CN108821796A - Color decoration technology on a kind of ceramic glaze - Google Patents
Color decoration technology on a kind of ceramic glaze Download PDFInfo
- Publication number
- CN108821796A CN108821796A CN201810649610.2A CN201810649610A CN108821796A CN 108821796 A CN108821796 A CN 108821796A CN 201810649610 A CN201810649610 A CN 201810649610A CN 108821796 A CN108821796 A CN 108821796A
- Authority
- CN
- China
- Prior art keywords
- finished product
- semi
- time
- dried
- color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses decoration technologies color on a kind of ceramic glaze, it is comprised the following steps：One, on burned pottery, one layer of oiliness overglaze color pigment is smeared, and it is half-dried to dry in the air, the half-dried process time that dries in the air is 10-16 hours, and semi-finished product are made, and forms oil colour layer on the outer surface of semi-finished product at this time；Two, on semi-finished product, with writing brush, hairbrush or other painting tools, the oil colour layer being coated on pottery is smeared out, required pattern is drawn；Three, it is dried, flash-off time is one day or a couple of days；Four, kiln-firing is fired 4-6 hours under 780 DEG C of -830 DEG C of environment, and after soaking time 10-20 minutes, natural cooling is come out of the stove, finished product；Color decoration technology on a kind of ceramic glaze of the present invention, technique is unique, and pattern and color can be with changeable multiplicity.
Description
Technical field
The present invention relates to ceramic glazing technical fields, and in particular to color decoration technology on a kind of ceramic glaze.
Background technique
Porcelain is that one kind is made of porcelain stone, kaolin etc., and outer top application has the sundries of glaze or colored drawing.The forming of porcelain will pass through
Pass through high temperature in kiln（About 1280 DEG C -1400 DEG C）Fire, come across Shang dynasty middle and advanced stage earliest, the glaze colours on porcelain surface can because
The difference of temperature is to occur various chemical changes.The porcelain tire of sintering generally contain only 3% less than ferro element, and it is waterproof, because
The common people of its more cheap cost and wear-resisting fluid-tight characteristic widely all over the world are used.The high porcelain of raw material degree of purity
Device can issue the clear and melodious sound of metalloid collision in mutual collision.Advanced porcelain possesses the production much higher than general porcelain
Technology difficulty, therefore also it is no lack of the collection of exquisite porcelain in imperial family in ancient times.
Glazing is exactly so-called in fire porcelain, should fire blank first, glazing is taken out after burned, is then reburned
A kind of mode.It is applied on the blank baked and is covered with one layer of vitreous glaze layer, primarily serve protection and decorative effect.Tradition
Glazing method be that Freehandhand-drawing is carried out after the completion of blank biscuiting, pattern obtained and color fidelity be not high, and is difficult to changeable.
Summary of the invention
In view of the defects and deficiencies of the prior art, the present invention intends to provide decoration technologies color on a kind of ceramic glaze.
To achieve the above object, the technical solution adopted by the present invention is that：It is comprised the following steps：
One, on burned pottery, one layer of oiliness overglaze color pigment is smeared, and it is half-dried to dry in the air, the half-dried process time that dries in the air is 10-
16 hours, semi-finished product are made, form oil colour layer on the outer surface of semi-finished product at this time；
Two, on semi-finished product, with writing brush, hairbrush or other painting tools, the oil colour layer being coated on pottery is smeared out,
Draw required pattern；
Three, it is dried, flash-off time is one day or a couple of days；
Four, kiln-firing is fired 4-6 hours under 780 DEG C of -830 DEG C of environment, after soaking time 10-20 minutes, natural cooling,
It comes out of the stove, finished product.
After adopting the above scheme, the present invention has the beneficial effect that：Color decoration technology, work on a kind of ceramic glaze of the present invention
Skill is unique, and pattern and color can be with changeable multiplicity.
Specific embodiment
The present invention is further illustrated below.
Embodiment:Color decoration technology on a kind of ceramic glaze, it is comprised the following steps：
One, on burned pottery, one layer of oiliness overglaze color pigment is smeared, and it is half-dried to dry in the air, the half-dried process time that dries in the air is 14
Hour, semi-finished product are made, form oil colour layer on the outer surface of semi-finished product at this time；
Two, on semi-finished product, with writing brush, hairbrush or other painting tools, the oil colour layer being coated on pottery is smeared out,
Draw required pattern；
Three, it is dried, flash-off time is one day or a couple of days；
Four, kiln-firing is fired 5 hours under 780 DEG C of -830 DEG C of environment, and soaking time after twenty minutes, come out of the stove by natural cooling,
Finished product.
Porcelain floral disc made from the scheme of the present embodiment, technique is unique and simple, beautiful and generous.
The above is merely illustrative of the technical solution of the present invention, rather than limits those of ordinary skill in the art to this hair
The other modifications or equivalent replacement that bright technical solution is made, as long as it does not depart from the spirit and scope of the technical scheme of the present invention,
It is intended to be within the scope of the claims of the invention.
Claims (1)
1. color decoration technology on a kind of ceramic glaze, it is characterised in that it is comprised the following steps：
One, on burned pottery, one layer of oiliness overglaze color pigment is smeared, and it is half-dried to dry in the air, the half-dried process time that dries in the air is 10-
16 hours, semi-finished product are made, form oil colour layer on the outer surface of semi-finished product at this time；
Two, on semi-finished product, with writing brush, hairbrush or other painting tools, the oil colour layer being coated on pottery is smeared out,
Draw required pattern；
Three, it is dried, flash-off time is one day or a couple of days；
Four, kiln-firing is fired 4-6 hours under 780 DEG C of -830 DEG C of environment, after soaking time 10-20 minutes, natural cooling,
It comes out of the stove, finished product.