景技术
随着墓葬业的不断发展，现在人们会发觉在城市中墓葬区域不断开发，很多城市的墓葬园区都已渐趋饱和，这表明了现在墓葬数量达到了一个非常大的量，而墓葬中石材堆砌的墓碑、基座也自然被大量使用，而这些随着使用年限的增加，人们会发觉墓地园区的总体环境还是比较恶劣的，因为按照我们国家的风俗习惯，每一个投入使用的墓穴都会频率不一地迎接逝者亲朋好友的祭奠，尤其是每年的重要日期，园区内的祭奠活动会更加密集。而按照风俗，祭奠活动都会包括燃烧锡箔香烛等物、泼撒酒水，有时还会溅落饭菜油污。墓碑和墓体承载了祭奠的功能，祭拜者通常会在墓碑或墓体附近进行上述祭奠行为。
其中，燃烧锡箔香烛等物，会致使墓体局部地方接受明火高温的炙烤，而产生色变、开裂等问题，这时，清洁剂去除不了火渍，只有通过打磨的方式将色变处，打磨掉然后再抛光，恢复石材本身的光泽度与颜色。同时有些还伴随着撒酒、饭菜油污等情况，这些较为恶劣的场地环境都使得墓碑墓体表面污渍、色变、陈旧。现有技术中除了打磨抛光，并没有特别好的解决办法，而打磨抛光一个是工程量大，另外这种方式也不可能无限次地做，一般处理几次之后就需要更换墓碑墓体。
发明内容
本发明所要解决的技术问题是提供一种新颖独特的墓碑石材翻新的方法，能简单有效地使得石材表面获得崭新的效果，并且能够较长时间地保持表面效果。
为了解决这个技术问题，本发明采用的技术方案如下：
一种墓碑石材翻新的方法，步骤包括：
a、清洁墓碑石材表面；
c、将翻新涂料覆盖墓碑石材表面，所述的翻新涂料为液体玻璃、乙醇或水；
d、翻新涂料干燥、凝结成膜即可。
进一步地，所述步骤a的清洁墓碑石材表面包括去脂去污去油的物理除垢清洁和使用中性或弱酸性清洁剂的化学清洁。
进一步地，所述步骤a还包括，对于使用中性清洁剂去除不了火渍，通过打磨、抛光的方式恢复石材本身的光泽度与颜色。
进一步地，所述步骤a和c之间还有步骤b：覆盖墓碑石材上的花纹、文字部分表面；步骤d之后还有步骤e：待表膜硬化后，清除花纹、文字部分表面覆盖物。
进一步地，步骤b，使用浆糊或黄泥或塑料薄膜覆盖花纹、文字部分表面。
进一步地，所述步骤d翻新涂料干燥、凝结成膜的过程中，使用防尘罩遮盖墓碑石材以防止凝结过程中沾染粘结灰尘。
进一步地，该方法的最后还有一个保护层喷涂步骤，所述的保护层材料为含氟丙烯酸树脂。
进一步地，所述翻新涂料的组分中还包含有辅料：染色剂和/或珠光粉。
进一步地，所述翻新涂料的组分中还包含有辅料：玻璃微珠。
目前对于墓园日渐陈旧的墓碑石材，使用了本发明的翻新方法，既能一次性地简单有效地使得石材表面获得崭新的效果，而且由于巧妙合理地使用了液体玻璃给墓碑石材覆上了一层防水、防尘、耐热、耐酸和抗紫外线的透明保护膜，也使得石材的翻新效果能够得到长时间地保持。不但大大节省了维护成本，也更加节能环保。
附图说明
为让本发明的上述目的、特征和优点能更明显易懂，以下结合附图对本发明的具体实施方式作详细说明，其中：
图1是本发明墓碑石材翻新方法的工艺流程示意图。
具体实施方式
以下结合附图和实施例对本发明作进一步详细说明：
图1示出了本发明的一种墓碑石材翻新的方法，该方法适用于墓区的墓碑、基座、石材围栏等墓碑石材的表面翻新处理。
该方法的步骤包括：
a、清洁墓碑石材表面；
主要包括去脂去污去油的物理除垢清洁和使用中性清洁剂的化学清洁。
其中，物理除垢清洁墓碑石材包括先用毛刷将墓碑和基座清理干净，有比较坚固的附着物，可用刮刀将其铲除，操作中不能破坏石材及石材表面。
物理除垢清洁后，用配置好的中性或者弱酸性清洁剂，涂抹在石材表面，然后进行洗刷，直至干净，然后用清水清洗。等待干燥。干燥后仔细观察，哪些地方还有被油渍、蜡烛油渗透的地方，用清洁剂拔去油渍，后用清水洗净。等待风干。
因为墓碑、基座承载了祭奠的功能，祭拜者在燃烧锡箔、香烛等物，而使墓体局部地方接受过明火高温的炙烤，而产生色变，开裂等问题，这时，一般的清洁剂去除不了的火渍，只有通过打磨的方式将色变处打磨掉，然后再抛光，恢复石材本身的光泽度与颜色。
b、覆盖花纹、文字部分表面；
墓碑和基座通常会有雕刻的花纹，雕刻的花纹通常不进行抛光等镜面处理，以达到与进行过抛光处理的地方有颜色反差的作用，起到美化墓碑的作用，在翻新施工过程中，需要避免将翻新涂料涂擦到花纹处。
