CN110105863A - 一种耐热底漆及其制备方法 - Google Patents

一种耐热底漆及其制备方法 Download PDF

Info

Publication number
CN110105863A
CN110105863A CN201910382727.3A CN201910382727A CN110105863A CN 110105863 A CN110105863 A CN 110105863A CN 201910382727 A CN201910382727 A CN 201910382727A CN 110105863 A CN110105863 A CN 110105863A
Authority
CN
China
Prior art keywords
heat
component
priming paint
phosphate
ppg
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201910382727.3A
Other languages
English (en)
Other versions
CN110105863B (zh
Inventor
李志士
王华进
张立国
姜清淮
王明强
赵薇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Marine Chemical Research Institute Co Ltd
Original Assignee
Marine Chemical Research Institute Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Marine Chemical Research Institute Co Ltd filed Critical Marine Chemical Research Institute Co Ltd
Priority to CN201910382727.3A priority Critical patent/CN110105863B/zh
Publication of CN110105863A publication Critical patent/CN110105863A/zh
Application granted granted Critical
Publication of CN110105863B publication Critical patent/CN110105863B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种耐热底漆及其制备方法，耐热底漆包括如下组分：A组分(重量百分比)：双酚A型环氧树脂15～30；羟基丙烯酸酯树脂0～10；无机填料20～50；防锈颜料2～5；非浮型铝粉2～5；阻燃剂5～15；分散剂0.5～2；消泡剂0.1～0.5；流平剂0.1～0.5；混合有机溶剂20～40；B组分(重量百分比)：改性异氰酸酯100；所述A组分与所述B组分的重量比为2.5～4：1。本发明耐热底漆可长期使用于200℃高温环境下，常温固化，柔韧性好，具有一定的阻燃性，耐受各类溶剂油、有机溶剂。

Description

一种耐热底漆及其制备方法
技术领域
本发明属于涂料领域，具体涉及一种耐热底漆及其制备方法。
背景技术
耐热涂料广义上所指的是可长期使用于100 ℃以上的高温下的涂料，涂层不变色、涂层性能不失效。耐热涂料在日常生活中有着广泛应用，例如，工业上可用于石化行业的输油管路、高温工作的电机壳体、动力舱、高温炉体的外表面、航空航天等重要领域；在民用中，可用于电器绝缘、家用电器的加热器件等。
目前，耐热涂料主要以有机硅树脂体系，或有机硅改性树脂体系为主，有机硅类涂料的耐热性较好，但通常需要高温固化，会增加施工的难度，同时有机硅体系硬度高，柔韧性差。
因此，需要提供一种新的耐热底漆及其制备方法以解决上述问题。
发明内容
