CN109825025A - 一种abs组合物、制备方法及其组合物制得的户外家具 - Google Patents
一种abs组合物、制备方法及其组合物制得的户外家具 Download PDFInfo
- Publication number
- CN109825025A CN109825025A CN201910059028.5A CN201910059028A CN109825025A CN 109825025 A CN109825025 A CN 109825025A CN 201910059028 A CN201910059028 A CN 201910059028A CN 109825025 A CN109825025 A CN 109825025A
- Authority
- CN
- China
- Prior art keywords
- butyl
- bis
- ester
- phenyl
- tert
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种ABS组合物，以质量百分数计，95％～99.55％的聚甲醛，0.15％～1％的抗氧化剂，0.15％～2％的紫外线吸收剂，0.15％～2％的光稳定剂。一种ABS组合物及其制作的户外家具，这种材料组合物能够显著提高ABS材料的耐热、耐光性能，延缓ABS的降解、老化过程，延长通过ABS组合物制作的家具使用寿命。
Description
技术领域
本发明涉及高分子材料领域，具体涉及一种ABS组合物、制备方法及其组合物制得的户外家具。
背景技术
ABS通称丙烯腈丁二烯苯乙烯，是由丙烯腈-丁二烯-苯乙烯三种单体共聚而成。由于三种单体的比例不同，可有不同性能和熔融温度、流动性能的ABS和其他添加剂共混，可以扩大至不同用途和性能的ABS。ABS主要应用于汽车、电子电器和建材领域。不同的领域所应用的ABS的材质不同。
例如将ABS应用于家具行业。因为室外条件复杂，一般塑料易于老化，ABS材质的家具容易出现破碎的现象。为了延长ABS材质的户外家具的使用寿命，需要针对性解决老化现象。家具在室外使用时，与空气充分接触，光照、温度均都会对加快家具的老化。
在合成ABS过程中加入抗氧剂制备的具有抗氧化功能的ABS材料在实际应用中灵活性低，不如在制作制品时根据制品的特性针对性加入抗氧剂灵活性高且针对性强。
发明内容
针对现有技术中所存在的不足，本发明的目的在于提供一种ABS组合物，这种材料组合物能够显著提高ABS材料的耐热、耐光性能，延缓ABS的降解、老化过程，延长通过ABS组合物制作的家具使用寿命。
为实现上述目的，本发明采用了如下的技术方案：
一种ABS组合物，以质量百分数计，95％～99.55％的聚甲醛，0.15％～1％的抗氧化剂，0.15％～2％的紫外线吸收剂，0.15％～2％的光稳定剂。
