CN107903593A - 一种环保工程塑料 - Google Patents
一种环保工程塑料 Download PDFInfo
- Publication number
- CN107903593A CN107903593A CN201711410783.0A CN201711410783A CN107903593A CN 107903593 A CN107903593 A CN 107903593A CN 201711410783 A CN201711410783 A CN 201711410783A CN 107903593 A CN107903593 A CN 107903593A
- Authority
- CN
- China
- Prior art keywords
- environment
- engineering plastics
- friendly engineering
- starch
- sodium citrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保工程塑料，涉及工程塑料技术领域，由以下成分制成：聚对苯二甲酸乙二醇脂、变性淀粉、矿粉、聚丙烯、硬脂酸、玻璃纤维、纳米二氧化钛、聚氨基甲酸乙酯树脂、硫代氯甲酸‑S‑异丙酯、柠檬酸钠改性凹凸棒土、钛酸钾晶须、增塑剂；本发明一种环保工程塑料，通过各成分之间的协同作用，使得制备的环保工程塑料具有高冲击性能；本发明的一种环保工程塑料采用了PET为基材，通过添加变性淀粉的作用，改善了保护塑料的耐热性。
Description
技术领域
本发明属于工程塑料技术领域，具体涉及一种环保工程塑料。
背景技术
聚对苯二甲酸乙二醇酯(简称PET)是当今产量最大的热塑性聚酯，主要应用于纺织纤维领域。PET树脂韧性较强，耐摩擦、刚性高、硬度大、尺寸稳定性好、并且具有原料成本低，耐热性好、在较宽的温度范围内能保持优良的物理机械性能，对大多数有机溶剂和无机酸稳定的特点。但由于PET存在抗冲击强度低的缺点，在工程塑料领域应用受限。
发明内容
本发明的目的是针对现有的问题，提供了一种环保工程塑料。
本发明是通过以下技术方案实现的：
一种环保工程塑料，按重量份计由以下成分制成：聚对苯二甲酸乙二醇脂80-85、变性淀粉10-14、矿粉1-3、聚丙烯10-18、硬脂酸1.2-1.8、玻璃纤维1.5-1.8、纳米二氧化钛0.3-0.5、聚氨基甲酸乙酯树脂2.5-3.0、硫代氯甲酸-S-异丙酯1-3、柠檬酸钠改性凹凸棒土10-15、钛酸钾晶须1.35-1.38、增塑剂0.22-0.42。
进一步的，所述变性淀粉制备方法为：将淀粉采用质量分数为2.8%的乙醇溶液在90℃下浸泡20min，然后进行过滤，烘干至恒重，再采用800W微波处理11s，即得。
进一步的，所述淀粉为木薯淀粉。
进一步的，所述玻璃纤维直径为20μm。
进一步的，所述纳米二氧化钛粒度为95nm。
进一步的，所述柠檬酸钠改性凹凸棒土制备方法为：将凹凸棒土采用800W微波处理20s，然后添加到质量分数为10%的柠檬酸钠溶液中在78℃下浸泡2小时，然后，过滤，烘干至恒重，过1250目筛，即得。
进一步的，所述增塑剂为邻苯二甲酸二丁酯。
本发明相比现有技术具有以下优点：本发明一种环保工程塑料，通过各成分之间的协同作用，使得制备的环保工程塑料具有高冲击性能；本发明的一种环保工程塑料采用了PET为基材，通过添加变性淀粉的作用，改善了保护塑料的耐热性；经检测，本发明制备的环保工程塑料悬臂梁缺口冲击强度（GB/T1843-2008）为49kJ/m2，扯断拉伸强度（GB/T1040.2-2006）为42MPa，极限伸长率（GB/T1040.2-2006）为380%。热变形温度（GB/T1634.1/2-2004）130℃。
具体实施方式
实施例1
一种环保工程塑料，按重量份计由以下成分制成：聚对苯二甲酸乙二醇脂80、变性淀粉10、矿粉1、聚丙烯10、硬脂酸1.2、玻璃纤维1.5、纳米二氧化钛0.3、聚氨基甲酸乙酯树脂2.5、硫代氯甲酸-S-异丙酯1、柠檬酸钠改性凹凸棒土10、钛酸钾晶须1.35、增塑剂0.22。
