CN111114184A - Method for manufacturing platinum crystal picture - Google Patents
Method for manufacturing platinum crystal picture Download PDFInfo
- Publication number
- CN111114184A CN111114184A CN201911369876.2A CN201911369876A CN111114184A CN 111114184 A CN111114184 A CN 111114184A CN 201911369876 A CN201911369876 A CN 201911369876A CN 111114184 A CN111114184 A CN 111114184A
- Authority
- CN
- China
- Prior art keywords
- platinum crystal
- glue
- making
- pet film
- manufacturing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a method for making platinum crystal painting, comprising four steps of making a base, wire inlay, glue making, making and the like, and the finished painting made is perfectly thick and heavy, has clear and luxurious pattern and lines, is bright in color, never fades, and has great artistic value and collection value. The manufacturing method of the invention ensures that the visual effect of the manufactured finished product is glass texture, the color and the particle texture of the oil are very obvious, the color saturation and the definition are obviously improved, the touch feeling of the platinum crystal painting after the manufacturing is improved qualitatively, and the smooth picture has more integrity of the finished product.
Description
Technical Field
The invention relates to the technical field of handicraft manufacturing, in particular to a method for manufacturing a platinum crystal picture.
Background
With the progress and development of science and technology, the carriers and the emerging forms of the decorative pictures are more and more abundant, and the pursuit and love of the life of people are greatly improved.
As the most popular platinum crystal decorative painting at present, the expressive form of the frameless, unbounded and unbounded frameless painting is more and more popular with people, and the simple, fashionable and modern design style and the expressive form full of vitality also make the frameless painting become the trend of modern decoration, however, most of the painting cores of the platinum crystal painting on the market at present adopt materials such as photographic paper, portrait cloth and canvas, and the problems of glue failure, bubbling, discoloration, deformation and the like easily occur after a long time, so that the defect rate is reduced, the purpose of reducing the manufacturing cost is achieved, and the problem which needs to be solved by the invention is provided.
Disclosure of Invention
In order to solve the technical problems, the invention provides a method for manufacturing a platinum crystal painting.
The invention realizes the purpose through the following technical scheme:
a method for manufacturing a platinum crystal picture comprises the following steps:
s1, tire manufacturing: selecting a bamboo-wood fiberboard with a proper specification and attaching waterproof paper;
s2, wire inlaying: after the pattern is rubbed by the rubbing paper, the pattern is cloched by a metal wire, the enamel glaze is uniformly dripped into the gap of the metal wire after the cloisonne, and then diluted white latex is sprayed;
s3, preparing glue: putting the resin adhesive and the curing agent into a clean container according to the proportion for mixing, then fully stirring clockwise until the liquid is completely transparent, and standing;
s4, sealing glue: and (3) uniformly spreading the glue prepared in the step (S3) on the surface of the platinum crystal picture, attaching a PET film on the surface of the platinum crystal picture, uniformly scraping the surface of the platinum crystal picture by using a scraper, pressing four corners of the PET by using a weight, and taking down the PET film after the PET film is dried.
Preferably, the S3 is stirred until the solution is transparent and then is kept stand for 60 to 180 seconds, so that bubbles are fully released.
Preferably, the PET film used in S4 has a preferred thickness of 0.075 to 0.3 mm.
Preferably, the PET film used in S4 has a thickness of 0.08-0.2 mm.
Preferably, the PET film used in S4 has a thickness of 0.1-0.15 mm.
Preferably, the S4 is uniformly scraped with a surface of a doctor blade, preferably 1 to 6 times, for extruding the excess resin paste and bubbles in the paste.
Preferably, the S4 is uniformly scraped with a surface of a doctor blade, preferably 1 to 4 times, for extruding the excess resin paste and bubbles in the paste.
Preferably, the S4 is uniformly scraped with a surface of a doctor blade, preferably 1-2 times, for extruding the excess resin paste and bubbles in the paste.
Preferably, the weight ratio of the resin gum to the curing agent is 1-10: 1.
Preferably, the weight ratio of the resin gum to the curing agent is 2-5: 1.
The invention has the following beneficial effects through the technical scheme: the resin is solidified to ensure that the visual effect of the finished product is glass texture, the color and the particle texture of the glaze are very obvious, the color saturation and the definition are obviously improved, the touch feeling of the manufactured platinum crystal painting is improved qualitatively, and the smooth picture has more integrity of the finished product.