进一步，所述组合物中：抗氧化剂为以下中的一种或者几种组合：四[β-(3，5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯、β-(3,5-二叔丁基-4-羟基苯基)丙酸十八碳醇酯、1,3,5-三甲基-2,4,6-三(3，5-二叔丁基-4-羟基苄基)苯、三甘醇双β-(3-叔丁基-4-羟基-5-甲基苯基)丙酸酯、1,3,5-三(3，5-二叔丁基-4-羟基苄基)-1,3,5-三嗪-2,4,6(1H，3H，5H)-三酮、2,2′-草酰胺基-双[乙基-3-(3,5-二叔丁基-4-羟苄基)]丙酸酯、4,4′-亚甲基双(2,6-二叔丁基苯酚)、硫代二丙酸双十八酯、硫代二丙酸双十二醇酯、1，1，3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷、4，4′-亚丁基-双[2-(1，1-二甲基乙基)-5-甲基]苯酚、亚磷酸三(2,4-二叔丁基苯基)酯、3，9-双(十八氧基)-2，4，8，10-四氧杂-3，9-二磷螺[5,5]十一烷、季戊四醇四(3-正十二烷基硫代丙酸酯)、双十八烷基季戊四醇双亚磷酸酯、双(2,4-二叔丁基苯基)季戊四醇二亚磷酸酯、三(2,4-二叔丁基)亚磷酸苯酯、三乙二醇醚-二(3-叔丁基-4-羟基-5-甲基苯基)丙酸酯、4,4′-二(苯基异丙基)二苯胺、4-甲基-苯酚与二环戊二烯和异丁烯的反应产物、双(2,4-二叔丁基苯酚)季戊四醇二亚磷酸酯、2,2′-硫代二乙基双[3-(3,5-二叔丁基-4-羟苯基)丙酸酯]、2-(2-羟基-3-叔丁基-5-甲基苄基)-4-甲基-6-叔丁基苯基丙烯酸酯、三(3，5-二叔丁基-4-羟苄基)异氰尿酸酯、2-{1-[2-羟基-3，5-双(2-甲基丁-2-基)苯基]乙基}-4，6-二(2-甲基丁-2-基)苯基丙烯酸酯、双(2，6-二叔丁基-4-甲基苯基)季戊四醇二磷酸酯、1，2-双[β-(3,5-二叔丁基-4-羟基苯基)丙酰]肼、三(壬基酚)亚磷酸酯、4，4′-对开异丙基二苯基C12-15-醇亚磷酸酯、亚磷酸二苯基异癸基酯、亚磷酸一苯二异癸酯、亚磷酸三异癸基脂、亚磷酸苯基二(十三烷基)酯、亚磷酸苯基二(乙基-己基)酯、亚磷酸三(十二烷基)酯、亚磷酸三(异十三烷基)酯、二亚磷酸四异癸基双酚A酯、四苯基二丙二醇二亚磷酸酯、聚(二丙二醇)苯基亚磷酸酯、3，9-二癸烷氧基-2，4，8，10-四氧杂-3，9-二磷螺[5,5]十一烷、4，4′-亚丁基双-(3-甲基-6-叔丁苯基)-四(十三烷基)二亚磷酸酯；
紫外线吸收剂为以下中的一种或者几种组合：2-(2-羟基-3-叔丁基-5-甲基苯基)-5-氯代苯并三唑、2-(2′-羟基-3′，5′-二叔丁基苯基)-5-氯代苯并三唑、2-(2′-羟基-5′-甲基苯基)苯并三唑、2-羟基-4-正辛氧基二苯甲酮、2-羟基-4-甲氧基二苯甲酮、3,5-二叔丁基-4-羟基苯甲酸-2,4-二叔丁基苯酯、2-(2H-苯并三唑-2-基)-4,6-二(1-甲基-1-苯基乙基)苯酚、N-(2-乙氧基苯基)-N′-(2-乙苯基)-乙二酰胺、2-(2H-苯并三氮唑-2-基)-4,6-双(1，1-二甲基乙基)苯酚、2-(2-羟基-5-叔辛苯基)苯并三唑、3,5-二叔丁基-4-羟基苯甲酸十六酯、2-氰基-3，3-二苯基丙烯酸乙酯、2-氰基-3，3-二苯基-2-丙烯酸(2-乙基己基)酯；
