CN109560381A - 一种陶瓷天线罩提高强度的预增强方法 - Google Patents

一种陶瓷天线罩提高强度的预增强方法 Download PDF

Info

Publication number
CN109560381A
CN109560381A CN201811432055.4A CN201811432055A CN109560381A CN 109560381 A CN109560381 A CN 109560381A CN 201811432055 A CN201811432055 A CN 201811432055A CN 109560381 A CN109560381 A CN 109560381A
Authority
CN
China
Prior art keywords
antenna house
enhancement
wall
antenna
ceramic radome
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201811432055.4A
Other languages
English (en)
Other versions
CN109560381B (zh
Inventor
刘冬晖
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Institute of Remote Sensing Equipment
Original Assignee
Beijing Institute of Remote Sensing Equipment
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing Institute of Remote Sensing Equipment filed Critical Beijing Institute of Remote Sensing Equipment
Priority to CN201811432055.4A priority Critical patent/CN109560381B/zh
Publication of CN109560381A publication Critical patent/CN109560381A/zh
Application granted granted Critical
Publication of CN109560381B publication Critical patent/CN109560381B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种陶瓷天线罩提高强度的预增强方法，通过改进天线罩增强的工艺过程，在保证天线罩的性能不变的情况下，提高了天线罩产品的抗热冲击能力。其具体步骤为：第一步，天线罩内壁均匀短时增强；第二步，静置晾干；第三步，天线罩外表面喷涂防潮涂层；第四步，烘干；第五步，天线罩内壁再次增强；第六步，固化烘干。通过天线罩的预增强的方法，即可实现对天线罩的强度提高，从而有效提天线罩产品可靠性。本发明的优点是：实施简便、成本相对低廉，利用现有条件，不用增加新的工艺设备，通过对工艺工程的改进，实现对天线罩的强度提高，从而有效提天线罩产品可靠性。

Description

一种陶瓷天线罩提高强度的预增强方法
技术领域
本发明涉及一种陶瓷天线罩提高强度的方法，特别是一种陶瓷天线罩提高强度的预增强方法。
背景技术
陶瓷天线罩具有耐烧蚀、电气性能优良、工艺稳定等特点。陶瓷为多孔材料，为了提高陶瓷天线罩的承载能力，陶瓷天线罩普遍采用有机硅溶液进行罩体增强，提高石英陶瓷罩体材料抗弯强度。目前陶瓷天线罩常用的增强方法为将陶瓷罩体倒置在工装上，将增强液倒进倒置的罩体内，静置1小时后将增强液抽出，放置晾干。主要的增强过程是依靠增强液本身的液体重力与压力将增强液浸入陶瓷罩体。但是陶瓷罩体并不是增强液浸入的越多越好，当浸入的厚度太大时，虽然抗弯强度加大了，但是陶瓷罩体本身的抗热冲击能力会下降。所以如何控制增强液浸入厚度，达到抗弯强度与抗热冲击能力的最佳匹配。
发明内容
本发明的目的在于提供一种陶瓷天线罩提高强度的预增强方法，解决了增强液浸入过多从而降低陶瓷天线罩体抗热冲击能力下降的问题。
为解决上述技术问题，本发明提供的技术方案是：一种陶瓷天线罩提高强度的预增强方法的具体步骤为：
第一步天线罩罩体内壁一次短时增强；
第二步将天线罩内壁增强液晾干；
第三步天线罩外壁做外防潮涂层；
第四步烘干；
第五步天线罩罩体内壁再进行增强液浸泡；
第六步增强液固化烘干。
本发明实现了以下显著的有益效果：
实施简便，通过天线罩预增强的方法，有效提高了天线罩的抗热冲击性能，在产品地面热强度试验考核过程中，有效地提高了产品通过地面试验考核的能力，从而保证了天线罩产品的可靠性能。
附图说明
图1为本发明的陶瓷天线罩提高强度的预增强方法的流程图。
具体实施方式
以下结合附图和具体实施例对本发明作进一步详细说明，根据下面说明和权利要求书，本发明的优点和特征将更清楚。需要说明的是，附图均采用非常简化的形式且均适用非精准的比例，仅用以方便、明晰地辅助说明本发明实施例的目的。
需要说明的是，为了清楚地说明本发明的内容，本发明特举多个实施例以进一步阐释本发明的不同实现方式，其中，该多个实施例是列举式而非穷举式。此外，为了说明的简洁，前实施例中已提及的内容往往在后实施例中予以省略，因此，后实施例中未提及的内容可相应参考前实施例。
虽然该发明可以以多种形式的修改和替换来扩展，说明书中也列出了一些具体的实施图例并进行详细阐述。应当理解的是，发明者的出发点不是将该发明限于所阐述的特定实施例，正相反，发明者的出发点在于保护所有给予由本权利声明定义的精神或范围内进行的改进、等效替换和修改。同样的元器件号码可能被用于所有附图以代表相同的或类似的部分。
请参照图1，本发明的一种陶瓷天线罩提高强度的预增强方法，其具体步骤为：
第一步天线罩内壁均匀短时增强
将天线罩倒置在专用工装上，底端朝上，将增强液倒进天线罩内腔，当液面覆盖住天线罩内壁后，将增强液抽出。
第二步静置晾干
将抽完增强液的天线罩静置晾干。
第三步天线罩外表面喷涂防潮涂层
天线罩表面喷涂防潮涂层。
第四步烘干
喷涂完天线罩外防潮涂层后，进入烘箱，120℃保持4小时。
第五步天线罩内壁再次增强
烘干后，将天线罩再次倒置在工装上，内腔倒入增强液，保持半小时，再将增强液抽出。
第六步固化烘干
增强液固化两天后，再次放入烘箱，120℃保持4小时。
至此陶瓷天线罩提高强度的预增强方法。
实施例2
一种陶瓷天线罩提高强度的预增强方法，其具体步骤为：
第一步天线罩内壁均匀短时增强
将天线罩倒置在专用工装上，底端朝上，将增强液倒进天线罩内腔，当液面覆盖住天线罩内壁后，将增强液抽出。
第二步静置晾干
将抽完增强液的天线罩静置晾干。
第三步天线罩外表面喷涂防潮涂层
天线罩表面喷涂防潮涂层。
第四步烘干
喷涂完天线罩外防潮涂层后，进入烘箱，121℃保持3.5小时。
第五步天线罩内壁再次增强
烘干后，将天线罩再次倒置在工装上，内腔倒入增强液，保持半小时，再将增强液抽出。
第六步固化烘干
增强液固化两天后，再次放入烘箱，121℃保持3.5小时。
实施例3
一种陶瓷天线罩提高强度的预增强方法，其具体步骤为：
第一步天线罩内壁均匀短时增强
将天线罩倒置在专用工装上，底端朝上，将增强液倒进天线罩内腔，当液面覆盖住天线罩内壁后，将增强液抽出。
第二步静置晾干
将抽完增强液的天线罩静置晾干。
第三步天线罩外表面喷涂防潮涂层
天线罩表面喷涂防潮涂层。
第四步烘干
喷涂完天线罩外防潮涂层后，进入烘箱，118℃保持4.5小时。
第五步天线罩内壁再次增强
烘干后，将天线罩再次倒置在工装上，内腔倒入增强液，保持半小时，再将增强液抽出。
第六步固化烘干
增强液固化两天后，再次放入烘箱，118℃保持4.5小时。
本发明实现了以下显著的有益效果：
实施简便，通过天线罩预增强的方法，有效提高了天线罩的抗热冲击性能，在产品地面热强度试验考核过程中，有效地提高了产品通过地面试验考核的能力，从而保证了天线罩产品的可靠性能。
根据本发明技术方案和构思，还可以有其他任何合适的改动。对于本领域普通技术人员来说，所有这些替换、调整和改进都应属于本发明所附权利要求的保护范围。