Additional features and advantages of the invention will be set forth in the detailed description which follows.
Drawings
The accompanying drawings, which are included to provide a further understanding of the embodiments of the invention and are incorporated in and constitute a part of this specification, illustrate embodiments of the invention and together with the description serve to explain the embodiments of the invention without limiting the embodiments of the invention.
FIG. 1 is a sample prepared according to the method of example 1 of the present invention;
FIG. 2 is a sample prepared according to the method of example 2 of the present invention.
Detailed Description
The invention provides a method for manufacturing a platinum crystal picture, which comprises the following steps: s1, tire manufacturing: selecting a bamboo-wood fiberboard with a proper specification and attaching waterproof paper; s2, wire inlaying: after the pattern is rubbed by the rubbing paper, the pattern is cloched by a metal wire, the enamel glaze is uniformly dripped into the gap of the metal wire after the cloisonne, and then diluted white latex is sprayed; s3, preparing glue: putting the resin adhesive and the curing agent into a clean container according to the proportion for mixing, then fully stirring clockwise until the liquid is completely transparent, and standing; s4, sealing glue: and (3) uniformly spreading the glue prepared in the step (S3) on the surface of the platinum crystal picture, attaching a PET film on the surface of the platinum crystal picture, uniformly scraping the surface of the platinum crystal picture by using a scraper, pressing four corners of the PET by using a weight, and taking down the PET film after the PET film is dried. The aim of the invention is to ensure that the visual effect of the platinum crystal picture after the glue sealing presents glass texture, the color and the particle texture of the glaze are very obvious, and the color saturation and the definition of the picture are improved. The manufacturing method comprises the steps of firstly selecting a bamboo-wood fiberboard with a proper specification to attach waterproof paper, rubbing the pattern with a piece of blue rubbing paper, then inlaying the pattern with a metal wire, inlaying enamel glaze uniformly into gaps of the metal wire after inlaying the pattern, then spraying diluted white latex for fixing the enamel glaze to prevent the enamel glaze from flowing everywhere, putting resin glue and a curing agent into a clean container according to the proportion of 3:1 for mixing, then fully stirring clockwise until liquid is completely transparent, standing, uniformly scattering the prepared resin glue on the surface of a platinum crystal picture, then attaching a PET film on the surface of the platinum crystal picture, uniformly scraping the surface of a scraper, then pressing four corners of the PET with a heavy object, drying the PET film in the air, taking the PET film down, and finishing the platinum crystal picture.
In a preferred embodiment, the S3 is stirred to be transparent and then is kept stand for 60 to 180 seconds, so that bubbles are fully released.
In a preferred embodiment, the PET film used in S4 preferably has a thickness of 0.075 to 0.3 mm.
In a preferred embodiment, the PET film used in S4 preferably has a thickness of 0.08 to 0.2 mm.
In a preferred embodiment, the PET film used in S4 preferably has a thickness of 0.1 to 0.15 mm.
In a preferred embodiment, the S4 is uniformly scraped with a surface of a doctor blade, preferably 1 to 6 times, for extruding the excess resin and bubbles in the glue.
In a preferred embodiment, the S4 is uniformly scraped with a surface of a doctor blade, preferably 1 to 4 times, for extruding the excess resin and bubbles in the glue.
In a preferred embodiment, the S4 is uniformly scraped with a surface of a doctor blade, preferably 1-2 times, for extruding the excess resin and bubbles in the glue.
According to the invention, the weight ratio of resin gum to curing agent is preferably 1 to 10:1, preferably 2 to 5:1, particularly preferably 3: 1.
The technical scheme has the following effects: the resin is solidified to ensure that the visual effect of the finished product is glass texture, the color and the particle texture of the glaze are very obvious, the color saturation and the definition are obviously improved, the touch feeling of the manufactured platinum crystal painting is improved qualitatively, and the smooth picture has more integrity of the finished product.
The invention is further illustrated by the following specific examples:
example 1
The manufacturing method of the platinum crystal picture of the invention takes the manufacturing of deer as an example as shown in figure 1.