光稳定剂为以下中的一种或者几种组合：癸二酸双2,2,6,6，-四甲基哌啶醇酯、聚丁二酸(4-羟基-2,2,6,6-四甲基-1-哌啶乙醇)酯、聚{[6-[(1,1,3,3-四甲基丁基)氨基]]-1,3,5-三嗪-2,4-双[(2,2,6,6-四甲基哌啶基)亚氨基]-1,6-己二撑[(2,2,6,6-四甲基-4-哌啶基)亚氨基]}与聚丁二酸(4-羟基-2,2,6,6-四甲基-1-哌啶乙醇)酯的复合物、癸二酸双(1，2，2，6，6-五甲基-4-哌啶)酯与1-甲基-8-(1，2，2，6，6-五甲基-4-哌啶)癸二酸酯的混合物、1，5，8，12-四[4，6-二(N-丁基-N-1，2，2，6，6-五甲基-4-哌啶基氨基)-1，3，5-三嗪-2-基]-1，5，8，12-四氮杂十二烷、双(1，2，2，6，6-五甲基-4-哌啶)癸二酸酯与1-甲基-8-(1，2，2，6，6-五甲基-4-哌啶)癸二酸酯的混合物。
进一步，所述抗氧剂的的质量百分含量为0.15％～0.3％或者0.55％～0.85％。
进一步，紫外线吸收剂的质量百分含量为0.35～0.55％、0.65～0.95％或者1.05～1.45％。
进一步，光稳定剂的质量百分含量为0.35～0.55％、0.65～0.95％或者1.05～1.45％。
一种由ABS组合物制作的户外家具。。
本发明与现有技术相比，具有如下有益效果：
1、ABS组合物中的抗氧剂、紫外线吸收剂、光稳定剂不仅仅针对性的解决了氧化和光照对ABS组合物制品的影响，而且抗氧剂、紫外线吸收剂、光稳定剂之间存在这协同效应，可以有效的延缓ABS组合物制品的老化时间。
2、ABS组合物针对制作户外家具进行配置，用本发明制作的户外家具具有较长使用寿命，能够保持户外家具的性能的同时，保持观赏性。
3、本发明的ABS组合物应用灵活，加工工艺简单，容易调配控制。
具体实施方式
ABS
ABS是由丙烯腈、丁二烯、苯乙烯组成的三元共聚物，主要生产方法包括掺合法、接枝法、联用法、接枝-掺合法，一般三种单体的比例范围大致为丙烯腈25～35％，丁二烯25～30％和苯乙烯40～50％。本发明所用的ABS为外购，型号为：奇美-7475
抗氧剂
抗氧剂在ABS组合物中的主要机制为俘获自由基或者分解自由基引发的氢过氧化物。本发明中的抗氧剂。本发明的氧化剂包括以下中的一种或者几种组合：四[β-(3，5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯、β-(3,5-二叔丁基-4-羟基苯基)丙酸十八碳醇酯、1,3,5-三甲基-2,4,6-三(3，5-二叔丁基-4-羟基苄基)苯、三甘醇双β-(3-叔丁基-4-羟基-5-甲基苯基)丙酸酯、1,3,5-三(3，5-二叔丁基-4-羟基苄基)-1,3,5-三嗪-2,4,6(1H，3H，5H)-三酮、2,2′-草酰胺基-双[乙基-3-(3,5-二叔丁基-4-羟苄基)]丙酸酯、4,4′-亚甲基双(2,6-二叔丁基苯酚)、硫代二丙酸双十八酯、硫代二丙酸双十二醇酯、1，1，3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷、4，4′-亚丁基-双[2-(1，1-二甲基乙基)-5-甲基]苯酚、亚磷酸三(2,4-二叔丁基苯基)酯、3，9-双(十八氧基)-2，4，8，10-四氧杂-3，9-二磷螺[5,5]十一烷、季戊四醇四(3-正十二烷基硫代丙酸酯)、双十八烷基季戊四醇双亚磷酸酯、双(2,4-二叔丁基苯基)季戊四醇二亚磷酸酯、三(2,4-二叔丁基)亚磷酸苯酯、三乙二醇醚-二(3-叔丁基-4-羟基-5-甲基苯基)丙酸酯、4,4′-二(苯基异丙基)二苯胺、4-甲基-苯酚与二环戊二烯和异丁烯的反应产物、双(2,4-二叔丁基苯酚)季戊四醇二亚磷酸酯、2,2′-硫代二乙基双[3-(3,5-二叔丁基-