本发明的目的在于提供一种常温固化，柔韧性好，阻燃性、耐受性优异的耐热底漆。
本发明的另一目的在于提供一种上述耐热底漆的制备方法。
本发明涉及的一种耐热底漆，为双组分防火涂料，由A组分和B组分组成，配方如下：
B组分 含量wt％
改性异氰酸酯 100
A、B组分的比例为2.5：1～4：1。
成膜物会影响涂层在基材上附着力、柔韧性、耐介质性、耐热性等理化性能。本发明在选择成膜物时，考虑到树脂应满足耐高低温性、柔韧性、低粘度、适当的交联度、具有良好的粘结力等要求。本发明的成膜物选用聚氨酯改性环氧树脂的体系(A组分中双酚A型环氧树脂和/或羟基丙烯酸酯树脂与B组分的混合体系)。优选的A组分中使用双酚A型环氧树脂(环氧值0.12～0.56)和羟基丙烯酸酯树脂混合使用。双酚A型环氧树脂以环氧基和羟基为端基，可与NCO反应，形成交联网络，增加聚合物分子量，当B组分选用多元醇，可调整成膜物的柔韧性和强度，满足实际使用需求。
所述的无机填料为滑石粉、云母粉、沉淀硫酸钡、重钙、金红石型钛白粉、气相二氧化硅、陶土里的一种或几种。无机填料的用量及配比根据临界体积浓度(CPVC)计算，上下不超过10％。无机填料具有较高的吸油量，可起到增稠剂的作用。
所述的防锈颜料为磷酸盐类、锌粉中的一种或几种，磷酸盐类防锈颜料包括但不限于：磷酸锌、磷酸钼锌、三聚磷酸铝，可增加涂层的防腐性。
所述的非浮型铝粉，在涂料的制备过程中，研磨分散后搅拌加入，非浮型铝粉可增加涂层的散热性，在高温条件对涂层的影响降低，进而提高涂层的耐热性；同时，根据防腐涂料电化学机理，非浮型铝粉还可增加底漆的防腐性。
阻燃剂可分解吸热产生不燃气体，分解产生自由基，或其他阻燃机理。使用阻燃剂可减少涂层自身的燃烧，降低防火涂层相应时间，协助防火涂层的成碳反应。所述的阻燃剂可包括有机阻燃剂和/或无机阻燃剂，有机阻燃剂用量与双酚A型环氧树脂的比例为2：1～0.05：1，无机阻燃剂的用量与双酚A型环氧树脂的比例为0.5：1～0.02：1。所述的有机阻燃剂包括：磷酸酯及其衍生物、膦酸酯、亚磷酸酯中的一种或几种。磷酸酯阻燃剂包括：磷酸三甲苯酯、磷酸三苯酯、三羟甲基丙烷三丙烯酸酯、磷酸三异丙基苯酯、磷酸三乙酯、磷酸三丁酯、磷酸三辛酯、异丙基化磷酸三苯酯、亚磷酸三苯酯、磷酸甲苯二苯酯、磷酸三丁氧基乙酯、1，3，5-吡唑酮(PMP)、甲苯基二苯基磷酸酯、间苯二酚—双(磷酸二苯酯)、双酚A—双(磷酸二苯酯)、间苯二酚—双[二(2，6—二甲基苯基)磷酸酯]中的一种或几种。膦酸酯包括：N-羟甲基丙酰胺类甲基膦酸酯、环中膦酸酯、N、N-对苯二胺基(2-羟基)二苄基膦酸四乙酯、甲基膦酸二甲酯中的一种或几种。所述的无机阻燃剂包括：氢氧化铝、氢氧化镁、氧化铝、三氧化二锑、五氧化二锑、二氧化钛、氧化锌、氧化钼、三氧化钼、钼酸铵、二钼酸铵、四钼酸铵、八钼酸铵、钼酸锌、氧化锡、氧化亚铜、可膨胀石墨中的一种或几种。氢氧化铝、氢氧化镁两者均为填料型阻燃剂，无卤、无毒、抑烟，通过分解吸热，生成水蒸气，以稀释作用发挥阻燃效能。本发明采用多种阻燃剂复配的方法，以发挥协同阻燃效应。优选磷酸酯、氢氧化铝、氢氧化镁为阻燃剂。
所述的分散剂为毕克化学的BYK-AT203，BYK-AT204，BYK-9076，BYK-9077，BYK-P104S，BYK-ATU，BYK-103，BYK-110，BYK-142，BYK-161，BYK-162，BYK-163，BYK-164，BYK-170，BYK-180，BYK-182，中的一种或几种。
所述的消泡剂为毕克化学的BYK-051，BYK-052，BYK-053，BYK-054，BYK-055，BYK-057，BYK-060，BYK-065，BYK-066N，BYK-067A，BYK-070，BYK-071，BYK-072，BYK-077，BYK-085，BYK-088，BYK-A525，BYK-A530，BYK-A535，BYK-A550，BYK-A555，BYK-A560，BYK-1752，BYK-1790，中的一种或几种。
