CN107940956A - A kind of rare earth zinc steel strand wires electricity consumption heating, drying case - Google Patents
A kind of rare earth zinc steel strand wires electricity consumption heating, drying case Download PDFInfo
- Publication number
- CN107940956A CN107940956A CN201711384866.7A CN201711384866A CN107940956A CN 107940956 A CN107940956 A CN 107940956A CN 201711384866 A CN201711384866 A CN 201711384866A CN 107940956 A CN107940956 A CN 107940956A
- Authority
- CN
- China
- Prior art keywords
- drying
- rare earth
- strand wires
- steel strand
- heating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of rare earth zinc steel strand wires electricity consumption heating, drying case, including drying cabinet frame, drying babinet is equipped with the drying cabinet frame, drying babinet includes upper box and lower box, the upper box is erected on lower box and forms an empty slot, equidistant in length and breadth on the bottom plate in empty slot to be equipped with 4 × 4 pieces of heating plates；Temperature thermocouple is installed on the side plate of empty slot side, the penetration pipe passed through for rare earth zinc steel strand wires is transversely provided with the middle part of upper box, the both ends of penetration pipe are stretched to drying cabinet frame extension；Heating plate connects electric cabinet by power cord, and electric cabinet is connected by power cord with temperature thermocouple.The present invention solves existing production technology when producing diameter 3.00mm above steel wires, the moisture of steel wire surface, drying effect can be reached by zinc liquid surface temperature during the self-contained temperature of steel wire and follow-up cabling, cause steel wire to immerse quick-fried zinc phenomenon caused by zinc liquid.
Description
Technical field
The present invention relates to the manufacture field of rare earth zinc steel strand wires, and in particular to a kind of rare earth zinc steel strand wires electricity consumption heating, drying
Case.
Background technology
Wire galvanization process is consecutive production mode, first to bright steel wire carry out oil removing → washing → acid pickling and rust removing →
Plating coating → drying → leaching zinc cylinder galvanizing → charcoal is cleaned → helps to smear and wipe → zinc-coated wire take-up → and tie up → inspection → and be put in storage.
When steel wire is after ammonium chloride quickening liquid trough pool, drying and processing is carried out to steel wire using the temperature that zinc cylinder surfaces distribute,
To entrance zinc cylinder galvanizing by dipping program.
Problems and disadvantages existing in the prior art：
Due to the difference of product specification, it is desirable to upper zinc amount it is different, galvanizing time and take-up speed are naturally different.It is existing
Ammonium chloride solution temperature（90 DEG C of ＞）When producing diameter 3.00mm above steel wires, the moisture of steel wire surface carrying, is to pass through steel
Zinc liquid surface temperature carries out oven-dried condition to steel wire during the self-contained temperature of silk and follow-up cabling, due to not reaching drying
Temperature, the moisture that steel wire surface carries can not be dried thoroughly, and quick-fried zinc phenomenon is produced when immersing zinc liquid, and quick-fried zinc can cause zinc liquid to fly
Splash, when increase zinc loss, second, being also a kind of hidden danger to operating personnel's personal safety.
The content of the invention
In order to overcome the deficiencies in the prior art, there is provided the rare earth zinc steel strand wires electricity consumption of a kind of heat block, good heat insulation
Heating, drying case.
To achieve the above object, the invention discloses a kind of rare earth zinc steel strand wires electricity consumption heating, drying case, including drying baker
Frame, the drying cabinet frame is interior to be equipped with drying babinet, and drying babinet includes upper box and lower box, and the upper box is set up
On lower box and an empty slot is formed, it is equidistant in length and breadth on the bottom plate in empty slot to be equipped with 4 × 4 pieces of heating plates；Empty slot side
Temperature thermocouple is installed on side plate, the penetration pipe passed through for rare earth zinc steel strand wires is transversely provided with the middle part of upper box, is worn
Stretched to drying cabinet frame extension at the both ends of spool；Heating plate connects electric cabinet by power cord, and electric cabinet is by power cord with surveying
Warm galvanic couple is connected.
Preferably, the binding post to connect with power cord is installed in the heating plate.
Preferably, the electric cabinet be equipped with main power air switch, earth leakage circuit-breaker, heating plate power switch,
Temperature display and Automatic Temperature Control.
Preferably, heat-preservation cotton sealing is laid with the upper box.
Preferably, the bottom of the lower box is laid with heat-preservation cotton.