4-羟苯基)丙酸酯]、2-(2-羟基-3-叔丁基-5-甲基苄基)-4-甲基-6-叔丁基苯基丙烯酸酯、三(3，5-二叔丁基-4-羟苄基)异氰尿酸酯、2-{1-[2-羟基-3，5-双(2-甲基丁-2-基)苯基]乙基}-4，6-二(2-甲基丁-2-基)苯基丙烯酸酯、双(2，6-二叔丁基-4-甲基苯基)季戊四醇二磷酸酯、1，2-双[β-(3,5-二叔丁基-4-羟基苯基)丙酰]肼、三(壬基酚)亚磷酸酯、4，4′-对开异丙基二苯基C12-15-醇亚磷酸酯、亚磷酸二苯基异癸基酯、亚磷酸一苯二异癸酯、亚磷酸三异癸基脂、亚磷酸苯基二(十三烷基)酯、亚磷酸苯基二(乙基-己基)酯、亚磷酸三(十二烷基)酯、亚磷酸三(异十三烷基)酯、二亚磷酸四异癸基双酚A酯、四苯基二丙二醇二亚磷酸酯、聚(二丙二醇)苯基亚磷酸酯、3，9-二癸烷氧基-2，4，8，10-四氧杂-3，9-二磷螺[5,5]十一烷、4，4′-亚丁基双-(3-甲基-6-叔丁苯基)-四(十三烷基)二亚磷酸酯。
抗氧剂的百分含量为0.15％～1％，优选为0.15％～0.3％或者0.55％～0.85％。
紫外线吸收剂
本发明ABS组合物中的紫外线吸收剂可以将光能转变为分子之间的振动最终以热的形式释放，防止光对ABS引发自由基。本发明的紫外线吸收剂为以下有机材料中的一种或者几种组合：2-(2-羟基-3-叔丁基-5-甲基苯基)-5-氯代苯并三唑、2-(2′-羟基-3′，5′-二叔丁基苯基)-5-氯代苯并三唑、2-(2′-羟基-5′-甲基苯基)苯并三唑、2-羟基-4-正辛氧基二苯甲酮、2-羟基-4-甲氧基二苯甲酮、3,5-二叔丁基-4-羟基苯甲酸-2,4-二叔丁基苯酯、2-(2H-苯并三唑-2-基)-4,6-二(1-甲基-1-苯基乙基)苯酚、N-(2-乙氧基苯基)-N′-(2-乙苯基)-乙二酰胺、2-(2H-苯并三氮唑-2-基)-4,6-双(1，1-二甲基乙基)苯酚、2-(2-羟基-5-叔辛苯基)苯并三唑、3,5-二叔丁基-4-羟基苯甲酸十六酯、2-氰基-3，3-二苯基丙烯酸乙酯、2-氰基-3，3-二苯基-2-丙烯酸(2-乙基己基)酯。
紫外线吸收剂的百分含量为0.15％～2％，优选为0.35～0.55％、0.65～0.95％或者1.05～1.45％。
光稳定剂
光稳定剂的作用与紫外线吸收剂的原理相同，都是阻断紫外光对ABS的影响。
本发明光稳定剂包括一种或者几种组合：癸二酸双2,2,6,6，-四甲基哌啶醇酯、聚丁二酸(4-羟基-2,2,6,6-四甲基-1-哌啶乙醇)酯、聚{[6-[(1,1,3,3-四甲基丁基)氨基]]-1,3,5-三嗪-2,4-双[(2,2,6,6-四甲基哌啶基)亚氨基]-1,6-己二撑[(2,2,6,6-四甲基-4-哌啶基)亚氨基]}与聚丁二酸(4-羟基-2,2,6,6-四甲基-1-哌啶乙醇)酯的复合物、癸二酸双(1，2，2，6，6-五甲基-4-哌啶)酯与1-甲基-8-(1，2，2，6，6-五甲基-4-哌啶)癸二酸酯的混合物、1，5，8，12-四[4，6-二(N-丁基-N-1，2，2，6，6-五甲基-4-哌啶基氨基)-1，3，5-三嗪-2-基]-1，5，8，12-四氮杂十二烷、双(1，2，2，6，6-五甲基-4-哌啶)癸二酸酯与1-甲基-8-(1，2，2，6，6-五甲基-4-哌啶)癸二酸酯的混合物。
本发明光稳定剂的百分含量为0.15％～2％，优选为0.35～0.55％、0.65～0.95％或者1.05～1.45％。