所说的流平剂为毕克化学的，BYK-300，BYK-301，BYK-306，BYK-307，BYK-310，BYK-320，BYK-323，BYK-322，BYK-331，BYK-333，BYK-354，BYK-358N，BYK-361N，BYK-370，BYK-371，BYK-378，BYK-388，中的一种或几种。
所述的混合有机溶剂为二甲苯、醋酸丁酯、PMA(丙二醇甲醚醋酸酯)的混合溶液，二甲苯、醋酸丁酯、PMA的重量比例为5：3：2或1：1：1。
所述的改性异氰酸酯的合成方法如下，在反应釜中加入IPDI(异佛尔酮二异氰酸酯)，升温至50℃，N2保护，搅拌下滴加多元醇的溶液，0.5～1h内滴加完毕，保持温度在80～90℃下反应2～3h后，测定NCO含量，出料冷却至室温，加入醋酸丁酯，调整固含量至70～80wt％，得到底漆改性异氰酸酯。
上述多元醇包括二官能度、三官能度的聚醚多元醇、聚酯多元醇中的一种或几种，其中聚醚多元醇包括但不限于PPG-200、PPG-400、PPG-600、PPG-1000、PPG-1500、PPG-2000、PPG-3000、PPG-4000、PPG-6000、PPG-8000中的一种或几种。聚酯多元醇包括乙二醇、丙二醇、二乙二醇、一缩二乙二醇、三羟甲基丙烷、1，4-丁二醇、己二酸、癸二酸、1,6-己二醇、新戊二醇、3-甲基-1,5戊二醇、十二烷二酸、异酞酸、壬二酸、聚已酸内酯中的一种或几种。优选2～3种多元醇的混合液，优选多元醇配比为1：(1～4)，或1：(1～4)：(1～2)。
上述异氰酸酯预聚体的NCO含量(质量分数)在8％～15％之间。
本发明的耐热底漆的制备方法包括以下步骤：
1、制备混合有机溶剂：将二甲苯、醋酸丁酯、丙二醇甲醚醋酸酯按重量比为5：3：2或1：1：1进行混合；
2、制备A组分：将A组分中的双酚A型环氧树脂，在转速为600～700r/min的搅拌下加入至混合有机溶剂中，待树脂完全分散后，加入除非浮型铝粉、助剂之外的全部成分，使用篮式砂磨机，转速为1900～2000r/min下，研磨至细度≤45μm，在转速为600～700r/min的搅拌加入助剂，80目滤网过滤，200～300r/min搅拌下加入研磨分散后的非浮型铝粉，分散均匀后，得到A组分；
3、制备B组分：在反应釜中加入IPDI，升温至50℃，N2保护，搅拌下滴加多元醇溶液，0.5～1h内滴加完毕，保持温度在80～90℃下反应2～3h后，测定NCO含量，出料冷却至室温，加入醋酸丁酯，调整固含量至70～80wt％，得到B组分；
在施工前将本发明的耐热底漆中的A、B组分按比例2.5～4：1进行混合，之后可以采用喷涂、刷涂、滚涂的方法进行施工。
本发明的耐热底漆使用聚氨酯改性环氧树脂体系，可长期使用于200℃高温环境下，常温固化，柔韧性好，具有一定的阻燃性，耐受各类溶剂油、有机溶剂，满足工业上高温使用环境的要求，还可与防火涂料、防火隔热涂料等功能型涂料配套使用，增加膨胀碳层与基材的附着，保证防火涂料的防火性能。
本发明的耐热底漆的制备方法简便，易操作。
具体实施方式
以下实施例用来进一步说明本发明。
实施例1
具体制备步骤：
1、制备混合有机溶剂：将二甲苯、醋酸丁酯、丙二醇甲醚醋酸酯按重量比为5：3：2进行混合；
2、制备A组分：将A组分中的30g双酚A型环氧树脂(环氧值0.51)，在转速为600～700r/min的搅拌下加入至混合有机溶剂中，待树脂完全分散后，加入10g云母粉、10g沉淀硫酸钡、5g金红石型钛白粉、5g磷酸锌、2g氢氧化镁、2g双酚A—双(磷酸二苯酯)、2g磷酸甲苯二苯酯(除非浮型铝粉、助剂之外的全部成分)使用篮式砂磨机，转速为1900～2000r/min下，研磨至细度≤45μm，在转速为600～700r/min的搅拌加入1.5gBYK-AT203、0.2gBYK-051、0.3gBYK-310，80目滤网过滤，200～300r/min搅拌下加入2g非浮型铝粉，分散均匀后，得到A组分；