The beneficial effects of the present invention are：
Compared with prior art, this electrical heating drying baker technical solution has the following advantages：According to product specification, upper zinc amount, leaching
Zinc time and the difference of take-up speed, carry in existing ammonium chloride solution temperature in production diameter 3.00mm above steel wire surface
Water regime, heats steel strand wires using automatic temperature-adjusting control drying baker, ensure that the moisture of various specifications steel wire surface is thorough
Drying, zinc liquid splashes caused by quick-fried zinc phenomenon will not occur for into rare earth zinc liquid when, effectively controls the loss of zinc, operating personnel
Safety in production environment strengthened.Existing production technology is solved when producing diameter 3.00mm above steel wires, steel wire
The moisture on surface, can reach drying by zinc liquid surface temperature during the self-contained temperature of steel wire and follow-up cabling
Effect, causes steel wire to immerse quick-fried zinc phenomenon caused by zinc liquid.
Brief description of the drawings
Fig. 1 is the structure diagram of the present invention.
Embodiment
Below in conjunction with the accompanying drawings and specific embodiment, the present invention is furture elucidated, it should be understood that these embodiments are merely to illustrate
The present invention rather than limit the scope of the invention, after the present invention has been read, those skilled in the art are to of the invention each
The modification of kind equivalent form falls within the application appended claims limited range.
As shown in Figure 1, the present invention provides a kind of rare earth zinc steel strand wires electricity consumption heating, drying case, including drying cabinet frame 1, institute
Drying babinet is equipped with the drying cabinet frame stated, drying babinet includes upper box 2 and lower box 3, and the upper box 2 is erected at down
On babinet 3 and an empty slot 4 is formed, it is equidistant in length and breadth on the bottom plate in empty slot 4 to be equipped with 4 × 4 pieces of heating plates 5；4 side of empty slot
Temperature thermocouple 6 is installed on side plate, the penetration pipe 7 passed through for rare earth zinc steel strand wires is transversely provided with the middle part of upper box,
Stretched to drying cabinet frame extension at the both ends of penetration pipe；Heating plate by power cord connect electric cabinet 8, electric cabinet by power cord with
Temperature thermocouple is connected.
The binding post 9 to connect with power cord is installed in the heating plate, and is connected by binding post by power cord
Electric cabinet 8.
The electric cabinet is equipped with main power air switch 81, earth leakage circuit-breaker 82, heating plate power switch 83, temperature
Display screen 84 and Automatic Temperature Control 85 are spent, corresponding control is made to the drying baker by each switch.
In order to further improve heat insulation effect, heat-preservation cotton sealing 10 is laid with upper box, the bottom of lower box is laid with insulation
Cotton 11.
The principle of the present invention is：
The electrical heating drying baker is seated in ammonium chloride and helps plating trough pool outlet side, the self-service plating trough pool outlet of steel wire, and steel strand wires enter
The penetration pipe of drying baker, drying baker starts to carry out it heating, drying, and is shown in temperature display by temperature thermocouple thermometric
On, dry and complete after a period of time, rare earth zinc is plated into rare earth zinc cylinder.
The above is only the preferred embodiment of the present invention, it is noted that is come for those of ordinary skill in the art
Say, without departing from the principle of the present invention, some variations and modifications can also be made, these also should be regarded as belonging to the present invention
Protection domain.
Claims (5)
1. a kind of rare earth zinc steel strand wires electricity consumption heating, drying case, it is characterised in that including drying cabinet frame, the drying box-frame
It is equipped with drying babinet in frame, drying babinet includes upper box and lower box, and the upper box is erected on lower box and forms one
A empty slot, it is equidistant in length and breadth on the bottom plate in empty slot to be equipped with 4 × 4 pieces of heating plates；Thermometric heat is installed on the side plate of empty slot side
Galvanic couple, is transversely provided with the penetration pipe passed through for rare earth zinc steel strand wires in the middle part of upper box, and the both ends of penetration pipe are to drying baker
Extend outside frame；Heating plate connects electric cabinet by power cord, and electric cabinet is connected by power cord with temperature thermocouple.
2. rare earth zinc steel strand wires electricity consumption heating, drying case according to claim 1, it is characterised in that：In the heating plate
The binding post to connect with power cord is installed.
3. rare earth zinc steel strand wires electricity consumption heating, drying case according to claim 1, it is characterised in that：On the electric cabinet
Equipped with main power air switch, earth leakage circuit-breaker, heating plate power switch, temperature display and Automatic Temperature Control.
4. rare earth zinc steel strand wires electricity consumption heating, drying case according to claim 1, it is characterised in that：In the upper box
It is laid with heat-preservation cotton sealing.
5. rare earth zinc steel strand wires electricity consumption heating, drying case according to claim 1, it is characterised in that：The lower box
Bottom is laid with heat-preservation cotton.