制备方法
S1：取抗氧剂、紫外线吸收剂、光稳定剂溶解于硅油中，配置成硅油溶液；
S2：将ABS颗粒在80℃下干燥2～4小时，粉碎，过300目筛，
S3：低速搅拌：称取定量的ABS置于混合机中，控制搅拌温度为35-45℃，低速搅拌，搅拌速度为100～300r/min,搅拌90min,同时加入50％硅油溶液，滴加速度控制在6ml/min；
S4：高速搅拌：高速搅拌搅拌速度控制在500～800r/min,搅拌120-180min,控制滴加50％硅油溶液的速度为1ml/min；
S5：高温搅拌：高速搅拌结束后，继续高温搅拌，搅拌速度控制在200～600r/min，温度控制在98～110℃，搅拌50min。
S6：挤压：搅拌结束后，保持温度在90～105℃，输送至螺杆机中挤压；螺杆长径比为30，螺杆转动速度为55rm，挤压温度控制在螺杆机的一区：180～190℃；二区：190～220℃；三区215～230℃；四区215～230℃；五区230-240℃；六区220～230℃；七区220～230℃；八区215～225℃；九区215～225℃；十区220～220℃。
实施例1
ABS的质量百分含量为98.7％；抗氧剂为3，9-双(十八氧基)-2，4，8，10-四氧杂-3，9-二磷螺[5,5]十一烷，质量百分含量为1％；紫外线吸收剂为3,5-二叔丁基-4-羟基苯甲酸十六酯，质量百分含量为0.15％；光稳定剂为癸二酸双2,2,6,6，-四甲基哌啶醇酯，质量百分含量0.15％。ABS组合物由此组分构成，制成板状。
实施例2
ABS的质量百分含量为97.5％；抗氧剂为1,3,5-三(3，5-二叔丁基-4-羟基苄基)-1,3,5-三嗪-2,4,6(1H，3H，5H)-三酮，质量百分含量为0.15％；紫外线吸收剂为2-羟基-4-正辛氧基二苯甲酮，质量百分含量为2％；光稳定剂为聚丁二酸(4-羟基-2,2,6,6-四甲基-1-哌啶乙醇)酯，质量百分含量0.35％。ABS组合物由此组分构成，制成板状。
实施例3
ABS的质量百分含量为97.48％；抗氧剂为2,2′-草酰胺基-双[乙基-3-(3,5-二叔丁基-4-羟苄基)]丙酸酯，质量百分含量为0.17％；紫外线吸收剂为2-羟基-4-甲氧基二苯甲酮，质量百分含量为0.35％；光稳定剂为聚丁二酸(4-羟基-2,2,6,6-四甲基-1-哌啶乙醇)酯酯，质量百分含量2％。ABS组合物由此组分构成，制成板状。
实施例4
ABS的质量百分含量为97.15％；抗氧剂为2,2′-草酰胺基-双[乙基-3-(3,5-二叔丁基-4-羟苄基)]丙酸酯，质量百分含量为0.15％，抗氧剂为四苯基二丙二醇二亚磷酸酯，质量百分含量为0.7％；紫外线吸收剂为2-羟基-4-甲氧基二苯甲酮，质量百分含量为0.55％；光稳定剂为聚{[6-[(1,1,3,3-四甲基丁基)氨基]]-1,3,5-三嗪-2,4-双[(2,2,6,6-四甲基哌啶基)亚氨基]-1,6-己二撑[(2,2,6,6-四甲基-4-哌啶基)，质量百分含量1.45％。ABS组合物由此组分构成，制成板状。
实施例5