3、B组分：在反应釜中加入IPDI，升温至50℃后，N2保护下，在搅拌下滴加PPG-400和PPG-2000的混合溶液，二者比例为1：2，0.5h内滴加完毕，保持温度在80～90℃下反应2.5h后，测定NCO含量后出料冷却至室温，加入醋酸丁酯，调整固含量至75wt％，得到B组分。
A、B两组分按3：1的比例混合使用。
测试漆膜性能如下。
实施例2
1.制备混合有机溶剂：将二甲苯、醋酸丁酯、丙二醇甲醚醋酸酯按重量比为1：1：1进行混合；
2.制备A组分：将A组分中的15g双酚A型环氧树脂(环氧值0.44)和5g羟基丙烯酸酯树脂，在转速为600～700r/min的搅拌下加入至混合有机溶剂中，待树脂完全分散后，加入3g金红石型钛白粉、12g气相二氧化硅、5g陶土、10g滑石粉、5g三聚磷酸铝、5g磷酸三苯酯、2g氢氧化铝、1g三氧化二锑，使用篮式砂磨机，转速为1900～2000r/min下，研磨至细度≤45μm，在转速为600～700r/min的搅拌加入1.5gBYK-161、0.1gBYK-065、0.4gBYK-333，80目滤网过滤，200～300r/min搅拌下加入5g非浮型铝粉，分散均匀后，得到A组分；
3.B组分：在反应釜中加入IPDI，升温至50℃后，N2保护下，在搅拌下滴加PPG-200和PPG-1000的混合溶液，二者比例为1：4，1h内滴加完毕，保持温度在80～90℃下反应2.5h后，测定NCO含量后出料冷却至室温，加入醋酸丁酯，调整固含量至70wt％。
A、B两组分按2.5：1的比例混合使用。
测试漆膜性能如下。
编号 测试项目 测试结果
1 柔韧性 1mm
2 耐冲击 100cm
3 耐热性 200℃下100h，涂层不鼓包、不脱落，轻微失光变色
4 耐高温溶剂油 90d
5 耐丙酮擦拭 往复100次，不露底
6 阻燃性(UL94) V-0级
7 极限氧指数LOI 32.1
8 附着力 4.2MPa
实施例3
1.制备混合有机溶剂：将二甲苯、醋酸丁酯、丙二醇甲醚醋酸酯按重量比为1：1：1进行混合；
2.制备A组分：将A组分中的20g双酚A型环氧树脂(环氧值0.21)、10g羟基丙烯酸酯树脂，在转速为600～700r/min的搅拌下加入至混合有机溶剂中，待树脂完全分散后，加入2g金红石型钛白粉、6g重钙、4g陶土、8g云母粉、2g锌粉、10g甲基膦酸二甲酯、2g氢氧化镁，使用篮式砂磨机，转速为1900～2000r/min下，研磨至细度≤45μm，在转速为600～700r/min的搅拌加入0.5g BYK-9076、0.1g BYK-053、0.4g BYK-331，80目滤网过滤，200～300r/min搅拌下加入2g非浮型铝粉、2g可膨胀石墨，分散均匀后，得到A组分；
3.B组分：在反应釜中加入IPDI，升温至50℃后，N2保护下，在搅拌下滴加1，4-丁二醇、PPG-1500、一缩二乙二醇的混合溶液，三者比例为1：4：2，1h内滴加完毕，保持温度在80～90℃下反应2.5h后，测定NCO含量后出料冷却至室温，加入醋酸丁酯，调整固含量至70wt％。
A、B两组分按3.5：1的比例混合使用。
测试漆膜性能如下。
编号 测试项目 测试结果
1 柔韧性 1mm
2 耐冲击 100cm
3 耐热性 200℃下120h，涂层不鼓包、不脱落，轻微失光变色
4 耐高温溶剂油 90d
5 耐丙酮擦拭 往复100次，不露底
6 阻燃性(UL94) V-0级
7 极限氧指数LOI 29.6
8 附着力 3.9MPa
以上所述，仅是本发明的较佳实施例而已，并非是对本发明作其它形式的限制，任何熟悉本专业的技术人员可能利用上述揭示的技术内容加以变更或改型为等同变化的等效实施例。但是凡是未脱离本发明技术方案内容，依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与改型，仍属于本发明技术方案的保护范围。

Claims (10)

1.一种耐热底漆，其特征在于，所述耐热底漆包括如下组分：
所述A组分与所述B组分的重量比为2.5～4：1。
2.根据权利要求1所述的耐热底漆，其特征在于，所述双酚A型环氧树脂的环氧值为0.12～0.56；所述无机填料为滑石粉、云母粉、沉淀硫酸钡、重钙、金红石型钛白粉、气相二氧化硅、陶土里的一种或几种；所述防锈颜料为磷酸盐类、锌粉中的一种或几种。