进一步的，所述变性淀粉制备方法为：将淀粉采用质量分数为2.8%的乙醇溶液在90℃下浸泡20min，然后进行过滤，烘干至恒重，再采用800W微波处理11s，即得。
进一步的，所述淀粉为木薯淀粉。
进一步的，所述玻璃纤维直径为20μm。
进一步的，所述纳米二氧化钛粒度为95nm。
进一步的，所述柠檬酸钠改性凹凸棒土制备方法为：将凹凸棒土采用800W微波处理20s，然后添加到质量分数为10%的柠檬酸钠溶液中在78℃下浸泡2小时，然后，过滤，烘干至恒重，过1250目筛，即得。
进一步的，所述增塑剂为邻苯二甲酸二丁酯。
实施例2
一种环保工程塑料，按重量份计由以下成分制成：聚对苯二甲酸乙二醇脂85、变性淀粉14、矿粉3、聚丙烯18、硬脂酸1.8、玻璃纤维1.8、纳米二氧化钛0.5、聚氨基甲酸乙酯树脂3.0、硫代氯甲酸-S-异丙酯3、柠檬酸钠改性凹凸棒土15、钛酸钾晶须1.38、增塑剂0.42。
进一步的，所述变性淀粉制备方法为：将淀粉采用质量分数为2.8%的乙醇溶液在90℃下浸泡20min，然后进行过滤，烘干至恒重，再采用800W微波处理11s，即得。
进一步的，所述淀粉为木薯淀粉。
进一步的，所述玻璃纤维直径为20μm。
进一步的，所述纳米二氧化钛粒度为95nm。
进一步的，所述柠檬酸钠改性凹凸棒土制备方法为：将凹凸棒土采用800W微波处理20s，然后添加到质量分数为10%的柠檬酸钠溶液中在78℃下浸泡2小时，然后，过滤，烘干至恒重，过1250目筛，即得。
进一步的，所述增塑剂为邻苯二甲酸二丁酯。
实施例3
一种环保工程塑料，按重量份计由以下成分制成：聚对苯二甲酸乙二醇脂82、变性淀粉12、矿粉2、聚丙烯15、硬脂酸1.5、玻璃纤维1.6、纳米二氧化钛0.4、聚氨基甲酸乙酯树脂2.8、硫代氯甲酸-S-异丙酯2、柠檬酸钠改性凹凸棒土12、钛酸钾晶须1.36、增塑剂0.28。
进一步的，所述变性淀粉制备方法为：将淀粉采用质量分数为2.8%的乙醇溶液在90℃下浸泡20min，然后进行过滤，烘干至恒重，再采用800W微波处理11s，即得。
进一步的，所述淀粉为木薯淀粉。
进一步的，所述玻璃纤维直径为20μm。
进一步的，所述纳米二氧化钛粒度为95nm。
进一步的，所述柠檬酸钠改性凹凸棒土制备方法为：将凹凸棒土采用800W微波处理20s，然后添加到质量分数为10%的柠檬酸钠溶液中在78℃下浸泡2小时，然后，过滤，烘干至恒重，过1250目筛，即得。
进一步的，所述增塑剂为邻苯二甲酸二丁酯。
本发明制备的环保工程塑料悬臂梁缺口冲击强度（GB/T1843-2008）为49kJ/m2，扯断拉伸强度（GB/T1040.2-2006）为42MPa，极限伸长率（GB/T1040.2-2006）为380%。热变形温度（GB/T1634.1/2-2004）130℃。
Claims (7)
1.一种环保工程塑料，其特征在于，按重量份计由以下成分制成：聚对苯二甲酸乙二醇脂80-85、变性淀粉10-14、矿粉1-3、聚丙烯10-18、硬脂酸1.2-1.8、玻璃纤维1.5-1.8、纳米二氧化钛0.3-0.5、聚氨基甲酸乙酯树脂2.5-3.0、硫代氯甲酸-S-异丙酯1-3、柠檬酸钠改性凹凸棒土10-15、钛酸钾晶须1.35-1.38、增塑剂0.22-0.42。
2.如权利要求1所述的一种环保工程塑料，其特征在于，所述变性淀粉制备方法为：将淀粉采用质量分数为2.8%的乙醇溶液在90℃下浸泡20min，然后进行过滤，烘干至恒重，再采用800W微波处理11s，即得。
3.如权利要求2所述的一种环保工程塑料，其特征在于，所述淀粉为木薯淀粉。
4.如权利要求1所述的一种环保工程塑料，其特征在于，所述玻璃纤维直径为20μm。
5.如权利要求1所述的一种环保工程塑料，其特征在于，所述纳米二氧化钛粒度为95nm。
6.如权利要求1所述的一种环保工程塑料，其特征在于，所述柠檬酸钠改性凹凸棒土制备方法为：将凹凸棒土采用800W微波处理20s，然后添加到质量分数为10%的柠檬酸钠溶液中在78℃下浸泡2小时，然后，过滤，烘干至恒重，过1250目筛，即得。
7.如权利要求1所述的一种环保工程塑料，其特征在于，所述增塑剂为邻苯二甲酸二丁酯。