ABS的质量百分含量为97.45％；抗氧剂为四苯基二丙二醇二亚磷酸酯，质量百分含量为0.55％；紫外线吸收剂为3,5-二叔丁基-4-羟基苯甲酸-2,4-二叔丁基苯酯，质量百分含量为0.7％，紫外线吸收剂为2-羟基-4-甲氧基二苯甲酮，质量百分含量为0.75％；光稳定剂为癸二酸双(1，2，2，6，6-五甲基-4-哌啶)酯与1-甲基-8-(1，2，2，6，6-五甲基-4-哌啶)癸二酸酯的混合物，质量百分含量0.55％。ABS组合物由此组分构成，制成板状。
实施例6
ABS的质量百分含量为97.7％；抗氧剂为四苯基二丙二醇二亚磷酸酯，质量百分含量为0.3％；紫外线吸收剂为2-羟基-4-甲氧基二苯甲酮，质量百分含量为1.05％；光稳定剂为1，5，8，12-四[4，6-二(N-丁基-N-1，2，2，6，6-五甲基-4-哌啶基氨基)-1，3，5-三嗪-2-基]-1，5，8，12-四氮杂十二烷，质量百分含量为0.65％，光稳定剂为双(1，2，2，6，6-五甲基-4-哌啶)癸二酸酯与1-甲基-8-(1，2，2，6，6-五甲基-4-哌啶)癸二酸酯的混合物，质量百分含量0.3％。ABS组合物由此组分构成，制成板状。
实施例7
ABS的质量百分含量为97.23％；抗氧剂为四苯基二丙二醇二亚磷酸酯，质量百分含量为0.55％，抗氧剂为2,2′-草酰胺基-双[乙基-3-(3,5-二叔丁基-4-羟苄基)]丙酸酯，质量百分含量为0.22％；紫外线吸收剂为2-羟基-4-甲氧基二苯甲酮，质量百分含量为0.65％，紫外线吸收剂为2-羟基-4-甲氧基二苯甲酮，质量百分含量为0.3％；光稳定剂为1，5，8，12-四[4，6-二(N-丁基-N-1，2，2，6，6-五甲基-4-哌啶基氨基)-1，3，5-三嗪-2-基]-1，5，8，12-四氮杂十二烷，质量百分含量为0.7％，光稳定剂为双(1，2，2，6，6-五甲基-4-哌啶)癸二酸酯与1-甲基-8-(1，2，2，6，6-五甲基-4-哌啶)癸二酸酯的混合物，质量百分含量0.35％。ABS组合物由此组分构成，制成板状。
实施例8
ABS的质量百分含量为97.87％；抗氧剂为四苯基二丙二醇二亚磷酸酯，质量百分含量为0.57％，抗氧剂为2,2′-草酰胺基-双[乙基-3-(3,5-二叔丁基-4-羟苄基)]丙酸酯，质量百分含量为0.26％；紫外线吸收剂为2-羟基-4-甲氧基二苯甲酮，质量百分含量为0.35％，紫外线吸收剂为2-羟基-4-甲氧基二苯甲酮，质量百分含量为0.3％；光稳定剂为1，5，8，12-四[4，6-二(N-丁基-N-1，2，2，6，6-五甲基-4-哌啶基氨基)-1，3，5-三嗪-2-基]-1，5，8，12-四氮杂十二烷，质量百分含量为0.3％，光稳定剂为双(1，2，2，6，6-五甲基-4-哌啶)癸二酸酯与1-甲基-8-(1，2，2，6，6-五甲基-4-哌啶)癸二酸酯的混合物，质量百分含量0.35％。ABS组合物由此组分构成，制成板状。
将实施例1-8制备的板，放置在加速箱中进行加速实验，按照国家标准GB13022检测ABS的拉伸强度，断裂伸长率。
表一实施例1-8拉伸强度，断裂伸长率
对比例1：不加入任何抗氧剂、紫外线吸收剂、光稳定剂，直接进行加工，按照上述实验数据进行检测：初始拉伸强度为47.5Mpa；初始断裂伸长率23％；加速后拉伸强度37Mpa；加速后断裂伸长率16％。
结论：
本发明公开的ABS组合物，相比与不加入抗氧剂、紫外线吸收剂、光稳定剂的ABS对比例，在拉伸强度、断裂伸长率方面均有很大的提神，而且经过加速实验后可以延长ABS组合物制备的户外家具的寿命。