3.根据权利要求2所述的耐热底漆，其特征在于，所述磷酸盐类为磷酸锌、磷酸铝、磷酸钼锌、三聚磷酸铝。
4.根据权利要求1所述的耐热底漆，其特征在于，所述的阻燃剂包括有机阻燃剂和/或无机阻燃剂，所述有机阻燃剂与双酚A型环氧树脂的重量比为0.05～2：1，所述无机阻燃剂与双酚A型环氧树脂的重量比为0.02～0.5：1；所述有机阻燃剂包括：磷酸酯及其衍生物、膦酸酯、亚磷酸酯中的一种或几种；所述无机阻燃剂包括：氢氧化铝、氢氧化镁、氧化铝、三氧化二锑、五氧化二锑、二氧化钛、氧化锌、氧化钼、三氧化钼、钼酸铵、二钼酸铵、四钼酸铵、八钼酸铵、钼酸锌、氧化锡、氧化亚铜、可膨胀石墨中的一种或几种。
5.根据权利要求4所述的耐热底漆，其特征在于，所述磷酸酯及其衍生物包括：磷酸三甲苯酯、磷酸三苯酯、三羟甲基丙烷三丙烯酸酯、磷酸三异丙基苯酯、磷酸三乙酯、磷酸三丁酯、磷酸三辛酯、异丙基化磷酸三苯酯、亚磷酸三苯酯、磷酸甲苯二苯酯、磷酸三丁氧基乙酯、1，3，5-吡唑酮、甲苯基二苯基磷酸酯、间苯二酚—双(磷酸二苯酯)、双酚A—双(磷酸二苯酯)、间苯二酚—双[二(2，6—二甲基苯基)磷酸酯]中的一种或几种；所述膦酸酯包括：N-羟甲基丙酰胺类甲基膦酸酯、环中膦酸酯、N、N-对苯二胺基(2-羟基)二苄基膦酸四乙酯、甲基膦酸二甲酯中的一种或几种。
6.根据权利要求1所述的耐热底漆，其特征在于，所述混合有机溶剂为二甲苯、醋酸丁酯、丙二醇甲醚醋酸酯的混合溶液，二甲苯、醋酸丁酯、丙二醇甲醚醋酸酯的重量比为5：3：2或1：1：1。
7.根据权利要求1所述的耐热底漆，其特征在于，所述改性异氰酸酯的合成方法如下：在反应釜中加入异佛尔酮二异氰酸酯，升温至50℃，N2保护，搅拌下滴加多元醇溶液，0.5～1h内滴加完毕，保持温度在80～90℃下反应2～3h后，测定NCO含量，出料冷却至室温，加入醋酸丁酯，调整固含量至70～80wt％；所述多元醇溶液包括二官能度、三官能度的聚醚多元醇、聚酯多元醇中的一种或几种。
8.根据权利要求7所述的耐热底漆，其特征在于，当所述多元醇溶液为两种多元醇混合时，所述两种多元醇的重量比为1：(1～4)；当所述多元醇溶液为三种多元醇混合时，所述三种多元醇的重量比1：(1～4)：(1～2)。
9.根据权利要求7或8所述的耐热底漆，其特征在于，所述聚醚多元醇为PPG-200、PPG-400、PPG-600、PPG-1000、PPG-1500、PPG-2000、PPG-3000、PPG-4000、PPG-6000、PPG-8000中的一种或几种；所述聚酯多元醇包括乙二醇、丙二醇、二乙二醇、一缩二乙二醇、三羟甲基丙烷、1，4-丁二醇、己二酸、癸二酸、1,6-己二醇、新戊二醇、3-甲基-1,5戊二醇、十二烷二酸、异酞酸、壬二酸、聚已酸内酯中的一种或几种。
10.一种根据权利要求1所述的耐热底漆的制备方法，其特征在于，所述制备方法包括以下步骤：
(1)制备混合有机溶剂：将二甲苯、醋酸丁酯、丙二醇甲醚醋酸酯按重量比为5：3：2或1：1：1进行混合；
(2)制备A组分：将A组分中的双酚A型环氧树脂，在转速为600～700r/min的搅拌下加入至混合有机溶剂中，待树脂完全分散后，加入除非浮型铝粉、助剂之外的全部成分，使用篮式砂磨机，转速为1900～2000r/min下，研磨至细度≤45μm，在转速为600～700r/min的搅拌加入助剂，80目滤网过滤，200～300r/min搅拌下加入研磨分散后的非浮型铝粉，分散均匀后，得到A组分；
(3)制备B组分：在反应釜中加入异佛尔酮二异氰酸酯，升温至50℃，N2保护，搅拌下滴加多元醇溶液，0.5～1h内滴加完毕，保持温度在80～90℃下反应2～3h后，测定NCO含量，出料冷却至室温，加入醋酸丁酯，调整固含量至70～80wt％，得到B组分。
CN201910382727.3A 2019-05-09 2019-05-09 一种耐热底漆及其制备方法 Active CN110105863B (zh)