Firstly, attaching a layer of waterproof paper on a bamboo-wood fiberboard, rubbing a pattern on a designed deer by using rubbing paper, then nipping the pattern by using a metal wire according to the pattern, then uniformly dropping a gold enamel glaze required on the design into a gap of the metal wire, then spraying diluted white latex, pouring resin glue and a curing agent into a clean container according to a ratio of 3:1, mixing, fully stirring until the liquid is completely transparent, standing for 120s, uniformly scattering the prepared glue on the surface of the pattern, then attaching a PET film with the thickness of 0.12mm on the surface of the pattern, uniformly scraping 2 times on the PET film by using a scraper to flatten the surface, then pressing four corners of the PET by using a heavy object, standing for 24 hours, airing, and taking down the PET film to obtain a complete deer platinum crystal painting product.
Example 2:
the method for making platinum crystal picture of the present invention is shown in figure 2 of hand and pigeon production.
Firstly, a layer of waterproof paper is attached on a bamboo-wood fiber board, a designed hand pigeon is rubbed with a pattern by a piece of blue rubbing paper, using a metal wire to inlay the pattern according to the pattern, then uniformly dropping the enamel glaze into the gap of the metal wire according to the required color on the pattern, the color of the pattern city design drawing formed by metal color is distributed, diluted white latex is sprayed on the pattern city design drawing, resin gum and curing agent are put into a clean container according to the proportion of 3:1 for mixing, then fully stirring until the liquid is completely transparent, standing for 80-180s, uniformly spreading the prepared glue on the surface of the pattern, then attaching a PET film with the thickness of 0.15mm on the surface of the pattern, uniformly scraping 1 time on the PET film by using a scraper to flatten the surface, then pressing the four corners of the PET by a weight, placing for 24 hours, airing, and taking down the PET film to obtain the complete platinum crystal painting product from the handbook and the pigeon.
The foregoing shows and describes the general principles, essential features, and advantages of the invention. It will be understood by those skilled in the art that the present invention is not limited to the embodiments described above, which are given by way of illustration of the principles of the present invention, and that various changes and modifications may be made without departing from the spirit and scope of the invention. Such variations and modifications are intended to be within the scope of the claimed invention.
Claims (10)
1. A method for manufacturing a platinum crystal picture is characterized by comprising the following steps:
s1, tire manufacturing: selecting a bamboo-wood fiberboard with a proper specification and attaching waterproof paper;
s2, wire inlaying: after the pattern is rubbed by the rubbing paper, the pattern is cloched by a metal wire, the enamel glaze is uniformly dripped into the gap of the metal wire after the cloisonne, and then diluted white latex is sprayed;
s3, preparing glue: putting the resin adhesive and the curing agent into a clean container according to the using proportion, mixing, fully stirring until the liquid is completely transparent, and standing;
s4, sealing glue: and (3) uniformly spreading the glue prepared in the step (S3) on the surface of the platinum crystal picture, then attaching a PET film on the surface of the platinum crystal picture, uniformly scraping the surface of the platinum crystal picture by using a scraper, then pressing the four corners of the PET by using a weight, and taking down the PET film after the PET film is dried.
2. The method for making a platinum crystal picture according to claim 1, wherein said S3 is stirred until it is transparent and then left standing for 60-180S to release bubbles sufficiently.
3. The method for manufacturing a platinum crystal painting according to claim 1, wherein the thickness of the PET film used in the S4 is 0.075-0.3 mm.
4. The method for manufacturing a platinum crystal picture according to claim 1, wherein the thickness of the PET film used in the S4 is 0.08-0.2 mm.
5. The method for manufacturing a platinum crystal picture according to claim 1, wherein the thickness of the PET film used in the step S4 is 0.1-0.15 mm.
6. The method for making a platinum crystal painting according to claim 1, wherein the S4 is uniformly scraped with a scraper blade, preferably 1-6 times, for extruding the excess resin glue and bubbles in the glue.
7. The method for making a platinum crystal painting according to claim 1, wherein the S4 is uniformly scraped with a scraper blade, preferably 1-4 times, for extruding the excess resin glue and bubbles in the glue.
8. The method for making a platinum crystal painting according to claim 1, wherein the S4 is uniformly scraped with a scraper, preferably 1-2 times, for extruding the excess resin glue and bubbles in the glue.
9. The method for making a platinum crystal picture according to claim 1, wherein the weight ratio of the resin adhesive to the curing agent is 1-10: 1.
10. The method for making a platinum crystal picture according to claim 9, wherein the weight ratio of the resin adhesive to the curing agent is 2-5: 1.