最后说明的是，以上实施例仅用以说明本发明的技术方案而非限制，尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的宗旨和范围，其均应涵盖在本发明的权利要求范围当中。
Claims (7)
1.一种ABS组合物，其特征在于：以质量百分数计，包括：95％～99.55％的聚甲醛，0.15％～1％的抗氧化剂，0.15％～2％的紫外线吸收剂，0.15％～2％的光稳定剂。
2.根据权利要求1所述的一种ABS组合物，其特征在于：所述组合物中
抗氧化剂为以下中的一种或者几种组合：四[β-(3，5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯、β-(3,5-二叔丁基-4-羟基苯基)丙酸十八碳醇酯、1,3,5-三甲基-2,4,6-三(3，5-二叔丁基-4-羟基苄基)苯、三甘醇双β-(3-叔丁基-4-羟基-5-甲基苯基)丙酸酯、1,3,5-三(3，5-二叔丁基-4-羟基苄基)-1,3,5-三嗪-2,4,6(1H，3H，5H)-三酮、2,2′-草酰胺基-双[乙基-3-(3,5-二叔丁基-4-羟苄基)]丙酸酯、4,4′-亚甲基双(2,6-二叔丁基苯酚)、硫代二丙酸双十八酯、硫代二丙酸双十二醇酯、1，1，3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷、4，4′-亚丁基-双[2-(1，1-二甲基乙基)-5-甲基]苯酚、亚磷酸三(2,4-二叔丁基苯基)酯、3，9-双(十八氧基)-2，4，8，10-四氧杂-3，9-二磷螺[5,5]十一烷、季戊四醇四(3-正十二烷基硫代丙酸酯)、双十八烷基季戊四醇双亚磷酸酯、双(2,4-二叔丁基苯基)季戊四醇二亚磷酸酯、三(2,4-二叔丁基)亚磷酸苯酯、三乙二醇醚-二(3-叔丁基-4-羟基-5-甲基苯基)丙酸酯、4,4′-二(苯基异丙基)二苯胺、4-甲基-苯酚与二环戊二烯和异丁烯的反应产物、双(2,4-二叔丁基苯酚)季戊四醇二亚磷酸酯、2,2′-硫代二乙基双[3-(3,5-二叔丁基-4-羟苯基)丙酸酯]、2-(2-羟基-3-叔丁基-5-甲基苄基)-4-甲基-6-叔丁基苯基丙烯酸酯、三(3，5-二叔丁基-4-羟苄基)异氰尿酸酯、2-{1-[2-羟基-3，5-双(2-甲基丁-2-基)苯基]乙基}-4，6-二(2-甲基丁-2-基)苯基丙烯酸酯、双(2，6-二叔丁基-4-甲基苯基)季戊四醇二磷酸酯、1，2-双[β-(3,5-二叔丁基-4-羟基苯基)丙酰]肼、三(壬基酚)亚磷酸酯、4，4′-对开异丙基二苯基C12-15-醇亚磷酸酯、亚磷酸二苯基异癸基酯、亚磷酸一苯二异癸酯、亚磷酸三异癸基脂、亚磷酸苯基二(十三烷基)酯、亚磷酸苯基二(乙基-己基)酯、亚磷酸三(十二烷基)酯、亚磷酸三(异十三烷基)酯、二亚磷酸四异癸基双酚A酯、四苯基二丙二醇二亚磷酸酯、聚(二丙二醇)苯基亚磷酸酯、3，9-二癸烷氧基-2，4，8，10-四氧杂-3，9-二磷螺[5,5]十一烷、4，4′-亚丁基双-(3-甲基-6-叔丁苯基)-四(十三烷基)二亚磷酸酯；