花纹与刻的字的处理方式：墓碑石材上的花纹雕刻，一般有阴刻和阳刻两种，阴刻的花纹，可以用浆糊或黄泥或塑料薄膜将阴刻花纹进行覆盖，以避免翻新涂料接触到阴刻花纹影响翻新效果。阳刻花纹，也可用塑料薄膜将其包裹，或用黄泥将其覆盖，也可以交叉使用。
当然，对于某些墓碑，文字、花纹特别简单又比较粗大的话，如果处理涂料时能够完美地避开文字、花纹部分，则也可以省去上述巧妙的覆盖文字花纹的步骤；其后续清除花纹、文字部分表面覆盖物的步骤自然也一并省去。
c、将翻新涂料覆盖墓碑石材表面，所述的翻新涂料为液体玻璃、乙醇或水；
翻新涂料的主要组分是液体玻璃，液体玻璃的主要成分是高纯度的纳米级二氧化硅，高纯度的纳米级二氧化硅接触到石材后，会逐渐渗透到石材表层，并慢慢硬化结膜，对石材形成保护。液体玻璃翻新涂层环保，并具有防水、防尘、防污、抗菌、防霉、疏油、防雾化、防风化、透气、耐热、易清洁、耐酸、抗紫外线等诸多特性。
因为不同产地的石材，密度、颜色、纹理、石材毛孔的粗细等都不相同，所以我们进一步可以在翻新涂料的组分中加入辅料：染色剂和/或珠光粉和/或玻璃微珠。从而获得更加完美、真实、崭新的翻新效果；其中玻璃微珠可以增加涂层的亮度和光泽，提供更好的遮盖力，并减少涂层的吸湿性。此外，玻璃微珠在涂料中还可以用作填充剂，改善裂缝等缺陷的填充性，增加涂层的强度和耐久性。
上述翻新涂料覆盖石材表大多采用刷涂工艺。当然也可以使用其它常规的涂覆方式，譬如喷涂等，只要能均匀有效地涂覆即可。涂覆好之后对于需要亚光处理的部分可以在液体玻璃即将初步固化前，使用高光洁度的纤维织物进行均匀的擦拭，将附着于石材表面的液体玻璃擦去一部分，这样可以破坏石材表层液体玻璃成膜效果，而达到非亮光效果，同时不影响渗透到石材里面的液体玻璃对于石材的保护。
d、翻新涂料干燥、凝结成膜；
期间，因为翻新涂料具有较强的粘性、容易沾染灰尘，所以在多尘的环境时，我们使用防尘罩(譬如简易帐篷等)遮盖墓碑石材以防止凝结过程中沾染粘结灰尘。
e、待表膜硬化后，清除花纹、文字部分表面覆盖物。
f、为了让所述翻新涂料的效果更持久、更加防水耐腐蚀耐风吹雨淋，我们最后设置保护层喷涂步骤，所述的保护层材料为含氟丙烯酸树脂。保护层的喷涂不需要避开花纹文字可以覆盖墓碑石材上的花纹、文字部分表面，因为保护层的覆盖不会改变花纹、文字部分表面的色彩。
以上所述，仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，可轻易想到变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应所述以权利要求的保护范围为准。
Claims (9)
1.一种墓碑石材翻新的方法，其特征在于步骤包括：
a、清洁墓碑石材表面；
c、将翻新涂料覆盖墓碑石材表面，所述的翻新涂料为液体玻璃、乙醇或水；
d、翻新涂料干燥、凝结成膜即可。
2.根据权利要求1所述的方法，其特征在于：所述步骤a的清洁墓碑石材表面包括去脂去污去油的物理除垢清洁和使用中性或弱酸性清洁剂的化学清洁。
3.根据权利要求2所述的方法，其特征在于：所述步骤a还包括，对于使用中性清洁剂去除不了火渍，通过打磨、抛光的方式恢复石材本身的光泽度与颜色。
4.根据权利要求1所述的方法，其特征在于：
所述步骤a和c之间还有步骤b：覆盖墓碑石材上的花纹、文字部分表面；
步骤d之后还有步骤e：待表膜硬化后，清除花纹、文字部分表面覆盖物。
5.根据权利要求4所述的方法，其特征在于，步骤b，使用浆糊或黄泥或塑料薄膜覆盖花纹、文字部分表面。
6.根据权利要求4所述的方法，其特征在于：所述步骤d翻新涂料干燥、凝结成膜的过程中，使用防尘罩遮盖墓碑石材以防止凝结过程中沾染粘结灰尘。
7.根据权利要求1至6中任一项所述的方法，其特征在于：该方法的最后还有一个保护层喷涂步骤，所述的保护层材料为含氟丙烯酸树脂。
8.根据权利要求1至6中任一项所述的方法，其特征在于，所述翻新涂料的组分中还包含有辅料：染色剂和/或珠光粉。
9.根据权利要求8所述的方法，其特征在于，所述翻新涂料的组分中还包含有辅料：玻璃微珠。