Claims (9)

1.一种陶瓷天线罩提高强度的预增强方法，其特征在于，包括：
第一步 天线罩罩体内壁一次短时增强；
第二步 将天线罩内壁增强液晾干；
第三步 天线罩外壁做外防潮涂层；
第四步 烘干；
第五步 天线罩罩体内壁再进行增强液浸泡；
第六步 增强液固化烘干。
2.根据权利要求1所述的陶瓷天线罩提高强度的预增强方法，其特征在于，所述天线罩罩体内壁一次短时增强包括：将天线罩内壁先均匀涂刷增强液一遍。
3.根据权利要求1所述的陶瓷天线罩提高强度的预增强方法，其特征在于，所述将天线罩内壁增强液晾干包括：内壁刷涂完增强液后静置晾干。
4.根据权利要求1所述的陶瓷天线罩提高强度的预增强方法，其特征在于，所述天线罩外壁做外防潮涂层包括：天线罩外壁喷涂防潮涂层。
5.根据权利要求1所述的陶瓷天线罩提高强度的预增强方法，其特征在于，所述烘干包括：天线罩进入烘箱进行烘干。
6.根据权利要求1所述的陶瓷天线罩提高强度的预增强方法，其特征在于，所述增强液固化烘干包括：等增强液固化后，进入烘箱烘干。
7.根据权利要求1所述的陶瓷天线罩提高强度的预增强方法，其特征在于，所述天线罩进入烘箱进行烘干包括：进入烘箱，120℃保持4小时。
8.根据权利要求1所述的陶瓷天线罩提高强度的预增强方法，其特征在于，所述天线罩罩体内壁再进行增强液浸泡包括：将天线罩再次倒置在工装上，内腔倒入增强液，保持半小时，再将增强液抽出。
9.据权利要求1所述的陶瓷天线罩提高强度的预增强方法，其特征在于，所述增强液固化烘干包括：增强液固化两天后，再次放入烘箱，120℃保持4小时。
CN201811432055.4A 2018-11-28 2018-11-28 一种陶瓷天线罩提高强度的预增强方法 Active CN109560381B (zh)