紫外线吸收剂为以下中的一种或者几种组合：2-(2-羟基-3-叔丁基-5-甲基苯基)-5-氯代苯并三唑、2-(2′-羟基-3′，5′-二叔丁基苯基)-5-氯代苯并三唑、2-(2′-羟基-5′-甲基苯基)苯并三唑、2-羟基-4-正辛氧基二苯甲酮、2-羟基-4-甲氧基二苯甲酮、3,5-二叔丁基-4-羟基苯甲酸-2,4-二叔丁基苯酯、2-(2H-苯并三唑-2-基)-4,6-二(1-甲基-1-苯基乙基)苯酚、N-(2-乙氧基苯基)-N′-(2-乙苯基)-乙二酰胺、2-(2H-苯并三氮唑-2-基)-4,6-双(1，1-二甲基乙基)苯酚、2-(2-羟基-5-叔辛苯基)苯并三唑、3,5-二叔丁基-4-羟基苯甲酸十六酯、2-氰基-3，3-二苯基丙烯酸乙酯、2-氰基-3，3-二苯基-2-丙烯酸(2-乙基己基)酯；
光稳定剂为以下中的一种或者几种组合：癸二酸双2,2,6,6，-四甲基哌啶醇酯、聚丁二酸(4-羟基-2,2,6,6-四甲基-1-哌啶乙醇)酯、聚{[6-[(1,1,3,3-四甲基丁基)氨基]]-1,3,5-三嗪-2,4-双[(2,2,6,6-四甲基哌啶基)亚氨基]-1,6-己二撑[(2,2,6,6-四甲基-4-哌啶基)亚氨基]}与聚丁二酸(4-羟基-2,2,6,6-四甲基-1-哌啶乙醇)酯的复合物、癸二酸双(1，2，2，6，6-五甲基-4-哌啶)酯与1-甲基-8-(1，2，2，6，6-五甲基-4-哌啶)癸二酸酯的混合物、1，5，8，12-四[4，6-二(N-丁基-N-1，2，2，6，6-五甲基-4-哌啶基氨基)-1，3，5-三嗪-2-基]-1，5，8，12-四氮杂十二烷、双(1，2，2，6，6-五甲基-4-哌啶)癸二酸酯与1-甲基-8-(1，2，2，6，6-五甲基-4-哌啶)癸二酸酯的混合物。
3.根据权利要求1-2中的任意一项所述的一种ABS组合物，其特征在于：所述抗氧剂的的质量百分含量为0.15％～0.3％或者0.55％～0.85％。
4.根据权利要求1-2中的任意一项所述的一种ABS组合物，其特征在于：紫外线吸收剂的质量百分含量为0.35～0.55％、0.65～0.95％或者1.05～1.45％。
5.根据权利要求1-2中的任意一项所述的一种ABS组合物，其特征在于：光稳定剂的质量百分含量为0.35～0.55％、0.65～0.95％或者1.05～1.45％。
6.一种由权利要求1-2中的任意一项所述ABS组合物制作的户外家具。
7.一种如权利要求1所述的一种ABS组合物的制备方法，其特征在于：包括如下步骤：
S1：取抗氧剂、紫外线吸收剂、光稳定剂溶解于硅油中，配置成硅油溶液；
S2：将ABS颗粒在80℃下干燥2～4小时，粉碎，过300目筛，
S3：低速搅拌：称取定量的ABS置于混合机中，控制搅拌温度为35-45℃，低速搅拌，搅拌速度为100～300r/min,搅拌90min,同时加入50％硅油溶液，滴加速度控制在6ml/min；
S4：高速搅拌：高速搅拌搅拌速度控制在500～800r/min,搅拌120-180min,控制滴加50％硅油溶液的速度为1ml/min；
S5：高温搅拌：高速搅拌结束后，继续高温搅拌，搅拌速度控制在200～600r/min，温度控制在98～110℃，搅拌50min。
S6：挤压：搅拌结束后，保持温度在90～105℃，输送至螺杆机中挤压；螺杆长径比为30，螺杆转动速度为55rm，挤压温度控制在螺杆机的一区：180～190℃；二区：190～220℃；三区215～230℃；四区215～230℃；五区230-240℃；六区220～230℃；七区220～230℃；八区215～225℃；九区215～225℃；十区220～220℃。